Abstract: The present invention relates to a heterophasic polypropylene resin comprising a propylene homo- or copolymer matrix (A) and an ethylene-propylene rubber phase (B) dispersed within the matrix, wherein the heterophasic polypropylene resin has a fraction insoluble in p-xylene at 25° C. (XCU) with an intrinsic viscosity of 1.5 dl/g or less, determined according to DIN EN ISO 1628-1 and -3 and an amount of propylene monomer units of at least 95 mol %, and a fraction soluble in p-xylene at 25° C. (XCS) with an intrinsic viscosity of 1.5 to 3.0 dl/g, determined according to DIN EN ISO 1628-1 and -3, and an amount of propylene monomer units of 50 to 75 mol %, and a MFR (2.16 kg, 230° C.) of more than 100 g/10 min, determined according to ISO 1133, a heterophasic polypropylene composition comprising such a resin, a process for preparing that resin, and an article made thereof.

Abstract: The present invention relates to a capacitor film comprising a biaxially oriented polypropylene wherein a) said polypropylene has a draw ratio in machine direction of at least 4.0 and a draw ratio in transverse direction of at least 4.0, and b) said polypropylene has an electrical breakdown strength EB63% according to IEC 60243-part 1 (1988) of at least 300 kV/mm at a draw ratio in machine direction and in transverse direction of 4.0.

Abstract: The present invention provides a semiconductive polymer composition having (a) from 30 to 90 wt % of a polymer component, (b) from 10 to 60 wt % of carbon black and (c) from 0 to 8 wt % additives, based on the total semiconductive polymer composition, and wherein the composition comprises less than 23 particles per m2 having a width of larger than 150 ?m at the half height of a particle protruding from the surface of the tape sample, less than 10 particles per m2 having a width of larger than 200 ?m at the half height of a particle protruding from the surface of the tape sample, and preferably, about 0 particles per m2 having a width of larger than 500 ?m at the half height of a particle protruding from the surface of the tape sample.

Abstract: The present invention relates to a heterophasic polypropylene resin comprising a polypropylene homo- or copolymer matrix phase (A) and an ethylene-propylene copolymer phase (B) dispersed within the matrix, wherein the heterophasic polypropylene resin has a fraction insoluble in p-xylene (XCU) at 25° C. with an intrinsic viscosity of 2.0 dl/g or less, determined according to DIN EN ISO 1628-1 and -3, and a fraction soluble in p-xylene (XCS) at 25° C. having an intrinsic viscosity of 2.0 to 4.5 dl/g, determined according to DIN EN ISO 1628-1 and -3, and an amount of ethylene monomer units of 60 to 85 mol %, a heterophasic polypropylene composition comprising such a resin, a process for preparing that resin, and an article made thereof.

Abstract: Polyolefin coated steel pipes with high dynamic fracture toughness of the coating of the steel pipes during installation handling and in service, consisting of a steel pipe core, optionally an intermediate foamed plastic material, and a polyolefin coating of ?-nucleated propylene copolymers whereby a test polyolefin pipe fabricated from the ?-nucleated propylene copolymer has a critical pressure of >25 bars and a dynamic fracture toughness >3.5 MNm?3/2. The polyolefin coated steel pipes are suitable for off-shore transport of crude oil or gas products or district heating applications.

Abstract: The present invention relates to novel and unique catalyst particles, a method for preparing same, the use of the catalyst particles for polymerization reactions and methods of controlling the catalyst particle morphology.

Abstract: The application relates to a process for preparing a crosslinked cable, including:—applying one or more layers including a polymer composition on a conductor, wherein at least one layer includes one or more free radical generating agents,—crosslinking by radical reaction said at least one layer comprising said free radical generating agent(s),—cooling the obtained crosslinked cable in pressurized conditions.

Abstract: Industrial polyolefin piping system with improved stiffness, impact strength for use at high service temperature, comprising single or multilayer pipes, fitting, chambers, valves and vessels, consisting of ?-nucleated propylene homopolymers with an IR??0.98 having a tensile modulus ?1500 MPa, a Charpy impact strength, notched, at +23° C.?30 kJ/m2 and a Vicat B temperature >90° C. and a Heat Distortion Temperature >100° C. The industrial polyolefin piping system is suitable for chemical plant constructions comprising single or multilayer pipes, fittings, chambers, valves and vessels with improved stiffness, impact strength and high service temperature, preferred for conveyance of natural gas, dangerous liquids and/or toxic liquids.

Abstract: Single- or multilayer propylene polymer pipes and pipe components for pipelines with improved resistance to rapid crack propagation made from a propylene homopolymer with a melt index of 0.05 to 10 g/10 min at 230° C./2.16 kg or propylene block copolymer from 90.0 to 99.9 wt % of propylene and 0.1 to 10.0 wt % of a ?-olefins with 2 or 4 to 18 carbon atoms with a melt index of 0.05 to 8 g/10 min at 230° C./2.16 kg or mixtures thereof, wherein the propylene homopolymers or propylene block copolymers are ?-nucleated propylene polymers, and the propylene polymer pipes for pipelines made from the ?-nucleated propylene homopolymers have a rapid crack propagation characterized by a critical temperature of ?5 to +40° C. and a critical pressure?3 bar below the critical temperature and the propylene polymer pipes made from ?-nucleated propylene block copolymers have a rapid crack propagation characterized by a critical temperature of ?25 to 0° C. and a critical pressure?3 bar below the critical temperature.

Abstract: The present invention relates to a polymer composition, comprising (i) a polypropylene homopolymer, (ii) a polypropylene random copolymer, prepared by copolymerization of propylene with an olefin comonomer and having an amount of olefin comonomer units of 0.2 to 5 wt %, and (iii) an elastomeric copolymer of propylene and at least one olefin comonomer, the polymer composition having a tensile modulus, determined according to ISO 527-2/1B at 1 mm/min. and 23° C., of at least 1200 MPa.

Abstract: A process for the removal of by-products from a phenolic mixture, which process may include the following steps: subjecting a phenolic mixture to extractive distillation to produce an initial phenolic mixture, contacting the initial phenolic mixture containing phenol and one or more by products with a catalyst to produce a first purified phenol product mixture, and distilling the first purified phenol product mixture to produce a second purified phenol product mixture; wherein the extractive distillation is carried out in two columns, a higher pressure column and a lower pressure column.

Abstract: The invention relates to a colored ?-nucleated polypropylene composition having a high content of ?-modification, wherein the polypropylene composition comprises at least one ?-nucleating agent and an inorganic blue pigment and an inorganic yellow pigment.

Abstract: The present technology relates to a biaxially oriented polypropylene film. The biaxially oriented polypropylene film comprises a polypropylene material having xylene solubles of at least 0.5 percent by weight. The polypropylene also has a strain hardening index of at least 0.15 measured at a deformation rate d?/dt of 1.00 s?1 at a temperature of 180° C. In certain embodiments, the strain hardening index is defined as the slope of a logarithm to the basis 10 of a tensile stress growth function as a function of a logarithm to the basis 10 of a Hencky strain for the range of Hencky strains between 1 and 3.

Abstract: The present invention relates to a pipe or a supplementary pipe article comprising a polyethylene composition comprising a base resin which comprises (A) a first ethylene homo- or copolymer fraction, and (B) a second ethylene homo- or copolymer fraction, wherein fraction (A) has a lower average molecular weight than fraction (B), the base resin has a flexural modulus determined according to ISO 178 of 1000 MPa or higher, and the composition further comprises (C) an inorganic mineral filler, wherein inorganic mineral filler (C) is present in the composition in an amount of 1 to 70 wt. %, and to the use of said composition for the production of a pipe or a supplementary pipe article.

Abstract: The present invention relates to a polyethylene composition comprising a base resin which comprises (a) an ethylene homo- or copolymer fraction (A); and (b) an ethylene homo- or copolymer fraction (B), wherein (i) fraction (A) has a lower average molecular weight than fraction (B); (ii) the base resin has a density of 940 to 947 kg/m3; (iii) the polyethylene composition has an MFR5 of 0.1 to 0.5 g/10 min; and (iv) the polyethylene composition has an SHI(2.7/210) of 10 to 49. Furthermore, the present invention relates to an article, preferably a pipe comprising said composition and to the use of said composition for the production of an article, preferably a pipe.

Abstract: Coated pipes have a layer of multimodal polyethylene. The multimodal ethylene copolymer is a copolymer of ethylene with one or more alpha-olefin comonomers having from 4 to 10 carbon atoms and has a weight average molecular weight of from 70000 g/mol to 250000 g/mol, the ratio of the weight average molecular weight to the number average molecular weight, Mw/Mn, of from 15 to 50, a melt index MFR2 of from 0.05 g/10 min to 5 g/10 min, a melt index MFR5 of from 0.5 to 10 g/10 min and a density of from 930 kg/m3 to 955 kg/m3.

Abstract: Catalyst in form of solid particles, wherein the particles—have a specific surface area of less than 20 m2/g, comprise a transition metal compound which is selected from one of the groups 4 to 10 of the periodic table (IUPAC) or a compound of actinide or lanthanide, comprise a metal compound which is selected from one of the groups 1 to 3 of the periodic table (IUPAC), and—comprise solid material, wherein the solid material does not comprise catalytically active sites, has a specific surface area below 500 m2/g, and has a mean particle size below 100.

Abstract: The invention relates to a reactor system and process for the catalytic polymerization of olefin monomer and optionally comonomer(s), having one or more inlets for olefin monomer, catalyst, optionally for comonomer, chain growth controllers or chain transfer agents, and/or inert gas, an outlet for gas and an outlet for polymerized particles. The reactor system has at least one fluidized bed unit and at least one moving bed unit, wherein the fluidized bed unit has means for maintaining a fluidized bed in the fluidized bed unit and wherein the moving bed unit is provided with an inlet and an outlet which are connected to the fluidized bed unit, wherein the outlet of the moving bed unit is provided with means for displacing metered quantities of polymerized particles from the moving bed unit into the fluidized bed unit, and to the use of such reactor system.

Abstract: The invention relates to a polyethylene composition for the production of peroxide crosslinked polyethylene and a method for the production thereof. The invention further relates to the use of such a polymer composition and to a peroxide crosslinked polyethylene pipe made from the polyethylene composition.

Abstract: The present invention relates to a polymer composition comprising a polyolefin base resin comprising (A) a propylene homopolymer with a MWD of 1.5 to 5.0, and (B) an ethylene copolymer with one or more comonomers selected from alphaolefins with 4 to 12 carbon atoms, having a density of not greater than 920 kg/m3 wherein the polyolefin base resin has a weight ratio of propylene homopolymer (A) to ethylene copolymer (B) from 95:5 to 60:40, the use of such a polymer composition for the manufacture of an injection molded article, an article produced from such a polymer composition, an article with a grained surface structure produced from such a polymer composition showing having a scratch resistance, determined as the difference of the luminance ?L at a load of 10 N, of not more than 1 and a gloss at an angle of 60° of not more than 2.8%, and the use of a polymer composition for the production of such an article.