Abstract: Ferritic stainless steel, comprising the following composition by weight: 0%<C≦0.030% 1%≦Si≦3% 0%<Mn≦0.5% 10%≦Cr≦13% 0%<Ni≦0.5% 0%<Mo≦3% N≦0.030% Cu≦0.5% Ti≦0.5% Nb≦1% Ca≧1×10−4% 0≧10×10−4% S≦0.030% P≦0.030% the remainder being iron and the impurities which are inevitable from the production of the steel.

Abstract: Resulfurized stainless steel with high machinability and having an improved corrosion resistance, which includes, in its composition, anorthite- and/or pseudo-wollastonite- and/or gehlenite-type lime aluminosilicate inclusions combined with CrMnS inclusions, the chromium content of which is between 30% and 70%.

Abstract: Ferritic stainless steel, compirsing the following composition by weight:

Abstract: Nickel-based alloy useful for welding, welding method, and welding electrode.

Abstract: Resulfurized stainless steel with high machinability and having an improved corrosion resistance, which includes, in its composition, anorthite- and/or pseudo-wollastonite- and/or gehlenite-type lime aluminosilicate inclusions combined with CrMnS inclusions, the chromium content of which is between 30% and 70%.

Abstract: Composite wire comprising a core made of carbon steel the chemical composition of which consists, by weight, of: 0.15%≦C≦0.6%; 0.1%≦Si≦0.3%; 0.3%≦Mn≦1%; 0% V≦0.3%; the remainder being iron and impurities resulting from processing; and an outer layer made of stainless steel the composition of which consists, by weight, of 0.005%≦C≦0.05%; 0.005%≦N≦0.05%; 0.1%≦Si≦2%; 0.1%≦Mn≦5%; 5%≦Ni≦12%; 10%≦Cr ≦20%; 0%≦Mo≦3%; 0%≦Cu≦4%; the remainder being iron and impurities resulting from processing. The diameter of the wire is less than 1 mm and the tensile strength of the wire is in excess of 2000 MPa.

Abstract: The invention concerns the adjustment of the linear distribution of an injected shearing fluid, during casting, through a slot (20) provided in the cooled metal body (1)—refractory riser block (14) interface of an ingot mold for continuous metal casting charge and emerging along said ingot inner periphery, the latter being provided with clamping means for adjusting the slot thickness. The invention is characterized in that it consists in “cold” injecting through said slot (20) a regulating inflammable fluid, which is ignited on its exit from the slot, and in acting on the clamping means (25, 26, 28, 29) such that the height of the flames (39) coming out of the slot (20) is substantially constant along the whole ingot inner periphery. The invention provides the advantage of an accurate and lasting adjustment of the injected flow rate without requiring the adjustment of the injection slot thickness. The invention is applicable to continuous steel charge casting in particular.

Abstract: Corrosion-resistant low-nickel austenitic stainless steel having the following compostion in percentages by weight: 0.01%<carbon<0.08%, 0.1%<silicon<1%, 5%<manganese<11%, 15%<chromium<17.5%, 1%<nickel<4%, 1%<copper<4%, 1×10−4%<sulfur<20×10−4%, 1×10−4%<calcium<50×10−4%, 0%<aluminum<0.03%, 0.005%<phosphorus<0.1%, boron<5×10−4%, oxygen<0.01%, the balance being iron and impurities resulting from the smelting operation.

Abstract: The continuous casting installation includes an ingot mould the walls (1) of which are formed by cooled metal walls (2) surmounted by a hot-top element (3) made of a heat insulating material. Holes for injecting a gas under pressure, such as a slot (10), lead into the ingot mould at least at the interface between the hot-top element and the metal wall. The insulation includes means (13 to 17), connected to the said holes, for supplying a gas or a gaseous mix with a thermal expansion capacity adjustable according to the composition of the cast metal alloy and the casting conditions. The adjustment of the thermal expansion capacity of the injected gas enables the adjustment of the heat flux density extracted from the cast metal in the zone where it starts to solidify.

Abstract: A process for producing a foaming slag above a stainless steel melted in an electric furnace, in which: a powder containing at least one metal oxide and carbon in its composition is introduced into the slag, at least one oxide present in the powder is reduced by its reaction with the carbon to form in the slag bubbles composed of the metal of the metal oxide and of carbon monoxide, the bubbles present in the slag giving rise to a slag in the form of a stable foam.

Abstract: Austenitic stainless steel for the production of wire, which can be used in the field of drawing wire down to diameters of less than 0.3 mm and in the field of producing components subjected to fatigue, characterized by the following composition by weight:5.times.10.sup.-3 %.ltoreq.carbon.ltoreq.200.times.10.sup.-3 %5.times.10.sup.-3 %.ltoreq.nitrogen.ltoreq.400.times.10.sup.-3 %0.2%.ltoreq.manganese.ltoreq.10%12%.ltoreq.chromium.ltoreq.23%0.1%.ltoreq.nickel.ltoreq.17%0.1%.ltoreq.silicon.ltoreq.2%,in which the residual elements are controlled so as to obtain inclusions of oxides in the form of a glassy mixture, the proportions by weight of which are as follows:40%.ltoreq.SiO.sub.2 .ltoreq.60%5%.ltoreq.MnO.ltoreq.50%1%.ltoreq.CaO.ltoreq.30%0%.ltoreq.MgO.ltoreq.4%5%.ltoreq.Al.sub.2 O.sub.3 .ltoreq.25%0%.ltoreq.Cr.sub.2 O.sub.3 .ltoreq.4%0%.ltoreq.TiO.sub.2 .ltoreq.4%.

Abstract: Nickel-based alloy, the chemical composition of which comprises, by weight, from 24.5% to 26.5% chromium and from 13.5% to 16.5% molybdenum, the remainder being nickel, optionally one or more complementary alloy elements selected from iron, aluminium and magnesium, and impurities resulting from processing. Drawn wire made of nickel-based alloy, and welding electrode including a drawn wire made of nickel-based alloy.

Abstract: Steel, steel wire, and a process for forming a drawn wire, especially tire-reinforcing wire of diameter smaller than 0.4 mm, by drawing a steel of the following composition by weight: 0.005%.ltoreq.carbon.ltoreq.0.050%; 0.005%.ltoreq.nitrogen.ltoreq.0.050%; 0.1%.ltoreq.silicon.ltoreq.2.0%; 0.1%.ltoreq.manganese.ltoreq.5%; 5%.ltoreq.nickel.ltoreq.12%; 10%.ltoreq.chromium.ltoreq.20%; 0.01%.ltoreq.copper.ltoreq.4%; 0.01%.ltoreq.molybdenum.ltoreq.3%,the base wire being subjected to:drawing to a cumulative deformation ratio .epsilon. of larger than 2 and smaller than 4,an intermediate annealing treatment at above 700.degree. C.final drawing to a cumulative deformation ratio .epsilon. of smaller than 4.5 and larger than 3.