Abstract: The invention relates to a method of producing imide bond-containing resins and flame retardants comprising such resins. The method comprises subjecting a halogenated phthalic anhydride, a specific copolymer and a diamine to dehydration reaction in an inert solvents to give an imide bond-containing resin. The resins provide flammable substances with good fire or flame resistance and at the same time themselves have good heat resistance and weather resistance. Therefore, the flame retardants comprising these resins have a wide field of application.

Abstract: Hexabromocyclododecane may be synthesized at a high yield in pure form by brominating 1,5,9-cyclododecatriene with bromine in a C.sub.4 -C.sub.8 saturated aliphatic alcohol in the presence of a boron trifluoride complex, neutralizing the reaction mixture with a non-aqueous base, and recovering the resulting crystals of hexabromocyclododecane.

Abstract: A granular flame retardant additive is provided comprising from 70 to 99.5% by weight of an organohalide flame retardant and from 0.5 to 30% by weight of thermoplastic synthetic resin as a binder. The additive is easy to handle and resistant to disintegration during transportation and mixing with fabricating resin pellets. Uniform distribution thereof in fabricated thermoplastic articles is achieved by simply co-feeding the granules and the fabricating resin to a fabricating machine.

Abstract: A water-soluble film or sheet made of a polyoxyalkylene compound having an average molecular weight of at least 50,000 produced by linking chains of a polyether having an average molecular weight of at least 3,000 and an oxyethylene unit content of at least 70% by weight with each other through ester linkages by reaction of the polyether and a polycarboxylic acid, its anhydride or its lower alkyl ester. The film or sheet is also soluble in organic solvents and has properties comparable or superior to known water-soluble polymer films or sheets.

Abstract: A process for preparing polyoxyalkylene high molecular weight compounds having an average molecular weight of more than 20,000 and being soluble in solvents and moldable by addition-polymerizing ethylene oxide alone or a mixture of alkylene oxides containing ethylene oxide to an organic compound having at least 2 active hydrogen groups to produce a polyhydroxyl compound having an average molecular weight of not less than 1,000, and esterifying the polyhydroxyl compound with a polycarboxylic acid, its anhydride or its lower alkyl ester.