Abstract: A fluoropolymer gum of 60 to 85 mol percent vinylidene fluoride, 10 to 40 mol percent of hexafluoropropene and 0.15 to 3 mol percent 1-bromo-2,2-difluoroethylene is provided which can be blended with fluorosilicone gum and vulcanized in presence of free-radical initiators to produce elastomeric vulcanizates with desired balance of chemical solvent or fluid resistance, high temperature stability, and low temperature flexibility, coupled with good physical properties such as high tensile strength and elongation.

Abstract: A blend of (a) 90 to 20 parts fluoropolymer gum of 60 to 85 mol percent vinylidene fluoride, 10 to 40 mol percent of hexafluoropropene and 0.15 to 3 mol percent bromine-containing olefin, and (b) 10 to 80 parts fluorosilicone gum is provided which can be vulcanized in presence of free-radical initiators to produce elastomeric vulcanizates with desired balance of chemical solvent or fluid resistance, high temperature stability, and low temperature flexibility.

Abstract: Hollow cellulosic fibers are produced by nitrosating and dissolving a cellulosic material in an aprotic solvent selected from the group consisting of a dialkylacylamide and dimethylsulfoxide and regenerating the dissolved cellulose by contacting the cellulose solution with a regenerant. The regenerant is n-octanol where the solvent is a dialkylacylamide and n-hexanol where the solvent is dimethylsulfoxide. The fibers are hollow as regenerated and require no special spinnerette designs nor special spinning conditions.

Abstract: Shaped cellulosic fibers are produced by nitrosating and dissolving a cellulosic material in an aprotic solvent selected from the group consisting of a dialkylacylamide and dimethylsulfoxide and regenerating the dissolved cellulose by contacting the cellulose solution with a regenerant. The regenerant is butanol, pentanol or benzyl alcohol where the solvent is a dialkylacylamide and propanol, butanol or benzyl alcohol where the solvent is dimethylsulfoxide. The fibers have a generally crenulated shape as regenerated and require no special spinnerette designs nor special spinning conditions.

Abstract: Thermally stable, fluoroelastomeric terpolymers of vinylidene fluoride, hexafluoropropene and chlorotrifluoroethylene in respective mol % composition of 55-70, 25-40 and 1-8 produce vulcanizates with improved fluid resistant properties and low temperature flexibility.