Abstract: A biaxially oriented polypropylene (BOPP) film made from or containing a copolymer of propylene and ethylene having: i) the content of ethylene derived units ranging from 0.5 wt % to 2.2 wt %; ii) a xylene soluble fraction at 25°° C. ranging from 4.3 wt % to 6.5 wt %; and iii) a melt flow rate, MFR, measured according to ISO 1133-1:2012 at 230° C. with a load of 2.16 kg, ranging from 0.5 g/10 min to 7.0 g/10 min.

Abstract: A prepolymerized catalyst component for the polymerization of olefins made from or containing (i) a solid catalyst component made from or containing Ti, Mg, and an internal donor mixture (IDM) made from or containing (a) from 15 to 75% of 1,3-diethers and (b) from 25 to 85% of succinates based on the total amount of 1,3-diethers and succinates, and (ii) an amount of an ethylene polymer ranging from 0.1 up to 3 g per g of the solid catalyst component (i), wherein the prepolymerized catalyst component has an intrinsic viscosity [?] in tetraline at 135° C. ranging from 2.5 to 5.20 dl/g.

Abstract: A propylene ethylene copolymer having the following features: an ethylene content of between 1.0 and 4.0% by weight; a molecular weight distribution (MWD), expressed in terms of Mw/Mn, of greater than 4.0; a content of xylene soluble fraction (XS) and ethylene content (C2) that fulfills the following relationship: (C2×1.1)+1.25<XS<(C2×1.1)+2.50 where: XS=% by weight of the fraction soluble in xylene at 25° C.; C2=% by weight of ethylene units in the copolymer determined via NMR; a melt flow rate (MFR; 230° C., 2.16 kg) of between 30 to 75 g/10 min; an intrinsic viscosity of the copolymer of lower than 1.5 dl/g; and an intrinsic viscosity of the fraction soluble in xylene at 25° C. of higher than 0.32 dl/g.

Abstract: A process for preparing a catalyst component made from or containing Mg, Ti, and at least an electron donor compound (ID), including the steps of: (a) reacting a Mg based compound with a Ti compound, having at least a Ti—Cl bond, in an amount such that the Ti/Mg molar ratio is greater than 3 and at a temperature ranging from 0 to 150° C., thereby yielding an intermediate solid catalyst component containing Mg and Ti; and (b) contacting the intermediate solid catalyst component with a gaseous stream containing the electron donor compound (ID) in a gaseous dispersing medium, thereby yielding a final solid catalyst component having an ID/Ti molar ratio ranging from 0.5:1 to 20:1.

Abstract: A propylene polymer composition made from or containing: a) from 15 wt % to 35 wt % of a propylene 1-hexene copolymer containing from 6.2 to 8.5% by weight, of 1-hexene derived units and having a Melt Flow Rate from 3.5 to 8.5 g/10 min; b) from 15 wt % to 35 wt % of a propylene 1-hexene copolymer containing from 10.4 wt % to 14.5 wt %, of 1-hexene derived units and having a Melt Flow Rate from 3.5 to 8.5 g/10 min; and c) from 38 wt % to 68 wt % of a propylene ethylene copolymer containing from 3.4 wt % to 5.7 wt % of ethylene derived units and having a Melt Flow Rate from 3.5 to 12.0 g/10 min, wherein the sum of the amount of a), b) and c) being 100.

Abstract: A solid catalyst component for the polymerization of olefins made from or containing Mg, Ti, halogen, and an electron donor compound selected from glutarates, wherein the catalyst has specific porosity features.

Abstract: A process for the preparation of a solid catalyst component for the polymerization of CH2?CHR olefins, wherein R is hydrogen or hydrocarbyl radical with 1-12 carbon atoms, made from or containing a Ti compound on a Mg chloride based support, including the steps of (a) reacting a Mg based compound with a liquid medium made from or containing a Ti compound, at a temperature ranging from 0 to 150° C., thereby yielding solid particles; and (b) suspending the solid particles coming from step (a) in a liquid medium made from or containing hydrocarbons at a temperature ranging from 10 to 100° C., wherein step (a) or (b) is carried out in the presence of 0.2 to 20.0% by weight, with respect to the amount of Mg compound, of particles of a solid compound containing more than 50% by weight of SiO2 units and having average particle size from 1 to 100 ?m.

Abstract: A propylene 1-hexene copolymer containing from 5.7 to 7.7% by weight of 1-hexene derived units, based upon the total weight of the propylene 1-hexene copolymer, having: a) a solubility in xylene at 25° C. ranging from 7.0 wt % to 15.0 wt %, based upon the total weight of the propylene 1-hexene copolymer; b) a melting temperature, measured by DSC ranging from 143.0° C. to 148.0° C.; c) a Melt Flow Rate (MFR, measured according to ASTM D 1238, 230° C./2.16 kg) from 3.5 to 8.0 g/10 min.; and d) a content of 1-hexene derived units in the fraction soluble in xylene at 25° C. ranging from 13.5 wt % to 18.5 wt %, based upon the total weight of the soluble fraction.

Abstract: A propylene ethylene copolymer having the following features: an ethylene content of between 1.0 and 4.0% by weight; a molecular weight distribution (MWD), expressed in terms of Mw/Mn, of greater than 4.0; a content of xylene soluble fraction (XS) and ethylene content (C2) that fulfills the following relationship: (C2×1.1)+1.25<XS<(C2×1.1)+2.50 where: XS=% by weight of the fraction soluble in xylene at 25° C.; C2=% by weight of ethylene units in the copolymer determined via NMR; a melt flow rate (MFR; 230° C., 2.16 kg) of between 30 to 75 g/10 min; an intrinsic viscosity of the copolymer of lower than 1.5 dl/g; and an intrinsic viscosity of the fraction soluble in xylene at 25° C. of higher than 0.32 dl/g.

Abstract: A catalyst component made from or containing Ti, Mg, chlorine, an amount of a first internal donor selected from esters of aliphatic monocarboxylic acids (EAA), and an amount of a second internal donor selected from cyclic ethers (CE), wherein the EAA/CE molar ratio ranges from 0.02 to less than 20.

Abstract: A polypropylene composition made from or containing: A) from 50 wt % to 90 wt %, based upon the total weight of the polypropylene composition, of a propylene homopolymer; and B) from 10 wt % to 50 wt %, based upon the total weight of the polypropylene composition, of a copolymer of propylene and ethylene having from 30.0 wt % to 70.0 wt %, based upon the total weight of the copolymer, of ethylene derived units; the polypropylene composition having: i) an intrinsic viscosity of the fraction soluble in xylene at 25° C. between 2.2 and 4.0 dl/g; ii) a MFR L from 0.5 to 100 g/10 min; and iii) a xylene soluble fraction ranging from 10 wt % to 50 wt %, based upon the total weight of the polypropylene composition.

Abstract: A propylene 1-hexene copolymer containing from 5.7 to 7.7% by weight of 1-hexene derived units, based upon the total weight of the propylene 1-hexene copolymer, having: a) a solubility in xylene at 25° C. ranging from 7.0 wt % to 15.0 wt %, based upon the total weight of the propylene 1-hexene copolymer; b) a melting temperature, measured by DSC ranging from 143.0° C. to 148.0° C.; c) a Melt Flow Rate (MFR, measured according to ASTM D 1238, 230° C./2.16 kg) from 3.5 to 8.0 g/10 min.; and d) a content of 1-hexene derived units in the fraction soluble in xylene at 25° C. ranging from 13.5 wt % to 18.5 wt %, based upon the total weight of the soluble fraction.

Abstract: A process for the preparation of a solid catalyst component for the polymerization of CH2?CHR olefins, wherein R is hydrogen or hydrocarbyl radical with 1-12 carbon atoms, made from or containing a Ti compound on a Mg chloride based support, including the steps of (a) reacting a Mg based compound with a liquid medium made from or containing a Ti compound, at a temperature ranging from 0 to 150° C., thereby yielding solid particles; and (b) suspending the solid particles coming from step (a) in a liquid medium made from or containing hydrocarbons at a temperature ranging from 10 to 100° C., wherein step (a) or (b) is carried out in the presence of 0.2 to 20.0% by weight, with respect to the amount of Mg compound, of particles of a solid compound containing more than 50% by weight of SiO2 units and having average particle size from 1 to 100 ?m.

Abstract: A Prepolymerized catalyst component for the polymerization of olefins comprising a solid catalyst component which comprises Mg, Ti, and chlorine atoms and an electron donor (ID) said prepolymerized catalyst component being characterized by the fact that: the electron donor (ID) is constituted by at least 80% mol of 1,3 diethers with respect to the total molar amount of electron donor compounds; the prepolymerized catalyst has a porosity due to pores with diameters up to 1 ?m of less than 0.2 cm3/g; it contains an amount of ethylene prepolymer of less than 45% with respect to the total weight of prepolymerized catalyst.

Abstract: A catalyst component made from or containing Ti, Mg, chlorine, an amount of a first internal donor selected from esters of aliphatic monocarboxylic acids (EAA), and an amount of a second internal donor selected from cyclic ethers (CE), wherein the EAA/CE molar ratio ranges from 0.02 to less than 20.

Abstract: Solid adducts comprising MgCl2 and an alcohol ROH in which R is a C1-C20 hydrocarbon group, in which the amount of alcohol ranges from higher than 42% to 60% by weight and the porosity determined with Hg method due to pores up to 1 ?m and expressed in cm3/g, is such that the value of its ratio with the amount of alcohol in percentage falls above the straight line defined by the equation y=?0.0158x+1.03 in which y is the porosity of the adduct and x is the alcohol percentage by weight.

Abstract: Solid adducts comprising MgCl2, ethanol and water characterized in that the amount of ethanol ranges from 50% to less than 57% by weight, the amount of water is ranges from 0.5 to 5% by weight, the ethanol/water weight ratio is lower than 60 and the porosity determined with Hg method due to pores with radius up to 1 ?m and expressed in cm3/g, is lower than 0.2.

Abstract: A process for the preparation of high purity propylene polymers carried out in the presence of a catalyst comprising the product obtained by contacting: (a) a solid catalyst component comprising Mg, Ti and at least a first internal electron donor compound (1ID) selected among the succinates and a second internal electron donor compound (2ID) selected among the 1,3-diethers, wherein the molar ratio of first internal donor over second internal donor 1ID:2ID is comprised between 4:6 and 9:1, with (b) an organo-aluminum compound, and optionally with (c) an external electron donor compound, said process being carried out at a temperature equal or higher than 78° C. and by employing a molar ratio of organo-aluminum compound over solid catalyst component (b):(a) of lower than 5.

Abstract: A Prepolymerized catalyst component for the polymerization of olefins comprising a solid catalyst component which comprises Mg, Ti, and chlorine atoms and an electron donor (ID) said prepolymerized catalyst component being characterized by the fact that: the electron donor (ID) is constituted by at least 80% mol of 1,3 diethers with respect to the total molar amount of electron donor compounds; the prepolymerized catalyst has a porosity due to pores with diameters up to 1 ?m of less than 0.2 cm3/g; it contains an amount of ethylene prepolymer of less than 45% with respect to the total weight of prepolymerized catalyst.

Abstract: Films or sheets of polypropylene, particularly biaxially oriented polypropylene (BOPP) films, exhibiting excellent physical and mechanical properties combined with good processing characteristics can be prepared from propylene polymers prepared in the presence of Ziegler-Natta catalysts comprising a succinate and a diether compound.