Abstract: The process is for continuously cooking chemical pulp in a digester system consisting of at least one vessel for impregnating and cooking comprising an inlet into which a mixture of chips and process liquid is fed. The chips are impregnated at a predetermined impregnation temperature, Timp, and cooked at a predetermined cooking temperature, Tcook, after which dissolved pulp is fed out at the outlet of the digester system. The process liquid which is continually extracted is retained outside the digester system during a dwell time, t, of at least 30 min, without any heating above 140°, and thereafter returned to the digester system to a position which is substantially at the same level as the extraction, or downstream thereof, and thereby constitute part of the process liquid in the subsequent treatment zone. The process results in improved tear strength, beatability, bleachability and reduced color reversion, and increased yield across the digester.

Abstract: The invention relates to a method for the modification of cellulose fiber with the object of increasing the strength properties of the pulp. Cellulose derivative, preferably in the form of CMC, is added in association with alkali cooking and/or delignification of cellulose chips in a suspension with treatment fluid, in an amount exceeding 2 kg, preferably at least 5–7 kg, per ton of cellulose fibers. The addition of cellulose derivative to the suspension takes place when the suspension has a concentration of calcium released from the cellulose exceeding 20 mg/l. The conditions required for an efficient deposit of cellulose derivative onto the cellulose fibers can be established in this way, where the natural content of calcium in the wood raw material has been released and contributes to a high ionic strength, while an advantageous high temperature is established. No additional process stages are required and operating costs can be kept low.

Abstract: The invention relates to a method for the modification of cellulose fiber with the object of increasing the strength properties of the pulp. Cellulose derivative, preferably in the form of CMC, is added in association with alkali cooking and/or delignification of cellulose chips in a suspension with treatment fluid, in an amount exceeding 2 kg, preferably at least 5-7 kg, per ton of cellulose fibers. The addition of cellulose derivative to the suspension takes place when the suspension has a concentration of calcium released from the cellulose exceeding 20 mg/l. The conditions required for an efficient deposit of cellulose derivative onto the cellulose fibers can be established in this way, where the natural content of calcium in the wood raw material has been released and contributes to a high ionic strength, while an advantageous high temperature is established. No additional process stages are required and operating costs can be kept low.

Abstract: The process is for continuously cooking chemical pulp in a digester system consisting of at least one vessel for impregnating and cooking comprising an inlet into which a mixture of chips and process liquid is fed. The chips are impregnated at a predetermined impregnation temperature, Timp, and cooked at a predetermined cooking temperature, Tcook, after which dissolved pulp is fed out at the outlet of the digester system. The process liquid which is continually extracted is retained outside the digester system during a dwell time, t, of at least 30 min, without any heating above 140°, and thereafter returned to the digester system to a position which is substantially at the same level as the extraction, or downstream thereof, and thereby constitute part of the process liquid in the subsequent treatment zone. The process results in improved tear strength, beatability, bleachability and reduced color reversion, and increased yield across the digester.