Abstract: A room temperature-curable composition comprising (A) a silanol-terminated polydiorganosiloxane having a viscosity measured at 25.degree. C. of from 100 to 200,000 cSt, (B) an epoxy-terminated polyether, (C) an organosilicon compound, (D) an inorganic filler, and (E) a curing catalyst. The composition is suitably used as a building sealant which causes no fouling of the areas surrounding joints even after applied to the joints.

Abstract: A room temperature curing composition comprising:(A) a silanol-terminated polydiorganosiloxane;(B) a hydrolyzable silyl-terminated polymer obtained by reacting:(a) an epoxy-terminated polyether;(b)(i) an heterocyclic compound containing imino groups, and/or;(ii) an aromatic compound or a heterocyclic compound containing mercapto groups; and,(c) an organosilicon compound containing an epoxy group and a hydrolyzable group;(C) an inorganic filler; and,(D) a curing catalyst.

Abstract: A room-temperature curable composition comprising(A) 100 parts by weight of a polymer having a hydrolyzable silyl group at the terminal of the molecular chain, the main chain being substantially a polyether,(B) from 0.01 to 20 parts by weight of an organic silicon compound represented by the general formula ##STR1## wherein two R.sup.1 s, which may be the same or different, each represents a monovalent hydrocarbon group; two R.sup.2 s, which may be the same or different, each represents an unsubstituted hydrocarbon group having from 1 to 6 carbon atoms; two Q.sup.1 s, which may be the same or different, each represents a divalent hydrocarbon group; a and b each represents 2 or 3; and A represents a hydrogen atom, a monovalent hydrocarbon group, or a monovalent group shown by the formula ##STR2## wherein R.sup.1, R.sup.2 and Q.sup.1 have the same meaning as defined above and c represents 2 or 3; and(C) from 0.01 to 10 parts by weight of a curing catalyst.

Abstract: A room temperature-curable composition comprising(a) 100 parts by weight of a siloxane-amide block copolymer represented by the formula (1) ##STR1## wherein Y represents a hydrolyzable group-containing organosilyl group of the formula --SiR.sup.5.sub.a X.sub.a-ain whichR.sup.5 represents a substituted or unsubstituted monovalent hydrocarbon group,a is an integer of 0, 1 or 2, andX is directly bonded to the silicon atom and represents a hydolyzable group or a hydroxyl group,R.sup.1 represents a divalent group selected from the group consisting of ##STR2## in which R.sup.6 represents a hydrogen atom, a substituted or unsubstituted monovalent hydrocarbon group, or an organosilyl group of the formula --SiR.sup.8.sub.b X.sub.3-bin whichR.sup.8 represents a substituted or unsubstituted monovalent hydrocarbon group,b is an integer of 0, 1, 2, or 3, and X is the same as defined above, andR.sup.

Abstract: A polyether having molecular weight from 1,000 to 50,000, end-blocked with hydrolyzable silyl groups and represented by the general formula (P): ##STR1## where R.sup.1, R.sup.2, R.sup.6 and R.sup.7 individually represent a divalent hydrocarbon group, R.sup.4 represents a monovalent hydrocarbon group, R.sup.8 represents an alkyl group with 1 to 6 carbon atoms, X represents an aromatic or heterocyclic ring, a represents a number from 1 to 3, m represents a number from 10 to 500, n represents a number of 1 or greater is produced and utilized in room temperature curing compositions containing inorganic filler and curing catalyst. There is also disclosed a method for producing the above polyether by reacting polyoxyalkylene end-blocked with epoxy groups, dimercapto compound and organo silicon compound.

Abstract: There are provided polyethers end-blocked with hydrolyzable silyl groups which have molecular weight from 500 to 50,000 and are represented by the formula: ##STR1## where R.sup.1, R.sup.2, R.sup.3 and R.sup.4 individually represent a divalent hydrocarbon group, R.sup.5 represents a monovalent hydrocarbon group, R.sup.6 represents an alkyl group with 1 to 6 carbon atoms, A represents a substituted or non-substituted divalent aromatic group, a represents a number of 1 to 3, m represents a number of 10 to 500 and n represents a number of 1 or greater. The polyether is produced by reacting an epoxy end-blocked polyoxyalkylene, a mono-epoxy substituted hydrolyzable silane, and an aromatic diamine.

Abstract: A siloxane-amide block copolymer represented by formula (I): ##STR1## wherein the symbols are as defined in the specification, is disclosed. The polymer of formula (I) is produced by reacting a polycondensate of a diaminosiloxane and a dicarboxylic acid dihalide with an epoxysilane to induce ring-opening addition reaction between the terminal amino groups of the polymer and the epoxy group of the epoxysilane. The siloxane-amide block copolymer exhibits excellent processability and reactive curability due to the hydrolyzable silyl groups at the both terminals.

Abstract: A polyether having molecular weight from 1,000 to 50,000, end-blocked with hydrolyzable silyl groups and represented by the general formula (P): ##STR1## where R.sup.1, R.sup.2, R.sup.6 and R.sup.7 individually represent a divalent hydrocarbon group, R.sup.4 represents a monovalent hydrocarbon group, R.sup.8 represents an alkyl group with 1 to 6 carbon atoms, a represents a number from 1 to 3, m represents a number from 10 to 500, n represents a number of 1 or greater and --N.dbd.X.dbd.N-- represents a residue group of a diimino heterocyclic compound, from which nitrogen-bonded hydrogen atoms are eliminated, said diimino heterocyclic compound having no ##STR2## bond in a molecule is produced and utilized in room temperature curing compositions containing inorganic filler and curing catalyst. There is also disclosed a method for producing the above polyether by reacting polyoxyalkylene end-blocked with epoxy groups, diimino heterocyclic compound and organo silicon compound.

Abstract: A polyether having molecular weight from 1,000 to 50,000, end-blocked with hydrolyzable silyl groups and represented by the general formula (P): ##STR1## where R.sup.1, R.sup.2, R.sup.6 and R.sup.7 individually represent a divalent hydrocarbon group, R.sup.4 represents a monovalent hydrocarbon group, R.sup.8 represents an alkyl group with 1 to 6 carbon atoms, X represents an aromatic or heterocyclic ring, a represents a number from 1 to 3, m represents a number from 10 to 500, n represents a number of 1 or greater is produced and utilized in room temperature curing compositions containing inorganic filler and curing catalyst. There is also disclosed a method for producing the above polyether by reacting polyoxyalkylene end-blocked with epoxy groups, dimercapto compound and organo silicon compound.

Abstract: Polyethers end-blocked with hydrolyzable silyl groups are manufactured by reacting an epoxy end-blocked linear polyoxyalkylene, a mono-epoxy substituted hydrolyzable silane and an aromatic diamine and compounded with filler to produce a room temperature curable elastomer.

Abstract: A composition curable to a dustproof film comprising:(A) 100 parts by weight of an alkyd resin,(B) 5 to 200 parts by weight of methyltrimethoxysilane,(C) a curing catalyst; and(D) 50 to 5000 parts by weight of a solvent mixture consisting of(a) a volatile organosilicon compound which has a boiling point of 70.degree. to 250.degree. C. at atmospheric pressure and has a formula selected from the group consisting of(R.sup.1).sub.4 Si, (R.sup.2).sub.3 SiO[(R.sup.3).sub.2 SiO].sub.m Si(R.sup.2).sub.3R.sup.4 Si[OSi(R.sup.5).sub.3 ].sub.3 and [(R.sup.6).sub.2 SiO].sub.nwherein R.sup.1 to R.sup.6 respectively represent the same or different alkyl groups, m represents 0 or a positive integer and n represents a positive integer of 3 or above, and(b) a hydrocarbon solvent substantially free of methanol, wherein the amount of (a) is 5 to 95 wt. % of the total amount of (a) and (b).

Abstract: There is provided a method of forming a stainproof film on silicone elastomers comprised of coating a surface with a combination of an aminoxy functional organosilicon compound, a mixture or condensation products, of a benzene soluble polyorganosiloxane and a silanol-terminated polydiorganosiloxane, together with a mixed solvent comprised of a volatile organosilicon compound and a hydrocarbon solvent.

Abstract: There is provided a silicone film-forming composition and method for forming dust-resistant films from such compositions which are comprised of a condensation product of a benzene soluble polysiloxane and a silanol terminated polydiorganosiloxane in combination with a mixed solvent comprised of a volatile organosilicon compound and a hydrocarbon solvent.

Abstract: An adhesive polyorganosiloxane composition suitably employable as a sealant for joint portions of buildings, constructions, etc. which comprises:(A) a polydiorganosiloxane being end-blocked by silanol group and having the viscosity of 100-200,000 cSt at 25.degree. C.;(B) an aminoxy group-containing organosilicon compound having organoaminoxy groups of more than 2 per a molecule on the average;(C) an inorganic filler; and(D) a monovalent alcohol having the formula R--OH, in which R is a primary or secondary hydrocarbon group selected from the group consisting of a monovalent saturated aliphatic hydrocarbon group and an aralkyl group, and having the vapor pressure of at least 0.1 mmHg at 20.degree. C.

Abstract: There is disclosed a compositon forming an elastic foam at normal temperature essentially comprising(A) polydiorganosiloxane end-blocked by silanol group and a viscosity within the range between 500 and 200,000 cSt at 25.degree. C.,(B) an aminoxy group-containing organosilicon compound having more than two silicon-bonded organoaminoxy groups on the average in one molecule,(C) a silicon-hydrogen bond containing polyorganosiloxane having more than two silicon-hydrogen bonds on the average in one molecule, with the proportion of said silicon-hydrogen bonds being 10% or more of the number of silicon atoms,(D) fumed silica,(E) an isocyanato group-containing organic compound, and optionally(F) a polyhydric alcohol having two or more alcoholic hydroxyl groups bonded to primary carbon atoms and/or two or more alcoholic hydroxyl groups bonded to secondary carbon atoms in one molecule.

Abstract: There is provided a paintable room temperature curable polyorganosiloxane composition which is comprised of a silanol-terminated polydiorganosiloxane, an aminoxy functional organosilicon compound, an inorganic filler and a monohydric unsaturated alcohol containing a carbon-to-carbon triple bond and a hydroxyl group bonded with a primary or secondary carbon atom.