Abstract: The present invention provides an iron-loaded aluminosilicate zeolite having a maximum pore opening defined by eight tetrahedral atoms and having the framework type CHA, AEI, AFX, ERI or LTA, wherein the iron (Fe) is present in a range of from about 0.5 to about 5.0 wt. % based on the total weight of the iron-loaded aluminosilicate zeolite, wherein an ultraviolet-visible absorbance spectrum of the iron-loaded synthetic aluminosilicate zeolite comprises a band at approximately 280 nm, wherein a ratio of an integral, peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for the band at approximately 280 nm to an integral peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for a band at approximately 340 nm is >about 2.

Abstract: A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Jr and Pt.

Abstract: A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Ir and Pt.

Abstract: The present invention further provides a method of making an metal-loaded aluminosilicate zeolite having a maximum pore opening defined by eight tetrahedral atoms from pre-existing aluminosilicate zeolite crystallites, wherein the metal is present in a range of from 0.5 to 5.0 wt. % based on the total weight of the metal-loaded aluminosilicate zeolite.

Abstract: A novel method for synthesizing AEI zeolites is provided which results in high overall relative yields on silica and the structure directing agent.

Abstract: The present invention provides an iron-loaded aluminosilicate zeolite having a maximum pore opening defined by eight tetrahedral atoms and having the framework type CHA, AEI, AFX, ERI or LTA, wherein the iron (Fe) is present in a range of from about 0.5 to about 5.0 wt. % based on the total weight of the iron-loaded aluminosilicate zeolite, wherein an ultraviolet-visible absorbance spectrum of the iron-loaded synthetic aluminosilicate zeolite comprises a band at approximately 280 nm, wherein a ratio of an integral, peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for the band at approximately 280 nm to an integral peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for a band at approximately 340 nm is >about 2.

Abstract: A catalyst for selective catalytic reduction of NOx having one or more transition metals selected from Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Ir, Pt, and mixtures thereof supported on a support, wherein the support has a molecular sieve having at least one intergrowth phase having at least two different small-pore, three-dimensional framework structures.

Abstract: A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Ir and Pt.

Abstract: A novel method for synthesizing AEI zeolites is provided which results in high overall relative yields on silica and the structure directing agent.

Abstract: A novel method for synthesizing AEI zeolites is provided which results in high overall relative yields on silica and the structure directing agent. Structure directing agents useful in the present invention include the cations N,N-Dimethyl-3,5-dimethylpiperidinium, N,N-Dimethyl-2-(2-hydroxyethyl)piperidinium, N,N-Dimethyl-2-ethylpiperidinium, and 2,2,4,6,6-Pentamethyl-2-azoniabycyclo[3.2.1]octane.

Abstract: Fe-SAPO-34 silicoaluminophosphates having Fe2+ organic complexes and methods for their direct synthesis in the absence of a co-templating agent are described. Fe-SAPO-34 silicoaluminophosphate having Fe3+ located in extra-framework locations within the pores of cages of the crystal are described. They are prepared by calcining the Fe-SAPO-34 silicoaluminphosphates containing Fe2+ polyamine complexes. Methods of using the Fe-SAPO-34 having Fe3+ located in extra-framework locations within the pores of cages of the crystal in the treatment of exhaust gases are described.

Abstract: Provided is a catalyst composition having an aluminosilicate molecular sieve having an AEI structure and a mole ratio of silica-to-alumina of about 20 to about 30 loaded with about 1 to about 5 weight percent of a promoter metal, based on the total weight of the molecular sieve material. Also provided are method, articles, and systems utilizing the catalyst composition.

Abstract: A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Ir and Pt.

Abstract: A passive NOx adsorber is disclosed. The passive NOx adsorber is effective to adsorb NOx at or below a low temperature and release the adsorbed NOx at temperatures above the low temperature. The passive NOx adsorber comprises a noble metal and a molecular sieve having a MAZ Framework Type. The invention also includes an exhaust system comprising the passive NOx adsorber, and a method for treating exhaust gas from an internal combustion engine utilizing the passive NOx adsorber.

Abstract: Fe-SAPO-34 silicoaluminophosphates having Fe2+ organic complexes and methods for their direct synthesis in the absence of a co-templating agent are described. Fe-SAPO-34 silicoaluminophosphate having Fe3+ located in extra-framework locations within the pores of cages of the crystal are described. They are prepared by calcining the Fe-SAPO-34 silicoaluminphosphates containing Fe2+ polyamine complexes. Methods of using the Fe-SAPO-34 having Fe3+ located in extra-framework locations within the pores of cages of the crystal in the treatment of exhaust gases are described.

Abstract: Provided is a catalyst composition having an aluminosilicate molecular sieve having an AEI structure and a mole ratio of silica-to-alumina of about 20 to about 30 loaded with about 1 to about 5 weight percent of a promoter metal, based on the total weight of the molecular sieve material. Also provided are method, articles, and systems utilizing the catalyst composition.

Abstract: Provided is a catalyst composition having an aluminosilicate molecular sieve having an AEI structure and a mole ratio of silica-to-alumina of about 20 to about 30 loaded with about 1 to about 5 weight percent of a promoter metal, based on the total weight of the molecular sieve material. Also provided are method, articles, and systems utilizing the catalyst composition.

Abstract: A catalyst for selective catalytic reduction of NOx having one or more transition metals selected from Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Ir, Pt, and mixtures thereof supported on a support, wherein the support has a molecular sieve having at least one intergrowth phase having at least two different small-pore, three-dimensional framework structures.

Abstract: A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Jr and Pt.

Abstract: A method of converting nitrogen oxides in a gas to nitrogen by contacting the nitrogen oxides with a nitrogenous reducing agent in the presence of a zeolite catalyst containing at least one transition metal, wherein the zeolite is a small pore zeolite containing a maximum ring size of eight tetrahedral atoms, wherein the at least one transition metal is selected from the group consisting of Cr, Mn, Fe, Co, Ce, Ni, Cu, Zn, Ga, Mo, Ru, Rh, Pd, Ag, In, Sn, Re, Ir and Pt.