Abstract: The present invention relates to a positive electrode active material which makes it possible to improve the electrochemical properties and stability of a positive electrode active material including a lithium composite oxide by adjusting the direction of a concentration gradient of a metal element of the lithium composite oxide, and a lithium secondary battery using a positive electrode including the positive electrode active material.

Abstract: A lithium complex oxide includes a mixture of first particles of n1 (n1>40) aggregated primary particles and second particles of n2 (n2?20) aggregated primary particles, the lithium complex oxide represented by Chemical Formula 1 and having FWHM (deg., 2?) of 104 peak in XRD, defined by a hexagonal lattice having R-3m space group, in a range of Formula 1: where M is selected from: B, Ba, Ce, Cr, F, Mg, Al, Cr, V, Ti, Fe, Zr, Zn, Si, Y, Nb, Ga, Sn, Mo, W, P, Sr, and any combination thereof, 0.9?a?1.3, 0.6?x?1.0, 0.0?y?=0.4, 0.0?z?0.4, and 0.0?1?x?y?z?0.

Abstract: The present invention relates to a positive electrode active material and a lithium secondary battery using a positive electrode containing the positive electrode active material. More particularly, the present invention relates to a positive electrode active material that is able to solve a problem of increased resistance according to an increase in Ni content by forming a charge transport channel in a lithium composite oxide and a lithium secondary battery using a positive electrode containing the positive electrode active material.

Abstract: A lithium complex oxide includes a mixture of first particles of n1 (n1>40) aggregated primary particles and second particles of n2 (n2?20) aggregated primary particles, the lithium complex oxide represented by Chemical Formula 1 and having FWHM (deg., 2?) of 104 peak in XRD, defined by a hexagonal lattice having R-3m space group, in a range of Formula 1: LiaNixCoyMnzM1-x-y-zO2,??[Chemical Formula 1] where M is selected from: B, Ba, Ce, Cr, F, Mg, Al, Cr, V, Ti, Fe, Zr, Zn, Si, Y, Nb, Ga, Sn, Mo, W, P, Sr, and any combination thereof, 0.9?a?1.3, 0.6?x?1.0, 0.0?y?=0.4, 0.0?z?0.4, and 0.0?1-x-y-z?0.4, ?0.025?FWHM(104)?{0.04+(xfirst particle?0.6)×0.25}?0.025,??[Formula 1] where FWHM(104) is represented by Formula 2, FWHM(104)={(FWHMChemical Formula 1 powder(104)?0.1×mass ratio of second particles)/mass ratio of first particles}?FWHMSi powder (220).

Abstract: The present invention relates to a positive electrode active material and a lithium secondary battery using a positive electrode containing the positive electrode active material. More particularly, the present invention relates to a positive electrode active material that is able to solve a problem of increased resistance according to an increase in Ni content by forming a charge transport channel in a lithium composite oxide and a lithium secondary battery using a positive electrode containing the positive electrode active material.

Abstract: The present invention relates to a positive electrode active material having improved electrical characteristics by adjusting an aspect ratio gradient of primary particles included in a secondary particle. a positive electrode including the positive electrode active material, and a lithium secondary battery using the positive electrode.

Abstract: The present invention relates to a positive electrode active material having improved electrical characteristics by adjusting an aspect ratio gradient of primary particles included in a secondary particle, a positive electrode including the positive electrode active material, and a lithium secondary battery using the positive electrode.

Abstract: A lithium complex oxide includes a mixture of first particles of n1 (n1>40) aggregated primary particles and second particles of n2 (n2?20) aggregated primary particles, the lithium complex oxide represented by Chemical Formula 1 and having FWHM (deg., 2?) of 104 peak in XRD, defined by a hexagonal lattice having R-3m space group, in a range of Formula 1: LiaNixCoyMnzM1-x-y-zO2, ??[Chemical Formula 1] where M is selected from: B, Ba, Ce, Cr, F, Mg, Al, Cr, V, Ti, Fe, Zr, Zn, Si, Y, Nb, Ga, Sn, Mo, W, P, Sr, and any combination thereof, 0.9?a?1.3, 0.6?x?1.0, 0.0?y?=0.4, 0.0?z?0.4, and 0.0?1-x-y-z?0.4, ?0.025?FWHM(104)?{0.04+(xfirst particle?0.6)×0.25}?0.025, ??[Formula 1] where FWHM(104) is represented by Formula 2, FWHM(104)={(FWHMChemical Formula 1 powder(104)?0.1×mass ratio of second particles)/mass ratio of first particles}?FWHMSi powder (220).

Abstract: The present invention relates to a positive electrode active material and a lithium secondary battery comprising the same, and more specifically, to a positive electrode active material including a lithium composite oxide containing at least nickel and titanium, wherein the titanium is present in an oxide form in at least a portion of the surface of the lithium composite oxide at the same time as being doped in the lithium composite oxide, and thus it is possible to simultaneously improve the output efficiency and high-temperature lifetime characteristics (high-temperature cycle capacity retention rate) of a lithium secondary battery using the positive electrode active material, and a lithium secondary battery including the same.

Abstract: A lithium complex oxide includes a mixture of first particles of n1 (n1>40) aggregated primary particles and second particles of n2 (n2?20) aggregated primary particles, the lithium complex oxide represented by Chemical Formula 1 and having FWHM (deg., 2?) of 104 peak in XRD, defined by a hexagonal lattice having R-3m space group, in a range of Formula 1: LiaNixCoyMnzM1-x-y-zO2,??[Chemical Formula 1] where M is selected from: B, Ba, Ce, Cr, F, Mg, Al, Cr, V, Ti, Fe, Zr, Zn, Si, Y, Nb, Ga, Sn, Mo, W, P, Sr, and any combination thereof, 0.9?a?1.3, 0.6?x?1.0, 0.0?y?=0.4, 0.0?z?0.4, and 0.0?1?x?y?z?0.4, ?0.025?FWHM(104)?{0.04+(xfirst particle?0.6)×0.25}?0.025,??[Formula 1] where FWHM(104) is represented by Formula 2, FWHM(104)={(FWHMChemical Formula 1 powder(104)?0.1×mass ratio of second particles)/mass ratio of first particles}?FWHMSi powder(220).

Abstract: The present invention relates to a positive electrode active material having improved electrical characteristics by adjusting an aspect ratio gradient of primary particles included in a secondary particle, a positive electrode including the positive electrode active material, and a lithium secondary battery using the positive electrode.

Abstract: The present invention relates to a positive electrode active material which makes it possible to improve the electrochemical properties and stability of a positive electrode active material including a lithium composite oxide by adjusting the direction of a concentration gradient of a metal element of the lithium composite oxide, and a lithium secondary battery using a positive electrode including the positive electrode active material.

Abstract: The present invention relates to a positive electrode active material and a lithium secondary battery including the same, and more particularly, to a bimodal-type positive electrode active material that includes a first lithium composite oxide which is a small particle and a second lithium composite oxide which is a large particle, which have different average particle diameters, thereby improving an increasing deviation of an average particle diameter and degraded impedance and lifetime characteristics due to excessive calcination for any one of the small and large particles during simultaneous calcination, a positive electrode including the same, and a lithium secondary battery using the same.

Abstract: The present invention relates to a positive electrode active material having improved electrical characteristics by adjusting an aspect ratio gradient of primary particles included in a secondary particle, a positive electrode including the positive electrode active material, and a lithium secondary battery using the positive electrode.

Abstract: The present invention relates to a lithium composite oxide capable of improving capacity and lifetime characteristics of a lithium secondary battery and a lithium secondary battery including the same. According to the present invention, since the atomic ratio of boron (B) and nickel (Ni) in the surface region of the lithium composite oxide including primary particles enabling lithium intercalation and deintercalation and secondary particles formed by aggregating the primary particles is in a specific range, the stability of the lithium composite oxide may be improved, and thus it is possible to improve the capacity and lifetime characteristics of the lithium secondary battery using the lithium composite oxide as a positive electrode active material.

Abstract: A lithium complex oxide includes a mixture of first particles of n1 (n1>40) aggregated primary particles and second particles of n2 (n2?20) aggregated primary particles, the lithium complex oxide represented by Chemical Formula 1 and having FWHM (deg., 2?) of 104 peak in XRD, defined by a hexagonal lattice having R-3m space group, in a range of Formula 1: LiaNixCoyMnzM1-x-y-zO2,??[Chemical Formula 1] where M is selected from: B, Ba, Ce, Cr, F, Mg, Al, Cr, V, Ti, Fe, Zr, Zn, Si, Y, Nb, Ga, Sn, Mo, W, P, Sr, and any combination thereof, 0.9?a?1.3, 0.6?x?1.0, 0.0?y?=0.4, 0.0?z?0.4, and 0.0?1?x?y?z?0.4, ?0.025?FWHM(104)?{0.04+(xfirst particle?0.6)×0.25}?0.025,??[Formula 1] where FWHM(104) is represented by Formula 2, FWHM(104)={(FWHMChemical Formula 1 powder(104)?0.1×mass ratio of second particles)/mass ratio of first particles}?FWHMSi powder(220).

Abstract: The present invention relates to a positive electrode active material and a lithium secondary battery using a positive electrode containing the positive electrode active material. More particularly, the present invention relates to a positive electrode active material that is able to solve a problem of increased resistance according to an increase in Ni content by forming a charge transport channel in a lithium composite oxide and a lithium secondary battery using a positive electrode containing the positive electrode active material.

Abstract: The present invention relates to a lithium composite oxide including a coating layer having a boron-containing oxide and a lithium secondary battery including the same. More particularly, the present invention relates to a lithium composite oxide improved in lifetime and capacity characteristics by inducing a predetermined correlation between the molar ratio of nickel in a lithium composite oxide including a coating layer having a boron-containing oxide and a full width at half-maximum (FWHM; deg., 2?) of a (104) peak among XRD peaks defined by the hexagonal lattice with an R-3m space group, and a lithium secondary battery including the same.