Abstract: A composition comprising the following components: a) a first ethylene/alpha-olefin interpolymer that comprises the following properties: i) a melt viscosity (177° C.) from 2,000 to 50,000 mPa·s, ii) a density from 0.855 to 0.885 g/cc; b) a second ethylene/alpha-olefin interpolymer that comprises the following properties: i) a melt viscosity (177° C.) from 2,000 to 50,000 mPa·s, ii) a density from 0.900 to 0.960 g/cc; and wherein the weight ratio of component a to component b is from 1.0 to 100.

Abstract: A composition comprising at least the following components: A) an ethylene-based polymer; B) a cycloolefin inter-polymer comprising, in polymerized form, ethylene and at least one bridged cyclic olefin selected from Structures a-d, as described herein, or any combination of Structures a-d; and wherein component A is present in an amount ?50 wt %, based on the weight of the composition, and wherein component B is present in an amount from 5 to 12 wt %, based on the sum weight of components A and B.

Abstract: The present disclosure provides a composition. The composition can be formed into a foam composition. In an embodiment, the composition includes a neat ethylene/propylene/nonconjugated polyene interpolymer. The neat ethylene/propylene/nonconjugated polyene interpolymer includes from greater than 6.0 wt % to 15.0 wt % nonconjugated polyene. The neat ethylene/propylene/nonconjugated polyene interpolymer has the following properties: (i) a molecular weight (Mw) from 240,000 to 270,000; (ii) a Mooney viscosity (ML (1+4), 125° C.) from 85 to 95; (iii) a rheology ratio (RR) from 35 to 65; (iv) a Mw/Mn from 2.2 to 3.5; and (v) Mw<1389.6 [g/mole] MV+140,000 g/mol wherein Mw is the weight average molecular weight and MV is the Mooney Viscosity (ML 1+4, 125° C.). MV is the Mooney Viscosity (ML 1+4, 125° C.), and Mw is the weight average molecular weight, as determined by conventional GPC.

Abstract: The present disclosure relates to a curable composition comprising: (A) a polyolefin; (B) a fumed alumina; (C) a silane compound; (D) a UV stabilizer; and, optionally, (E) a crosslinking agent, where the curable composition demonstrates improved electrical properties. The present disclosure further relates to a crosslinked polymer composition that is the reaction product of the curable composition, where improved electrical properties are demonstrated as well.

Abstract: The present disclosure provides a composition. The composition can be formed into a foam composition. In an embodiment, the composition includes a neat ethylene/propylene/nonconjugated polyene interpolymer. The neat ethylene/propylene/non-conjugated polyene interpolymer includes from greater than 6.0 wt % to 15.0 wt % nonconjugated polyene. The neat ethylene/propylene/nonconjugated polyene interpolymer has the following properties: (i) a molecular weight (Mw) from 240,000 to 270,000; (ii) a Mooney viscosity (ML (1+4), 125° C.) from 85 to 95; (iii) a rheology ratio (RR) from 35 to 65; (iv) a Mw/Mn from 2.2 to 3.5; and (v) a Mw<1389.6 [g/mole] MV+140,000 g/mol wherein Mw is the weight average molecular weight and MV is the Mooney Viscosity (ML 1+4, 125° C.). MV is the Mooney Viscosity (ML 1+4, 125° C.), and Mw is the weight average molecular weight, as determined N by conventional GPC.

Abstract: The present disclosure relates to unsaturated polyolefins and processes for preparing the same. The present disclosure further relates to curable formulations comprising the unsaturated polyolefins that show improved crosslinking.

Abstract: The present disclosure relates to novel telechelic poly-olefins of the formula (I) and processes for preparing the same. The present disclosure further relates to curable formulations comprising the telechelic polyolefin of the formula (I).

Abstract: A composition composed of at least a first ethylene/?-olefin/nonconjugated polyene interpolymer, which can be used to produce low compression set, foamed rubber materials, articles made from the composition, and methods of producing the composition and articles.

Abstract: Crosslinkable polymeric compositions comprising (a) 10 to 99 weight percent of an ethylene-based interpolymer having the following properties: (i) a density of 0.93 g/cm3 or less, (ii) a high-shear viscosity (V100) at 190° C. and 10% strain of 1,200 Pa-s or less, and (iii) a shear thinning ratio (V0.1/V100) at 190° C. and 10% strain of at least 8; and (b) 0 to less than 10 weight percent of a filler, where the ethylene-based interpolymer is not prepared in a high-pressure reactor. Such crosslinkable polymeric compositions may be employed as insulation layers in flexible power cables.

Abstract: A composition comprising an ethylene/alpha-olefin/non-conjugated polyene, and wherein the ethylene/alpha-olefin/non-conjugated polyene comprises the following property: a “13C NMR % iCB Peak Area,” which is the {[(13C NMR peak area from 34.4 ppm to 34.6 ppm) divided by (the 13C NMR sum integral area from 160.0 to 100.0 and from 60.0 ppm to 0.00 ppm)]×100}, that is >0.010%, as determined by 13C NMR.

Abstract: The present disclosure provides a film. In an embodiment, a multilayer film having at least three layers is provided. The multilayer film includes two skin layers, each skin layer composed of a blend of a low density polyethylene and an ethylene-based elastomer having a density less than 0.90 g/cc. The multilayer film also includes a core layer located between the skin layers. The core layer includes a propylene-based plastomer having a density less than 0.90 g/cc. The multilayer film has an onset end temperature from 90° C. to 110° C. and a heat seal strength at 120° C. from 1.5 N/cm to 2.5 N/cm.

Abstract: The invention provides a composition comprising a first composition, comprising a first ethylene/alpha-olefin/non-conjugated polyene and a second ethylene ethylene/alpha-olefin/non-conjugated polyene, and wherein the first composition comprises the following property: Mw>1389.6 [g/mole] MV+115,000 g/mole, wherein MV is the Mooney Viscosity (ML 1+4, 125C), and Mw is the weight average molecular weight, as determined by conventional GPC.

Abstract: Crosslinkable polymeric compositions comprising: (a) a polymer blend comprising: (1) 10 to 94 weight percent, based on the total weight of the crosslinkable polymeric composition, of an ethylene-based interpolymer having the following properties: (i) a density of 0.93 g/cm3 or less, (ii) a melt index (I2) at 190° C. of greater than 0.2 g/10 minutes, and (iii) a shear thinning ratio (V0.1/V100) at 190° C. and 10% strain of less than 8; and (2) 5 to 90 weight percent, based on the total weight of the crosslinkable polymeric composition, of a high-pressure polyethylene; and (b) 0 to less than 40 weight percent, based on the total weight of the crosslinkable polymeric composition, of a filler, where the ethylene-based interpolymer of component (a) is not prepared in a high-pressure reactor or process. Additionally, the polymer blend has the following properties: (i) a shear thinning ratio (V0.1/V100) at 190° C.

Abstract: Crosslinkable polymeric compositions comprising (a) 10 to 89 weight percent of an ethylene-based interpolymer having the following properties: (i) a density of 0.93 g/cm3 or less, (ii) a high-shear viscosity (V100) at 190 C and 10% strain of 1,200 Pa·s or less, (iii) a shear thinning ratio (V0.1/V100) at 190 C and 10% strain of at least 8, and (iv) a melt index (I2) greater than 1 g/10 minutes; and (b) 10 to less than 90 weight percent of a filler, where the ethylene-based interpolymer is not prepared in a high-pressure reactor. Such crosslinkable polymeric compositions may be employed as insulation layers in flexible power cables.

Abstract: A composition composed of at least a first ethylene/?-olefin/nonconjugated polyene interpolymer, which can be used to produce low compression set, foamed rubber materials, articles made from the composition, and methods of producing the composition and articles.

Abstract: The invention provides a process to form a polymer composition comprising at least one ethylene/?-olefin/non-conjugated polyene interpolymer, and wherein the polymer composition has at least the following properties: a) a Mw/V0.1 ratio greater than, or equal to, 1.80 (g/mol)/(Pa·s); said process comprising polymerizing one or more mixture(s) comprising ethylene, an ?-olefin and a non-conjugated polyene in the presence of a catalyst system comprising a metal-ligand complex of Formula (I), as described herein.

Abstract: The present disclosure provides a film. In an embodiment, a multilayer film having at least three layers is provided. The multilayer film includes two skin layers, each skin layer composed of a blend of a low density polyethylene and an ethylene-based elastomer having a density less than 0.90 g/cc. The multilayer film also includes a core layer located between the skin layers. The core layer includes a propylene-based plastomer having a density less than 0.90 g/cc. The multilayer film has an onset end temperature from 90° C. to 110° C. and a heat seal strength at 120° C. from 1.5 N/cm to 2.5 N/cm.

Abstract: Crosslinkable polymeric compositions comprising (a) 10 to 89 weight percent of an ethylene-based interpolymer having the following properties: (i) a density of 0.93 g/cm3 or less, (ii) a high-shear viscosity (V100) at 190 C and 10% strain of 1,200 Pa·s or less, (iii) a shear thinning ratio (V0.1/V100) at 190 C and 10% strain of at least 8, and (iv) a melt index (I2) greater than 1 g/10 minutes; and (b) 10 to less than 90 weight percent of a filler, where the ethylene-based interpolymer is not prepared in a high-pressure reactor. Such crosslinkable polymeric compositions may be employed as insulation layers in flexible power cables.

Abstract: Crosslinkable polymeric compositions comprising (a) 10 to 99 weight percent of an ethylene-based interpolymer having the following properties: (i) a density of 0.93 g/cm3 or less, (ii) a high-shear viscosity (V100) at 190° C. and 10% strain of 1,200 Pa-s or less, and (iii) a shear thinning ratio (V0.1/V100) at 190° C. and 10% strain of at least 8; and (b) 0 to less than 10 weight percent of a filler, where the ethylene-based interpolymer is not prepared in a high-pressure reactor. Such crosslinkable polymeric compositions may be employed as insulation layers in flexible power cables.

Abstract: Crosslinkable polymeric compositions comprising: (a) a polymer blend comprising: (1) 10 to 94 weight percent, based on the total weight of the crosslinkable polymeric composition, of an ethylene-based interpolymer having the following properties: (i) a density of 0.93 g/cm3 or less, (ii) a melt index (I2) at 190° C. of greater than 0.2 g/10 minutes, and (iii) a shear thinning ratio (V0.1/V100) at 190° C. and 10% strain of less than 8; and (2) 5 to 90 weight percent, based on the total weight of the crosslinkable polymeric composition, of a high-pressure polyethylene; and (b) 0 to less than 40 weight percent, based on the total weight of the crosslinkable polymeric composition, of a filler, where the ethylene-based interpolymer of component (a) is not prepared in a high-pressure reactor or process. Additionally, the polymer blend has the following properties: (i) a shear thinning ratio (V0.1/V100) at 190° C.