Abstract: Provided is an after-cure type laminated film having a low reflectance. A laminated film comprising: a transparent support substrate, an uncured hard coat layer formed on at least one surface of the transparent support substrate, and an uncured optical interference layer formed on the uncured hard coat layer, wherein the uncured hard coat layer comprises an active energy ray-curable composition for forming a hard coat layer, the uncured optical interference layer comprises an active energy ray-curable composition for forming an optical interference layer, the transparent support substrate has a thickness of 50 ?m or more and 600 ?m or less, a stretch ratio of the laminated film at 160° C. is 50% or more, and the laminated film heat-treated at a temperature of 90° C. for 30 minutes has a minimum value RAH of a reflectance taken between wavelengths of 380 nm and 780 nm of 2% or less and measured from a side of the uncured optical interference layer.

Abstract: Provided is a method for manufacturing a laminated film that can be molded into a complicated shape.

Abstract: Provided is a laminated film that can be molded into a complicated shape. A laminated film comprising a transparent support substrate; an uncured hard coat layer formed on at least one surface of the transparent support substrate; and an uncured optical interference layer formed on the uncured hard coat layer, wherein the uncured hard coat layer comprises an active energy ray-curable composition for forming a hard coat layer, the uncured optical interference layer comprises an active energy ray-curable composition for forming a optical interference layer, a thickness of the transparent support substrate is 50 ?m or more and 600 ?m or less, a luminous reflectance including regular reflected light measured from an uncured optical interference layer side is 0.1% or more and 4.0% or less, and a stretch ratio at 160° C. is 50% or more.

Abstract: Provided is a method for manufacturing a laminated film that can be molded into a complicated shape.

Abstract: An object of the present invention is to provide a laminated member for decoration that can be molded into a complicated shape and has a superior hardcoating property.

Abstract: An ink jet recording medium having an ink receiving layer containing a binder which containing an acrylonitrile butadiene type copolymer, the butadiene concentration of the copolymer is 50 weight % or more, and an inorganic pigment on one or two sides of a base paper mainly composed of wood pulp, wherein the concentration ratio of the acrylonitrile butadiene type copolymer to 100 parts by weight of the inorganic pigment is from one part by weight to eight parts by weight, while 60 weight % or more of the inorganic pigment is kaolin with particles of 0.4 ?m or more and below 4.2 ?m which account for 64% or more as the cumulative value of the volumetric basis when measured using a laser diffraction method, and the surface roughness of the ink receiving layer is from 0.6 ?m to 1.4 ?m when a hard backing is used at a clamp pressure of 1,000 kPa according to JIS P8151.

Abstract: An inkjet recording medium comprising an ink receiving layer formed by applying a coating layer containing a pigment and a binder to at least one side of a support having air permeability, and applying a coagulation solution for coagulating the binder on a surface of the coating layer by a coagulation cast coating method, wherein a boron compound, a cationic resin and cationic colloidal silica contained in the coagulation solution exist on the surface of the ink receiving layer.

Abstract: An inkjet recording medium comprising an ink-receiving layer containing a pigment and a binder formed on at least one side of a base paper containing calcium carbonate as a filler and pulp by a cast coating method, wherein the ash content of the calcium carbonate in the base paper is 15-30% by mass, and the ink-receiving layer contains colloidal silica as the pigment having a primary particle diameter of 30-70 nm and a ratio of the secondary particle diameter to the primary particle diameter of 1.5-3.0.

Abstract: An ink jet recording medium having an ink receiving layer containing a binder which containing an acrylonitrile butadiene type copolymer, the butadiene concentration of the copolymer is 50 weight % or more, and an inorganic pigment on one or two sides of a base paper mainly composed of wood pulp, wherein the concentration ratio of the acrylonitrile butadiene type copolymer to 100 parts by weight of the inorganic pigment is from one part by weight to eight parts by weight, while 60 weight % or more of the inorganic pigment is kaolin with particles of 0.4 ?m or more and below 4.2 ?m which account for 64% or more as the cumulative value of the volumetric basis when measured using a laser diffraction method, and the surface roughness of the ink receiving layer is from 0.6 ?m to 1.4 ?m when a hard backing is used at a clamp pressure of 1,000 kPa according to JIS P8151.