Abstract: A die cast, heat treated shaped aluminum silicon alloy article consisting essentially of, based on an alloy weight, from 13 or 25 wt % silicon, from 2 to 6 wt % copper, up to 1 wt % magnesium, balance alumium, said heat treated alloy being formed by the process comprising:subjecting said alloy while in molten condition to a primary pressure die casting at a casting pressure of from about 450 to about 500 kg/cm.sup.2 to form a primary pressure die cast product;removing the primary casting pressure from said primary pressure die cast product;prior to the time said aluminum silicon alloy completely solidifies, subjecting said primary pressure die cast alloy to a secondary pressure die casting so as to reduce the volume thereof from about 1.5 to about 3%;heating the thus treated product to a temperature of from about 460.degree. C. to about 520.degree. C. for a period of time of from about 2 to about 10 hours; andrapidly quenching said product to produce said article.

Abstract: A die cast, heat treated shaped aluminum silicon alloy article consisting essentially of, based on an alloy weight, from 13 to 25 wt % silicon, from 2 to 6 wt % copper, up to 1 wt % magnesium, balance aluminum, said heat treated alloy being formed by the process comprising: subjecting said alloy while in molten condition to a primary pressure die casting at a casting pressure of from about 450 to about 500 kg/cm.sup.2 to form a primary pressure die cast product; removing the primary casting pressure from said primary pressure die cast product; prior to the time said aluminum silicon alloy completely solidifies, subjecting said primary pressure die cast alloy to a secondary pressure die casting so as to reduce the volume thereof from about 1.5% to about 3%; heating the thus treated product to a temperature of from about 460.degree. C. to about 520.degree. C. for a period of time of from about 2 to about 10 hours; and rapidly quenching said product to produce said article.

Abstract: There are disclosed a shoe which is interposed between a swash plate and a piston of a swash plate type compressor and which converts rotary movement of the swash plate into reciprocal movement of the piston, and a method for manufacturing the same. The shoe has a hemispherical part which is in slidable contact with the surface of a piston defining a hemispherical recess, and a flat end face which is in slidable contact with a bottom end face of the swash plate. According to the method of the invention, a columnar element is compressed in the axial direction for plastic deformation in such a manner that one end of the columnar element is deformed along the inner surface of a hemispherical recess of a die while the other end is urged against the flat end surface of another die.

Abstract: There are disclosed a shoe which is interposed between a swash plate and a piston of a swash plate type compressor and which converts rotary movement of the swash plate into reciprocal movement of the piston, and a method for manufacturing the same. According to the method of the invention, a columnar element is compressed in the axial direction for plastic deformation in such a manner that one end of the columnar element is deformed along the inner surface of a hemispherical recess of a die while the other end is urged against the flat end surface of another die. A shoe can be easily manufactured with this method, which has a flank between the hemispherical part which is in slidable contact with the surface of the piston defining the hemispherical recess and the bottom end face of the swash plate which is in slidable contact with the swash plate.