Abstract: Disclosed are resin-coated paper having on one side of its base paper a first resin layer made of a resin composition obtained by melt-blending 90 to 65 parts by weight of a high-density polyethylene resin having a melt flow rate of 10.0 g/10 min to 40.0 g/10 min and a density of 0.960 g/cm.sup.3 or more and 10 to 35 parts by weight of a low-density polyethylene resin or a medium-density polyethylene resin, which has a melt flow rate of 0.2 g/10 min to 2 g/10 min, a density of 0.935 g/cm.sup.3 or less, a percentage of molecules with a molecular weight of 500,000 or more of 10% by weight or more and a critical shear rate of 0.5 (l/sec) or less, said resin composition obtained by the melt-blending having a critical shear rate of 10 (l/sec) or less; and a process for producing the resin-coated paper. The resin-coated paper is good in the molding processability of the resin layer, is excellent in the adhesion between the resin layer and the base paper, and contains only a small amount of a gel formed.