Abstract: An alkali metal acrylate polymer obtained by suspending an aqueous solution of acrylic acid and an alkali metal acrylate in an alicyclic or aliphatic hydrocarbon solvent containing a surfactant having an HLB value of 8-12 and subjecting the suspension to inverse suspension polymerization in the presence of a water-soluble radical polymerization initiator has a much higher water-absorbency and particularly salt solution-absorbency than known ones. If said polymer is crosslinked with a crosslinking agent, its stability in the fluid-absorbed state for a long period of time is improved and the absorption rate when absorbing water is also improved.

Abstract: A coating composite containing sulfochlorinated polyolefin having a sulfur content ranging from 0.2 to 2.5% by weight and a chlorine content ranging from 18 to 37% by weight is applied directly as an adhesive layer or is applied on one surface of a thermoplastic resin base to be contacted with a metal surface, which resin base is coated on the metal surface.When the coating composite is pressed thereafter under a pressure, a coating on the metal surface with excellent adhesion, water and impact resistances is provided.