Abstract: In a monolithic refractory, in terms of a proportion in 100 mass % of a refractory raw material having a grain size of 8 mm or smaller, an amount of CaXSr1?XAl2O4 (where, 0?X?0.5) is 0.5 mass % or more and 10 mass % or less, and a polyvalent metal salt of oxycarboxylic acid is 0.05 mass % or more and 1.0 mass % or less.

Abstract: In order to address the technical problem of allowing an unshaped refractory material using a spinel-containing alumina cement to provide further improved corrosion resistance and slag infiltration resistance while reducing the occurrence of crack/peeling, an unshaped refractory material is provided which comprises a refractory raw material mixture having a particle size of 8 mm or less, with the refractory raw material mixture having an alumina cement at least a part of which is a spinel-containing alumina cement, and, with respect to 100 mass % of the refractory raw material mixture, the alumina cement contains CaO in an amount of 0.5 to 2.5 mass %, and the spinel-containing alumina cement contains spinel in an amount of 3.5 to 10.5 mass %.

Abstract: In a monolithic refractory, in terms of a proportion in 100 mass % of a refractory raw material having a grain size of 8 mm or smaller, an amount of CaXSr1?XAl2O4 (where, 0?X?0.5) is 0.5 mass % or more and 10 mass % or less, and a polyvalent metal salt of oxycarboxylic acid is 0.05 mass % or more and 1.0 mass % or less.

Abstract: In order to address the technical problem of allowing an unshaped refractory material using a spinel-containing alumina cement to provide further improved corrosion resistance and slag infiltration resistance while reducing the occurrence of crack/peeling, an unshaped refractory material is provided which comprises a refractory raw material mixture having a particle size of 8 mm or less, with the refractory raw material mixture having an alumina cement at least a part of which is a spinel-containing alumina cement, and, with respect to 100 mass % of the refractory raw material mixture, the alumina cement contains CaO in an amount of 0.5 to 2.5 mass %, and the spinel-containing alumina cement contains spinel in an amount of 3.5 to 10.5 mass %.

Abstract: Disclosed is a method and apparatus for spray application of a monolithic refractory material, designed to add water to a powder material and knead the powder material during feeding. In the method and apparatus, a primary water injector 7 is arranged in a feed hose 5 extending from a spray-material supply device 1 to a distal spray nozzle 4, and a secondary water injector 8 is arranged in the feed hose at a position just before the distal spray nozzle 4. The primary water injector 7 is arranged on an upstream side of the secondary water injector 8 with a given distance therebetween. 10 to 50 mass %, preferably 15 to 40 mass %, of application water on the basis of the total application water required for the spray application is added from the primary water injector together with compression air in the form of water particles having an average particle size of 100 ?m or less, to evenly wet a spray material during feeding to the extent capable of preventing the spray material from being slurried.

Abstract: Disclosed is a method and apparatus for spray application of a monolithic refractory material, designed to add water to a powder material and knead the powder material during feeding. In the method and apparatus, a primary water injector 7 is arranged in a feed hose 5 extending from a spray-material supply device 1 to a distal spray nozzle 4, and a secondary water injector 8 is arranged in the feed hose at a position just before the distal spray nozzle 4. The primary water injector 7 is arranged on an upstream side of the secondary water injector 8 with a given distance therebetween. 10 to 50 mass %, preferably 15 to 40 mass %, of application water on the basis of the total application water required for the spray application is added from the primary water injector together with compression air in the form of water particles having an average particle size of 100 ?m or less, to evenly wet a spray material during feeding to the extent capable of preventing the spray material from being slurried.