Abstract: Thermoplastic molding compositions comprising, as substantive constituents, A) from 5 to 96% by weight of a vinylaromatic polymer with a syndiotactic structure, B) from 2 to 50% by weight of an inorganic filler, C) from 1 to 15% by weight of a thermoplastic elastomer based on copolymers made from vinylaromatic monomers, dienes and, where appropriate, 1,1-diphenylethylene, D) from 1 to 10% by weight of a compatibilizer, and, where appropriate, E) from 1 to 15% by weight of an elastomeric particulate styrene-diene block copolymer whose diene content may have been completely or to some extent hydrogenated, and, where appropriate, F) additives, where the total of the percentages by weight of A) to F) is 100.

Abstract: Ring-hydrogenated block copolymers composed of vinylaromatic monomers and dienes having at least two S blocks with differing molar mass composed of vinylaromatic monomers, mixtures with ring-hydrogenated polystyrene, and a process for their preparation.

Abstract: The invention relates to phosphacyclohexanes of general formulae I and II, wherein the following designations, among others, apply: R can represent hydrogen, C1-100-alkyl, C7-20-aralkyl, C7-20-alkaryl, and C6-12-aryl: R1 to R10 can independently represent hydrogen, C1-20-alkyl, C7-20-aralkyl, C7-20-alkaryl, and C6-12-aryl: W, W′ can independently represent single bonds or bridges comprising 1 to 20 carbon atoms, which can form part of a cyclic or aromatic group and can be interrupted by heteroatoms. Said phosphacyclohexanes are used as ligands in transition metal complexes of transition metals belonging to groups VIII to X of the periodic table.

Abstract: Thermoplastic molding compositions comprising, as substantive constituents A) from 5 to 95% by weight of a vinylaromatic polymer having a syndiotactic structure, B) from 2 to 50% by weight of an inorganic filler, C) from 1 to 45% by weight of an elastomeric, particulate graft polymer, D) from 1 to 10% by weight of a compatibilizer, and, where appropriate, E) from 1 to 45% by weight of an elastomeric particulate styrene-diene block copolymer whose diene fraction may have been completely or to some extent hydrogenated, and, where appropriate, F) from 1 to 35% by weight of a thermoplastic elastomer based on copolymers made from vinylaromatic monomers, dienes, and, where appropriate, 1,1-diphenylethylene, and, where appropriate, G) additives, where the total of the percentages by weight of A) to G) is 100.

Abstract: A process for the preparation of linear polymers or block copolymers of styrene by anionic polymerization comprises carrying out the chain termination with an n-alkyl glycidyl ether or a dialkyl ketone.

Abstract: A thermoplastic elastomer composition comprises a) from 5 to 99% by weight of a block copolymer which is composed of hard blocks S made from vinyl aromatic monomers and of one or more random soft blocks B/S made from dienes and from vinyl aromatic monomers, b) from 1 to 95% by weight of a plasticizer with a higher polarity than white oil and with a lower polarity than diisooctyl phthalate, c) from 0 to 50% by weight of a polyolefin, and d) from 0 to 60% by weight of additives, where the total of a) to d) is 100% by weight. The use of the molding compositions to produce flexible or elastic moldings is described, as are the resultant moldings.

Abstract: Linear or star block copolymers which have at least one polymer block A which is essentially composed of isobutene units and at least two polymer blocks B which are essentially composed of units which are derived from vinylaromatic monomers are used as resilient sealing material. In particular, such sealing materials are used for sealing the edge joints in insulation glass panes, and insulation glass panes have a flexible edge joint seal which contains one of the block copolymers.

Abstract: Thermoplastic molding compositions comprising, as substantive constituents,

Abstract: Block copolymers comprise at least two hard blocks S1 and S2 made from vinylaromatic monomers and, between these, at least one random soft block B/S made from vinylaromatic monomers and from dienes, where the proportion of the hard blocks is above 40% by weight, based on the total block copolymer.

Abstract: Thermoplastic molding compositions comprising, as substantive constituents

Abstract: Thermoplastic molding compositions comprising (A) 5 to 98%-wt., based on components (A) through (E), of at least one elastomeric graft copolymer, (B) 1 to 90%-wt., based on components (A) through (E), of a further copolymer, (C) 1 to 70%-wt., based on components (A) though (D), of an elastomeric block copolymer composed of at least one block CA (hard phase) having copolymerized units of a vinylaromatic monomer, and at least one elastomeric block C(B/A) (soft phase) having copolymerized units of a vinylaromatic monomer, and of a diene, (D) 0 to 300%-wt., based on components (A) through (C), of a polycarbonate, and (E) 0 to 30%-wt., based on components (A) through (E), of conventional additives and processing aids, are useful for producing films, moldings or fibers.

Abstract: Block copolymers comprise at least two hard blocks S1 and S2 made from vinyl aromatic monomers and, between these, at least ore random soft block B/S made from vinyl aromatic monomers and from dienes, where the proportion of the hard blocks is above 40% by weight, based on the total block copolymer, wherein the 1,2-vinyl content in the soft block B/S is less than 20%.

Abstract: A process for the continuous anionic polymerization or copolymerization of styrene or diene monomers using an alkali metal alkyl compound as polymerization initiator is carried out in the presence of an alkyl- or arylmetal compound of an element which occurs in at least divalent form as rate regulator, preferably under non-isothermal conditions and without back-mixing in a tubular or tube-bundle reactor, preferably using an alkyl- or arylmetal compound A of the formula R1M1 and an alkyl- or arylmetal compound B of the formula R2nM2 in a molar ratio between B and A of from 0.1:1 to 500:1, where M1 is Li, Na or K; R1 is hydrogen, C1-C20-alkyl, C6-C20-aryl, or C7-C20-alkyl-substituted aryl; M2 is an n-valent element from group 2a, 2b or 3a of the Periodic Table; and R2 is hydrogen, halogen, C1-C20-alkyl or C6-C20-aryl; and a special anionic polymerization initiator containing no Lewis base.

Abstract: Polymerization initiator comprising an alkaline earth metal compound chosen from the group a) of heteroleptic alkaline earth metal compounds of the formula I L—M—R  (I)  or b) of cationic alkaline earth metal complexes of the formula II [D→M—R]+X−  (II),  where M: is Ca, Sr or Ba, L: is a polymerization-inactive ligand, R: is a polymerization-active ligand, D: is a donor ligand, and X: is a non-coordinating anion, and processes for the preparation of the polymerization initiators and processes for anionic polymerization in the presence of the polymerization initiators.

Abstract: A process for the reaction of an organic compound in the presence of a catalyst comprising, as active metal, ruthenium alone or together with at least one Group Ib, VIIb, or VIIIb metal in an amount of from 0.01 to 30 wt %, based on the total weight of the catalyst, applied to a support, wherein from 10 to 50% of the pore volume of the support comprises macropores having a pore diameter in the range of from 50 nm to 10,000 nm and from 50 to 90% of the pore volume of the support comprises mesopores having a pore diameter in the range of from 2 to 50 nm, the sum of said pore volumes being 100%, and said catalyst as such.

Abstract: Polymer mixtures comprise P1) from 1 to 85% by weight of an elastomeric block copolymer which has been built up from hard blocks S made from vinylaromatic monomers and from random soft blocks B/S made up from dienes and from vinylaromatic monomers, and which contains at least the block structure S-B/S-S, where the diene content is less than 50 percent by weight and the proportion of the soft phase formed from the blocks B/S is at least 60 percent by weight, based in each case on the entire block copolymer, P2) from 5 to 89% by weight of a block copolymer differing from P1) and made from vinylaromatic monomers and from dienes, P3) from 10 to 94% by weight of glass-clear or impact-modified polystyrene or mixtures thereof, and P4) from 0 to 84% by weight of other additives, where the total of components P1) to P4) is 100%.

Abstract: In a process for the preparation of block copolymers from vinylaromatic monomers and dienes, the monomers are polymerized in the presence of at least one alkali metal organyl or alkali metal alkoxide and at least one magnesium, aluminum or zinc organyl.

Abstract: In a process for the homopolymerization of vinylaromatic monomers or the copolymerization of vinylaromatic monomers and dienes in the presence of at least one alkali metal compound and at least one compound of an element of group 3a of the Periodic Table of the elements, the compounds contain, based on the sum of molar equivalents of alkali metal and elements of group 3a, in each case a) from 0.1 to 3.9 molar equivalents of oxygen, sulfur, nitrogen or phosphorus and b) from 0.1 to 3.9 molar equivalents of an organyl ligand.

Abstract: A process for the preparation of bisorganoalkaline earth metal compounds comprises reacting an organometallic compound RnM2 with an alkaline earth metal salt M1Xm.

Abstract: A molding material as based on from 60 to 98% by weight of a hard matrix A comprising polymerized or copolymerized units of at least one vinylaromatic monomer or at least one vinylaromatic monomer and at least one polar comonomer and from 2 to 40% by weight, the percentages in each case being based on the molding material comprising A and B, of a soft phase B formed from a hydrogenated or unhydrogenated block copolymer prepared by anionic polymerization and comprising a vinylaromatic monomer V and a diene D, having at least one random or quasi-random block (V/D) of vinylaromatic monomer and diene and containing from 10 to 80% by weight, based on the soft phase B, of occlusions of matrix material (a) formed during the polymerization of the hard matrix A in the presence of the block rubber, and said molding material is used for the production of films, sheets or moldings.