Abstract: The invention provides wire rod excellent in drawability and steel wire made from the wire rod as starting material with high productivity at good yield and low cost. A hard steel wire rod of a specified composition is hot rolled, the hot-rolled steel is coiled in a specified temperature range, and the coiled steel is subjected to patenting at a predetermined cooling rate, thereby affording a high-carbon steel wire excellent in workability. It is high-strength steel wire excellent in drawability comprising a pearlite structure of an area ratio of 97% or greater and the balance of non-pearlite structures including bainite, degenerate-pearlite and pro-eutectoid ferrite and having a pearlite block size of not less than 20 ?m and not greater than 45 ?m. The invention also provides a high-carbon steel wire excellent in ductility, which is manufactured by subjecting the wire rod to intermediate patenting and cold drawing and has a tensile strength of 2800 MPa or greater.

Abstract: The invention provides wire rod excellent in drawability and steel wire made from the wire rod as starting material with high productivity at good yield and low cost. A hard steel wire rod of a specified composition is heated in a specified temperature range to conduct post-reaustenization patenting and thereby obtain a high-carbon steel wire excellent in ductility that has a pearlite structure of an area ratio of 97% or greater and the balance of non-pearlite structures including bainite, degenerate-pearlite and pro-eutectoid ferrite and whose fracture reduction of area RA satisfies Expressions (1), (2) and (3) below: RA?RAmin??(1), where RAmin=a?b×pearlite block size (?m), a=?0.0001187×TS (MPa)2+0.31814×TS (MPa)?151.32??(2) b=0.0007445×TS (MPa)?0.3753??(3).

Abstract: The invention provides wire rod excellent in drawability and steel wire made from the wire rod as starting material with high productivity at good yield and low cost. A hard steel wire rod of a specified composition is heated in a specified temperature range to conduct post-reaustenization patenting and thereby obtain a high-carbon steel wire excellent in ductility that has a pearlite structure of an area ratio of 97% or greater and the balance of non-pearlite structures including bainite, degenerate-pearlite and pro-eutectoid ferrite and whose fracture reduction of area RA satisfies Expressions (1), (2) and (3) below: RA?Ramin??(1), where RAmin=a?b×pearlite block size (?m), a=?0.0001187×TS (MPa)2+0.31814×TS (MPa)?151.32??(2) b=0.0007445×TS (MPa)?0.3753??(3).

Abstract: The invention provides wire rod excellent in drawability and steel wire made from the wire rod as starting material with high productivity at good yield and low cost. A hard steel wire rod of a specified composition is hot rolled, the hot-rolled steel is coiled in a specified temperature range, and the coiled steel is subjected to patenting at a predetermined cooling rate, thereby affording a high-carbon steel wire excellent in workability. It is high-strength steel wire excellent in drawability comprising a pearlite structure of an area ratio of 97% or greater and the balance of non-pearlite structures including bainite, degenerate-pearlite and pro-eutectoid ferrite and having a pearlite block size of not less than 20 ?m and not greater than 45 ?m. The invention also provides a high-carbon steel wire excellent in ductility, which is manufactured by subjecting the wire rod to intermediate patenting and cold drawing and has a tensile strength of 2800 MPa or greater.