Abstract: The present invention relates to a sinter powder (SP) comprising at least one semicrystalline terephthalate polyester (A), at least one amorphous terephthalate polyester (B) and at least one phosphinic salt (C). The present invention further relates to a method of producing a shaped body by sintering the sinter powder (SP) or by an FFF (fused filament fabrication) method, to a shaped body obtainable by the method of the invention, and to the use of a phosphinic salt in a sinter powder (SP) for broadening the sintering window (WSP) of the sinter powder (SP).

Abstract: The present invention relates to a process for producing a polyamide powder (PP) comprising at least one semicrystalline polyamide (P) and at least one additive (A). The semicrystalline polyamide (P) and the at least one additive (A) are initially compounded with one another in an extruder and subsequently introduced into a solvent (SV) in which the at least one semicrystalline polyamide (P) then crystallizes to obtain the polyamide powder (PP). The present invention further relates to the thus obtainable polyamide powder (PP) and to the use of the polyamide powder (PP) as sintering powder (SP) and also to a process for producing a shaped body by selective laser sintering of a polyamide powder (PP).

Abstract: The present invention relates to a process for producing a shaped body, wherein, in step i), a layer of a sinter powder (SP) comprising at least one mineral flame retardant inter alia is provided and, in step ii), the layer provided in step i) is exposed. The present invention further relates to a process for producing a sinter powder (SP) and to a sinter powder (SP) obtainable by this process. The present invention also relates to the use of the sinter powder (SP) in a sintering process and to shaped bodies obtainable by the process of the invention.

Abstract: The present invention relates to a process for the production of a reinforced polyamide (rP) in an extruder. In this process, a first mixture (M1), a second mixture (M2) and a third mixture (M3) are added into the extruder, and subsequently at least one carbon material is added to obtain a carbon containing polymerizable mixture (cpM) in the extruder. This carbon containing polymerizable mixture (cpM) is polymerized and subsequently devolatilized to obtain the reinforced polyamide (rP). Furthermore, the present invention relates to the reinforced polyamide (rP) obtainable by the inventive process.

Abstract: The present invention relates to a sinter powder (SP) comprising at least one semicrystalline terephthalate polyester (A), at least one amorphous terephthalate polyester (B) and at least one phosphinic salt (C). The present invention further relates to a method of producing a shaped body by sintering the sinter powder (SP) or by an FFF (fused filament fabrication) method, to a shaped body obtainable by the method of the invention, and to the use of a phosphinic salt in a sinter powder (SP) for broadening the sintering window (WSP) of the sinter powder (SP).

Abstract: The present invention relates to a method of producing a shaped body, wherein, in step i), a layer of a sinter powder (SP) comprising at least one polyhydric alcohol inter alia is provided and, in step ii), the layer provided in step i) is exposed. The present invention further relates to a method of producing a sinter powder (SP) and to a sinter powder (SP) obtainable by this method. The present invention also relates to use of the sinter powder (SP) in a sintering method, and shaped bodies obtainable by the method of the invention.

Abstract: A process for the production of sinter powder particles (SP), comprising the steps a) providing at least one continuous filament, b) coating, the at least one continuous filament provided in step a) with at least one thermoplastic polymer to obtain a continuous strand comprising the at least one continuous filament, coated with the at least one thermoplastic polymer, wherein the average cross-sectional diameter of the strand is in the range of 10 to 300 pm, and c) size reducing of the continuous strand provided in step b) in order to obtain the sinter powder particles (SP), wherein the average length of the sinter powder particles (SP) is in the range of 10 to 300 pm.

Abstract: A thermoplastic molding composition containing A) 20 to 99.9 wt % of a thermoplastic polyamide, B) 0.1 to 40 wt % of an alkenylsuccinic acid derivative obtained by reaction of polyiso-butene (B1) having a number-average molecular weight Mn of 10,000 to 50,000 at temperatures of 180° C. to 250° C. with maleic acid or derivatives thereof (B2) in a stoichiometric ratio of at least 2 equivalents of ?,?-unsaturated mono- and dicarboxylic acid or derivatives thereof (B2) per reactive double bond in the polyisobutene (B1) for a duration of at least 15 minutes to 10 hours and up to 10 bar of positive pressure, wherein the derivatives are anhydrides, mono- or dialkyl esters, and mixed esters, and wherein the reactive double bonds are the sum total of the terminal ?- and ?-double bonds in the polyisobutene (B1), and C) 0 to 60 wt % of further additives, wherein the weight percentages for the components A) to C) sum to 100%.

Abstract: The present invention relates to a process for producing a shaped body, wherein, in step i), a layer of a sinter powder (SP) comprising at least one near infrared reflector inter alia is provided and, in step ii), the layer provided in step i) is exposed. The present invention further relates to a process for producing a sinter powder (SP) and to the sinter powder (SP) obtainable by this process, and to the use of a near infrared reflector in a sinter powder (SP). The present invention also relates to a shaped body obtainable by the process of the invention.

Abstract: The present invention relates to a process for producing a shaped body, wherein, in step i), a layer of a sinter powder (SP) comprising at least one mineral flame retardant inter alia is provided and, in step ii), the layer provided in step i) is exposed. The present invention further relates to a process for producing a sinter powder (SP) and to a sinter powder (SP) obtainable by this process. The present invention also relates to the use of the sinter powder (SP) in a sintering process and to shaped bodies obtainable by the process of the invention.

Abstract: A thermoplastic molding composition containing A) 20 to 99.9 wt % of a thermoplastic polyamide, B) 0.1 to 40 wt % of an alkenylsuccinic acid derivative obtained by reaction of polyiso-butene (B1) having a number-average molecular weight Mn of 10,000 to 50,000 at temperatures of 180° C. to 250° C. with maleic acid or derivatives thereof (B2) in a stoichiometric ratio of at least 2 equivalents of ?,?-unsaturated mono- and dicarboxylic acid or derivatives thereof (B2) per reactive double bond in the polyisobutene (B1) for a duration of at least 15 minutes to 10 hours and up to 10 bar of positive pressure, wherein the derivatives are anhydrides, mono- or dialkyl esters, and mixed esters, and wherein the reactive double bonds are the sum total of the terminal ?- and ?-double bonds in the polyisobutene (B1), and C) 0 to 60 wt % of further additives, wherein the weight percentages for the components A) to C) sum to 100%.

Abstract: The present invention relates to a process for the production of a reinforced polyamide (rP) in an extruder. In this process, a first mixture (M1), a second mixture (M2) and a third mixture (M3) are added into the extruder, and subsequently at least one carbon material is added to obtain a carbon containing polymerizable mixture (cpM) in the extruder. This carbon containing polymerizable mixture (cpM) is polymerized and subsequently devolatilized to obtain the reinforced polyamide (rP). Furthermore, the present invention relates to the reinforced polyamide (rP) obtainable by the inventive process.

Abstract: The present invention relates to a process for producing a shaped body by selective laser sintering of a sinter powder (SP). The sinter powder (SP) comprises at least one semicrystalline polyamide, at least one nylon-6I/6T and at least one reinforcing agent. The present invention further relates to a shaped body obtainable by the process of the invention and to the use of nylon-6I/6T in a sinter powder (SP) comprising at least one semicrystalline polyamide, at least one nylon-6I/6T and at least one reinforcing agent for broadening the sintering window (WSP) of the sinter powder (SP).