Abstract: A colored base coating composition includes a chlorinated polyolefin resin grafted with an acrylic component in which the acrylic component has a glass transition temperature (Tg) of 60° C. or more and an OH group-containing acrylic resin. The chlorinated polyolefin resin grafted with the acrylic component and the OH group-containing acrylic resin have a mass ratio of nonvolatile matters thereof ranging from 70/30 to 50/50. The colored base coating composition is applied on a substrate made of a nonpolar resin to form a colored base coat, and the coat is dried so that a nonvolatile matter of the coat becomes 70 to 100% by mass. A clear coating composition having a coating viscosity of 15 to 50 mPa·s is applied on the colored base coat to form the clear coat, and the clear coat is irradiated with an active energy ray in an atmosphere having an oxygen content of 5% by mass or less to be cured.

Abstract: It is an object of the present invention to provide a method of coating a plastic molding which is appropriately applicable to various plastic substrates, an ultraviolet-curable under coating for metal evaporation, which is to be used in that method of coating, and a plastic molding obtained by that method of coating.

Abstract: It is an object of the present invention to provide a method of coating a plastic molding which is appropriately applicable to various plastic substrates, an ultraviolet-curable under coating for metal evaporation, which is to be used in that method of coating, and a plastic molding obtained by that method of coating.

Abstract: An ultraviolet-curing liquid undercoating composition for use in metallizing FRP, which is a one-component type, has an unlimited pot life, and is excellent in adhesion and heat resistance. The composition comprises 20 to 80 parts by weight of a compound(s) containing at least two (meth)acryloyl groups in its molecule, 80 to 20 parts by weight of oil-modified alkyd resin(s), and 2 to 15 parts by weight of a sensitizer, optionally further 5 to 20 parts by weight of an amino resin based on 100 parts by weight in total of the above compound and the above alkyd resin(s). It is suited for the undercoating of an automotive reflector.