Abstract: The present disclosure pertains to methods of capturing CO2 from an environment at pressures above 1 bar by associating the environment with a porous material that has a surface area of at least 2,800 m2/g, and a total pore volume of at least 1.35 cm3/g, where a majority of pores of the porous material have diameters of less than 2 nm. The present disclosure also pertains to methods for the separation of CO2 from natural gas in an environment at partial pressures of either component above 1 bar by associating the environment with a porous material that has a surface area of at least 2,200 m2/g, and a total pore volume of at least 1.00 cm3/g, where a majority of pores of the porous material have diameters of greater than 1 nm and less than 2 nm.

Abstract: The present disclosure pertains to materials for CO2 adsorption at pressures above 1 bar, where the materials include a porous material with a surface area of at least 2,800 m2/g, and a total pore volume of at least 1.35 cm3/g, where a majority of pores of the porous material have diameters of less than 2 nm as measured from N2 sorption isotherms using the BET (Brunauer-Emmett-Teller) method. The present disclosure also pertains to materials for separation of CO2 from natural gas at partial pressures of either component above 1 bar, where the materials include a porous material with a surface area of at least 2,200 m2/g, and a total pore volume of at least 1.00 cm3/g, where a majority of pores of the porous material have diameters of greater than 1 nm and less than 2 nm as measured from N2 sorption isotherms using the BET method.

Abstract: The present disclosure pertains to methods of capturing CO2 from an environment at pressures above 1 bar by associating the environment with a porous material that has a surface area of at least 2,800 m2/g, and a total pore volume of at least 1.35 cm3/g, where a majority of pores of the porous material have diameters of less than 2 nm. The present disclosure also pertains to methods for the separation of CO2 from natural gas in an environment at partial pressures of either component above 1 bar by associating the environment with a porous material that has a surface area of at least 2,200 m2/g, and a total pore volume of at least 1.00 cm3/g, where a majority of pores of the porous material have diameters of greater than 1 nm and less than 2 nm.

Abstract: The present disclosure pertains to materials for CO2 adsorption at pressures above 1 bar, where the materials include a porous material with a surface area of at least 2,800 m2/g, and a total pore volume of at least 1.35 cm3/g, where a majority of pores of the porous material have diameters of less than 2 nm as measured from N2 sorption isotherms using the BET (Brunauer-Emmett-Teller) method. The present disclosure also pertains to materials for separation of CO2 from natural gas at partial pressures of either component above 1 bar, where the materials include a porous material with a surface area of at least 2,200 m2/g, and a total pore volume of at least 1.00 cm3/g, where a majority of pores of the porous material have diameters of greater than 1 nm and less than 2 nm as measured from N2 sorption isotherms using the BET method.

Abstract: The present disclosure pertains to materials for CO2 adsorption at pressures above 1 bar, where the materials include a porous carbon material with a surface area of at least 2800 m2/g, a total pore volume of at least 1.35 cm3/g, and a carbon content of 80%-95%. The porous carbon material is prepared by heating organic polymer precursors or biological materials in the presence of KOH at 700° C.-800° C. The present disclosure also pertains to materials for the separation of CO2 from natural gas at partial pressures above 1 bar, where the material includes a porous carbon material with a surface area of at least 2000 m2/g, a total pore volume of at least 1.00 cm3/g, and a carbon content of greater than 90%. The porous carbon materials can be prepared by heating organic polymer precursors or biological materials in the presence of KOH at 600° C.-700° C.