Abstract: A water-based polyurethane resin and a method for manufacturing the same are provided. The method for manufacturing the water-based polyurethane includes: a preparation step of a prepolymer, a dilution step of the prepolymer, a water dispersion and chain extension step, and an acrylic synthesis step. The method further includes mixing polyol and polyisocyanate to obtain a prepolymer, and diluting the prepolymer by adding acrylic monomer in the prepolymer. In the water-based polyurethane resin, at least one of the polyhydric alcohol, polyisocyanate, and the acrylic monomer includes a compound with a cyclic structure.

Abstract: A modified bismaleimide resin, a method for preparing the same, a prepreg, a copper clad laminate, and a printed circuit board are provided. The modified bismaleimide resin is formed by a reaction between a diamine compound having a nonpolar backbone structure and maleic anhydride, and a molecular structure thereof contains a greater amount of non-polar and hydrophobic groups.

Abstract: An organosilicon-modified polyurethane resin and a method for producing the same are provided. The organosilicon-modified polyurethane resin includes organosilicon ingredients obtained by chemically bonding a first organosilicon chain extender having a chemical structure of formula (I) and a second organosilicon chain extender having a chemical structure of formula (II) into a molecular structure of a polyurethane resin during a polymerization reaction: in which R11 is a substituent of —CH2CH2— or —CH2CH(CH3)—, n1 is a positive integer between 0 and 50, m1 is a positive integer between 0 and 50, and x1 is a positive integer between 4 and 100; in which R21 is a substituent of —CH3 or —CH2CH3, R22 is a substituent of —CH2CH2CH2—, and R23 is a substituent of —CH2CH2— or —CH2CH(CH3)—, n2 is a positive integer between 6 and 130, and m2 is a positive integer between 4 and 50.

Abstract: A method for preparing an aqueous polyurethane dispersion includes the following steps. The method characterized in that it introduces an ethoxy group to sodium ethylenediamine sulfonate (H2N—CH2CH2NHCH2CH2SO3Na) serving as an anionic chain extender to form sodium ethylenediamino ethoxyethyl sulfonate (H2NCH2CH2NHCH2CH2OCH2CH2SO3Na). Next, hydrophilic groups of sodium ethylenediamino ethoxyethyl sulfonate are used to prepare an aqueous polyurethane to improve the flowability of the resin, in which the polyurethane prepolymer has an isocyanate group at its end. More than one acrylate monomer is used for dilution and reduction of viscosity, and hydrophilic and amine groups containing sulfonate is used for water dispersion and to carry out a chain extension reaction. After that, an initiator is added for acrylic polymerization, so as to modify polyurethane with graft acrylic.

Abstract: A water-based surface treatment agent is provided. The water-based surface treatment agent is suitable to be coated onto a surface of a synthetic leather. The water-based surface treatment agent at least includes waterborne polyurethane, silicone powder, and water. Based on 100 parts by weight of the water-based surface treatment agent, a content of the waterborne polyurethane is within 15 to 35 parts by weight, and a content of the silicone powder is within 3 to 20 parts by weight. A non-volatile matter content of the waterborne polyurethane is within a range from 20 wt % to 30 wt %. Each grain of the silicone powder has a particle size within a range from 0.2 ?m to 15 ?m, a specific gravity within a range from 0.9 to 1.5, a water content within a range from 0.1% to 0.5%, and a hardness (A) within a range from 30 to 90.

Abstract: An aqueous acrylic resin with high heat resistance, a polymeric composition, and a method for preparing the aqueous acrylic resin with high heat resistance are provided. The polymeric composition includes a monomer composition and a reactive emulsifier. Based on 100 wt % of the monomer composition, the monomer composition includes at least one alkyl group containing methyl acrylate, at least one carboxyl group containing methacrylic acid, an alkene-based unsaturated group containing methyl acrylate, a hydroxyl group containing acrylic polyester polyol and/or a hydroxyl group containing acrylic polyether polyol, and an alkoxysilane.

Abstract: A fiber having both thermal-insulating and cool-feeling functions and a fabric having both thermal-insulating and cool-feeling functions are provided. The fiber includes a thermal-insulating part and a cool-feeling part encapsulating the thermal-insulating part. A material of the thermal-insulating part includes a first base material and a near infrared reflective material dispersed in the first base material. The near infrared reflective material is selected from the group consisting of iron, cobalt, chromium, copper, nickel, bismuth, and an alloy thereof. A material of the cool-feeling part includes a second base material and a cool feeling material dispersed in the second base material. The cool feeling material is a silicate containing at least one metal selected from the group consisting of calcium, magnesium, sodium, and aluminum. The fabric having both thermal-insulating and cool-feeling functions is woven from the fiber having both thermal-insulating and cool-feeling functions.

Abstract: A visible light shielding structure is provided. The visible light shielding structure includes a metal foil layer, two adhesive layers, and two synthesized paper layers. The metal foil layer has a first surface and a second surface opposite to the first surface. The two adhesive layers are disposed on the first surface and the second surface of the metal foil layer, respectively. The two synthesized paper layers are disposed on the two adhesive layers, respectively. Each of the two synthesized paper layers is a polypropylene based resin layer.

Abstract: A release film for high-capacity multilayer ceramic capacitor (MLCC) 0.5-0.8 ?m ceramic slurry and a production method thereof. The release film includes at least three layers of co-extruded polyester resin having a layer A, a layer B and a layer C, and stretching the same in longitudinal and transverse directions. In addition, the layer B includes recycled polyester resin, the layers A and C include new polyester resin raw materials, and a releasing agent having a phenyl releasing control agent. The production method for the release film includes coating a releasing agent on one or both sides of a polyester film, and winding into a roll after drying and hardening.

Abstract: A method for manufacturing high heat resistant and high scratch resistant water-based polyurethane, which can improve the mechanical strength and water resistance of water-based polyurethane by using acrylate graft modification, is provided. In particular, 2-hydroxyethyl acrylate (2-HEA), methyl methacrylate (MMA), ethyl acrylate (EA), acrylic acid (AA), glycidyl methacrylate (GMA) and triallyl isocyanuric acid ester (TAIC) are used to dilute polyurethane prepolymer. As a result, the prepolymer has a good dispersing effect, and further, waterborne bridging agent and cellulose nanofiber are added to the water-based polyurethane to obtain water-based polyurethane which has high heat resistance and scratch resistance.

Abstract: A curing agent composition and a curing agent coating formula thereof are provided. The curing agent composition includes 5 to 25 wt % of an ester group-containing amine end group adduct, 2 to 25 wt % of a C8-C22 hydrophobic saturated or unsaturated fatty amine, 2 to 25 wt % of a polyamine compound, 2 to 20 wt % of a silane compound, and 10 to 60 wt % of an ether solvent.

Abstract: A curing agent and method for producing the same are provided, the method includes: esterification reaction: reacting a polyhydric alcohol with a polybasic acid anhydride to obtain an ester-based emulsifier (A); chain extension reaction: reacting an ester-based emulsifier (A) with a bifunctional epoxy resin to obtain a polymer intermediate (B); and reacting the polymer intermediate (B) with a polyamine compound to obtain a curing agent (C).

Abstract: An aqueous coating material for synthetic papers includes 26 wt % to 75 wt % of an acrylic emulsion, 2 wt % to 10 wt % of hollow latex microspheres and 26 wt % to 70 wt % of an inorganic ink-absorbing material. Each of the hollow latex microspheres has a particle size between 500 nm and 1100 nm, and includes a hollow core, a buffering layer covering the hollow core, and a shell covering the buffering layer. The aqueous coating material can be applied onto a surface of a synthetic paper substrate and formed into a surface coating layer.

Abstract: A dark-colored and infrared-reflective fiber without metal composition, a manufacturing method thereof, and a dark-colored and infrared-reflective textile are provided. The dark-colored and infrared-reflective fiber includes a polymer resin material and an organic azo pigment. The organic azo pigment is dispersed in the polymer resin material in the form of a plurality of micro particles. The organic azo pigment has an average particle size between 0.2 micrometers and 4 micrometers and a heat-resistant temperature of not less than 300° C. The organic azo pigment has an infrared reflectance of not less than 50% in an infrared wavelength range between 780 nm and 2,500 nm.

Abstract: An eco-friendly synthetic paper and a method for manufacturing the same are provided. The eco-friendly synthetic paper includes a light-shielding adhesive layer and two polypropylene-based resin layers. The light-shielding adhesive layer has a first surface and a second surface opposite to the first surface. The two polypropylene-based resin layers are respectively attached to the first surface and the second surface of the light-shielding adhesive layer. The light-shielding adhesive layer contains an adhesive component and a black colorant. The adhesive component is present in an amount between 35.9 wt % and 63.1 wt % of the total weight of the light-shielding bonding layer, and the black colorant is present in an amount between 12.9 wt % and 21.7 wt % of the total weight of the light-shielding bonding layer.

Abstract: A liquid crystal polymer film, and a composite film of liquid crystal polymer and polyimide and a manufacturing method thereof are provided. The liquid crystal polymer film includes 63 wt % to 74 wt % of p-hydroxybenzoic acid, 21 wt % to 26 wt % of 6-hydroxy-2-naphthoic acid, and 5 wt % to 11 wt % of p-hydroxycinnamic acid. The composite film is manufactured by thermocompressing a single layer or multi layers of liquid crystal polymer film and polyimide film so that the composite film can have high flatness and the surface roughness Sa of the composite film is ranging from 0.1 ?m to 10 ?m. In the production process of the composite film, the composite film is rolled up and attached to a copper foil to form a high frequency substrate with good processability. After peeling the polyimide film, the liquid crystal polymer film can be thermocompressed to form a four-layered, six-layered, eight-layered or eight-layered high frequency substrate.

Abstract: A method for preparing an aqueous polyurethane dispersion includes the following steps. The method characterized in that it introduces an ethoxy group to sodium ethylenediamine sulfonate (H2N—CH2CH2NHCH2CH2SO3Na) serving as an anionic chain extender to form sodium ethylenediamino ethoxyethyl sulfonate (H2NCH2CH2NHCH2CH2OCH2CH2SO3Na). Next, hydrophilic groups of sodium ethylenediamino ethoxyethyl sulfonate are used to prepare an aqueous polyurethane to improve the flowability of the resin, in which the polyurethane prepolymer has an isocyanate group at its end. More than one acrylate monomer is used for dilution and reduction of viscosity, and hydrophilic and amine groups containing sulfonate is used for water dispersion and to carry out a chain extension reaction. After that, an initiator is added for acrylic polymerization, so as to modify polyurethane with graft acrylic.

Abstract: An optical clear adhesive (OCA) and a manufacturing method thereof are provided. The OCA is a three-layer laminated structure including an OCA transparent film, a high release film coated on a lower surface of the OCA transparent film and a light release film coated on an upper surface of the OCA transparent. The high release film and the light release film contain 0.01 to 3 wt % of UV absorber. After UV light irradiation, the OCA transparent film has a suitable peeling force between the light release film and the high release film.

Abstract: A process for preparing solvent-free aqueous polyurethane dispersion modified with acrylic grafting is divided into four steps. The first step is a reaction of a diisocyanate with a polyol to prepare a prepolymer; the second step involves diluting the prepolymer with an acrylate monomer and adding a sulfonate-based chain extender to react; the third step involves adding deionized water and a water-soluble diamine-based chain extender to obtain a solvent-free sulfonate-based aqueous polyurethane dispersion; and the fourth step involves letting the aqueous polyurethane become modified with acrylic grafting. The resulting aqueous polyurethane has excellent mechanical strength, heat resistance and water resistance.

Abstract: A release film for high-capacity multilayer ceramic capacitor (MLCC) 0.5-0.8 ?m ceramic slurry and a production method thereof. The release film includes at least three layers of co-extruded polyester resin having a layer A, a layer B and a layer C, and stretching the same in longitudinal and transverse directions. In addition, the layer B includes recycled polyester resin, the layers A and C include new polyester resin raw materials, and a releasing agent having a phenyl releasing control agent. The production method for the release film includes coating a releasing agent on one or both sides of a polyester film, and winding into a roll after drying and hardening.