Abstract: A vehicle windshield wiper blade comprising: a blade support portion; and a lip portion, wherein the lip portion has a tapered portion having a cross section that is taken along a direction perpendicular to the longitudinal direction of the wiper blade and that has a width that gradually decreases from a side closer to the blade support portion towards a direction farthest away from the blade support portion, the lip portion has a tip surface and first and second tapered surfaces constituting the tapered portion, and, in a specific observation region of the first and second tapered surfaces, the average value of the elastic modulus measured at a 0.1 ?m pitch is 15-470 MPa and the coefficient of variation of the elastic modulus is at most 17.6%.

Abstract: A cleaning wiper blade comprises a hand grip part and an elastic part. The elastic part comprises a polyurethane. The polyurethane comprises a reactant of a composition including an isocyanate compound which includes diisocyanate and polyfunctional isocyanate, and an alcohol which includes polyfunctional alcohol. The diisocyanate has an aromatic ring in a molecule. When a molecule of the polyurethane is ionized with a mass spectrometer of a direct sample injection system, then obtained M1, M2 and M3 satisfy the is 0.013 to 0.300, and a concentration of the polyfunctional alcohol in the polyurethane is 0.12 mmol/g to 0.65 mmol/g.

Abstract: A vehicle windshield wiper blade comprising: a blade support portion; and a lip portion, wherein the lip portion has a tapered portion having a cross section that is taken along a direction perpendicular to the longitudinal direction of the wiper blade and that has a width that gradually decreases from a side closer to the blade support portion towards a direction farthest away from the blade support portion, the lip portion has a tip surface and first and second tapered surfaces constituting the tapered portion, and, in a specific observation region of the first and second tapered surfaces, the average value of the elastic modulus measured at a 0.1 ?m pitch is 15-470 MPa and the coefficient of variation of the elastic modulus is at most 17.6%.

Abstract: A wiper blade comprising: a hand grip portion; and an elastic portion supported by the hand grip portion and that is pressed against a surface to be cleaned; the elastic portion having, on a tip side, a main surface opposing a member to be cleaned, and a tip surface that forms a tip side edge together with the main surface, and in a specific observation region of the tip surface and the main surface, the average value of elastic modulus values obtained through measurement at a 0.1 ?m pitch being 15 MPa to 470 MPa, and the coefficient of variation of the elastic modulus being 17.6% or less.

Abstract: A vehicle wiper blade comprises a blade support part and a lip part coupled swingably with the blade support part via a neck. The lip part comprises polyurethane. The polyurethane comprises a reactant of a composition including an isocyanate compound which includes diisocyanate and tri- or higher functional polyfunctional isocyanate, and an alcohol which includes tri- or higher functional polyfunctional alcohol. The diisocyanate has an aromatic ring in a molecule. When a molecule of the polyurethane is ionized with a mass spectrometer of a direct sample injection system, then obtained M1, M2 and M3 satisfy the following relation: M2/M1 is 0.001 to 0.028, M3/M1 is 0.020 to 0.110, and M2/M3 is 0.013 to 0.300, and a concentration of the polyfunctional alcohol in the polyurethane is 0.12 mmol/g to 0.65 mmol/g.

Abstract: The present invention is aimed at providing an electrophotographic cleaning blade that has excellent chipping resistance and can exhibit excellent cleaning performance. This cleaning blade is provided with an elastic member that includes a polyurethane and a support member that supports the elastic member, and cleans the surface of a member to be cleaned that is moving, by bringing a part of the elastic member into contact with the surface of the member to be cleaned. The average value of the elastic modulus of the elastic member obtained when measured using SPM is at least 15 MPa and not more than 470 MPa, and the coefficient of variation thereof is not more than 6.0%.

Abstract: The electrophotographic apparatus and process cartridge comprising an electrophotographic photosensitive member, a cleaning blade, and developing unit containing a toner, wherein the cleaning blade comprising a support member and an elastic member whose portion is abutting a surface of the electrophotographic photosensitive member; the elastic member has an elastic modulus of 15 to 470 MPa with coefficient of variation for the elastic modulus being not more than 7.0%, and the absolute value of a difference between Martens hardness values is not more than 0.30 N/mm2 as measured under prescribed conditions; the toner contains a toner particle and an external additive whose a number-average primary particle diameter is from 5 to 25 nm, when X1 is a coverage ratio of the toner particle by the external additive and X2 is a theoretical coverage ratio, X1 is 50 to 85 area %, and X1/X2??0.0042×X1+0.60 is satisfied.

Abstract: The electrophotographic apparatus and process cartridge comprising an electrophotographic photosensitive member, a cleaning blade, and developing unit containing a toner, wherein the cleaning blade comprising a support member and an elastic member whose portion is abutting a surface of the electrophotographic photosensitive member; the elastic member has an elastic modulus of 15 to 470 MPa with coefficient of variation for the elastic modulus being not more than 7.0%, and the absolute value of a difference between Martens hardness values is not more than 0.30 N/mm2 as measured under prescribed conditions; the toner contains a toner particle and an external additive whose a number-average primary particle diameter is from 5 to 25 nm, when X1 is a coverage ratio of the toner particle by the external additive and X2 is a theoretical coverage ratio, X1 is 50 to 85 area %, and X1/X2??0.0042×X1+0.60 is satisfied.

Abstract: The present invention is aimed at providing an electrophotographic cleaning blade that has excellent chipping resistance and can exhibit excellent cleaning performance. This cleaning blade is provided with an elastic member that comprises a polyurethane and a support member that supports the elastic member, and cleans the surface of a member to be cleaned that is moving, by bringing a part of the elastic member into contact with the surface of the member to be cleaned. The average value of the elastic modulus of the elastic member obtained when measured using SPM is at least 15 MPa and not more than 470 MPa, and the coefficient of variation thereof is not more than 6.0%.

Abstract: The electrophotographic electroconductive member includes a support having an electroconductive outer surface, and an electroconductive layer on the surface of the support. The electroconductive layer has a matrix containing a crosslinked product of a first rubber, and domains dispersed in the matrix, and the domains each contain a crosslinked product of a second rubber and electroconductive particles. The matrix has a volume resistivity R1 of more than 1.0×1012 ?·cm, and the domains each have a volume resistivity R2 lower than the volume resistivity R1 of the matrix. The electroconductive layer further has a pore, and an inner wall of the pore is constituted by a part of the matrix and a part of the domains. The domains constituting the inner wall protrude into the pore at sites on the inner wall.

Abstract: An electro-conductive member for an electrophotographic image forming apparatus for which a change in resistance value is small even when a large current is applied at a high voltage for a long period of time is provided. The electro-conductive member includes a support having an electro-conductive outer surface and an electro-conductive layer on the outer surface of the support, in which the electro-conductive layer has a matrix including a cross-linked product of a first rubber and domains dispersed in the matrix, the domains include a cross-linked product of a second rubber different from the first rubber and an electrically conductive agent, and the cross-linked product of the second rubber has, in a molecule, a structural unit represented by Structural Formula (I). [—(CH2)n—O—]??Structural Formula (I) In Structural Formula (I), n is an integer of 1 to 3.