Abstract: Provided is a high strength steel sheet that has a predetermined chemical composition and is manufactured under optimum conditions, the high strength steel sheet having a steel microstructure including, by area, ferrite: 30% or more and 80% or less, martensite: 5% or more and 35% or less, and retained austenite: 8% or more, wherein the quotient of the area fraction of grains of the retained austenite, the grains having an aspect ratio of 2.0 or more and a minor axis length of 1 ?m or less, divided by the total area fraction of the retained austenite is 0.3 or more, wherein the quotient of the average Mn content (mass %) in the retained austenite divided by the average Mn content (mass %) in the ferrite is 1.5 or more.

Abstract: Provided are a high-strength hot-dip galvanized steel sheet that has a tensile strength of 1180 MPa or more and excellent ductility, stretch flangeability, bendability and LME resistance and can manufacture parts with high dimensional accuracy, and its manufacturing method. The high-strength steel sheet with a tensile strength of 1180 MPa or more has a chemical composition containing C, Si, Mn, P, S, Al and N, with [% Si], [% Mn], [% P], [% Mo] and [% Cr] satisfying a predetermined relationship and the balance being Fe and inevitable impurities, and a steel microstructure including ferrite, tempered martensite and bainite, and retained austenite, where the diffusible hydrogen amount in the steel sheet is 0.60 mass ppm or less, a thickness of softened surface layer is 5 ?m or more and 150 ?m or less, and a frequency of coincidence boundary in the steel sheet surface layer after a high-temperature tensile test is 0.45 or less.

Abstract: Provided are a high-strength galvannealed steel sheet, and a manufacturing method therefor. The manufacturing method is for a high-strength galvannealed steel sheet which includes a zinc coated layer with a coating weight of 20 to 120 g/m2 per side on a surface of a steel sheet having a chemical composition containing, in mass %, C: 0.03 to 0.35%, Si: 0.01 to 1.00%, Mn: 3.6 to 8.0%, Al: 0.001 to 1.00%, P: 0.100% or less, and S: 0.010% or less, with the balance being Fe and inevitable impurities. The method includes: setting a cold rolling reduction ratio to 20% or more and 35% or less when cold rolling is performed on the steel sheet, and setting a maximum steel sheet temperature to be reached in an annealing furnace to 600° C. or higher and 700° C. or lower when annealing is further performed on the steel sheet.

Abstract: An object is to provide a high strength steel sheet having a TS (tensile strength) of 980 MPa or more and excellent formability and a method for manufacturing the steel sheet. A high strength steel sheet which is excellent in terms of formability, which is manufactured under optimized manufacturing conditions, and which has a predetermined chemical composition and a steel microstructure including, in terms of area fraction, 35% or more and 80% or less of ferrite, 5% or more and 35% or less of as-quenched martensite, 0.1% or more and less than 3.0% of tempered martensite, and 8% or more of retained austenite, in which the average grain size of the ferrite is 6 ?m or less, in which the average grain size of the retained austenite is 3 ?m or less, in which a value calculated by dividing the average Mn content in the retained austenite by the average Mn content in the ferrite is 1.

Abstract: A method for producing a high-strength hot-dip galvannealed steel sheet, in which a high-strength steel sheet is used as a base material, includes a rolling step (x) of rolling a hot-dip galvannealed steel sheet with a coating layer having an Fe concentration of 8% to 17% by mass, and a heat treatment step (y) of heating the coated steel sheet which has been subjected to the rolling step (x) under the conditions satisfying the following formulae (1) and (2): (273+T)×(20+2×log10(t))?8000??(1) 40?T?160??(2) where T: heating temperature (° C.) of the coated steel sheet, and t: holding time (hr) at the heating temperature T.

Abstract: A collision performance evaluation test with few variations in test results with high accuracy in which a complicated phenomenon that actually occurs can be reproduced in a simple manner by considering the history of deformation in both the press forming and a collision. A collision performance evaluation test method for a metal sheet material for an automobile body is characterized in that a press working apparatus first forms a flat test specimen made of a metal sheet material to be tested into a V shape by primary bending, a bending test apparatus then deforms, by secondary bending, the test specimen formed by the primary bending in a direction intersecting with the primary bending direction, and a bending load and a bending stroke for the test specimen during the secondary bending deformation are recorded and evaluated.

Abstract: High-strength galvannealed steel sheet including any of a) an oxide containing Fe and Mn, b) an oxide containing Fe and Mn and an Fe oxide, c) an oxide containing Fe and Mn and a Mn oxide, d) an oxide containing Fe and Mn, an Fe oxide, and a Mn oxide, and e) an Fe oxide and a Mn oxide is present in a zinc coated layer. The total amount of oxide is 0.01 to 0.100 g/m2; the ratio by mass % of Mn to Fe, e.g., Mn/Fe, contained in the oxide is 0.10 to 10.00; an oxide of at least one selected from Fe and Mn is present in an amount of 60% or more; and an oxide of at least one selected from Fe and Mn is present in a surface layer portion of a steel sheet in an amount of 0.040 g/m2 or less (not including zero).

Abstract: A hot rolled steel sheet having a chemical composition containing, by mass %, C: 0.04% or more and 0.20% or less, Si: 0.7% or more and 2.3% or less, Mn: 0.8% or more and 2.8% or less, P: 0.1% or less, S: 0.01% or less, Al: 0.1% or less, N: 0.008% or less, and the balance being Fe and inevitable impurities. The microstructure of the hot rolled steel sheet includes ferrite and pearlites, in which the area ratio of the ferrite is 75% or more and less than 95%, the mean grain size of the ferrite is 5 ?m or more and 25 ?m or less, the area ratio of pearlite is 5% or more and less than 25%, the mean grain size of pearlite is 2.0 ?m or more, and the mean free path of pearlite is 5 ?m or more.

Abstract: A high-strength steel sheet includes a steel structure with: ferrite being 35% to 80%, martensite being 5% to 35%, and tempered martensite being 0% to 5% in terms of area fraction; retained austenite being 8% or more in terms of volume fraction; an average grain size of: the ferrite being 6 ?m or less; and the retained austenite being 3 ?m or less; a value obtained by dividing an area fraction of blocky austenite by a sum of area fractions of lath-like austenite and the blocky austenite being 0.6 or more; a value obtained by dividing, by mass %, an average Mn content in the retained austenite by an average Mn content in the ferrite being 1.5 or more; and a value obtained by dividing, by mass %, an average C content in the retained austenite by an average C content in the ferrite being 3.0 or more.

Abstract: A high-strength steel includes a steel structure with: in area fraction, 60.0% to less than 90.0% of ferrite, 0% to less than 5.0% of unrecrystallized ferrite, 2.0% to 25.0% of martensite, 0% to 5.0% of carbide, and 0% to 3.0% of bainite; in volume fraction, more than 7.0% of retained austenite; in a cross-sectional view of 100 ?m×100 ?m, a value obtained by dividing number of retained austenite that are not adjacent to retained austenite whose crystal orientations are different by a total number of retained austenite being less than 0.80, an average crystal grain size of the ferrite being 6.0 ?m or less, an average crystal grain size of the retained austenite being 3.0 ?m or less, and a value obtained by dividing, by mass %, an average content of Mn in the retained austenite by an average content of Mn in steel being 1.50 or more.

Abstract: Disclosed is a steel sheet having a predetermined chemical composition and a steel microstructure that contains, in area ratio, 35% or more and 80% or less of polygonal ferrite and 5% or more and 25% or less of martensite, and that contains, in volume fraction, 8% or more of retained austenite, in which the polygonal ferrite, the martensite, and the retained austenite have a mean grain size of 6 ?m or less, 3 ?m or less, and 3 ?m or less, respectively, and each have a mean grain aspect ratio of 2.0 or less, and in which a value obtained by dividing an Mn content in the retained austenite in mass % by an Mn content in the polygonal ferrite in mass % equals 2.0 or more.

Abstract: Provided is an automotive member, or particularly, a steel sheet having a tensile strength exceeding 900 MPa. The automotive member has a resistance weld for fixing two or more steel sheets containing a predetermined composition, in which a maximum hardness (HVBM) in a heat-affected zone of the resistance weld is at least 1.1 times hardness (HVW) of a nugget in the resistance weld formed in a softest steel sheet of a sheet set during resistance welding, and furthermore, an average grain size of a steel sheet structure of the heat-affected zone within 2 mm in a direction at a right angle to a sheet thickness from an end part of the nugget of the high-strength steel sheet is 3 ?m or less, and a minimum hardness (HVmin) in the heat-affected zone is at least 90% of hardness (HV?) of the high-strength steel sheet before the resistance welding.

Abstract: A method for producing a high-strength hot-dip galvannealed steel sheet, in which a high-strength steel sheet is used as a base material, includes a rolling step (x) of rolling a hot-dip galvannealed steel sheet with a coating layer having an Fe concentration of 8% to 17% by mass, and a heat treatment step (y) of heating the coated steel sheet which has been subjected to the rolling step (x) under the conditions satisfying the following formulae (1) and (2): (273+T)×(20+2×log10(t))?8000 ??(1) 40?T?160 ??(2) where T: heating temperature (° C.) of the coated steel sheet, and t: holding time (hr) at the heating temperature T.

Abstract: A high-strength steel sheet includes a steel structure with: ferrite being 35% to 80% and tempered martensite being greater than 5% and 20% or less in terms of area fraction; retained austenite being 8% or more in terms of volume fraction; an average grain size of: the ferrite being 6 ?m or less; and the retained austenite being 3 ?m or less; a value obtained by dividing an area fraction of blocky austenite by a sum of area fractions of lath-like austenite and the blocky austenite being 0.6 or more; a value obtained by dividing, by mass %, an average Mn content in the retained austenite by an average Mn content in the ferrite being 1.5 or more; and a value obtained by dividing, by mass %, an average C content in the retained austenite by an average C content in the ferrite being 3.0 or more.

Abstract: A high strength steel sheet having excellent surface quality and formability with a tensile strength of 980 MPa or more and a TS-El balance of 30000 MPa % or more is provided. A high strength steel sheet comprises: a chemical composition containing C: 0.08% to 0.30%, Si: 2.0% or less, Mn: more than 3.0% and 10.0% or less, P: 0.05% or less, S: 0.01% or less, Al: 1.5% or less, Ti: 0.010% to 0.300%, and N: 0.0020% to 0.0100% in a range satisfying 1.1?(Ti+Mn1/2/400)/(0.01+5N)?6.0; and a microstructure including a retained austenite phase and a ferrite phase, wherein a ratio ?Mn/?Mn of an average Mn concentration (?Mn) of the retained austenite phase to an average Mn concentration (?Mn) of the ferrite phase is 1.5 or more.

Abstract: A method for manufacturing a high strength galvanized steel sheet and a high strength galvanized steel sheet are provided. A base steel sheet having a chemical composition comprising C: 0.03% to 0.35%, Si: 0.01% to 0.50%, Mn: 3.6% to 8.0%, Al: 0.001% to 1.000%, P?0.10%, S?0.010%, and the balance comprising Fe and incidental impurities, on a percent by mass basis, is subjected to annealing and galvanization treatment, wherein the maximum steel sheet temperature in an annealing furnace is 600° C. or higher and 700° C. or lower, the steel sheet transit time in a temperature region of the maximum steel sheet temperature of 600° C. or higher and 700° C. or lower is specified to be 30 seconds or more and 10 minutes or less, and the dew point in an atmosphere is specified to be ?45° C. or lower.

Abstract: Provided are a high-strength galvannealed steel sheet, and a manufacturing method therefor. The manufacturing method is for a high-strength galvannealed steel sheet which includes a zinc coated layer with a coating weight of 20 to 120 g/m2 per side on a surface of a steel sheet having a chemical composition containing, in mass %, C: 0.03 to 0.35%, Si: 0.01 to 1.00%, Mn: 3.6 to 8.0%, Al: 0.001 to 1.00%, P: 0.100% or less, and S: 0.010% or less, with the balance being Fe and inevitable impurities. The method includes: setting a cold rolling reduction ratio to 20% or more and 35% or less when cold rolling is performed on the steel sheet, and setting a maximum steel sheet temperature to be reached in an annealing furnace to 600° C. or higher and 700° C. or lower when annealing is further performed on the steel sheet.

Abstract: Disclosed is a steel sheet having a predetermined chemical composition and a steel microstructure that contains, in area ratio, 15% or more and 55% or less of polygonal ferrite and 15% or more and 30% or less of martensite, and that contains, in volume fraction, 12% or more of retained austenite, in which the polygonal ferrite, the martensite, and the retained austenite have a mean grain size of 4 ?m or less, 2 ?m or less, and 2 ?m or less, respectively, and each have a mean grain aspect ratio of 2.0 or less, and in which a value obtained by dividing an Mn content in the retained austenite in mass % by an Mn content in the polygonal ferrite in mass % equals 2.0 or more.

Abstract: Disclosed is a high-strength steel sheet having a tensile strength (TS) of 780 MPa or more and excellent in ductility, fatigue properties, stretch flangeability, surface characteristics, and sheet passage ability that can be obtained by providing a predetermined chemical composition and a steel microstructure that contains, by area, 20-50% of ferrite, 5-25% of bainitic ferrite, 1-10% of martensite, and 5-15% of tempered martensite, and that contains, by volume, 10% or more of retained austenite, in which the retained austenite has a mean grain size of 2 ?m or less, a mean Mn content in the retained austenite in mass % is at least 1.2 times the Mn content in the steel sheet in mass %, the retained austenite has a mean free path of 1.2 ?m or less, and the tempered martensite has a mean free path of 1.2 ?m or less.

Abstract: Disclosed is a high-strength steel sheet having a tensile strength (TS) of 780 MPa or more and excellent in ductility, fatigue properties, balance between high strength and ductility, surface characteristics, and sheet passage ability that can be obtained by providing a predetermined chemical composition and a steel microstructure that contains, by area, 20-50% of ferrite, 5-25% of bainitic ferrite, and 5-20% of martensite, and that contains, by volume, 10% or more of retained austenite, in which the retained austenite has a mean grain size of 2 ?m or less, a mean Mn content in the retained austenite in mass % is at least 1.2 times the Mn content in the steel sheet in mass %, and the retained austenite has a mean free path of 1.2 ?m or less.