Downhole Slurry Method For Primary Cementing A Well

Abstract

A method of primary cementing well is provided utilizing a cement and cement activator cementing composition, in which one of the components is first placed in the annulus of the well. Next, the other component is placed in the annulus above the first placed component. Densities of the components have been selected such that the density of the second placed component is sufficiently higher then the density of the first placed component to facilitate gravity mixing of the two components as the second placed component moves through the first placed component and in the process activation occurs.

Description

RELATED APPLICATION DATA

This application is a continuation of U.S. patent application Ser. No. 11/162,443, filed Sep. 9, 2005, herein incorporated by reference, which application claimed priority/benefit of U.S. Provisional Patent Application Ser. Nos. 60/608,255, 60/608,256, and 60/608,257, all filed Sep. 9, 2004, and all herein incorporated by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to wells, drilling wells, well operations, to methods, apparatus and products for drilling wells. In another aspect, the present invention relates to wells, cementing wells, and to methods, apparatus and products for cementing wells. In even another aspect, the present invention relates to wells, primary cementing wells, and to methods, apparatus and products for primary cementing wells.

2. Brief Description of the Related Art

In the drilling and completion of an oil or gas well, a cementing composition is often introduced in the well bore for cementing pipe string or casing in a process known as primary cementing. In primary cementing, a cementing composition is pumped into the annular space between the walls of the well bore and the casing. The cementing composition sets in the annular space, supporting and positioning the casing, and forming a substantially impermeable barrier/mass or cement sheath. An essential function of cementing is to prevent fluid exchange between the different formation layers through which the hole passes and to control the ingress of fluid into the well, in particular to limit the ingress of water. In production zones, the casing, the cement and the formation are all perforated over a depth of a few centimeters.

A variety of cementing compositions exist in the art and have been used for primary cementing. Considerations for selecting a cementing composition include relatively short term concerns, such as set times for the cement slurry, as well as functional and long term concerns such as whether a composition is environmentally acceptable, easily mixable, non-settling under static and dynamic conditions, will develop near one hundred percent placement in the annular space, resist fluid influx, and have the desired density, thickening time, set up time, fluid loss, strength development, and zero free water.

A number of patents and patent applications are directed to primary cementing wells, the following of which are only a small few.

U.S. Pat. No. 4,768,593, issued Sep. 6, 1988, to Novak discloses This application discloses a process for drilling and primary cementing a well using a drilling fluid containing a polymeric material which may be cemented into a well cement by irradiation with a suitable radioactive source

U.S. Pat. No. 5,151,203, issued Sep. 29, 1992, to Riley et al., discloses a composition for and method of performing primary cementing operations. The method comprises the use of a water slurry of a thixotropic cementing composition which rapidly develops sufficient static gel strength to reduce if not eliminate annular gas migration.

U.S. Pat. No. 5,327,969, issued Jul. 12, 1994, to Sabins et al., discloses a method of preventing gas migration during primary well cementing. The method basically comprises the steps of displacing a cement slurry into the annulus between a string of pipe to be cemented in a well bore and the walls of the well bore, determining the initial surface pressure in the pipe after the cement slurry is placed in the annulus, displacing additional cement slurry into the annulus as is necessary to make up for losses in the surface pressure due to cement slurry gel strength development and volume reduction whereby the surface pressure is maintained substantially equal to the initial surface pressure until the cement slurry develops a predetermined gel strength sufficient by itself to prevent gas migration, and then allowing the cement slurry to set into a hard impermeable mass in the annulus.

U.S. Pat. No. 5,343,950, issued Sep. 6, 1994 to Hale et al., discloses An extended reach well such as the deviated wells typically drilled from offshore platforms is drilled using a drilling fluid comprising blast furnace slag and water which drilling fluid is circulated during the drilling to lay down a filter cake. Thereafter, an activator is added and generally, an alkaline material and additional blast furnace slag, to produce a cementitious slurry which is passed down a casing and up into an annulus to effect primary cementing.

U.S. Pat. No. 5,343,951, issued Sep. 6, 1994 to Cowan et al., discloses a slim hole well drilled using a drilling fluid comprising blast furnace slag and water which drilling fluid is circulated during the drilling to lay down a filter cake. Thereafter, an activator is added and generally, an alkaline material and additional blast furnace slag, to produce a cementitious slurry which is passed down a casing and up into an annulus to effect primary cementing.

U.S. Pat. No. 5,370,185, issued Dec. 6, 1994 to Cowan et al., a cementitious slurry produced by combining an aqueous drilling fluid with a slurry of Portland cement in oil. Generally the drilling fluid is an aqueous drilling fluid containing clay such as prehydrated bentonite. The resulting composition has a particular utility in primary cementing operations for oil wells.

U.S. Pat. No. 5,829,523, issued Nov. 3, 1998 to Sabins et al., discloses primary well cementing methods and apparatus. The methods basically comprise the steps of releasing a displacement plug into the casing to be cemented and pumping a first displacement fluid behind the displacement plug while measuring the quantity of the first displacement fluid required to land the displacement plug on a float collar or the like connected near the bottom of the casing, releasing a bottom cementing plug into the casing and pumping a cement slurry behind the bottom cementing plug in a predetermined quantity and then releasing a top cementing plug into the casing and pumping a second displacement fluid behind the top cementing plug in a quantity substantially equal to the measured quantity of the first displacement fluid thereby ensuring that the cement slurry is not under or over displaced in the annulus between the casing and the well bore.

U.S. Pat. No. 6,065,539, issued May 23, 2000 to Noik et al., discloses a method of cementing a casing in a well drilled in the ground comprises injecting a liquid material comprising phenol-formol resin from the surface, wherein the resin is modified by means of a determined amount of furfuryl alcohol, and an amount of mineral filler unreactive towards the resin is added. The invention further relates to a thermosetting cementing material comprising phenol-formol resin. The resin is modified by means of an amount of furfuryl alcohol and comprises at least a proportion of an unreactive granular filler.

U.S. Pat. No. 6,626,991, issued Sep. 30, 2003 to Drochon et al., discloses a cement slurry for cementing an oil well or the like, the slurry having a density lying in the range 0.9 g/cm.sup.3 to 1.3 g/cm.sup.3, and being constituted by a solid fraction and a liquid fraction, having porosity (volume ratio of liquid fraction over solid fraction) lying in the range 38% to 50%. The solid fraction is constitued by a mixture of lightweight particles, microcement and optionally portland cement and gypsum. Such cements have remarkable mechanical properties due to their very low porosity in spite of having very low density.

U.S. Pat. No. 6,776,237, issued Aug. 17, 2004 to Dao et al., discloses lightweight cement compositions and methods of cementing a subterranean zone penetrated by a well bore utilizing the compositions are provided. A lightweight cement composition of the invention is basically comprised of a coarse particulate hydraulic cement, an ultrafine particulate hydraulic cement mixture comprised of slag cement and a Portland or equivalent cement, fly ash, fumed silica, hollow glass spheres and water.

U.S. Pat. No. 6,793,730, issued Sep. 21, 2004 to Reddy et al., discloses methods for cementing. The methods are basically comprised of the steps of preparing a cement composition comprised of hydraulic cement, water, gas, surfactants, a cement early strength accelerator and a mildly set retarding cement dispersing agent, placing the cement composition in the annulus between the casing string and the well bore and allowing the cement composition to set into a hard impermeable mass. The cement composition used can alternatively comprise hydraulic cement, a water reducing additive, a dispersing additive, a set accelerating additive and water. Also, the cement composition can be made environmentally benign by using water reducing and dispersing additives, set retarding additives, and compressive strength and set accelerating additives which are environmentally degradable.

U.S. Pat. No. 6,892,814, issued May 17, 2005, to Heathman et al., discloses cement comprising barite, a process for preparing such cement, and methods of cementing in a subterranean formation or well bore using such cement are provided. The cement is prepared by introducing coarse barite to the cement, the course barite comprising particles having a particle size primarily greater than about 125 microns. Preferably, 90 percent of the barite particles is greater than about 125 microns in size. The presence of the coarse barite in the cement causes the cement to have a relatively low viscosity. Introducing the barite to the cement also increases the density of the cement, thus rendering the cement capable of controlling high hydrostatic pressures in a well bore.

In spite of the advances in the prior art, conventional cement systems suffer from a 6 hour safety margin to dump the slurry; long set times; low shear bond values; long cement lengths, and long wait on cement (WOC) times causing high expense.

Thus, there still exists a need in the art for improved methods, apparatus and products for cementing wells.

There also exists a need in the art for improved methods, apparatus and products for primary cementing operations of wells.

SUMMARY OF THE INVENTION

According to one embodiment of the present invention, there is provided an well comprising a well bore and a pipe residing in said well bore forming an annulus between the pipe and well bore; a first component residing in the annulus; and, a second component having a density greater than the density of the first component, and positioned in the annulus at a point above the first component that will allow for gravity flow of the second component down into the first component. The first component and the second component are selected from the group consisting of the cement component and the cement activator component, wherein the first component and the second component are different, and the density of the second component is higher than the density of the first component.

According to even another embodiment of the present invention, there is provided a method of conducting primary cementing operations on a well, said well comprising a well bore and a pipe residing in said well bore forming an annulus between the pipe and well bore. The method includes providing a cement component and a cement activator component, each having a density greater than the density of any well fluid residing in the well. The method also includes selecting a first component and a second component from the group consisting of the cement component and the cement activator component, wherein the first component and the second component are different, and the density of the second component is higher than the density of the first component. The method even further includes placing the first component in the annulus. The method still further includes placing the second component in the annulus at a point above the first component that will allow for gravity flow of the second component down into contact with the first component.

According to still another embodiment of the present invention, there is provided a method of primary cementing a well comprising a well bore and a pipe residing in said well bore forming an annulus between the pipe and well bore. The method includes providing a cement component and a cement activator component, each having a density greater than the density of any well fluid residing in the well. The method also includes selecting a first component and a second component from the group consisting of the cement component and the cement activator component, wherein the first component and the second component are different, and the density of the second component is higher than the density of the first component. The method even further includes placing the first component in the annulus. The method still further includes placing the second component in the annulus at a point above the first component that will allow for gravity flow of the second component down into contact with the first component. The method yet further includes allowing the first and second components to gravity contact and form a hard impermeable mass in the annulus.

DETAILED DESCRIPTION OF THE INVENTION

In the practice of present invention, the cementing composition of the present invention may be utilized in any known cementing method including any of the primary cementing methods disclosed in any of the references cited herein, all of which are herein incorporated by reference. Any known method for placing and/or positioning components of a cementing composition into an annulus may be used herein, all of which are herein incorporated by reference.

As used herein, a well generally refers to an underground, substantially vertically-extending well comprising a well bore. Generally, after a well bore is drilled during which the drilling fluid used is circulated through the well bore, the circulation of the drilling fluid is stopped, the well is usually logged and a string of pipe often called a casing, is run in the well bore. Generally the casing extends from the ground surface into the well bore and terminates at a predetermined depth in the well bore. The outer wall of the casing is generally spaced from the inner wall of the well bore to form an annulus. After the casing is set, the drilling fluid in the well bore is conditioned by circulating drilling fluid downwardly through the interior of the pipe and upwardly through the annulus between the exterior of the pipe and the walls of the well bore while removing drilling solids and gas therefrom. After conditioning, both the pipe and annulus are substantially filled with drilling fluid.

The next operation performed on the well is generally the step of primary cementing. By the process of primary cementing a hard impermeable barrier mass is formed in the annulus. This mass may also be referred to as a sheath or cement sheath. Primary cementing is carried out for a number of reasons including to prevent migration of fluids in the annulus, to support the casing or liner string, and to protect of the casing from corrosive formation fluids. Any of the number of methods known in the art for placing a cementing composition into an annulus may be used for the primary cementing compositions and methods of the present invention.

In general primary cementing is carried out as follows. Generally in primary cementing processes the components of a cementing composition are introduced from a source at the ground surface into the upper end of the casing and flow downwardly through the bottom end of the casing. The components of the cementing composition then flow to the bottom of the well bore where their flow direction is reversed causing them to flow up the annulus, thereby placing the components of the cementing composition in the annulus between the pipe and the walls of the well bore. In the primary cementing processes of the present invention, the components of the cementing composition may be placed into the annulus by any of the number of methods known in the art. The flow and addition of the components of the cementing composition is then terminated and the cementing composition is allowed to set into a hard impermeable mass.

The method of the present invention for primary cementing a well involves the use of a two part cementing composition, which is incorporated into known cementing methods.

In particular, the preferred two part cementing composition of the present invention comprises a slurry system comprising a sealant component and an activator component.

The cementing composition system utilized in the present invention may be any material suitable for forming a hard impermeable mass in the well annulus. Preferably, the sealant is a cement in the convention sense, that is, a silica based cement material of which Portland Cement is the best known example. Very well known in the prior art, Portland cement is manufactured by crushing, milling, and blending selected raw materials containing appropriate proportions of lime, iron, silica, and alumina, with certain Portland cements tailored specifically for plugging abandoned wells. Other hydraulic cements may be substituted for Portland cement. Activators for cements are well known, and any that are suitable for the particular well conditions and operation parameters may be utilized.

In the present invention, the slurry system comprises not only cement and activator, but may optionally include additives to improve thermal stability, control set time, generate expansion, and control fluid loss. The additives may be present as independent components, or may be incorporated into the cement component or the activator component.

As utilized in the present invention, the activator serves to activate/accelerate the set up or curing time for the cement and thus reduce the wait on cement (WOC) time. The activator causes the sealant to set under downhole temperature and pressure conditions at an accelerated rate. Of course, this activator will have to be carefully selected depending upon the material utilized as the first component.

In the present invention, accelerated set times are generally less than 12 hours, preferably less than 10 hours, more preferably less than 8 hours, even more preferably less than 6 hours, still more preferably less than 4 hours, and yet more preferably less than 2 hours.

The activator will cause the sealant to set under downhole conditions to cause the sealant to bond to the casing and or other formation surfaces in the well. The pipe may have coating of oil or water based drilling mud.

The activator component may be selected to not only accelerate cement set, but may optionally be selected to also alter slurry density, clean downhole surfaces, and/or improve bond.

Non-limiting examples of cement activators suitable for use as the second component include various amines, non-limiting examples of which include triethanol amies and diethanol amines, various metal salts, non-limiting exaples of which include sodium, calcium, magnesium, zine, and iron salts, various metal halides, including but not limited to metal chlorides and metal bromides, various formates, as well as combinations of the foregoing.

For example, alkanolamines have been proposed for reducing the set time of cements, see U.S. Pat. Nos. 2,437,842; 3,553,077; 4,257,814, 4,741,782, and most recently U.S. Pat. No. 6,869,474, all herein incorporated by reference. As another example, bromide-based accelerators. In the practice of the present invention, where the first component is a cement, the second component preferably comprises an alkanolamine, more preferably comprises at least one selected from triethanolamine, diethanolamine, monoethanolamine and mixtures thereof, and even more preferably comprises triethanolamine.

The method of the present invention for primary cementing wells, includes any of the known cementing methods in which is utilized the two component cementing composition as the cement material. While a generalized primary cementing method is described below, it should be understood that any suitable primary cementing method as is known in the art, including any described above in the backgound or described in any cited reference (all of which are herein incorporated by reference), may be utilized with the cementing composition of the present invention.

Generally in the practice of the method of the present invention, one of the components is selected as the first placed component and placed in the annulus, followed by placement of the other component as the second placed component in the annulus at a position above the first component, to allow the second component to gravity flow into the first component.

Preferably, in the practice of the present invention, the activator liquids are heavier than the well fluid and the cement component is heavier than the activator liquid.

In general, suitable delivery systems utilize a dump bailer, coiled tubing and jointed tubing. They require a base to stack up against such as a packer, petal basket or sand plug. While any suitable delivery mechanism can be utilized, more specific non-limiting examples of suitable delivery mechanisms include: dump bailer run on electric line or slick line; pumping through tubing, drillpipe, work strings or any tubulars; allowing fall through fluids via gravity; and pumping into an annulus or pipe without displacing (i.e., “bull heading”).

It is crucial that the first and second components have greater densities than the well fluid density. It is also crucial that the second placed component have a density greater than the first placed component so that the second placed component may displace the first component.

In some instances the selected first and second components will not have suitable densities, specifically, the densities of the first and second components may not be greater than that of the well fluid, or they may not have the suitable density for the order in which they are desired to be introduced into the well, or the densities may not have a suitable enough differential to achieve suitable displacement.

The present invention provides for the utilization of weighting agent additives to the first and second components to change the density of those components. Suitable additives to change the density include metal salts, preferably calcium chloride. Other examples of weighting agents include sand, barite, hemitite, calcium carbonate, FeO, MgO, and manganese ore. Sufficient amounts of the additive are utilized to achieve the desired density.

In the primary cementing method of the present invention first and second components are provided which have densities greater than the well fluid, with the component to be placed second having a greater density than the component to be placed first. Should the density of the first or second component need adjustment, a weighting agent as discussed above, will be added as necessary. The component with the greater density is then positioned into the annulus, the other component is then placed above the first placed component so that it may spontaneously gravity flow into contact with the first placed fluid. The density difference will allow displacement of the first placed fluid by the second placed fluid and allow for in-situ mixing.

It should be appreciated that the rate of displacement and thus in-situ mixing will increase with increasing density differential between the first and second components, and decrease with decreasing density differential between the first and second components.

It should also be appreciated that at some point, the density differential between the first and second components is so low as to result in too slow of displacement.

On the other hand, it should further be appreciated that at some point, the density differential between the first and second components is so great as to result in too rapid of displacement so as to avoid much mixing.

Thus, the density differential should be selected so as to provide fast enough displacement for the primary cementing operation, and to facilitate sufficient in-situ mixing, and this differential can be determined on a case by case basis, for example by observation in clear container and trial and error.

Typical densities for the well fluid will be in the range of about 8.33 ppg up to about 20.0 ppg, with typical densities for the activator in the range of about 8.33 ppg up to about 21.0 ppg, and with typical densities for the sealant system in the range of about 8.54 up to about 22.0 ppg.

It should be understood that other well fluid additives as are well known in the art may be incorporated into the first and/or second component, or added before, along with, or after the introduction of the first and/or second component, non-limiting examples of which include surfactants, surface bond enhancers (non-limiting examples include styrene butadiene latex, polyvinal alcohols, resins, other adhesives), emulsifiers, ph control agents, fluid loss additives, gas prevention additive, dispersants, expanding agents, and wetting agents.

It should also be understood that the activator viscosity and missablity much be such that the activator will not substantially mix with the well fluid as it passes thru the well fluid. Preferably, the activator viscosity and missablity much be such that the activator will mixes less than 20% with the well fluid as it falls through it, more preferably less than 10%, and even more preferably less than 2%.

It should be further understood that activator and sealant viscosities and missibility are such that the activator mixes less than 40% with the sealant as they contact each other, preferably less then 20%, more preferably less than 10%, and even more preferably less than 5%.

Although the present invention has been illustrated by reference to cement, especially Portland cement, and to an activator therefore, it should be understood that any cementing composition having two or more components can be utilized in the present invention.

All materials cited herein, including but not limited to any cited patents, publications, articles, books, journals, brochures, are herein incorporated by reference.

While the illustrative embodiments of the invention have been described with particularity, it will be understood that various other modifications will be apparent to and can be readily made by those skilled in the art without departing from the spirit and scope of the invention. Accordingly, it is not intended that the scope of the claims appended hereto be limited to the examples and descriptions set forth herein but rather that the claims be construed as encompassing all the features of patentable novelty which reside in the present invention, including all features which would be treated as equivalents thereof by those skilled in the art to which this invention pertains.

Claims

1. A method of primary cementing a well comprising a well bore and a pipe residing in the well bore forming an annulus between the pipe and well bore, the method comprising:

(A) providing a cement component and an cement activator component, each having a density greater than the density of the well fluid;

(B) selecting a first component and a second component from the group consisting of the cement component and the cement activator component, wherein the first component and the second component are different, and the density of the second component is higher than the density of the first component;

(C) placing the first component in the annulus;

(D) placing the second component in the annulus at a point above the first component that will allow for gravity flow of the second component down into contact with the first component.

2. The method of claim 1, wherein steps (C) and (D) are carried out utilizing one or more of a dump bailer; pumping through tubing, drillpipe, work strings or tubulars; gravity flow; and bull heading.

3. The method of claim 1, wherein the activator component comprises at least one selected from the group consisting of amines, metal salts, metal halides, and formats.

4. The method of claim 1, wherein the second component is the cement component, and the first component is the activator component.

5. The method of claim 1, wherein the well fluid density is in the range of about 8.33 ppg up to about 20.0 ppg, the activator density is in the range of about 8.33 ppg up to about 21.0 ppg, and the cement density is in the range of about 8.54 up to about 22.0 ppg.

6. The method of claim 1, wherein the activator mixes with less than 2 percent with the well fluid, and the activator mixes with less than 20% with the cement.

7. A method of primary cementing a well comprising a well bore and a pipe residing in the well bore forming an annulus between the pipe and well bore, the method comprising:

(A) providing a cement component and an cement activator component, each having a density greater than the density of the well fluid;

(B) selecting a first component and a second component from the group consisting of the cement component and the cement activator component, wherein the first component and the second component are different, and the density of the second component is higher than the density of the first component;

(C) placing the first component in the annulus;

(D) placing the second component in the annulus at a point above the first component that will allow for gravity flow of the second component down into the first component; and

(E) allowing the first and second components to gravity contact and form a hard impermeable mass.

8. The method of claim 7, wherein steps (C) and (D) are carried out utilizing one or more of a dump bailer; pumping through tubing, drillpipe, work strings or tubulars; gravity flow; and bull heading.

9. The method of claim 7, wherein the activator component comprises at least one selected from the group consisting of amines, metal salts, metal halides, and formats.

10. The method of claim 7, wherein the second component is the cement component, and the first component is the activator component.

11. The method of claim 7, wherein the well fluid density is in the range of about 8.33 ppg up to about 20.0 ppg, the activator density is in the range of about 8.33 ppg up to about 21.0 ppg, and the cement density is in the range of about 8.54 up to about 22.0 ppg.

12. The method of claim 7, wherein the activator mixes with less than 2 percent with the well fluid, and the activator mixes with less than 20% with the cement.

13. A cemented well comprising:

a well bore;

a pipe residing in said well bore forming an annulus between said pipe and well bore;

a first component residing in the annulus; and,

a second component having a density greater than the density of the first component, and residing in the annulus at a point above the first component that will allow for gravity flow of the second component down into the first component, wherein one of the first component and the second component is a cement component, and the other of the first component and second component is a cement activator component.

14. A cemented well comprising:

a well bore;

a pipe residing in said well bore forming an annulus between said pipe and well bore;

a first component residing in the annulus; and,

a second component having a density greater than the density of the first component, and in the state of gravity flowing thru the first component, wherein one of the first component and the second component is a cement component, and the other of the first component and second component is a cement activator component.