POROUS COMPOSITE PARTICULATE MATERIALS, METHODS OF MAKING AND USING SAME, AND RELATED APPARATUSES
In an embodiment, a porous composite particulate material includes a plurality of composite particles. Each composite particle includes an acid-base-resistant core particle at least partially surrounded by one or more layers of acid-base-resistant shell particles. The shell particles are adhered to the core particle by a polymeric layer. The shell particles and/or core particles may be made from an acid-base-resistant material that is stable in harsh chemical conditions. For example, the shell particles and/or core particles may be made from diamond, graphitic carbon, silicon carbide, boron nitride, tungsten carbide, combinations of the foregoing, or other acid-base-resistant materials. The porous composite particulate materials disclosed herein and related methods and devices may be used in separation technologies, including, but not limited to, chromatography, and solid phase extraction.
This application is a continuation of U.S. patent application Ser. No. 12/463,899 filed on 11 May 2009, entitled “Porous Composite Particulate Materials, Methods of Making and Using Same, and Related Apparatuses,” which claims the benefit of U.S. Provisional Application No. 61/052,185 filed on 10 May 2008, entitled “Synthesis of Porous Diamond Particles,” which is hereby incorporated herein, in its entirety, by this reference.
BACKGROUNDChromatography and solid-phase extraction (“SPE”) are commonly-used separation techniques employed in a variety of analytical chemistry and biochemistry environments. Chromatography and SPE are often used for separation, extraction, and analysis of various constituents, or fractions, of a sample of interest. Chromatography and SPE may also be used for the preparation, purification, concentration, and clean-up of samples.
Chromatography and SPE relate to any of a variety of techniques used to separate complex mixtures based on differential affinities of components of a sample carried by a mobile phase with which the sample flows, and a stationary phase through which the sample passes. Typically, chromatography and SPE involve the use of a stationary phase that includes an adsorbent packed into a cartridge or column. A commonly-used stationary phase includes a silica-gel-based sorbent material.
Mobile phases are often solvent-based liquids, although gas chromatography typically employs a gaseous mobile phases. Liquid mobile phases may vary significantly in their compositions depending on various characteristics of the sample being analyzed and on the various components sought to be extracted and/or analyzed in the sample. For example, liquid mobile phases may vary significantly in pH and solvent properties. Additionally, liquid mobile phases may vary in their compositions depending on the characteristics of the stationary phase that is being employed. Often, several different mobile phases are employed during a given chromatography or SPE procedure. Stationary phase materials may also exhibit poor stability characteristics in the presence of various mobile phase compositions and/or complex mixtures for which separation is desired. The poor stability characteristics of stationary phase materials in some mobile phases and complex mixtures, in some cases, may even preclude the possibility of using chromatography or SPE to perform the desired separation.
SUMMARYEmbodiments disclosed herein are directed to porous composite particulate materials, related methods of manufacture, and devices that incorporate such porous composite particulate materials for use in separation technologies, including, but not limited to, chromatography and solid phase extraction. In an embodiment, a porous composite particulate material includes a plurality of composite particles. Each composite particle includes an acid-base-resistant core particle at least partially surrounded by one or more layers of acid-base-resistant shell particles. The shell particles may be bonded to the core particles by a polymeric layer of one or more polymers. The shell particles and/or core particles may be made from a material that is stable in harsh chemical conditions. For example, the shell particles and/or core particles may be made from diamond, graphitic carbon, silicon carbide, boron nitride, tungsten carbide, combinations thereof, or other suitable acid-base-resistant material that is chemically stable in acids and bases over a wide pH range.
The one or more polymers used to adhere the shell particles to the core particles and/or to each other may also be selected to be stable in harsh chemical conditions. For example, in one embodiment, the one or more adhering polymer may be an amine polymer. The one or more adhering polymers may also be cross-linked (e.g., using epoxide moieties) to add mechanical strength to polymeric binding matrix and/or include functionalizing moieties (e.g., anionic moieties) to give the composite particulate material desired properties for separating components of a mobile phase.
The shell particles may be bonded to the outside of the core particle to achieve a composite particle with a desired size and/or surface area. Moreover, the relative size of the core particles and shell particles and the number of layers of shell particles may be selected to provide composite particles with a surface area and porosity suitable for chromatography and/or solid phase extraction. The use of core particles bonded to shell particles provides combinations of particle sizes and surface areas that may not be possible with simple mixtures of un-bonded particles of the same material.
In one embodiment, a method for manufacturing a porous composite particulate material includes providing a plurality of acid-base-resistant core particles and a plurality of acid-base-resistant shell particles. At least a portion of the core particles, at least a portion of the shell particles, or both may be coated with polymeric material. A portion of the shell particles are adhered to each core particle to form a plurality of composite particles. For example, each core particle may have a plurality of shell particles bonded thereto by the polymer material.
In another embodiment, a separation apparatus for performing chromatography or solid phase separation is described. The separation apparatus includes a vessel having an inlet and an outlet. Any of the porous composite particulate materials disclosed herein may be disposed within the vessel. The vessel may be a column or a cassette suitable for use in the fields of chromatography and/or solid phase separation (e.g., high performance liquid chromatography (“HPLC”)).
The separation apparatus may be used to physically separate different components from one another. In one embodiment, a mobile phase including at least two different components to be separated is caused to flow through the composite particulate material to physically separate the at least two different components. At least one of the two different components is recovered.
In one embodiment, the composite particles are made from diamond, graphitic carbon, silicon carbide, boron nitride, tungsten carbide, combinations thereof, or other suitable acid-base-resistant material that is stable in chemically harsh conditions. The composite particles in some cases may be used with a mobile phase that would typically degrade commonly used stationary phase materials, such as a silica gel. In the case where diamond particles are used as core particles and/or shell particles, the mobile phase may include organic solvents, which are useful for separating lipids.
Features from any of the disclosed embodiments may be used in combination with one another, without limitation. In addition, other features and advantages of the present disclosure will become apparent to those of ordinary skill in the art through consideration of the following detailed description and the accompanying drawings.
The drawings illustrate several embodiments of the invention, wherein identical reference numerals refer to identical elements or features in different views or embodiments shown in the drawings.
A. Acid-Base-Resistant Particles
The porous composite particulate materials disclosed herein include a plurality of composite particles. Each composite particle includes an acid-base-resistant core particle, and a plurality of acid-base-resistant shell particles that at least partially surround and are bonded to the core particle by a polymeric layer of polymer material to impart a desired size and surface area. The core particles and shell particles may be made from the same material or different materials. The core particles and/or shell particles may be of a solid, porous, composite, synthetic, and/or natural occurring material.
The core particles and the shell particles may have the same or different particle sizes. As used herein, the phrase “particle size” means the approximate average particle size, such as average diameter or other average cross-sectional dimension of a plurality of particles, unless otherwise specified. In an embodiment, the shell particles are much smaller than the core particles to achieve a desired composite-particle surface area. In an embodiment, the shell particles have a particle size that is in a range from about 1 nm to 1000 nm, more specifically in a range from about 2 nm to about 500 nm, even more specifically in a range from about 5 nm to about 200 nm, and yet even more specifically in a range from about 10 nm to about 100 nm (e.g., about 10 nm to about 20 nm). The core particles may have a particle size in a range from about 1 μm to about 500 μm, more specifically about 1 μm to about 200 μm, or even more specifically in a range from about 1 μm to about 100 μm. The desired particle size of the core particles may depend on the application in which the composite particle is to be used. In one embodiment, the core particles have a particle size in a range from about 1 μm to 10 μm, more specifically about 1.5 μm to about 7 μm. This range may be suitable for HPLC applications and the like. In another embodiment, the particle size of the core particles may be in a range from about 5 μm to about 500 μm, or more specifically in a range from about 10 μm to about 150 μm. This larger range may be suitable for solid phase extraction applications and the like.
The acid-base-resistant shell and core particles may have a composition that is selected to be stable in sundry mobile phases, including organic solvents, and chemically harsh acids and bases. Examples of acid-base-resistant materials from which the shell particles and the core particles may be made include, but are not limited to, diamond, graphitic carbon (e.g., graphite), silicon carbide, or another suitable material that is chemically stable in acids and bases over a pH range of at least 3 to 12. For example, diamond, graphite, and silicon carbide are chemically stable in acids and bases over a pH range of about 0 to about 14. Silica and alumina are examples of materials that are not acid-base-resistant materials, because they may significantly degrade in bases with a pH greater than 12. Other relatively acid-base-resistant materials include, but are not limited to, boron nitride and tungsten carbide.
Diamond possess remarkable chemical inertness, hardness, low compressibility, optical transparency, and high thermal conductivity that may help eliminate thermal gradients in ultra performance liquid chromatography. Unlike silica, diamond does not easily dissolve in aqueous alkaline or acidic media, and it may be used in extremely harsh chemical environments. These properties of diamond may be achieved with naturally occurring diamond and/or synthetic diamond. Diamond material may also include other inorganic carbon materials, such as graphitic carbon, fullerenes, combinations thereof, or other non-diamond carbon.
The acid-base-resistant shell and core particles may be produced through any suitable method, including, for example, by forming carbonaceous material into diamond material under ultra-high pressure and high-temperature conditions or other synthetic diamond particles. Additionally, the acid-base-resistant shell and core particles may be the product of natural processes or by chemical vapor deposition processes. Acid-base-resistant shell and core particles may be produced by crushing and/or grinding a mineral starting material to obtain a desired sized particle. In an embodiment, the acid-base-resistant core particles may comprise micron-sized diamond particles with, for example, a particle size of about 1 μm to about 500 μm (e.g., about 1 μm to about 100 μm) and the acid-base-resistant shell particles may comprise diamond particles, with for example, a particle size of about 1 nm to 1000 nm (e.g., about 2 nm to about 200 nm). The acid-base-resistant shell and core particles may have a spherical shape, a faceted shape, an irregular shape, or other suitable geometry.
B. Polymeric Materials
The coating or binding polymer used to bond to the shell particles to the core particle and/or other shell particles may be any polymeric material that may be applied in a coating to adhere the acid-base-resistant particles to one another. For example, the polymer coating may include a polymeric material comprising one or more polymers that provide the porous composite particulate material desired properties for separating components of a mobile phase. The polymer coating may include macromonomers, oligomers, and/or various polymers, without limitation. The polymer coating may include combinations and/or mixtures of different polymeric materials and/or used to form different layers of polymers as described more fully below.
In one embodiment, the polymer coating or binding polymer may include at least one amine group. The amine polymer may be selected to be chemically stable in many of the same mobile phases that diamond particles or other acid-base-resistant materials disclosed herein are stable. In an embodiment, the amine polymer includes at least one pendant amine group and/or at least one primary, secondary, tertiary, and/or quaternary amine group. In various embodiments, the polymer coating may include for example, polyallylamine, polyethylenimine, polylysine, polyvinylamine, chitosan, trimethylchitosan (i.e., quaternized chitosan), polydiallydimethyl ammonium chloride (“PDADMAC”), poly(N,N′-dimethylaminoethylmethacrylate), poly(2-vinylpyridine), poly(4-vinylpyridine), polyvinylimidazole, poly(2-(dimethylamino)ethyl acrylate), and/or poly(2-aminoethyl methacrylate)hydrochloride, combinations of the foregoing, and/or derivatives of the foregoing.
Polyethylenimine may be present in the polymer coating in a wide range of molecular weights and degrees of branching. Chitosan may be produced by the deacetylation of chitin, and chitin may be deacetylated to various degrees. Polymers in the coating may be substantially linear or at least partially branched. Polymers including amines therein may be protonated, deprotonated, or partially protonated prior to, during, and/or following deposition on a surface. Additionally, the polymer coating may comprise any suitable naturally occurring proteins and/or peptides.
In additional embodiments, the polymer coating may include a homopolymer and/or a copolymer compound formed from monomer subunits including, for example, allylamine, vinylamine, ethylenimine, vinyl amine, lysine, arginine, histidine, 2-isocyanatoethyl methacrylate, aziridine, 1-vinylimidazole, 1-vinyl-2-pyrrolidone, 2-vinylpyridine, 4-vinylpyridine, 2-(dimethylamino)ethyl acrylate, 2-aminoethyl methacrylate hydrochloride, and/or 2-(tert-butyl amino)ethyl methacrylate.
Additionally, the polymer coating may include any suitable monomers that may be converted into amines after polymerization by deprotection, hydrolysis, and/or by simple chemical transformation. In various embodiments, the polymer coating may include monomers based on oxazoline, which may be polymerized to form polyoxazolines and/or which may then be hydrolyzed. Amine-comprising monomers forming a polymeric compound in coating may be protonated, deprotonated, or partially protonated prior to, during, and/or following polymerization.
In at least one embodiment, monomers forming a polymer in the polymer coating may be interspersed with other monomer units such as 2-hydroxyethylacrylate, styrene, 1,3-butadiene, methyl methacrylate, methyl acrylate, butyl acrylate, dodecyl methacrylate, acrylonitrile, acrylic acid, methacrylic acid, 4-vinylbenzyl chloride, 4-(trifluoromethyl)styrene, 3-nitrostyrene, vinyl ether, or vinyl acetate.
The polymer coating may include a polymeric compound having various chain lengths and various degrees of branching. For example, the polymeric coating may include a polymeric compound having a weight-average molecular weight or number-average molecular weight ranging from about 1,000 to about 2,500,000. In certain embodiments, the polymer coating may include a polymeric compound having a weight-average molecular weight or number-average molecular weight ranging from about 5,000 to about 100,000. Additionally, the polymer coating may include a polymeric compound having a weight-average molecular weight or number-average molecular weight ranging from about 30,000 to about 60,000 monomer units. In additional embodiments, the polymer coating may include polymeric compounds having a weight-average molecular weight or number-average molecular weight of less than about 1,000. The polymer coating may optionally include oligomers having a chain length of from 2 to 100 monomer units in length. As used herein, the term “polymeric compound” includes oligomers as well as polymers of varying chain lengths and molecular weights, unless otherwise specified.
Additional information about suitable polymers for use in the porous composite particulate materials disclosed herein may also be found in U.S. patent application Ser. No. 12/039,382 filed on 28 Feb. 2008, entitled “Methods For Direct Attachment Of Polymers To Diamond Surfaces And Articles Formed Thereby,” naming Matthew R. Linford and Li Yang as inventors, which is hereby incorporated herein, in its entirety, by reference.
In some embodiments, the polymer coating includes one or more anionic polymers. Anionic polymers may be useful for ion exchange chromatography. Example of suitable anionic polymers include, but are not limited to poly(styrenesulfonic acid, sodium salt), poly(acrylic acid), poly(methacrylic acid), derivatives of these, and/or combinations of these. While the polymer coating may be suitable for separating components of a mobile phase, uncoated, exposed surfaces of the core particles and/or shell particles (e.g., diamond core and shell particles) may be functionalized for separating components of a mobile phase as an alternative to or in addition to using the polymer coating.
II. Methods for Making Porous Composite Particulate MaterialsReference is now made to
In step 110, a plurality of acid-base-resistant core particles 114 are immersed in a polymeric material that coats and at least partially surrounds each core particle 114 with a respective polymer coating 112. In step 120, a first portion of acid-base-resistant shell particles are adhered to each core particle 114 to form a first porous shell layer 116 of shell particles. The shell particles adhere to the core particles 114 via the polymer coating 112. The thickness and composition of polymer coating 112 may be any thickness that is sufficient so that the shell particles adhere to the core particles 114. The thickness of the polymer coating 112 is typically sufficiently sized so that the polymer does not fill all the voids between adjacent shell particles of the first porous shell layer 116. Maintaining a relatively thin coating may help to provide a desired surface area. In one embodiment, the thickness of the polymer coating 112 may be in a range from about 1 nm to about 1 μm thick, and more specifically in a range from about 5 nm to about 100 nm. In an embodiment, the thickness of the polymer coating is less than the average diameter of the shell particles, more specifically the thickness is less than about half the diameter of the shell particles, and even more specifically less than one-fourth the diameter of the shell particles. The polymer coating 112 may be cured or otherwise chemically modified in step 120 or in subsequent steps, as described more fully below.
The portion of shell particles may be applied to each core particle 114 by suspending the shell particles in a solvent and immersing the coated core particles 114 in the suspension of shell particles or, alternatively, the suspension of shell particles may be caused to flow over the core particles 114. Any solvent suitable for suspending the core particles and/or the shell particles may be used. In one embodiment, the core particles and/or the shell particles may be suspended in water. The coating of shell particles on the coated core particles 114 yields intermediate composite particles 128 having rough surfaces. The rough surface includes voids (i.e., recesses in the surface) between the individual shell particles of the first porous shell layer 116.
A plurality of the intermediate composite particles 128 may be used as a final product if desired and/or cross-linked to improve mechanical stability. However, substantially increased surface area may be achieved by repeating steps 110 and 120 to yield intermediate composite particles with increasing numbers of porous shell layers. As shown in step 130, a polymer coating 113 may be applied to the surface of the intermediate composite particle 128 to coat the shell particles of the first porous shell layer 116. The polymer coating 113 may be made from the same or a different polymeric material than the polymeric coating 112 used in step 110. The thickness of the polymer coating 113 is typically sufficiently sized so that the polymer does not fill all the voids between adjacent shell particles of the first porous shell layer 116. In step 140, a second portion of the shell particles may be applied to intermediate composite particle 138 to yield second intermediate composite particles 142 each having a second porous shell layer 144 of shell particles bonded to the first porous shell layer 116.
In step 150, yet a third polymer coating 115 may be coated on intermediate composite particle 144 to yield intermediate particles 152, with the shell particles of the second porous shell layer 144 being coated. The polymer coating 115 may be made from the same or a different polymeric material than the polymeric coatings 112 or 113 used in steps 110 or 130. The thickness of the polymer coating 115 is typically sufficiently sized so that the polymer does not fill all the voids between adjacent shell particles of the second porous shell layer 144. In step 160, a third portion of shell particles may be adhered to the second porous shell layer 144 of intermediate particles 152 to yield intermediate composite particles 164 having a third porous shell layer 162 of shell particles.
The porous shell layers 116, 144, and 162 may have differently or similarly sized shell particles. Also, the shell particles in the different layers may have a different composition and/or be bonded using different compositions of polymer. The different shell particles, core particles, and polymers may be selected from any combination of the components described herein or components known in the art that are similar and/or provide similar function.
The method of adding additional porous shell layers may be continued until a desired number of porous shell layers and/or a desired surface area is achieved for the composite particles. In one embodiment, the method of forming porous shell layers may be repeated at least 5 times, more specifically at least about 10 times, or even more specifically at least 20 times to yield composite particles having 5, 10, or 20 porous shell layers, respectively. This method continues until the desired number of porous shell layers is achieved. In one embodiment, the number of porous shell layers is at least about 3, more specifically at least about 5, even more specifically at least about 10, yet even more specifically at least 20, and most specifically at least 50.
The shell particles, core particles, and/or composite particles may each be completely or partially coated with the polymer coating. In many cases, the polymer coating is applied using immersion, which tends to apply a relatively even coating around an entire particle. However, in some embodiments, one or more of the acid-base-resistant particles may only be partially coated with a sufficient polymer coating to adhere to other particles. In addition, the application of the shell particles may be asymmetric so as to create asymmetric composite particles.
Once the polymer has been attached to the surface of the core particles, there are numerous chemical reactions that may be performed, including cross-linking and curing. The cross-linking and/or curing may be carried out separately at any of the steps described in method 100. In one embodiment, curing may be performed for each step that results in the formation of a porous shell layer. In one embodiment, cross-linking is carried out as a final step 170. However, the step 170 is optional and embodiments also include the use of polymers that do not require curing and/or cross-linking.
In embodiments where curing and/or cross-linking is performed, the polymer coating may be cured and/or cross linked using any suitable technique such as thermal curing and/or radiation curing such as curing using infrared or ultraviolet curing lights. Curing may increase the physical and/or chemical stability of the polymer coating. For example, curing may increase the stability of the polymer coating when exposed to harsh conditions, such as high and/or low pH solutions, which may allow a stationary phase including the porous composite particulate material to be cleaned and/or otherwise used under harsh conditions. Some porous composite particulate materials described herein may be used in combination with strong solvents, high pH conditions, and/or low pH conditions. The ability to clean a column under harsh conditions may enable reuse of a previously contaminated stationary phase. In at least one embodiment, curing may cause amide linkage to form between various compounds in the polymer coating. Additionally, curing may cause amide or other linkages to form between various compounds in the polymer coating and the surface of the acid-base-resistant particles.
In additional embodiments, a polymer in the coating may be allowed to react with another compound in the coating before, during, and/or after depositing the coating on the acid-base-resistant particles to increase the molecular weight of the coating. Increasing the molecular weight of the polymer may be advantageous in that the higher molecular weight coating may have increased stability in a variety of conditions.
In additional embodiments, the coating and/or at least a polymeric compound forming the coating may be cross-linked during a curing process, such as a thermal and/or pressure-induced curing process, as described above. Additionally, the curing of the coating and/or at least a polymeric compound forming the coating, may be cross linked by exposing the coating to radiation. Cross-linking may cause stable bonds to form with amine groups and/or other chemical moieties in a polymeric compound in the coating, thereby increasing the stability of coating. Additionally, cross-linking compounds in the coating using compounds having epoxy groups may produce hydroxyl groups in and/or on the coating, resulting in a change in chemical characteristics of the coating and providing potential reactive sites on the coating.
In certain embodiments, a cross-linking agent having at least two functional bonding sites may be used to effect cross-linking of at least a portion of the coating and/or at least a polymeric compound forming the coating. For example, a cross-linking agent may comprise a diepoxide compound having at least two epoxide groups, each of which may bond with an amine group. A cross-linking agent having at least two functional bonding sites may bond with at least one amine group on at least two or more polymeric molecules and/or compounds. In an additional embodiment, a cross-linking agent having at least two functional bonding sites may bond with at least one amine group on at least two separate sites on a single polymeric molecule. Additionally, a cross-linking agent having at least two functional bonding sites may bind to a polymeric compound forming the coating at only one of the at least two functional binding sites.
Examples of cross-linking agents suitable for cross-linking the polymer coating and/or at least a polymeric compound forming the polymer coating may include any type of compound containing two or more amine reactive functional groups, including, for example, diisocyanates, diisothiocyanates, dihalides, diglycidyl ethers, diepoxides, dianhydrides, dialdehydes, diacrylates, dimethacrylates, dimethylesters, di- and/or triacrylates, di- and/or trimethacrylates, and/or other diesters. In at least one embodiment, acrylates and/or methacrylates may react with an amine by Michael addition.
In addition, suitable cross-linking agents may include, without limitation, 1,2,5,6-diepoxycyclooctane, phenylenediisothiocyanate, 1,4-diisocyanatobutane, 1,3-phenylene diisocyanate, 1,6-diisocyanatohexane, isophorone diisocyanate, diethylene glycol diglycidyl ether, 1,4-butanediol diglycidyl ether, bisphenol A diglycidyl ether, poly(ethylene glycol)diglycidyl ether, polypropylene glycol)diglycidyl ether, octanedioic acid dichloride (suberic acid dichloride), phthaloyl dichloride, pyromellitic dianhydride, 1,3-butadiene diepoxide, p-phenylene diisothiocyanate, 1,4-dibromobutane, 1,6-diiodohexane, glutaraldehyde, 1,3-butanediol diacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate, dipentaerythritol pentaacrylate, 1,6-hexanediol dimethacrylate, and/or propoxylated (3) glyceryl triacrylate. Cross-linking agents may additionally comprise at least one functional group suitable for bonding with non-amine functional groups that may be present on polymers in the coating disclosed herein.
In at least one embodiment, an epoxide compound such as, 1,2,5,6-diepoxycyclooctane, may have at least one highly strained epoxide ring that may be reactive with various amine groups in the polymer coating. Various alcohols may be used as effective solvents for amine-epoxide reactions. Reaction of the at least one highly strained epoxide ring with an amine group in the coating may result in immobilization of hydrophobic cyclooctyl rings and hydrophilic hydroxyl groups in the coating, leading to the formation of a mixed-mode stationary phase in the coating. This type of mixed-mode stationary phase may be employed for various uses, including, for example, retention of proteins and small molecules such as drugs under reverse phase and/or normal conditions in an SPE column.
The amine group is an extremely versatile chemical reagent with a rich chemistry. Information about some of these reactions may be found in U.S. patent application Ser. No. 12/040,638 filed on 29 Feb. 2008, entitled, “Functionalized Diamond Particles And Methods For Preparing The Same,” naming Matthew R. Linford and Gauray Saini as inventors, which is hereby incorporated herein, in its entirety, by this reference.
In one embodiment, the porous composite particulate material may include a body of bonded composite particles. The body may be formed by forming a bed of coated intermediate composite particles (e.g., composite particles 224) and polymerizing or otherwise joining the individual composite particles together to form a coherent body. Forming a body of bonded composite particles may allow the individual particles to maintain their integrity.
In other embodiments, some of the core particles may be coated with polymer material and some of the core particles may be uncoated. Also some of the shell particles may be coated with polymer material and some of the shell particles may be uncoated. In such an embodiment, the coated/uncoated core particles may be mixed together with the coated/uncoated shell particles to form a plurality of composite particles.
The porous composite particulate materials described herein provide desired sizes, porosity, surface areas, and chemical stability suitable for chromatography and SPE techniques. When used in chromatography and SPE, high-resolution separation may be achieved with relatively low back pressure, which is in contrast to columns and cassettes that use high surface area particles without the composite structure described herein.
The porous composite particulate materials include a plurality of composite particles, with each composite particle including a core particle at least partially surrounded by one or more layers of shell particles. The shell particles are bonded to the core particles by a polymer coating. The shell particles and/or core particles may be made from the acid-base-resistant materials described above, including but not limited to diamond particles, graphitic carbon, silicon carbide, boron nitride, tungsten carbide, and combinations thereof. The porous composite particulate material may also have any combination of polymers described above. However, in an embodiment, the polymer coating that bonds the core particles to the shell particles and/or the shell particles to themselves is an amine polymer.
The composite particles may be provided in the form of finely divided discrete particles (e.g., a powder). Alternatively, the composite particles may be provided as a body of bonded composite particles. When the composite particles are provides as a body of bonded composite particles, the body may exhibit dimensions suitable for use in a separation apparatus, such as, but not limited to, separation devices used in HPLC.
In one embodiment, the composite particles have a particle size in a range from about 1 μm to 500 μm, more specifically about 1 μm to 200 μm, or even more specifically in a range from about 1 μm to about 150 μm. In one embodiment, the composite particles have a particle size in a range from about 1 μm to about 10 μm, or more specifically about 1.5 μm to about 7 μm. This particle range may be particularly useful for HPLC applications and the like. In another embodiment, the composite particles can have a particle size can be in a range from about 5 μm to about 500 μm, or more specifically in a range from about 10 μm to about 150 μm. This larger particle range may be more suitable for use in solid phase extraction applications and the like.
The composite particles may include a desired surface area. The surface area may depend on core and shell particle size, number of porous shell layers, and particle geometry. However, the surface area of the composite particles is higher than a similarly sized core particle due to the additional surface area provided by the shell particles. In an embodiment, the surface area may be measured using the Brunauer Emmett and Teller (“BET”) technique and is in a range from 1-500 m2/g for composite particles having a particle size in a range from about 1 μm to 500 μm, more specifically in a range from 25-300 m2/g, or even more specifically 50-200 m2/g. In one embodiment, the composite particles have a particle size in a range from about 1 μm to 10 μm may have a surface area in a range from about 10-500 m2/g, more specifically in a range from 25-200 m2/g, and even more specifically in a range from 25-60 m2/g. In another embodiment, composite particles having a particle size from about 10 μm to 150 μm may have a surface area in a range from about 5-200 m2/g, or more specifically 10-100 m2/g. In yet another embodiment, composite particles having a particle size in a range from about 250 μm to about 500 μm may have a surface area at least about 5 m2/g, and even more specifically at least about 10 m2/g for composite particles with a particle size in a range from about 250 μm to about 500 μm.
In a more detailed embodiment, a composite particle including a diamond core particle having a size of about 2.5 μm to about 5 μm and 1-50 porous shell layers of diamond shell particles having a particle size of about 5 nm to about 50 nm may have a surface area of about 1 m2/g to about 60 m2/g. In a more specific embodiment, a composite particle including a diamond core particle having a size of about 2.5 μm and 10-50 porous shell layers of diamond shell particles having a particle size of about 5 nm to about 10 nm may have a surface area of about 14 m2/g to about 60 m2/g. In another more specific embodiment, a composite particle including a diamond core particle having a size of about 5 μm and 10-50 porous shell layers of diamond shell particles having a particle size of about 5 nm to about 10 nm may have a surface area of about 7 m2/g to about 33 m2/g.
In some embodiments, an additional particulate component may be embedded in the porous shell layers of the shell particles. The additional particulate component may be any organic or inorganic material that provides a desired property to the porous composite particulate material. In one embodiment, the additional component may be initially included in the manufacture of the composite particles but then removed. For example, the porous shell layers may include silica particles that exhibit a selectivity to be removed over more acid-base-resistant particles, such as diamond, graphite, or boron nitride shell particles. This method may allow a composite particle to be formed with particular structural features. Alternatively, the additional component may be included with the purpose of removing or eluding out the component during use. For example, the additional component may be configured to elute out over time in the presence of a mobile phase.
In one embodiment, the additional component may be a particle that has affinity for a drug or other chemical reagent. In one embodiment, the additional component may include a catalytic reagent. The additional component may be included in the core particles and/or the layers of shell particles.
IV. Separation Apparatuses and MethodsThe column 502 may comprise any type of column or other device suitable for use in separation processes such as chromatography and solid phase extraction processes. Examples of the column 502 include, without limitation, chromatographic and solid phase extraction columns, tubes, syringes, cartridges (e.g., in-line cartridges), and plate containing multiple extraction wells (e.g., 96-well plates). The reservoir 504 may be defined within an interior portion of the column 502. The reservoir 504 may permit passage of various materials, including various solutions and solvents used in chromatographic and solid-phase extraction processes.
The porous body 506 may be disposed within at least a portion of reservoir 504 of the column 502 so that various solutions and solvents introduced into the column 502 to contact at least a portion of the porous body 506. The porous body 506 may comprise a plurality of substantially non-porous particles in addition to the composite porous material.
In certain embodiments, frits, such as glass frits, may be positioned within the reservoir 504 to hold porous body 506 in place, while allowing passage of various materials such as solutions and solvents. In some embodiments, a frit may not be necessary, such as the body of bonded-together composite particles as described above with reference to
In one embodiment, the separation apparatus 500 is used to separate two or more components in a mobile phase by causing the mobile phase to flow through the porous body 506. The mobile phase is introduced through an inlet and cause to flow through the porous body 506 and the separated components may be recovered from the outlet 512.
In one embodiment, the mobile phase includes concentrated organic solvents, acids, or bases. In one embodiment, the mobile phase includes a concentrated acid with a pH less than about 3, more specifically less than about 2. In another embodiment, the mobile phase includes a base with a pH greater than about 10, more specifically greater than about 12, and even more particularly greater than 13.
In one embodiment, the separation apparatus 500 is washed between a plurality of different runs where samples of mixed components are separated. In one embodiment, the washing may be performed with water. In another embodiment, a harsh cleaning solvent is used. In this embodiment, the harsh cleaning solvent may be a concentrated organic solvent and/or a strong acid or base. In one embodiment, the cleaning solvent has a pH less than about 3, more specifically less than about 2. In another embodiment, the cleaning solvent has a pH greater than about 10, more specifically greater than about 12, and even more particularly greater than 13.
V. ExamplesThe following examples are for illustrative purposes only and are not meant to be limiting with regards to the scope of the specification or the appended claims. For example, the present disclosure and claims are not limited to the use of diamond particles, unless otherwise specified.
Example 1 Synthesis Of Composite Diamond ParticlesExample 1 describes the synthesis of core-shell composite particles using an amine polymer, micron-sized core diamond particles, and nano-sized shell diamond particles.
The following reagents were provided: Poly(allylamine) (Mw ca. 65,000, 20 wt. % solution in water, Aldrich, Milwaukee, Wis.), polyethylenimine (Mw 25,000, Aldrich, Milwaukee, Wis.) (1,2,5,6-diepoxycyclooctane (96%, Aldrich) and 1,16-hexadecanedioic acid (>98%, Aldrich) were used as received. Diamond powders (50-70 μm and 100-250 nm) were provided by U.S. Synthetic Corporation of Orem, Utah.
Core-shell particles were synthesized from 50-70 μm core particles and 100-250 nm shell diamond particles. The microdiamond core particles were cleaned in piranha solution (70% H2SO4:30% conc. H2O2) at 100° C. for 1 h.
The piranha cleaned diamonds were then sonicated in ultrapure water, and washed extensively with ultrapure water on a filter funnel. The nanodiamond shell particles were not cleaned in piranha solution, but used as received.
Core-shell composite particles containing 0-5 and 9 bilayers of PAAm-nanodiamond were synthesized. A 0.25 wt. % solution of poly(allylamine) was made from 1.55 g of PAAm (20 wt. % solution in water) in 125 mL of ultrapure water, and 12 g of piranha-cleaned microdiamond powder were poured into this solution. The solution was shaken for ca. 10 s every 10 min for 1 h to expose the particles to PAAm. After immersion in the PAAm solution, the microdiamond powder was washed extensively with ultrapure water in a filter funnel. An aqueous suspension of nanodiamond powder was prepared by sonicating 1 g of nanodiamond shell particles in 120 mL of ultrapure water, and 12 g of PAAm-functionalized microdiamond powder was poured into this suspension for 1 h. This suspension of nanodiamond and PAAm-functionalized diamond was shaken gently for ca. 10 s every 10 min to expose all surfaces of the PAAm-functionalized microdiamond particles to nanodiamond particles (i.e., shell particles). After adsorption, the aqueous suspension was filtered on a medium pore size (25 μm-50 μm) filter funnel. As the size of the nanodiamond particles is much smaller than the pore size of the filter funnel, unbounded nanodiamond particles in the suspension easily pass through the pores of the filter funnel leaving behind microdiamonds containing one layer of adsorbed nanodiamond particles. These particles were washed extensively with ultrapure water on the filter funnel to remove any non-adsorbed nanodiamonds. Approximately 2.8 g of core-shell composite particles (having microdiamonds containing one layer of adsorbed nanodiamond particles) were taken from this lot for characterization.
Examples 2-4 Synthesis of Multi-Layered Diamond Composite ParticlesThe remaining composite particles from Example 1 were used as an intermediate composite particle to make composite particles having a plurality of layers of shell particles. The intermediate composite particles were poured into the aqueous solution of PAAm described in Example 1. The intermediate composite particles were held for 1 h to amine functionalize the outer surface of the first layer of shell particles. Treatment with the PAAm solution and the cleaning procedure were repeated as in Example 1 (vide supra). A powder was recovered and poured into an aqueous suspension of nanodiamonds. The deposition conditions were as for the earlier layer (vide supra). Another 2.8 g of this functionalized diamond powder were taken, and the remaining diamond powder was treated in the same way. This procedure of immersion in the aqueous solution of PAAm followed by immersion in the aqueous suspension of nanodiamond was performed 3, 5, and 9 times to achieve a composite particle with the desired number of layers of nanodiamond particles for Examples, 2-4, respectively. A flow diagram of the synthesis of the composite particles of Examples 2-4 is illustrated in
Example 5 describes the synthesis of core-shell composite particles that are bonded together. Bonded core-shell composite particles have been found to be particularly useful in HPLC. Core-shell particles were prepared from 5 μm and 10-50 nm diamond particles. Nanodiamond particles were used as their aqueous suspension (8.17 wt. %), which had a surfactant in it. The addition of surfactant prevented the agglomeration of nanodiamond particles. Unlike the preparation for core-shell composite particles for SPE (i.e., described in Example 1), the particles in Example 5 were prepared in a test tube. Approximately 1.6 g of 5 μm diamond powder was poured into ca. 30 ml water in a test tube. A 1.33 wt. % solution of polyethylenimine (“PEI”) was made in water, and 400 μl of this solution was added into the test tube. The test tube was shaken vigorously for 3 min to expose diamond particles to the polymer. After treatment with PEI solution, the solution was centrifuged for 1 min at 5000 rpm. As a result of that the centrifuging, diamond particles settled down at the bottom of the test tube. The supernatant was discarded, and more water was added to the test tube. The test tube was shaken vigorously to remove non-specifically adsorbed polymer from the surface, and centrifuged afterwards. This cleaning procedure was repeated two times. After cleaning, 400 μl of nanodiamond suspension was added to 30 ml suspension of PEI coated 5 μm diamond particles in the test tube, and the test tube was shaken vigorously for 3 minutes. After treatment with nanodiamond particles, the microdiamond particles were washed with copious amounts of water using the same procedure as for PEI treated particles mentioned before. The alternate treatment with PEI and nanodiamond was continued until 20 bilayers of nanodiamond and PEI were formed on the surface of the 5 μm diamond particles.
Examples 6-9 Chemical Cross-Linking of Composite ParticlesExamples 6-9 describes a method of improving the mechanical stability of core-shell composite particles by cross-linking the polymer of adjacent particles. Nanodiamond particles, microdiamond particles and adsorbed PAAm are attached to themselves through relatively weak non-covalent interactions. The mechanical stability of these particles was improved by chemical cross-linking with 1,2,5,6-diepoxycyclooctane.
In Examples 6-8, chemical cross-linking was carried out on the composite particles of Examples 2-4 respectively. The cross-linking was carried out as a final step in the synthesis of the core-shell particles. In each of Examples 6-8, a 2.3 wt. % solution of 1,2,5,6-diepoxycyclooctane (made by dissolving 0.1747 g in 7.5 mL isopropanol) was used to chemically cross-link the PAAm-nanodiamond of the core-shell composite particles of Examples 1-4, respectively. Approximately 2.6 g of each different core-shell particle was used for chemical cross-linking. The reaction was done in a sealed thick-walled glass tube at 80° C. overnight. After the reaction, the core-shell diamond powder was washed extensively in the filter funnel with copious amounts of isopropanol followed by dichloromethane.
FTIR based surface analysis of Examples 6-8 was performed with a Magna-IR 560 spectrometer from Nicolet (Madison, Wis.). Environmental scanning electron microscopy (“ESEM”) images of the samples were acquired using a FEI (Philips) XL30 ESEM FEG instrument. Since diamond is an insulator, the diamond powder was adhered to a conductive, double stick carbon tape, and the instrument was operated in low-vacuum mode to prevent the charging of the surface. Samples were sent to Micromeritics (Norcross, Ga.) for BET surface area and pore size analysis.
The layer-by-layer deposition of nanodiamond particles around a solid microdiamond core was monitored by four techniques: diffuse reflectant infrared Fourier transform (“DRIFT”), ESEM, BET surface-area measurements, and sorbent (analyte) capacity measurements.
Referring to
Core-shell composite particles were also characterized according to their number of shell layers.
Referring to
As a characterization tool, the SPE capacity of the core-shell composite particles was also determined.
The Examples demonstrate the effect of layer-by-layer deposition of nanodiamond particles on various parameters, i.e., surface area, capacity, IR adsorption, etc., was determined. Core-shell diamond particles have a higher surface area and capacity than solid diamond particles, which increases with the number of PAAm-nanodiamond bilayers.
While various aspects and embodiments have been disclosed herein, other aspects and embodiments are contemplated. The various aspects and embodiments disclosed herein are for purposes of illustration and are not intended to be limiting. Additionally, the words “including,” “having,” and variants thereof (e.g., “includes” and “has”) as used herein, including the claims, shall have the same meaning as the word “comprising” and variants thereof (e.g., “comprise” and “comprises”).
Claims
1. A porous composite particulate material, comprising:
- a plurality of composite particles, at least some the plurality of composite particles including, an acid-base-resistant core particle; a plurality of acid-base-resistant shell particles forming a plurality of porous shell particle layers at least partially surrounding the acid-base-resistant core particle, wherein the plurality of acid-base-resistant shell particles include at least one of diamond or graphitic carbon; and at least one polymer that is acid-base-resistant, each of the plurality of porous shell particle layers bonded to an adjacent one of the plurality of porous shell particle layers by a respective layer of the at least one polymer.
2. The porous composite particulate material of claim 1, wherein the at least one polymer is stable under the same mobile phase conditions as diamond.
3. The porous composite particulate material of claim 1, wherein the acid-base-resistant core particle includes a diamond particle.
4. The porous composite particulate material of claim 1, wherein the at least one polymer is stable under the same mobile phase conditions as diamond, the acid-base-resistant shell particles include graphitic carbon, and the acid-base-resistant core particle includes a diamond particle.
5. The porous composite particulate material of claim 4, wherein the at least one polymer includes at least one amine polymer.
6. The porous composite particulate material of claim 4, wherein the respective layer of the at least one polymer is at least partially cross-linked.
7. The porous composite particulate material of claim 4, wherein the at least one polymer includes at least one amine polymer, and the respective layer of the at least one polymer is at least partially cross-linked.
8. The porous composite particulate material of claim 1, wherein adjacent layers of the plurality of porous shell particle layers differ from one another by one or more of composition or size.
9. The porous composite particulate material of claim 1, further comprising a layer of anionic polymer coated on at least a portion of the plurality of acid-base-resistant shell particles.
10. The porous composite particulate material of claim 1, wherein adjacent porous shell layers of the plurality of porous shell particle layers include respective polymer coatings having a different polymeric material from one another.
11. The porous composite particulate material of claim 1, wherein the at least one polymer includes monomers that are convertible to amines.
12. The porous composite particulate material of claim 11, wherein the monomers are convertible to amines by one or more of deprotection, hydrolysis, or chemical transformation.
13. The porous composite particulate material of claim 11, wherein the at least one polymer includes monomers including oxazoline or polyoxazolines.
14. The porous composite particulate material of claim 1, wherein the at least one polymer includes poly(allylamine).
15. The porous composite particulate material of claim 1, wherein the at least one polymer includes one or more of a homopolymer or a copolymer.
16. The porous composite particulate material of claim 15, wherein the at least one polymer includes monomer units interspersed therein different from monomeric subunits of the at least one polymer.
17. The porous composite particulate material of claim 16, wherein the monomer units include 2-hydroxyethylacrylate, styrene, 1,3-butadiene, methyl methacrylate, methyl acrylate, butyl acrylate, dodecyl methacrylate, acrylonitrile, acrylic acid, methacrylic acid, 4-vinylbenzyl chloride, 4-(trifluoromethyl)styrene, 3-nitrostyrene, vinyl ether, or vinyl acetate
18. The porous composite particulate material of claim 1, wherein a layer of the at least one polymer is at least partially cross-linked.
19. The porous composite particulate material of claim 1, wherein the plurality of composite particles are bonded together.
20. The porous composite particulate material of claim 1, wherein the plurality of composite particles is in powder form.
21. A separation apparatus, comprising:
- a vessel having an inlet and an outlet; and
- a porous composite particulate material disposed within the vessel, the porous composite particulate material including, a plurality of composite particles, at least some the plurality of composite particles including: a plurality of acid-base-resistant shell particles forming a plurality of porous shell particle layers at least partially surrounding the acid-base-resistant core particle, wherein the plurality of acid-base-resistant shell particles include at least one of diamond or graphitic carbon; and at least one polymer that is acid-base-resistant, each of the plurality of porous shell particle layers bonded to an adjacent one of the plurality of porous shell particle layers by a respective layer of the at least one polymer.
22. A method for manufacturing a porous composite particulate material, the method comprising:
- providing a plurality of acid-base-resistant core particles and a plurality of acid-base-resistant shell particles, the plurality of acid-base-resistant shell particles including at least one of diamond or graphitic carbon;
- coating at least a portion of the plurality of acid-base-resistant core particles, at least a portion of the plurality of acid-base-resistant shell particles, or combinations thereof with an acid-base-resistant polymer material; and
- adhering a portion of the plurality of acid-base-resistant shell particles to each of the plurality of acid-base-resistant core particles with the acid-base-resistant polymer material to form a plurality of composite particles.
Type: Application
Filed: Mar 9, 2015
Publication Date: Jun 25, 2015
Inventor: Matthew R. Linford (Provo, UT)
Application Number: 14/642,332