METHOD AND SYSTEM FOR PRODUCING REFINED HYDROCARBONS FROM WASTE PLASTICS
Embodiments of the present disclosure relate to a method and system for producing refined hydrocarbons from waste plastics. The method and system for producing refined hydrocarbons from waste plastics according to the embodiments of the present disclosure may minimize formation of an ammonium chloride salt (NH4Cl) and may prevent an adhesion phenomenon of impurity particles in a reactor in a refining process of waste plastic pyrolysis oil containing impurities including chlorine and nitrogen. The method and system for producing refined hydrocarbons according to the present disclosure may have excellent refining efficiency and may implement a long-term operation of a process because a catalyst used in the process is prevented from being deactivated, and may produce lightened and refined hydrocarbons having a low content of impurities and a low content of olefins from waste plastics.
This application claims priority under 35 U.S.C. § 119 to Korean Patent Application No. 10-2023-0051637, filed on Apr. 19, 2023 and No. 10-2023-0153266, filed on Nov. 8, 2023, in the Korean Intellectual Property Office, the disclosures of which are incorporated herein by reference in their entirety.
TECHNICAL FIELDEmbodiments of the present disclosure relate to a method and system for producing refined hydrocarbons from waste plastics.
BACKGROUNDWaste plastics, which are produced by using petroleum as a feedstock, have a low rate of recycling, such as energy recovery in power generation, or mechanical recycling, and a significant amount of waste plastics is simply incinerated or landfilled. These wastes take a long time to degrade in nature, which causes contamination of the soil and serious environmental pollution. A method for recycling waste plastics includes pyrolysis of the waste plastics and converting the pyrolyzed waste plastics into usable oil. The oil produced by pyrolyzing waste plastics in this way is called waste plastic pyrolysis oil.
However, since pyrolysis oil obtained by pyrolyzing waste plastics has a higher content of impurities such as chlorine, nitrogen, and metals caused by waste materials than oil produced from crude oil by a general method, there is a risk of emission of air pollutants such as SOx and NOx when the pyrolysis oil is used as fuel, and the pyrolysis oil may be blended in a limited amount with a high-value-added fuel such as gasoline or diesel oil.
A refining method for removing impurities such as chlorine, nitrogen, oxygen, and metals contained in waste plastic pyrolysis oil, a method of performing dechlorination, denitrification, and deoxygenation by reacting waste plastic pyrolysis oil with hydrogen in the presence of a hydrotreating catalyst, and a method of removing chlorine contained in waste plastic pyrolysis oil by adsorption using a chlorine adsorbent, or the like are known.
Specifically, U.S. Pat. No. 3,935,295 discloses a technology for removing chloride contaminants from various hydrocarbon oils. The technology is a conventional technology of hydrotreating oil in the presence of a hydrotreating catalyst in a first reactor, introducing a fluid containing hydrogen chloride (HCl) produced at this time and refined oil into a second reactor, and then removing a chlorine component contained in the fluid by adsorption using an adsorbent.
However, as described in the conventional technology, when oil is allowed to react with hydrogen in the presence of a hydrotreating catalyst, a chlorine compound such as hydrogen chloride produced together with refined oil, and a nitrogen compound react with each other to form an ammonium chloride salt (NH4Cl), and the ammonium chloride salt causes various process issues. Specifically, the ammonium chloride salt formed inside the reactor by the reaction of oil and hydrogen not only causes corrosion of the reactor to reduce durability, but also causes various process issues such as an occurrence of a differential pressure and a resulting reduction in process efficiency. In addition, when the process is operated for a long period of time, adhesion of impurity particles in the waste plastic pyrolysis oil occurs inside the reactor, causing various process issues.
Therefore, there is a need to develop a method and system capable of stably producing refined hydrocarbons having a low content of impurities such as Cl from waste plastics.
SUMMARYVarious embodiments of the present disclosure will be described in greater detail with reference to the accompanying drawings. The drawings are schematic illustrations of various embodiments (and intermediate structures). As such, variations from the configurations and shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances, are to be expected. Thus, the described embodiments should not be construed as being limited to the particular configurations and shapes illustrated herein but may include deviations in configurations and shapes which do not depart from the spirit and scope of the present disclosure as defined in the appended claims.
It will be understood that, although the terms “first”, “second”, “third”, and so on may be used herein to describe various elements, these elements are not limited by these terms. These terms are used to distinguish one element from another element. Thus, a first element described below could also be termed as a second or third element without departing from the spirit and scope of the present disclosure.
It should be understood that the drawings are simplified schematic illustrations of the described processes and apparatuses and may not include well known details to avoid obscuring the features of the embodiments of the present disclosure.
It should also be noted that features present in one embodiment may be used with one or more features of another embodiment without departing from the scope of the present disclosure.
It is further noted, that in the various drawings, like reference numbers designate like elements.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the present disclosure.
As used herein, singular forms are intended to include the plural forms as well, unless the context clearly indicates otherwise.
It will be further understood that the terms “comprises,” “comprising,” “includes,” and “including” when used in this specification, specify the presence of the stated elements and do not preclude the presence or addition of one or more other elements. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items.
Unless otherwise defined, all terms including technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the embodiments belong in view of the present disclosure.
It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the present disclosure and the relevant art and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.
An embodiment of the present disclosure is directed to providing a method and system for producing refined hydrocarbons from waste plastics that minimize formation of ammonium chloride salt (NH4Cl) in a refining process of waste plastic pyrolysis oil containing impurities including chlorine and nitrogen.
Another embodiment of the present disclosure is directed to providing a method and system for producing refined hydrocarbons from waste plastics that have excellent refining efficiency and allow long-term operation because catalyst activity is maintained for a long time.
Still another embodiment of the present disclosure is directed to providing a method and system for producing refined hydrocarbons from waste plastics that may reduce or prevent an adhesion phenomenon of impurity particles.
Still another embodiment of the present disclosure is directed to providing a method and system for producing, from waste plastics, refined hydrocarbons that have a low content of impurities such as chlorine, nitrogen, oxygen, and metals and a low content of olefins, and may thus be blended with existing petroleum products in large quantities.
According to an embodiment of the present disclosure, a method for producing refined hydrocarbons from waste plastics includes: a pyrolysis operation introducing waste plastics into a pyrolysis reactor and pyrolyzing the waste plastics to produce pyrolysis gas; an oil production operation producing waste plastic pyrolysis oil by introducing the pyrolysis gas into a hot filter filled with a neutralizing agent; a dehydration operation applying a voltage to a first mixed solution obtained by mixing the waste plastic pyrolysis oil, washing water, and a demulsifier to dehydrate the first mixed solution; a hydrotreating operation hydrotreating a second mixed solution obtained by mixing the first mixed solution dehydrated in the dehydration operation and a sulfur source to produce refined oil from which impurities are removed; and a dewaxing operation dewaxing the refined oil from which impurities are removed.
In the dehydration operation, the waste plastic pyrolysis oil may be mixed in a greater volume than the washing water.
In the dehydration operation, the waste plastic pyrolysis oil and the washing water may be mixed in the first mixed solution at a volume ratio of 1:0.001 to 1:0.5.
In the dehydration operation, the waste plastic pyrolysis oil and the demulsifier may be mixed in the first mixed solution at a volume ratio of 1:0.000001 to 1:0.001.
The voltage may be applied as an alternating current or a combination of an alternating current and a direct current.
The voltage may be applied through a vertical electrode.
The method for producing refined hydrocarbons from waste plastics may further include, after the application of the voltage in the dehydration operation, removing a rag layer from the first mixed solution.
The dehydration operation may be performed under a temperature condition of 20° C. to 300° C.
A ratio of a content of moisture in the waste plastic pyrolysis oil to a content of moisture in the first mixed solution dehydrated in the dehydration operation may be 1:0.0001 to 1:0.9.
In the dehydration operation, the dehydrated first mixed solution may be additionally dehydrated by condensation of moisture.
A weight ratio of nitrogen to chlorine in the second mixed solution may be 1:1 to 1:10.
The sulfur source may include sulfur-containing oil.
The sulfur-containing oil may be included in an amount of less than 0.5 parts by weight with respect to 100 parts by weight of the first mixed solution dehydrated in the dehydration operation.
The sulfur source may include one or two or more sulfur-containing organic compounds selected from a disulfide-based compound, a sulfide-based compound, a sulfonate-based compound, and a sulfate-based compound.
The hydrotreating operation may be performed in the presence of a molybdenum-based hydrotreating catalyst.
The molybdenum-based hydrotreating catalyst may be a catalyst in which a molybdenum-based metal, or a metal including one or two or more selected from nickel, cobalt, and tungsten, and a molybdenum-based metal are supported on a support.
The molybdenum-based hydrotreating catalyst may include a molybdenum-based sulfide hydrotreating catalyst.
The hydrotreating may be performed under a pressure condition of 50 bar to 150 bar.
The method for producing refined hydrocarbons from waste plastics may further include, after the hydrotreating operation, subjecting a stream including the refined oil from which impurities are removed to gas-liquid separation and then washing the gas-liquid separated stream with water.
In an embodiment, the dewaxing operation is dewaxing a refined fraction separated by distilling the refined oil from which impurities are removed.
In an embodiment, the dewaxing operation is dewaxing a mixed oil obtained by mixing the refined oil from which impurities are removed and petroleum hydrocarbons.
Other features and aspects will be apparent from the following detailed description, the drawings, and the claims.
The advantages and features of the embodiments of the present disclosure and methods for accomplishing them will become apparent from embodiments described below in detail with reference to the accompanying drawings. However, the embodiments of the present disclosure is not limited to embodiments to be disclosed below, but may be implemented in various different forms. These embodiments are provided in order to make the present disclosure complete and allow those skilled in the art to better recognize the scope of the present disclosure. Therefore, the present disclosure is not limited by the embodiments disclosed herein.
Unless defined otherwise, all terms (including technical and scientific terms) used in the present specification have the same meanings as commonly understood by those skilled in the art to which the present disclosure pertains.
Unless the context clearly indicates otherwise, the singular forms of the terms used in the present specification may be interpreted as including the plural forms.
A numerical range used in the present specification includes upper and lower limits and all values within these limits, increments logically derived from a form and span of a defined range, all double limited values, and all possible combinations of the upper and lower limits in the numerical range defined in different forms. Unless otherwise specifically defined in this specification, values out of the numerical range that may occur due to experimental errors or rounded values also fall within the defined numerical range.
The term “reactor” used in the present specification may refer to a device that may be used in processes such as production, refining, separation, and mixing of waste plastic pyrolysis oil. For example, the reactor may be interpreted to mean a device such as a dehydrator, a coalescer, a hydrotreating reactor, or a separator used in a refining process of waste plastic pyrolysis oil.
The term “vertical electrode” used in the present specification may refer to an electrode erected in a vertical direction with respect to the ground, and the term “horizontal electrode” may refer to an electrode laid horizontally with respect to the ground.
Referring now to
In an embodiment of the present invention disclosure a method for producing refined hydrocarbons from waste plastics, may include: a pyrolysis operation introducing waste plastics into pyrolysis reactor 10 and pyrolyzing the waste plastics to produce pyrolysis gas 12; an oil production operation producing waste plastic pyrolysis oil 24 by introducing the pyrolysis gas into a hot filter 20 filled with a neutralizing agent; a dehydration operation applying a voltage to a first mixed solution obtained by mixing the waste plastic pyrolysis oil, washing water, and a demulsifier to dehydrate the first mixed solution; a hydrotreating operation hydrotreating a second mixed solution obtained by mixing the first mixed solution dehydrated in the dehydration operation and a sulfur source 38 to produce refined oil from which impurities are removed; and a dewaxing operation dewaxing the refined oil from which impurities are removed.
In a method and system for producing refined hydrocarbons from waste plastics according to embodiments of the present disclosure, a pyrolysis operation of producing pyrolysis gas by pyrolyzing waste plastics, an oil production operation of producing waste plastic pyrolysis oil from the pyrolysis gas, and a dehydration operation including water washing, demulsification, voltage application, and the like are performed, the dehydration operation performed to reduce issues such as catalyst deactivation due to moisture dispersed in the form of an emulsion in the waste plastic pyrolysis oil, and corrosion of a reactor due to chlorine contained in moisture and a low pH of moisture. In addition, a hydrotreating operation that may minimize formation of an ammonium chloride salt that causes various issues in a process of refining pyrolysis oil, oil refining and petrochemical processes using refined oil as a feedstock, and the like, and the dewaxing operation of dewaxing refined oil from which impurities are removed through the above operations. The method for producing refined hydrocarbons from waste plastics according to the present disclosure, the above series of operations are organically combined, such that process stability may be secured, and lightened and refined hydrocarbons that may be used as a feedstock for blending with existing petroleum products or oil refining and petrochemical processes may be produced.
Hereinafter, the method and system for producing refined hydrocarbons from waste plastics will be described in detail.
Various embodiments of the present disclosure provide a method for producing refined hydrocarbons from waste plastics, the method including: a pyrolysis operation introducing waste plastics into a pyrolysis reactor and pyrolyzing the waste plastics to produce pyrolysis gas; an oil production operation producing waste plastic pyrolysis oil by introducing the pyrolysis gas into a hot filter filled with a neutralizing agent; a dehydration operation applying a voltage to a first mixed solution obtained by mixing the waste plastic pyrolysis oil, washing water, and a demulsifier to dehydrate the first mixed solution; a hydrotreating operation hydrotreating a second mixed solution obtained by mixing the first mixed solution dehydrated in the dehydration operation and a sulfur source to produce refined oil from which impurities are removed; and a dewaxing operation dewaxing the refined oil from which impurities are removed.
First, a pyrolysis operation is performed. The pyrolysis operation introduces waste plastics into a pyrolysis reactor and pyrolyzes the waste plastics to produce pyrolysis gas.
The pyrolysis operation may be performed at a temperature of 400 to 550° C. in a non-oxidizing atmosphere. The non-oxidizing atmosphere may be an atmosphere in which waste plastics do not oxidize (combust). The non-oxidizing atmosphere may include an atmosphere in which an oxygen concentration is adjusted to 1 vol % or less, or an atmosphere of an inert gas such as nitrogen, water vapor, carbon dioxide, or argon. When the pyrolysis temperature is 400° C. or higher, fusion of chlorine-containing plastics may be prevented, and when the pyrolysis temperature is 550° C. or lower, chlorine in waste plastics may partially remain in a pyrolysis residue (char).
In the pyrolysis operation, a pyrolysis gas phase, a pyrolysis liquid phase including oil and wax, and a pyrolysis solid phase including a pyrolysis residue may be produced.
The waste plastics may include at least one selected from the group consisting of polyethylene (PE), polypropylene (PP), polyethylene terephthalate (PET), polyvinyl chloride (PVC), and polystyrene (PS). The waste plastics may contain organic chlorine (organic Cl) and inorganic chlorine (inorganic Cl). Waste oil produced through cracking and pyrolysis reactions of waste plastics, such as waste plastic pyrolysis oil, contains a large amount of impurities derived from waste plastics. Accordingly, there is a concern about emission of air pollutants when using waste oil, and in particular, organic chlorine and inorganic chlorine components are converted into HCl and discharged during a high-temperature treatment process, and thus, it is required to refine the waste oil to remove the impurities such as the chlorine components.
In general, waste plastics may be divided into domestic waste plastic and industrial waste plastic. The domestic waste plastic is a plastic in which PVC, PS, PET, PBT, and the like in addition to PE and PP are mixed, and may refer to a mixed waste plastic containing 3 wt % or more of PVC together with PE and PP. A content of chlorine in the domestic waste plastic is relatively high, for example, 5,000 ppm or more or 5,000 to 15,000 ppm. PE and PP accounts for most industrial waste plastic, and has a content of chlorine of 100 to 1,000 ppm, 500 to 1,000 ppm, or 700 to 1,000 ppm, which is lower than the content of chlorine in the domestic waste plastic. However, in the industrial waste plastic, a content of organic Cl originating from an adhesive or a dye component is high, and in particular, a proportion of chlorine contained in an aromatic ring is high.
In particular, chlorine originating from PVC in the domestic waste plastic is removed with HCl, or a process called hydrogen chloride elimination, whereas chlorine from PE and PP, which account for most industrial waste plastic, originates from an adhesive or a dye component. In most cases, organic Cl derived from the aromatic ring has a higher proportion than organic Cl formed at the end of the chain ring and is difficult to remove by general pyrolysis or a neutralizing agent.
The pyrolysis gas 12 produced in the pyrolysis operation may include, with respect to the total weight of the pyrolysis gas, 5 to 35 wt % of Naphtha (boiling point of 36° C. to 150° C.), 10 to 60 wt % of Kerosene (boiling point of 150 to 265° C.), 20 to 40 wt % of LGO (boiling point of 265 to 380° C.), and 5 to 40 wt % of AR (boiling point of 380° C. to 800° C.), and may include, with respect to the total weight of the pyrolysis gas, 5 to 30 wt % of Naphtha (boiling point of 36° C. to 150° C.), 15 to 50 wt % of Kerosene (boiling point of 150 to 265° C.), 20 to 35 wt % of LGO (boiling point of 265 to 380° C.), and 10 to 40 wt % of AR (boiling point of 380° C. to 800° C.), or 5 to 20 wt % of Naphtha (boiling point of 36° C. to 150° C.), 15 to 35 wt % of Kerosene (boiling point of 150 to 265° C.), 25 to 35 wt % of LGO (boiling point of 265 to 380° C.), and 15 to 40 wt % of AR (boiling point of 380° C. to 800° C.). In addition, in the pyrolysis gas, a weight ratio of light oils (the sum of Naphtha and Kero) to heavy oils (the sum of LGO and AR) may be 0.1 to 3, 0.1 to 2.0, or 0.2 to 1.0. When the pyrolysis gas having the above range of the oil composition is then introduced into a hot filter of the present disclosure, the pyrolysis oil may be lightened and impurities may be further removed. In an embodiment, in the hot filter, as a pyrolysis reaction occurs primarily at a high temperature, additional chlorine dissociation and lightening of oil proceed simultaneously, and secondarily, the dissociated chlorine comes into contact with a neutralizing agent (CaO) and is fixed in the form of salt. In particular, it is analyzed that the amount of HCl generated is large in pyrolysis oil derived from domestic waste plastic including PVC, and the HCl dissociated chlorine is not recombined with hydrocarbons and is fixed to the neutralizing agent (CaO) in the hot filter at a high ratio. Accordingly, the pyrolysis operation of the present disclosure may have better chlorine removal efficiency when using domestic waste plastic as a feedstock. However, the chlorine removal may be less efficient when the industrial waste plastic is used for feedstock because the content of chlorine in the feedstock is lower than that of domestic waste plastic, but the lightening effect may be significantly improved due to a difference in the composition of waste plastics.
The pyrolysis operation may be performed in an autoclave reactor, a batch reactor, a fluidized-bed reactor, a packed-bed reactor, or the like, and specifically, any reactor capable of controlling stirring and temperature rise may be applied. In an embodiment of the present disclosure, the pyrolysis operation may be performed in a batch reactor.
Meanwhile, the pyrolysis step may further include a pyrolysis gas recovery step of recovering a pyrolysis gas phase and a pyrolysis liquid phase as gas, and a separation step of separating the pyrolysis solid phase (solids) into fine particles and coarse particles.
In the pyrolysis gas recovery operation, pyrolysis gas containing low-boiling-point hydrocarbon compounds such as methane (CH4), ethane (C2H6), and propane (C3H8) in the gas phase generated in the pyrolysis operation is recovered. The pyrolysis gas generally contains combustible materials such as hydrogen, carbon monoxide, and low-molecular-weight hydrocarbon compounds. Examples of the hydrocarbon compounds include methane, ethane, ethylene, propane, propene, butane, and butene. Such pyrolysis gas contains a combustible material and may be used as fuel.
In the separation operation, solids in the solid phase generated in the pyrolysis operation, for example, carbides, a neutralizing agent, and/or a copper compound are separated into fine particles and coarse particles. Specifically, classification is performed using a sieve having a size smaller than an average particle diameter of the chlorine-containing plastics and larger than an average particle diameter of the neutralizing agent or the copper compound, such that the solids generated by the pyrolysis operation may be separated into fine particles and coarse particles. In the separation operation, the solids may be separated into fine particles containing a relatively large amount of the chlorine-containing neutralizing agent and the copper compound, and coarse particles containing a relatively large amount of carbides. The fine particles and carbides may be retreated as necessary, reused in the pyrolysis operation, used as fuel, or disposed of as waste, but the present disclosure is not limited thereto.
Subsequently, an oil production operation is performed. The oil production operation produces waste plastic pyrolysis oil by introducing the pyrolysis gas into a hot filter filled with a neutralizing agent.
The oil production operation may be performed in an oxygen-free atmosphere at a temperature of 400 to 550° C. and a pressure of normal pressure to 0.5 bar. The oxygen-free atmosphere may include an inert gas atmosphere or a closed system atmosphere without oxygen. In the above temperature range, the pyrolysis gas may be better lightened and clogging and a differential pressure caused by wax may be suppressed.
In addition, the oil production operation may be performed at a gas hourly space velocity (GHSV) of 0.3 to 1.2/hr or 0.5 to 0.8/hr. When the above condition is satisfied, the waste plastic pyrolysis oil may be lightened, and impurities in the pyrolysis oil may be reduced.
The neutralizing agent may be oxide, hydroxide, and carbonate of a metal, or a combination thereof, and the metal may be calcium, aluminum, magnesium, zinc, iron, copper, or a combination thereof. In an embodiment, for example, the neutralizing agent may be aluminum oxide, calcium oxide, magnesium oxide, zinc oxide, iron oxide, and/or copper oxide. In addition, the neutralizing agent may be a zeolite component such as a waste fluid catalytic cracking (FCC) catalyst (E-cat), and may further contain a waste FCC catalyst in the metal oxide. In an embodiment, the neutralizing agent may be calcium oxide, a waste FCC catalyst, copper metal, or copper oxide, or may be calcium oxide.
The neutralizing agent may have a particle size of 400 to 900 μm, or may have a particle size of 500 to 800 μm. As the hot filter is filled with the neutralizing agent having the above particle size, the GHSV of the pyrolysis gas is adjusted, such that the lightening of the pyrolysis oil may be achieved, and the differential pressure of the hot filter may be suppressed, which may improve the process operation efficiency.
Meanwhile, the particle size of the neutralizing agent may refer to D50, and D50 refers to a particle diameter when a cumulative volume from a small particle size accounts for 50% in measuring a particle size distribution by a laser scattering method. In this case, as for D50, the particle size distribution may be measured by collecting the sample from the prepared carbonaceous material according to KS A ISO 13320-1 standard using Mastersizer 3000 manufactured by Malvern Panalytical Ltd. In an embodiment, ethanol may be used as a solvent, and if necessary, the ethanol may be dispersed using an ultrasonic disperser, and then, a volume density may be measured.
The hot filter generally serves to separate pyrolysis gas and a residue (char) from pyrolyzed products in the art. However, in an embodiment of the present disclosure, a hot filter filled with a neutralizing agent is applied not only to achieve lightening but also to reduce impurities, and therefore, as described above, operating conditions such as a temperature of the hot filter and a particle size of the neutralizing agent are adjusted to specific ranges.
The oil production operation may satisfy the following Relational Expressions 1 and 2.
In Relational Expression 1, A1 represents a total amount (wt %) of Naphtha (boiling point of 36° C. to 150° C.) and Kerosene (boiling point of 150 to 265° C.) of the pyrolysis gas, and A2 represents a total amount (wt %) of Naphtha (boiling point of 36° C. to 150° C.) and Kerosene (boiling point of 150 to 265° C.) of the pyrolysis oil, and in Relational Expression 2, B1 represents a content (ppm) of chlorine in the pyrolysis gas, and B2 represents a content (ppm) of chlorine in the pyrolysis oil.
In an embodiment, Relational Expressions 1 and 2 may be 60<(A2−A1)/A1(%)<90, 65<(A2−A1)/A1(%)<85, or 70<(A2−A1)/A1(%)<80, and −75<(B2−B1/B1) (%)<−55, −70<(B2−B1/B1) (%)<−55, or −65<(B2−B1/B1) (%)<−55, respectively.
Relational Expressions 1 and 2 numerically represent light and heavy degrees of the waste plastic pyrolysis oil produced by the hot filter filled with the neutralizing agent of the present disclosure. In an embodiment of the present disclosure, the light degree of the pyrolysis oil may be improved to a significantly high level by controlling the oil composition and the content of chlorine of the pyrolysis oil introduced into the hot filter and the organic/inorganic materials containing chlorine.
The waste plastic pyrolysis oil produced in the oil production operation may include, with respect to the total weight of the waste plastic pyrolysis oil, 30 to 50 wt % of Naphtha (boiling point of 36° C. to 150° C.), 30 to 50 wt % of Kerosene (boiling point of 150 to 265° C.), 10 to 30 wt % of LGO (boiling point of 265 to 380° C.), and 0 to 10 wt % of AR (boiling point of 380° C. to 800° C.), and may include, with respect to the total weight of the waste plastic pyrolysis oil, 35 to 50 wt % of Naphtha (boiling point of 36° C. to 150° C.), 35 to 50 wt % of Kerosene (boiling point of 150 to 265° C.), 10 to 30 wt % of LGO (boiling point of 265 to 380° C.), and 0 to 8 wt % of AR (boiling point of 380° C. to 800° C.) or 35 to 45 wt % of Naphtha (boiling point of 36° C. to 150° C.), 35 to 45 wt % of Kerosene (boiling point of 150 to 265° C.), 10 to 20 wt % of LGO (boiling point of 265 to 380° C.), and 0 to 6 wt % of AR (boiling point of 380° C. to 800° C.). In addition, in the pyrolysis gas, a weight ratio of light oils (the sum of Naphtha and Kerosene) to heavy oils (the sum of LGO and AR) may be 2.5 to 5, 2.5 to 4, or 3 to 3.8.
In the method for producing refined hydrocarbons from waste plastics according to an embodiment of the present disclosure, the pyrolysis operation and the oil production operation may satisfy the following Relational Expression 3.
In Relational Expression 3, T1 is a temperature at which the waste plastics are pyrolyzed in the pyrolysis reactor in the pyrolysis operation, and T2 is a temperature at which the waste plastic pyrolysis oil is produced in the hot filter in the oil production operation.
When the T2/T1 value is 0.7 or less, a ratio of pyrolysis oil condensed in the hot filter to pyrolysis oil circulated to the pyrolysis reactor increases, and thus, a final boiling point of the pyrolysis oil may be excessively low. On the other hand, when the T2/T1 value is 1.3 or more, a ratio of pyrolysis oil condensed in the hot filter to pyrolysis oil lost in the gas phase may excessively increase, and thus, a yield of pyrolysis oil may be reduced.
In an embodiment, the T2/T1 value may be, for example, 0.7 to 1.2, 0.8 to 1.2, 0.8 to 1.1, 0.9 to 1.1, or 1. Therefore, the effects described above may be further improved.
Subsequently, a dehydration operation is performed. The dehydration operation includes applying a voltage to a first mixed solution obtained by mixing the waste plastic pyrolysis oil, washing water, and a demulsifier to dehydrate the first mixed solution.
Waste plastic pyrolysis oil contains moisture, and moisture in pyrolysis oil may cause problems such as deactivation of a hydrotreating catalyst and corrosion of a reactor. In addition, since water-soluble impurities are contained in moisture, it is required to remove moisture. Moisture present in the form of an emulsion in the waste plastic pyrolysis oil may be easily removed by performing the dehydration operation.
The waste plastic pyrolysis oil according to an embodiment of the present disclosure may contain impurities such as a chlorine compound, a nitrogen compound, an oxygen compound, a metal compound, and char-derived particles, may contain impurities in the form of compounds in which chlorine, nitrogen, oxygen, or a metal is bonded to hydrocarbons, and may contain paraffinic, olefinic, naphthenic, or aromatic hydrocarbons.
The washing water according to an embodiment of the present disclosure may serve to increase the probability of contact between emulsion-type moisture present in the waste plastic pyrolysis oil. In addition, a basic compound may be added to the washing water to remove a water-soluble acidic material contained in moisture, and the basic compound may be sodium hydroxide (NaOH), but is not limited thereto. The waste plastic pyrolysis oil according to an embodiment of the present disclosure may be mixed in a greater volume than the washing water. In an embodiment, the waste plastic pyrolysis oil and the washing water may be mixed in the first mixed solution at a volume ratio of 1:0.001 to 1:0.5, 1:0.005 to 1:0.4, or 1:0.01 to 1:0.3. When the volume ratio satisfies the above range, water washing is sufficiently performed, and thus, impurities in the pyrolysis oil may be significantly reduced, and costs required to remove washing water to be mixed may be minimized.
The demulsifier according to an embodiment of the present disclosure may be one or a mixture of two or more selected from the group consisting of polyethylene glycol, tert-butanol, acetone, alkylnaphthalene sulfonate, alkylbenzene sulfonate, a nonionic alkoxylated alkyl phenol resin, polyalkylene oxide, and polyoxyethylene sorbitan ester, but is not limited thereto. In an embodiment, the demulsifier may be added with the washing water.
In the first mixed solution according to an embodiment of the present disclosure, the waste plastic pyrolysis oil and the demulsifier may be mixed at a volume ratio of 1:0.000001 to 1:0.001, 1:0.000002 to 1:0.0005, or 1:0.000003 to 1:0.0001. When the volume ratio satisfies the above range, the emulsion may be decomposed with minimal impact on the quality of pyrolysis oil.
The demulsifier according to an embodiment of the present disclosure may have a weight average molecular weight of 200 to 2,000, 300 to 1,000, or 400 to 800. When the weight average molecular weight satisfies the above range, it is easy to mix the demulsifier with the waste plastic pyrolysis oil and the washing water under conditions where the dehydration operation is performed, and thus, the decomposition efficiency of the moisture emulsion is increased.
The moisture in the form of an emulsion contained in the first mixed solution in which the waste plastic pyrolysis oil, the washing water, and the demulsifier are mixed is still difficult to remove because it is stable. Therefore, a voltage may be applied to the first mixed solution to facilitate removal of moisture.
The voltage according to an embodiment of the present disclosure may be applied as a dual polarity, alternating current, direct current or a combination of an alternating current and a direct current. Some impurity particles contained in the waste plastic pyrolysis oil have polarities, and therefore, when a direct current voltage is applied, polarized impurity particles accumulate on a specific electrode, and when the process is performed for a long period of time, the impurities may adhere to the electrode. However, when an alternating current voltage is applied, the polarity of the electrode changes periodically, and therefore, the adhesion phenomenon of the impurity particles may be prevented. In addition, a frequency of the alternating current according to an embodiment of the present disclosure may be a single frequency or a combination of two or more frequencies. As a specific example, in the case of the single frequency, an alternating current with a frequency of 60 Hz may be applied, and in the case of the combination of two or more frequencies, alternating currents with frequencies of 50 Hz and 60 Hz may be applied alternately, but the embodiments of the present disclosure are not limited thereto.
The voltage according to an embodiment of the present disclosure may be applied through a vertical electrode. In a case where the impurity particles accumulate on the electrode during a mixed solution preparation process or a voltage application process, when the impurities particles are not artificially washed, the impurity particles may adhere to the electrode after a long period of time. However, when a vertical electrode is used, the adhesion phenomenon of the impurity particles may be prevented in advance because the impurity particles do not accumulate on the electrode but fall to the bottom of the reactor due to gravity even without an additional washing operation.
A magnitude of the voltage according to an embodiment of the present disclosure may be 0.1 to 50 kV, 1 to 30 kV, or 5 to 20 kV, but is not limited thereto.
The dehydration according to an embodiment of the present disclosure may be performed by any method known in the art. As a non-limiting example, after the application of the voltage, water may be removed by draining a water layer which is oil-water separated. Water may also be removed in a gas-liquid separator.
Metal impurities in the waste plastic pyrolysis oil stabilize the emulsion, hinder oil-water separation, and help form a stable emulsion layer, commonly called a rag layer. Such a rag layer may be formed between a desalinated oil layer at an upper portion of the first mixed solution and a water layer at a lower portion of the first mixed solution, and may be gradually thickened during a continuous dehydration operation. An excessively thickened rag layer may be discharged to equipment at the hydrotreating operation together with desalinated oil. This reduces the desalination effect of the desalinated oil and reduces the efficiency of the process. In addition, the rag layer may be discharged together with water and may cause issues in a wastewater treatment process. Therefore, in an embodiment, the rag layer formed between the desalinated oil layer and the water layer may be removed.
Therefore, the method for producing refined hydrocarbons from waste plastics according to an embodiment of the present disclosure may further include, after the application of the voltage in the dehydration operation, removing a rag layer from the first mixed solution. The removal of the rag layer may be performed through a pipe penetrating through a wall of a dehydrator and connected to the outside after measuring a change in density of the mixed solution by a density meter in the dehydrator to determine a formation location and a thickness of the rag layer, but is not limited thereto.
In the dehydration operation according to an embodiment of the present disclosure, after dehydrating the first mixed solution, the dehydrated first mixed solution may be additionally dehydrated by condensation of moisture.
The additional dehydration according to an embodiment of the present disclosure may be performed by supplying the dehydrated first mixed solution to a coalescer. In an embodiment, the residual moisture contained in the dehydrated first mixed solution may be removed through condensation by a collection filter in the coalescer, but this is only a specific example and the embodiments of the present disclosure are not limited thereto. As the content of moisture in the waste plastic pyrolysis oil is further reduced through the additional dehydration, deactivation of the catalyst due to moisture may be significantly reduced or prevented, and the process stability and the quality of the refined oil may be improved.
A ratio of a content of moisture in the waste plastic pyrolysis oil to a content of moisture in the dehydrated first mixed solution according to an embodiment of the present disclosure may be 1:0.0001 to 1:0.9, 1:0.0005 to 1:0.5, or 1:0.001 to 1:0.1. When the ratio satisfies the above range, a risk of issues occurring in subsequent processes such as during hydrotreating may be significantly reduced, and high-quality refined oil that can satisfy specifications may be produced as a feedstock, but embodiments of the present disclosure are not limited thereto.
The dehydration operation according to an embodiment of the present disclosure may be performed at a pressure of 50 bar or less. When the dehydration operation is performed at a pressure of 50 bar or less, moisture in the pyrolysis oil may be easily removed, and the process stability may be secured. In an embodiment, the dehydration operation may be performed at a pressure of 30 bar or less, or 20 bar or less, and 5 bar or more.
The dehydration operation according to an embodiment of the present disclosure may be performed at a temperature of 20° C. to 300° C. When the temperature satisfies the above range, the decomposition of the emulsion and the condensation of moisture are smoothly performed, and thus, the dehydration efficiency may be improved. In an embodiment, the dehydration operation may be performed at a temperature of 50° C. to 250° C., or 80° C. to 200° C.
In order to improve the dehydration efficiency in the dehydration operation according to an embodiment of the present disclosure, one or more additional processes selected from the group consisting of centrifugation and distillation may be performed before and/or after the dehydration. The additional centrifugation and distillation processes described above may be performed by known methods and are not limited to any particular method.
Next, a hydrotreating operation may be performed. The hydrotreating operation hydrotreats a second mixed solution obtained by mixing the first mixed solution dehydrated in the dehydration operation and a sulfur source to produce refined oil from which impurities are removed.
The second mixed solution according to an embodiment of the present disclosure may have a concentration of chlorine (Cl) of 10 ppm or more, 100 ppm or more, or 200 ppm or more. In an embodiment, the second mixed solution may have a concentration of chlorine (Cl) of 3,000 ppm or less. The embodiment of the present disclosure, however, is not limited thereto.
In the second mixed solution according to an embodiment of the present disclosure, a weight ratio of nitrogen to chlorine may be 1:0.1 to 1:10, 1:0.5 to 1:5, or 1:1 to 1:2, but the above weight ratio is only a specific example of what may be included in the waste plastic pyrolysis oil, and a composition of the waste plastic pyrolysis oil is not limited thereto.
The hydrotreating operation, according to an embodiment of the present disclosure, may be performed under a condition in which a ratio of hydrogen to the second mixed solution is 100 Nm3/Sm3 to 5,000 Nm3/Sm3, 500 Nm3/Sm3 to 3,000 Nm3/Sm3, or 1,000 Nm3/Sm3 to 1,500 Nm3/Sm3. When this condition is satisfied, impurities may be effectively removed, the high activity of the hydrotreating catalyst may be maintained for a long period of time, and the process efficiency may be improved.
The sulfur source refers to a sulfur source capable of continuously supplying a sulfur component during the refining process.
In the hydrotreating operation, the second mixed solution containing the sulfur source may be prepared, such that during the refining process, deactivation of a molybdenum-based hydrotreating catalyst due to lack of the sulfur source and high-temperature operation may be suppressed, and the catalytic activity may be maintained.
The sulfur source according to an embodiment of the present disclosure may include a sulfur-containing oil. The sulfur-containing oil refers to oil composed of hydrocarbons containing sulfur obtained from crude oil as a feedstock. The sulfur-containing oil is not particularly limited and may include oil containing sulfur. In an embodiment, the sulfur-containing oil may be, for example, light gas oil, straight-run naphtha, vacuum naphtha, pyrolysis naphtha, straight-run kerosene, vacuum kerosene, pyrolysis kerosene, straight-run gas oil, vacuum gas oil, pyrolysis gas oil, sulfur-containing waste tire oil, and any mixture thereof.
When waste tire oil is included as the sulfur-containing oil according to an embodiment of the present disclosure, a high content of sulfur contained in waste tires may be converted into oil together with hydrocarbons and may serve as a sulfur source for the waste plastic pyrolysis oil. In addition, diverting the waste tire oil into the sulfur source for the waste plastic pyrolysis oil is advantageous in terms of reducing the environmental load due to recycling of waste tires and maintaining the catalytic activity for a long period of time.
In an embodiment, the sulfur-containing oil may be light gas oil (LGO) with a specific gravity of 0.7 to 1. When this sulfur-containing oil is used, the sulfur-containing oil may be uniformly mixed with the dehydrated first mixed solution, and high hydrotreating efficiency may be exhibited. In an embodiment, the specific gravity may be 0.75 to 0.95, or, 0.8 to 0.9. The sulfur-containing oil may contain 100 ppm or more of sulfur. When the sulfur component is contained in an amount of less than 100 ppm, a content of the sulfur component supplied may be small, such that the effect of preventing deactivation of the molybdenum-based hydrotreating catalyst may be insufficient. In an embodiment, the sulfur component may be contained in an amount of 800 ppm or more, or 8,000 ppm or more, and 200,000 ppm or less.
The second mixed solution according to an embodiment of the present disclosure may contain 100 ppm or more of sulfur. As in the case of the sulfur-containing oil, when the sulfur component is contained in the second mixed solution in an amount of less than 100 ppm, the content of the sulfur component supplied may be small, such that the effect of preventing deactivation of the molybdenum-based hydrotreating catalyst may be insufficient. In an embodiment, the sulfur component may be contained in an amount of 800 ppm or more, or 8,000 ppm or more, and 200,000 ppm or less.
The sulfur-containing oil according to an embodiment of the present disclosure may be included in an amount of less than 0.5 parts by weight with respect to 100 parts by weight of the first mixed solution dehydrated in the dehydration operation. In an embodiment, the sulfur-containing oil may be included in an amount of less than 0.1 parts by weight, or less than 0.05 parts by weight, and more than 0.01 parts by weight. As the sulfur-containing oil is included in an amount of less than 0.5 parts by weight, the concentration of chlorine (Cl) or nitrogen (N) contained in the waste plastic pyrolysis oil may be diluted, such that a formation rate of an ammonium chloride salt (NH4Cl) may be controlled, and the process stability may be improved.
The sulfur source according to an embodiment of the present disclosure may include one or two or more sulfur-containing organic compounds selected from a disulfide-based compound, a sulfide-based compound, a sulfonate-based compound, and a sulfate-based compound. Specifically, the sulfur source may include one or a mixture of two or more selected from dimethyl disulfide, dimethyl sulfide, polysulfide, dimethyl sulfoxide (DMSO), methyl methanesulfonate, ethyl methanesulfonate, propyl methanesulfonate, propenyl propenesulfonate, propenyl cyanoethansulfonate, ethylene sulfate, bicyclo-glyoxal sulfate, and methyl sulfate. However, these compounds are only presented as examples and the embodiments of the present disclosure are not limited thereto.
The sulfur-containing organic compound according to an embodiment of the present disclosure may be included in an amount of 0.01 to 0.1 parts by weight with respect to 100 parts by weight of the first mixed solution dehydrated in the dehydration operation. Specifically, the sulfur-containing organic compound may be included in an amount of 0.02 to 0.08 parts by weight, and or, 0.03 to 0.06 parts by weight with respect to 100 parts by weight of the first mixed solution dehydrated in the dehydration operation. When the sulfur-containing organic compound is included in an amount of less than 0.01 parts by weight, the content of the sulfur component supplied may be small, such that the effect of preventing deactivation of the molybdenum-based hydrotreating catalyst may be insufficient.
The hydrotreating refers to a hydrogenation reaction that occurs by adding a reaction gas including hydrogen gas (H2) to the second mixed solution in which the first mixed solution dehydrated in the dehydration operation and the sulfur source are mixed in the presence of a molybdenum-based hydrotreating catalyst. Specifically, the hydrotreating may refer to hydrotreating, which is known in the related art, including a hydrodesulfurization reaction, a hydrocracking reaction, a hydro-dechlorination reaction, a hydro-denitrogenation reaction, a hydro-deoxygenation reaction, and a hydro-demetallization reaction. Through the hydrotreating, impurities including chlorine (Cl), nitrogen (N), and oxygen (O), and some olefins may be removed, other metal impurities may also be removed, and a by-product containing the impurities may be produced.
The by-product may be produced by reacting impurities such as chlorine (Cl), nitrogen (N), sulfur (S), or oxygen (O) contained in the waste plastic pyrolysis oil with the hydrogen gas (H2). In an embodiment, for example, the by-product may include hydrogen sulfide gas (H2S), hydrogen chloride (HCl), ammonia (NH3), water vapor (H2O), or the like, and in addition, may include unreacted hydrogen gas (H2), and a trace of methane (CH4), ethane (C2H6), propane (C3H8), butane (C4H10), or the like.
The molybdenum-based hydrotreating catalyst according to an embodiment of the present disclosure may be a catalyst in which a molybdenum-based metal, or a metal including one or two or more selected from nickel, cobalt, and tungsten, and a molybdenum-based metal are supported on a support. The molybdenum-based hydrotreating catalyst has high catalytic activity during hydrotreating, and the molybdenum-based hydrotreating catalysts may be used alone or, if necessary, in the form of a two-way catalyst combined with a metal such as nickel, cobalt, or tungsten.
As the support according to an embodiment of the present disclosure, alumina, silica, silica-alumina, titanium oxide, a molecular sieve, zirconia, aluminum phosphate, carbon, niobia, or a mixture thereof may be used, but the embodiments of the present disclosure are not limited thereto.
The molybdenum-based hydrotreating catalyst according to an embodiment of the present disclosure may include a molybdenum-based sulfide hydrotreating catalyst. For example, the molybdenum-based hydrotreating catalyst may include molybdenum sulfide (MoS) or molybdenum disulfide (MoS2), but is not limited thereto, and may include a known molybdenum-based sulfide hydrotreating catalyst.
The reaction gas according to an embodiment of the present disclosure may further include hydrogen sulfide gas (H2S). The hydrogen sulfide gas (H2S) included in the reaction gas may act as a sulfur source, and may regenerate the activity of the molybdenum-based hydrotreating catalyst deactivated during the refining process together with the sulfur source mixed with the waste plastic pyrolysis oil.
The hydrotreating according to an embodiment of the present disclosure may be performed at a pressure of 150 bar or less. In an embodiment, the hydrotreating may be performed at a pressure of 120 bar or less, or 100 bar or less, and 50 bar or more. It has been observed, that when the hydrotreating operation is performed under a pressure condition of more than 150 bar, ammonia and hydrogen chloride are produced in excess during the hydrotreating, an ammonium chloride salt formation temperature increases, and as a result, a differential pressure of the hydrotreating reactor (an or other process equipment) may increase, and the process stability may be significantly reduced. By controlling the contents of nitrogen and chlorine in the waste plastic pyrolysis oil, the increase in ammonium chloride salt formation temperature may be partially suppressed even under a condition of a pressure of more than 150 bar. However, this case is not appropriate because the waste plastics targeted in the production method according to an embodiment of the present disclosure may be extremely limited thereto.
The hydrotreating operation according to an embodiment of the present disclosure may be performed at a temperature of 150° C. to 500° C. This temperature refers to the temperature of the mixed solution in the hydrotreating reactor. When the temperature satisfies the above range, the hydrotreating efficiency may be improved. In an embodiment, the hydrotreating may be performed at a temperature of 200° C. to 400° C.
The hydrotreating according to an embodiment of the present disclosure may be performed in multiple stages, and as a specific example, may be performed in two stages. When the hydrotreating is performed in two stages, a first stage may be performed at a lower temperature than a second stage. In this case, the first stage may be performed at a temperature of 150° C. to 300° C., or 200° C. to 250° C., and the second stage may be performed at a temperature of 300° C. to 500° C., or 350° C. to 400° C., but the present disclosure is not limited thereto.
A method for producing refined hydrocarbons from waste plastics according to an embodiment of the present disclosure may further include, after the hydrotreating operation, subjecting a stream including the refined oil from which impurities are removed to gas-liquid separation (see separators 42-1 to 42-4) and then washing the gas-liquid separated stream with water.
The stream including the refined oil from which impurities are removed according to an embodiment of the present disclosure may contain hydrogen chloride, ammonia, unreacted hydrogen gas, and the like, in addition to the refined oil from which impurities are removed discharged from a rear end of the hydrotreating reactor where the hydrotreating operation is performed.
Through the gas-liquid separation according to an embodiment of the present disclosure, from the stream including the refined oil from which impurities are removed, ammonia and hydrogen chloride produced by the hydrotreating may be removed, and unreacted hydrogen gas may be recovered.
The gas-liquid separation according to an embodiment of the present disclosure may be performed by a method known in the art using a separator (see separator 42-1), but is not particularly limited.
The gas-liquid separation according to an embodiment of the present disclosure may be performed two to four times, three or four times, or four times as illustrated as an example in
A gas stream produced as a result of the gas-liquid separation according to an embodiment of the present disclosure may include off-gas containing light hydrocarbons, hydrogen sulfide, ammonia, hydrogen chloride, or the like, and unreacted hydrogen gas. According to a method known in the art, the off-gas and the unreacted hydrogen gas are separated, the separated unreacted hydrogen gas is recirculated in the process, and the off-gas is treated through an operation described below and may be used as a feedstock or discharged into the atmosphere.
Through the water washing according to an embodiment of the present disclosure, a salt included in the gas stream may be dissolved and removed, or salt formation may be suppressed by dissolving gas that may form a salt. The water washing may be performed by a method known in the art, but is not limited thereto.
The water washing according to an embodiment of the present disclosure may be performed two to four times, and specifically, two or three times. When the above range is satisfied, the salt removal and salt formation suppression effect may be sufficiently exhibited, such that high-quality refined oil may be obtained, and the process stability may be secured.
A method for producing refined hydrocarbons from waste plastics according to an embodiment of the present disclosure may further include, after the subjecting of the stream including the refined oil from which impurities are removed to the gas-liquid separation and then the washing of the gas-liquid separated stream with water: combusting the separated off-gas; and processing uncombusted off-gas.
The off-gas according to an embodiment of the present disclosure may contain C1-C4 light hydrocarbons, hydrogen sulfide (H2S), ammonia (NH3), and the like. Therefore, in order to use the off-gas as fuel, it is required to combust the off-gas to remove hydrogen sulfide (H2S), ammonia (NH3), and the like. Exhaust gas containing sulfur dioxide (SO2), nitrogen dioxide (NO2), and the like, produced by combustion of the off-gas may be discharged into the atmosphere after performing caustic scrubbing to meet emission standards.
In addition, after the combusting of the separated off-gas, uncombusted off-gas may be discharged as wastewater by being subjected to sour water stripping, adsorption, biological treatment, oxidation, amine scrubbing, or caustic scrubbing.
Next, the dewaxing operation may dewax the refined oil from which impurities are removed.
Through the dewaxing operation, the issues that occur because the refined oil contains a large amount of C22 to C45 long-chain normal paraffin and has an excessively high pour point may be prevented or reduced.
Through the dewaxing according to an embodiment of the present disclosure, wax components such as long-chain normal paraffin in the refined oil may be converted into lightened paraffin components, and the dewaxing operation may be performed in the presence of a dewaxing catalyst.
The dewaxing catalyst according to an embodiment of the present disclosure may contain a cracking component, a hydrotreating component, and a binder.
The cracking component according to an embodiment of the present disclosure may contain an amorphous silica/alumina phase and/or a zeolite such as Y-type or ultrastable Y (USY) zeolite, but is not limited thereto.
The binder according to an embodiment of the present disclosure may be silica or alumina, but is not limited thereto.
The hydrotreating component according to an embodiment of the present disclosure may be a Group VI, Group VII, or Group VIII metal or an oxide or sulfide thereof. In an embodiment, for example, the hydrotreating component may include one or more of molybdenum, tungsten, cobalt, and nickel, or a sulfide or oxide thereof, but is not limited thereto.
The amount of the hydrotreating component according to an exemplary embodiment of the present disclosure may be 1 wt % to 60 wt %, specifically, 5 wt % to 50 wt %, and more specifically, 10 wt % to 40 wt %, with respect to the total weight of the dewaxing catalyst, but is not limited thereto.
The dewaxing according to an embodiment of the present disclosure may be performed at a temperature of 100° C. to 400° C. Specifically, the dewaxing may be performed at a temperature of 300° C. to 400° C. In addition, the dewaxing according to an embodiment of the present disclosure may be performed at a pressure of 10 bar to 200 bar. Specifically, the dewaxing may be performed at a pressure of 100 bar to 200 bar. When the temperature and pressure satisfy the above ranges, the dewaxing efficiency may be improved.
In the dewaxing operation according to an embodiment of the present disclosure, a refined fraction separated by distilling the refined oil from which impurities are removed may be dewaxed. The refined fraction according to an embodiment of the present disclosure may be at least one selected from the group consisting of naphtha, kerosene, light gas oil, heavy gas oil, vacuum gas oil (VGO), and residue, and specifically, light gas oil or VGO, but is not limited thereto.
In the dewaxing operation according to an embodiment of the present disclosure, mixed oil obtained by mixing the refined oil from which impurities are removed and petroleum hydrocarbons may be dewaxed. In addition, mixed oil obtained by mixing the refined fraction and petroleum hydrocarbons may also be dewaxed.
The petroleum hydrocarbon refers to a mixture of naturally occurring hydrocarbons or oil separated from the mixture, and specifically, may be one or a mixture of two or more selected from the group consisting of kerosene, light gas oil, heavy gas oil, and vacuum gas oil (VGO) derived from crude oil, but is not limited thereto.
In the related art, when dewaxing was performed using only petroleum hydrocarbons as a feedstock, the catalyst was adversely affected by impurities such as sulfur (S) and nitrogen (N), and the dewaxing process did not last for a long time. However, the refined oil from which impurities are removed is included, such that this issue may be reduced or prevented. In addition, the refined oil has a low content of chlorine due to the dehydration and hydrotreating operations described above, and thus does not cause process issues such as reactor corrosion.
The mixed oil according to an embodiment of the present disclosure may include the refined oil from which impurities are removed in an amount of 5 wt % or more, 10 wt % or more, 20 wt % or more, 40 wt % or more, or 50 wt % or more, with respect to the total weight of the mixed oil, and an upper limit of the content of the refined oil from which impurities are removed may be 95 wt % or less, but is not limited thereto. The present disclosure is not limited to the above range. However, in general, the lower the content of impurities in the refined oil, the higher the proportion of refined oil that may be included in the mixed oil.
In addition, the present disclosure provides a system for producing refined hydrocarbons from waste plastics, the system including: a pyrolysis reactor for producing pyrolysis gas from waste plastics; a hot filter into which the pyrolysis gas is introduced and in which waste plastic pyrolysis oil is produced; a dehydrator performing dehydration by applying a voltage to a first mixed solution obtained by mixing the waste plastic pyrolysis oil, washing water, and a demulsifier; a hydrotreating reactor into which the first mixed solution dehydrated in the dehydrator and hydrogen gas are introduced and in which refined oil from which impurities are removed is produced by hydrotreating the first mixed solution in the presence of a hydrotreating catalyst; and dewaxing reactor dewaxing the refined oil from which impurities are removed.
The contents described for the methods for producing refined hydrocarbons from waste plastics may be equally applied to the description of a system for producing refined hydrocarbons from waste plastics to the extent of overlap.
The dehydrator according to an embodiment of the present disclosure may be provided with a vertical electrode. The number of vertical electrodes provided in the dehydrator according to an embodiment of the present disclosure may be at least two, four or more, or six or more, and twenty or less, but is not limited thereto.
The dehydrator according to an embodiment of the present disclosure may include a coalescer therein. The coalescer is a device that collects fine droplets to form large droplets, and any device commonly used in the industry may be used. The coalescer is not particularly limited.
The first mixed solution dehydrated in the dehydrator may be introduced into the coalescer according to an embodiment of the present disclosure, and an additionally dehydrated first mixed solution may be produced. When a dehydrator including the coalescer is used, the additionally dehydrated first mixed solution is also introduced into the hydrotreating reactor 40 together with the hydrogen gas.
The system for producing refined hydrocarbons from waste plastics according to an embodiment of the present disclosure may further include a separator 42-1 for subjecting the refined oil from which impurities are removed to gas-liquid separation, the refined oil being produced in the hydrotreating reactor.
The number of separators according to an embodiment of the present disclosure may be two to four, three or four, or four as illustrated in
A system for producing refined hydrocarbons from waste plastics according to an embodiment of the present disclosure may further include a recycle gas compressor recovering unreacted hydrogen gas from the separated gas stream from the separator and introducing the recovered unreacted hydrogen gas as recycle gas 36 into the hydrotreating reactor 40.
Hereinafter, a method and system for producing refined hydrocarbons from waste plastics according to embodiments of the present disclosure will be described in more detail with reference to Examples. However, the following Examples are only reference examples for describing the embodiments in detail, and the embodiments are not limited thereto and may be implemented in various forms. Unless otherwise defined, all technical terms and scientific terms used herein have the same meaning as commonly understood by those skilled in the art to which the present disclosure pertains. In addition, the terms used in the present disclosure are only to effectively describe specific examples, but are not intended to limit the embodiments of the present disclosure.
Example 1Domestic waste plastic including 73.4 wt % of PE, 10.4 wt % of PP, 9.8 wt % of PVC, 2.3 wt % of PET, 2.1 wt % of nylon, and 2.0 wt % of PU was used as a feedstock.
600 g of the domestic waste plastic feed was introduced into a batch pyrolysis reactor, and pyrolysis was performed at 500° C. The produced pyrolysis gas was introduced into a hot filter at 500° C. filled with 20 g of CaO having a particle size (D50) of 400 to 900 μm, collected in a condenser, and recovered in a recovery unit as waste plastic pyrolysis oil.
The waste plastic pyrolysis oil, washing water, and polyethylene glycol having a weight average molecular weight of 500 were introduced into a dehydrator under conditions of 150° C. and 10 bar at a volume ratio of 1:0.25:0.0001, and stirring was performed, thereby preparing a first mixed solution. The first mixed solution was separated into oil and water by applying an alternating current voltage of 15 kV through a vertical electrode, and then dehydration was performed by removing the water layer.
At this time, in the waste plastic pyrolysis oil, the content of moisture was about 5,000 ppm or more, and impurities at high concentrations of 500 ppm or more of nitrogen (N), 200 ppm or more of chlorine (Cl), and 20 vol % or more of olefins were contained.
A second mixed solution was prepared by mixing dimethyl disulfide in an amount of 0.04 parts by weight with respect to 100 parts by weight of the first mixed solution dehydrated in the dehydrator, and then the second mixed solution was hydrotreated under conditions of 300° C. and 70 bar, thereby producing refined oil from which impurities were removed.
Mixed oil obtained by mixing VGO separated by distilling the refined oil from which impurities were removed and VGO having a boiling point of 350° C. or higher derived from crude oil at a weight ratio of 1:1 was dewaxed under conditions of 350° C. and 160 bar in the presence of a silica/alumina-supported cobalt-molybdenum catalyst, thereby obtaining refined hydrocarbons.
Examples 2 and 3Refined hydrocarbons were obtained under the same conditions as those in Example 1, except that the waste plastic pyrolysis oil, washing water, and polyethylene glycol were introduced into the dehydrator at the volume ratio shown in Table 1.
Example 4Refined hydrocarbons were obtained under the same conditions as those in Example 1, except that a direct current voltage was applied through a horizontal electrode.
Example 5Refined hydrocarbons were obtained under the same conditions as those in Example 1, except that the dehydration of the first mixed solution was performed under a temperature condition of 120° C.
Example 6Refined hydrocarbons were obtained under the same conditions as those in Example 1, except that the waste plastic pyrolysis oil and polyethylene glycol were introduced at a volume ratio of 1:0.00001 and the hydrotreating was performed under a condition of a pressure of 180 bar in Example 5.
Example 7Refined hydrocarbons were obtained under the same conditions as those in Example 1, except that after the first mixed solution was dehydrated, the first mixed solution was additionally dehydrated through a coalescer.
Comparative Example 1Refined hydrocarbons were obtained under the same conditions as those in Example 1, except that washing water was not added as in Example 1.
Comparative Example 2Refined hydrocarbons were obtained under the same conditions as those in Example 1, except that polyethylene glycol was not introduced as in Example 1.
Comparative Example 3Refined hydrocarbons were obtained under the same conditions as those in Example 1, except that a voltage was not applied in Example 1.
Comparative Example 4Refined hydrocarbons were obtained under the same conditions as those in Example 1, except that dimethyl disulfide was not mixed with the dehydrated first mixed solution as in Example 1.
Evaluation Examples Measurement MethodsAfter the dehydration operation was completed, the contents of moisture and chlorine in the obtained mixed solution and the content of chlorine in the refined oil from which impurities were removed were measured through ICP and XRF analysis methods, and the measured results were shown.
A catalytic activity duration was measured and expressed in hours based on the time point when the content of nitrogen in the refined oil exceeded 10 ppm by performing Total Nitrogen & Sulfur (TNS element) analysis on the refined oil.
In addition, the process of each of Examples and Comparative Examples was operated for three months, and a particle adhesion rate was measured according to the following Equation 1.
The measurement results are shown in Table 1.
As shown in Table 1, in Comparative Examples 1 to 3, the introduction of washing water, introduction of demulsifier, and application of voltage were set differently from Examples, and as a result, the effect of removing moisture and Cl was poor. As waste plastic pyrolysis oil containing a large amount of impurities was hydrotreated, the content of Cl in the refined oil was high, and the hydrotreating catalyst was deactivated relatively quickly. In Comparative Example 4, it was confirmed that although moisture and some impurities in the waste plastic pyrolysis oil were sufficiently removed in the dehydration operation, the hydrotreating catalyst was deactivated within a short time due to an insufficient content of sulfur, and thus, when the refining process was maintained for a long period time, the content of Cl in the refined oil was high as in other Comparative Examples. In addition, it may be expected that the content of refined oil in the dewaxed mixed oil is inevitably limited because Cl contained in a large amount in the refined oil has a potential to cause corrosion of the dewaxing reactor. However, in Examples 1 to 7 according to an embodiment of the method for producing refined hydrocarbons from waste plastics of the present disclosure, a significant amount of moisture contained in the waste plastic pyrolysis oil was removed through the dehydration operation, and a sulfur source was added, and as a result, the activity of the hydrotreating catalyst was maintained for a remarkably long time. In addition, since some water-soluble impurities were preemptively removed in the dehydration operation and hydrotreating was performed, a content of impurities such as Cl in the refined oil was low. Therefore, it was confirmed that a impurities in the large amount of refined oil need not be additionally removed before dewaxing.
Meanwhile, when an alternating current voltage was applied using a vertical electrode, it was confirmed that the adhesion rate of impurity particles derived from char in the pyrolysis oil to the electrode surface was significantly low even when the process was continued for longer than three months. Through this, it was appreciated that when an alternating current voltage was applied or a vertical electrode was used, there was no need to stop the process for washing the inside of the reactor, and as a result, process efficiency was significantly improved.
In addition, in the case of Example 6, although the dehydration result was poor compared to other Examples, the content of Cl impurities in the refined oil was significantly low as the hydrotreating was performed under a high pressure condition. However, since ammonia and hydrogen chloride were produced in excess due to the high pressure, it was confirmed that a relatively large amount of ammonium chloride salt was formed even at the temperature at which the hydrotreating was performed.
In Example 7, as the additional dehydration was performed using a coalescer, the contents of moisture and chlorine after the dehydration were lower than those in other Examples. Therefore, it may be expected that the activation time of the catalyst, the process stability, and the quality of refined oil are relatively superior to those in other Examples.
In addition, it was confirmed that refined hydrocarbons having a high octane number were produced from waste plastics through the dewaxing operation.
As set forth above, the methods and system for producing refined hydrocarbons from waste plastics according to the embodiments of the present disclosure may prevent or minimize formation of an ammonium chloride salt (NH4Cl) and may prevent the adhesion phenomenon of impurity particles in a refining process of waste plastic pyrolysis oil containing impurities including chlorine and nitrogen.
The methods and system for producing refined hydrocarbons from waste plastics according to the embodiments of the present disclosure may prevent deactivation of the catalyst due to moisture, such that the refining efficiency may be excellent, and the process may be operated for a long period of time.
The methods and system for producing refined hydrocarbons from waste plastics according to the embodiments of the present disclosure may provide refined hydrocarbons from waste plastics that may be blended with existing petroleum products in large quantities due to a significantly low content of impurities such as chlorine, nitrogen, oxygen, and metals and a significantly low content of olefins.
The methods and system for producing refined hydrocarbons from waste plastics according to the embodiments of the present disclosure may be used in eco-friendly oil refining and production of petrochemical products using waste plastics.
Although the embodiments of the present disclosure have been described, the present disclosure is not limited to these embodiments, and those skilled in the art will appreciate that various modifications and alterations may be made without departing from the concept and scope of the claims described below.
While the present disclosure has been shown and described with reference to certain embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the scope of the present disclosure and any equivalents. Therefore, the scope of the present disclosure should not be limited to the above-described embodiments but should include the equivalents thereof.
In the above-described embodiments, all operations may be selectively performed, or part of the operations may be omitted. In each embodiment, the operations are not necessarily performed in accordance with the described order and may be rearranged. The embodiments disclosed in this specification and drawings are only examples to facilitate an understanding of the present disclosure, and the present disclosure is not limited thereto. That is, it should be apparent to those skilled in the art that various modifications can be made on the basis of the technological scope of the present disclosure.
The embodiments of the present disclosure have been described in the drawings and specification. Although specific terminologies are used here, those are only to describe the embodiments of the present disclosure. Therefore, the present disclosure is not restricted to the above-described embodiments and many variations are possible within the scope of the present disclosure. It should be apparent to those skilled in the art that various modifications can be made on the basis of the technological scope of the present disclosure in addition to the embodiments disclosed herein. Furthermore, the embodiments may be combined to form additional embodiments.
LIST OF NUMERALS IN THE FIGURES
-
- 2 waste plastics
- 10 pyrolysis reactor
- 12 pyrolysis gas
- 20 hot filter
- 22 condenser
- 24 waste plastic pyrolysis oil
- 26 water
- 28 demulsifier
- 30 dehydrator
- 32 coalescer
- 34 dehydrated first mixed solution
- 36 recycle gas
- 37 H2
- 38 Sulfur source
- 40 hydrotreating reactor
- 41 hydrotreated second mixed solution
- 42-1 to 42-4 gas liquid separators
- 44 off-gas
- 46 refined oil
- 48 fractionator
- 50 dewaxing reactor
- 52 refined hydrocarbons
Claims
1. A method for producing refined hydrocarbons from waste plastics, the method comprising:
- a pyrolysis operation introducing waste plastics into a pyrolysis reactor and pyrolyzing the waste plastics to produce pyrolysis gas;
- an oil production operation producing waste plastic pyrolysis oil by introducing the pyrolysis gas into a hot filter filled with a neutralizing agent;
- a dehydration operation applying a voltage to a first mixed solution obtained by mixing the waste plastic pyrolysis oil, washing water, and a demulsifier to dehydrate the first mixed solution;
- a hydrotreating operation hydrotreating a second mixed solution obtained by mixing the first mixed solution dehydrated in the dehydration operation and a sulfur source to produce refined oil from which impurities are removed; and
- a dewaxing operation dewaxing the refined oil from which impurities are removed.
2. The method of claim 1, wherein in the dehydration operation, the waste plastic pyrolysis oil is mixed in a greater volume than the washing water.
3. The method of claim 2, wherein in the dehydration operation, the waste plastic pyrolysis oil and the washing water are mixed in the first mixed solution at a volume ratio of 1:0.001 to 1:0.5.
4. The method of claim 1, wherein in the dehydration operation, the waste plastic pyrolysis oil and the demulsifier are mixed in the first mixed solution at a volume ratio of 1:0.000001 to 1:0.001.
5. The method of claim 1, wherein the voltage is applied as an alternating current or a combination of an alternating current and a direct current.
6. The method of claim 1, wherein the voltage is applied through at least one pair of vertical electrodes.
7. The method of claim 1, further comprising, after the application of the voltage in the dehydration operation, removing a rag layer from the first mixed solution.
8. The method of claim 1, wherein the dehydration operation is performed under a temperature condition of 20° C. to 300° C.
9. The method of claim 1, wherein a ratio of a content of moisture in the waste plastic pyrolysis oil to a content of moisture in the first mixed solution dehydrated in the dehydration operation is 1:0.0001 to 1:0.9.
10. The method of claim 1, wherein the first mixed solution in the dehydration operation is additionally dehydrated by condensation of moisture.
11. The method of claim 1, wherein a weight ratio of nitrogen to chlorine in the second mixed solution is 1:1 to 1:10.
12. The method of claim 1, wherein the sulfur source includes sulfur-containing oil.
13. The method of claim 12, wherein the sulfur-containing oil is included in an amount of less than 0.5 parts by weight with respect to 100 parts by weight of the first mixed solution dehydrated in the dehydration operation.
14. The method of claim 1, wherein the sulfur source includes one or two or more sulfur-containing organic compounds selected from a disulfide-based compound, a sulfide-based compound, a sulfonate-based compound, and a sulfate-based compound.
15. The method of claim 1, wherein the hydrotreating is performed in the presence of a molybdenum-based hydrotreating catalyst.
16. The method of claim 15, wherein the molybdenum-based hydrotreating catalyst is a catalyst in which a molybdenum-based metal, or a metal including one or two or more selected from nickel, cobalt, and tungsten, and a molybdenum-based metal are supported on a support.
17. The method of claim 1, wherein the hydrotreating operation is performed under a pressure condition of 50 bar to 150 bar.
18. The method of claim 1, further comprising, after the hydrotreating operation, subjecting a stream including the refined oil from which impurities are removed to gas-liquid separation and then washing the gas-liquid separated stream with water.
19. The method of claim 1, wherein the dewaxing operation dewaxes a refined fraction separated by distilling the refined oil from which impurities are removed.
20. The method of claim 1, wherein the dewaxing operation dewaxes mixed oil obtained by mixing the refined oil from which impurities are removed and petroleum hydrocarbons.
Type: Application
Filed: Feb 21, 2024
Publication Date: Oct 24, 2024
Inventors: Yong Woon KIM (Daejeon), Seo Yeong KANG (Daejeon), Soo Kil KANG (Daejeon), Min Gyoo PARK (Daejeon), Young Moo PARK (Daejeon), Min Woo SHIN (Daejeon), Jae Hwan LEE (Daejeon), Jin Seong JANG (Daejeon), Sang Hwan JO (Daejeon)
Application Number: 18/582,669