Abstract: The present invention is directed to a non-aqueous composition curable by UV radiation broadly comprising a mixture of two UV curable urethane acrylates. The invention is also directed to a coating process using such composition. One of the urethane acrylates is the reaction product of an isocyanate and a specific OH functional lactone ester (meth)acrylate. The other urethane acrylate is the reaction product of an isocyanate and a specific hydroxy functional (meth)acrylate.

Abstract: Chemically cross-linked polymeric particles are formed using mechanical rather than chemical processes, facilitating production of small-diameter particles in a manner largely independent of the viscosity or density of the polymer. For example, an uncross-linked resin may be provided in particulate form, agglomerated, and compressed into a mass of a desired shape with a desired diameter, and subsequently cross-linked.

Abstract: UV curable, liquid, oligomeric compositions are prepared from the reaction product of a Michael addition oligomer and an isocyanate capped polybutadiene. The UV curable, liquid, oligomeric compositions can be cured in the presence of fragrances to form articles that are characterized by a controlled release of the fragrance over time.

Abstract: The present invention relates to a free-radically radiation-curable, solvent-free and printable precursor of a pressure-sensitive adhesive, the precursor comprising: (i) 30-75 wt. % of one or more mono(meth)acrylate functional oligomer compounds at least one of said oligomer compounds comprising at least one urethane bond, (ii) 0-15 wt % of one or more poly(meth)acrylate functional oligomer compounds, (iii) 5-45 wt. % of one or more monomer compounds comprising one ethylenically unsaturated group, (iv) 0-5 wt. % of one or more monomer compounds comprising two or more ethylenically unsaturated groups, and (v) an effective amount of one or more free radical photoinitiators, wherein the percentages which are percentages by weight with respect to the mass of the precursor, are selected so that the precursor has a dynamic viscosity at 20° C. and at a shear rate of 100 s?1 of between 300 to 15,000 mPa·s.

Abstract: The invention provides compounds which can generate amine by irradiation with light and are excellent both in photodecomposability and in reactivity and compatibility with amine-curable compounds, and photo-setting compositions containing the compounds. The compounds are carbamoyloxyimino compounds represented by the structural formula (I); and the compositions each comprise one or more of the carbamoyloxyimino compounds and an amine-curable compound. In the formula (I), R1 is an n-valent organic group; R2 and R3 are each hydrogen or an aromatic or aliphatic group; and n is an integer of 1 or above.

Abstract: Disclosed are environmentally friendly, substantially all solids coating compositions which are curable using ultraviolet and visible radiation. In addition, the disclosed coating compositions are suitable for coating flexible objects and/or objects having angular features, such as, but not limited to, flexible metal objects with angular features. In addition, methods are disclosed for coating surfaces, or at least a portion of the surfaces, and curing of the coated surface to obtain partially or fully cured coated surfaces. Furthermore, articles of manufacture incorporating fully cured coated surfaces are disclosed, including, for example leaf springs. Also disclosed are methods, processes, production lines, articles of manufacture, and factories which incorporate these environmentally friendly, substantially all solids coating compositions curable using ultraviolet and visible radiation.

Abstract: The present invention relates to a fluororubber molded article obtained by subjecting a fluororubber composition to crosslinking by irradiation of ionizing radiation, wherein the fluororubber composition comprises: (i) a raw rubber having a metal element content of 1.5% or less and comprising a tetrafluoroethylene-propylene copolymer; and (ii) a prepolymer of triallyl isocyanurate. Also disclosed is a method for producing the fluororubber molded article.

Abstract: A method for the production of a cross-linked support matrix that in form of a bed will permit liquid flow velocities above 5 cm/h, preferably above 50 cm/h, to pass through the bed. The method is characterized in that it comprises the steps: (a) providing a starting support matrix that has pendent unsaturated groups, and (b) subjecting said starting support matrix to electron beam or gamma-ray irradiation. The use of a cross-linked support matrix produced by a method comprising the steps of: (a) providing a starting support matrix that has pendent unsaturated groups, and (b) subjecting said starting support matrix to electron beam or gamma-ray irradiation as a support matrix in liquid chromatography, cell culturing, step-wise solid phase synthesis of organic compounds, running catalytic reactions by the use of a solid phase bound catalyst.

Abstract: An object of the present invention is to provide an excellent process for production of a surface-treated particulate water-absorbent resin wherein the process adopts a surface-treatment process that can enhance the properties (which the water-absorbent resin is desired to have) to extremely high levels, and also can solve the prior problems in such as safety, and further can sufficiently carry out the treatment even at a reaction temperature near room temperature. As a means of achieving this object, the process according to the present invention for production of a surface-treated particulate water-absorbent resin is characterized by comprising the steps of: adding a treating liquid to a particulate water-absorbent resin as a base polymer, wherein the treating liquid contains a radically polymerizable compound; and then irradiating the particulate water-absorbent resin with active energy rays while fluidizing the particulate water-absorbent resin, thereby surface-treating it.

Abstract: Disclosed are environmentally friendly, substantially all solids coating compositions which are curable using ultraviolet and visible radiation. In addition, the disclosed coating compositions are suitable for coating thermally sensitive objects and/or rusted surfaces. In addition, methods are disclosed for coating surfaces, or at least a portion of the surfaces, and curing of the coated surface to obtain partially or fully cured coated surfaces are also disclosed. Furthermore, articles of manufacture incorporating fully cured coated surfaces are disclosed, including, for example gas tanks such as, barbeque propane tanks. Also disclosed are methods, processes, production lines, articles of manufacture, and factories which incorporate these environmentally friendly, substantially all solids coating compositions curable using ultraviolet and visible radiation.

Abstract: The invention is a pressure sensitive adhesive (PSA) composition, which is the ultraviolet radiation (UV) cured reaction product of a polyester-polyether-based urethane acrylate, one or more acrylate monomers, and a UV photosensitizer. The polyester-polyether-based urethane acrylate is the reaction product of between about 50 and 90 wt-% of a polyester diol having a molecular weight ranging from about 500 to 3200; between about 10 and 50 wt-% of a polyether polyol having a molecular weight ranging from about 1000 to 6000; between about 1 and 5 wt-% of a hydroxy-functional acrylate; and a polyisocyanate.

Abstract: A method of increasing the gas transmission rate of a packaging film comprises providing a packaging film that comprises at least about 0.001 weight % of single-walled carbon nanotube material based on the weight of the film. The packaging film is exposed to an amount of radiation energy effective to increase the oxygen transmission rate of the packaging film by at least about 100 cc (STP)/m2. day (1 atm, 0% RH, 23° C.).

Abstract: Disclosed are environmentally friendly, substantially all solids coating compositions which are curable using ultra violet and visible radiation. In addition, methods for coating surfaces, or at least a portion of the surfaces, and curing of the coated surface to obtain partially or fully cured coated surfaces are also disclosed. Furthermore, articles of manufacture incorporating fully cured coated surfaces are disclosed, in particular motor vehicles and motor vehicle parts or accessories.

Abstract: Laminates for electronic components are produced by applying a polyimide resin precursor solution containing a palladium compound on a polyimide substrate, drying the resulting coating to form a polyimide resin precursor layer, irradiating this layer with ultraviolet rays in the presence of a hydrogen donor to form nuclei for primer plating, forming a metal primer layer by electroless plating, and converting the polyimide resin precursor layer into a polyimide resin layer through imidation by heating either after or before the formation of a surface plating layer. The invention provides laminates for electronic components which are extremely improved in adhesion to metal layers without impairing the characteristics inherent in the substrate and are excellent in insulating properties, and polyimide resin precursor resin solution to be used in the production of the laminates.

Abstract: The present invention relates to a sinter powder composed of polyamide which also comprises PMMI, PMMA, or copolymers with PMMI, in particular PMMI-PMMA copolymers, to the use of this sinter powder for laser-sintering, and also to moldings produced from this sinter powder. The moldings made from the powder of the invention have marked advantages over conventional products in their appearance and in their surface quality, especially as far as roughness and dimensional stability during selective laser sintering (SLS) are concerned. In addition, moldings produced from the sinter powder of the invention also have better mechanical properties than moldings based on conventional nylon-12 powders, in particular in terms of modulus of elasticity and tensile strength. These moldings also have a density close to that of injection moldings.

Abstract: Mixtures curable thermally and with actinic radiation and containing carbamate and/or allophanate groups, comprising (A) at least one of (A1) low molecular mass compounds, oligomers and polymers containing allophanate groups, carbamate groups, and carbamate and allophanate groups, and (A2) low molecular mass compounds, oligomers and polymers containing allophanate groups, carbamate groups, and carbamate and allophanate groups, and additionally allophanate- and/or carbamate-reactive functional groups, ?which are substantially or entirely free from reactive functional groups which contain at least one bond which can be activated with actinic radiation, and (C) at least one constituent containing on average per molecule at least one reactive functional group having at least one bond which can be activated with actinic radiation; with the proviso that if only (A1) is used, the mixtures further comprise (B) at least one of low molecular mass compounds, oligomers and polymers containing allophanate- and/or c

Abstract: Crosslinkable resin compositions that are cured easily by irradiation with active energy beams and particularly cured quickly with ultraviolet ray are provided, which comprises a polymer containing a maleimido group and an ethylenically unsaturated group. The composition may be an aqueous composition. They provide cured films which are excellent in durability, free from coloring and odors, and also excellent in abrasion resistance, adhesion to substrates, surface smoothness, and chemical resistance.

Abstract: The invention relates to a curable resin composition, cured products thereof, and laminated materials. The curable composition comprises: (A-1) acicular oxide particles, the oxide being an oxide of at least one element selected from the group consisting of silicon, aluminum, zirconium, titanium, zinc, germanium, indium, tin, antimony, and cerium, (B) a compound having two or more polymerizable unsaturated groups, (C) a photopolymerization initiator is provided. After cure, the composition has excellent scratch resistance. In addition, it may have excellent antistatic characteristics and transparency. In a preferred embodiment the composition also comprises (A-2) particles other than the acicular particles (A-1), being oxide of at least one element selected from the group consisting of silicon, aluminum, zirconium, titanium, zinc, germanium, indium, tin, antimony, and cerium.

Abstract: Chemically cross-linked polymeric particles are formed using mechanical rather than chemical processes, facilitating production of small-diameter particles in a manner largely independent of the viscosity or density of the polymer. For example, an uncross-linked resin may be provided in particulate form, agglomerated, and compressed into a mass of a desired shape with a desired diameter, and subsequently cross-linked.

Abstract: Ultraviolet (UV)-curable polyurethane compositions are provided which are made by reacting an isocyanate with an ultraviolet (UV)-curable polyol that is made by co-polymerizing an alkylene oxide, an unsaturated carboxylic acid or anhydride and a hydroxy functional compound and which has an ultra-low level of unsaturation. The inventive ultraviolet (UV)-curable polyurethane compositions may find use in or as coatings, adhesives, sealants, elastomers and the like.

Abstract: A photosensitive resin composition which contains (A) polyamic acid, (B) (meth)acrylate having at least two photopolymerizable C?C unsaturated double bonds, (C) a photopolymerization initiator and (D) a flame retardant, with the (meth)acrylate (B) having at least two photopolymerizable C?C unsaturated double bonds being contained in an amount of 10 to 700 parts by weight based on 100 parts by weight of the polyamic acid (A).

Abstract: A polyamphoteric superabsorbent copolymer made up of polymerizerable acid monomer and of polymerizable base monomer and optionally a supplemental monomer. In particular, the invention includes a radiation curable coating composition that comprises from about 20 weight % to about 80 weight % of polymerizerable acid monomer and from about 20 weight % to about 80 weight of polymerizable base monomer; and from 0 weight % to about 50 weight % of supplemental monomer. On exposure to radiation the coating composition forms a polyamphoteric superabsorbent copolymer. The radiation curable coating composition may be used with suitable substrates.

Abstract: An object of the present invention is to provide a material which resolves the drawbacks associated with polyimide polymers, and yet retains the advantages offered by conventional polyimide polymers. An amino group containing phenol derivative of the present invention is represented by a general formula (1) show below, and the present invention also provides a polyimide precursor produced using such an amino group containing phenol derivative. (wherein, R1, R2 and R3, which may be the same or different, each represent an alkyl group of 1 to 9 carbon atoms, an alkoxy group of 1 to 10 carbon atoms, a COOR group (in which R represents an alkyl group of 1 to 6 carbon atoms) or a hydrogen atom; R4 and R5, which may be the same or different, each represent an alkyl group of 1 to 9 carbon atoms or a hydrogen atom; X represents —O—, —S—, —SO2—, —C(CH3)2—, —CH2—, —C(CH3)(C2H5)—, or —C(CF3)2—; and n represents an integer of 1 or greater).

Abstract: A photosensitive composition for forming a dielectric of the present invention comprising inorganic particles, an alkali developable resin and additives, wherein the additives comprise a compound having a quinonediazido group (C1), a compound containing at least two alkyletherified amino groups in the molecule (C2) and a thermal acid generator (C3), or wherein the inorganic particles comprise inorganic superfine particles (A-I) having a mean particle diameter of less than 0.05 ?m and inorganic fine particles (A-II) having a mean particle diameter of not less than 0.05 ?m. The composition can be calcined at low temperatures to form a dielectric layer with high dimensional precision, said layer having a high dielectric constant and a low dielectric loss. Also provided are a dielectric and an electronic part prepared from the composition.

Abstract: A process for the production of coatings with scratch-resistant durable surfaces that comprise as photoinitiator (B) in a photocurable formulation at least one surface-active photoinitiator, concentrated at the surface of the formulation, of formula (Ia) or (Ib), wherein Ra is a radical of formula (IIa), Rb is a radical of formula (IIb)), or Ra and Rb are naphthyl, anthracyl, phenanthryl or a heterocyclic radical each of which is unsubstituted or substituted; R1, R2, R3, R4, R5, R6, R7, R8, R9 and R10 are, for example, each independently of the others hydrogen; A-Y; C1–C12alkyl, halogen or phenyl; R11 and R12 are, for example, C1–C12 alkyl; X is —OR20 or —N(R21)(R22); R20 is, for example, hydrogen or C1–C4alkyl; R21 and R22 are, for example, hydrogen or C1–C12 alkyl; X1 is, for example, —O—; Y is, for example, a single bond or —O—; Y1 is, for example, a single bond; and A is, for example, C6–C30alkyl.

Abstract: Provided are radiation-cured, laminated materials, radiation-curable adhesive compositions suitable for use in forming the laminated materials, and methods of making laminated materials.

Abstract: In accordance with the present invention, there are provided novel thermosetting resin compositions which do not require solvent to provide a system having suitable viscosity for convenient handling. Invention compositions have the benefit of undergoing rapid cure. The resulting thermosets are stable to elevated temperatures, are highly flexible, have low moisture uptake and are consequently useful in a variety of applications, e.g., in adhesive applications since they display good adhesion to both the substrate and the device attached thereto.

Abstract: The present invention provides radiation curable resin compositions that contain no or essentially no volatile organic components (VOCs), and to methods of using these compositions. The radiation curable resin compositions find particular use as coating compositions. In particular, the radiation curable resin compositions of this invention comprise a vinyl dioxolane end-capped oligomer blended with a photoinitiator.

Abstract: A fast-curing, low viscosity composition for coating an optical waveguide, more specifically, an optical fiber, and optical fibers coated therewith are disclosed. The coating composition is a radiation curable composition containing: a radiation curable oligomer, a free radical photoinitiator, and a mixture of reactive diluents including a low molecular weight (meth)acrylate having tri-, tetra-, penta- or higher functionality.

Abstract: The present invention provides a novel photosensitive compound having an azido group suitable for exposure to light of a short wavelength; a photosensitive resin containing the photosensitive compound; and a photosensitive composition containing the photosensitive compound or photosensitive resin. The photosensitive compound containing a photosensitive unit represented by formula (1): wherein R is selected from among the following groups, R: X is selected from among the following groups, X: and each of Y and Z represents a hydrogen atom, an alkyl group, an acetal-group-containing alkyl group, an aryl group, an aralkyl group, or a substituent containing a base-forming nitrogen atom, wherein at least one of R and X contains an azido group.

Abstract: Active water compatible actinic radiation curable printing ink or coating compositions comprised of maleimide derivatives, water compatible resins and water, which are capable of curing at a practical intensity and energy level and a method for curing same.

Abstract: There is disclosed a method of easily producing a long-lived ion sensitive film having excellent durability and used in an ion sensor. The method starts with preparing a monomer mixture consisting chiefly of monomer units including a functional group and a second group of bonded atoms. The functional group has a function of identifying a certain chemical substance. The second group can become an active species that induces a polymerization or bridging reaction by being irradiated with an electron beam or radiation. Then, the monomer mixture is irradiated with the electron beam or radiation in a low energy range. Thus, the monomer mixture is polymerized.

Abstract: An object of the present invention is to provide a heavy metal ion scavenger having more excellent scavenging performance than previously. In order to attain this object, organic polymer materials of the present invention are characterized in that they have a polymer side chain derived from a haloalkyl-substituted styrene on the backbone of an organic polymer base and a functional group capable of forming a complex with a heavy metal ion has been introduced onto said polymer side chain. These organic polymer materials have excellent heavy metal ion scavenging performance so that they can be suitably used as heavy metal ion scavengers.

Abstract: The invention provides a reaction product derived from an epoxy-functional acrylic monomer and an alkylaminoalkylene polyalkoxysilane or from a reaction product derived from acrylic acid and an epoxidized polyalkoxysilane.

Abstract: This invention relates to a radiation-resistant acrylic adhesive composition with less reduction in the adhesion thereof upon irradiation with radiations, which composition comprises an acrylic polymer and a radiation-resistant agent, and a radiation-resistant adhesive product comprising the composition.

Abstract: Provided are an active energy ray-curable urethane (meth)acrylate and an active energy ray-curable composition for paints and coating agents having abrasion resistance and lubricity, and uses thereof. The curable urethane (meth)acrylate has a long chain alkyl group having 13 to 25 carbon atoms and an active energy ray-curable functional group and is modified with polycaprolactone. The urethane (meth)acrylate is obtainable by reacting an organic isocyanate having three or more isocyanate groups in one molecule, a long chain alkyl alcohol, and a polycaprolactone-modified hydroxyethyl (meth)acrylate. On the other hand, the active energy ray-curable composition contains the urethane (meth)acrylate.

Abstract: In accordance with the present invention, there are provided novel thermosetting resin compositions which do not require solvent to provide a system having suitable viscosity for convenient handling. Invention compositions have the benefit of undergoing rapid cure. The resulting thermosets are stable to elevated temperatures, are highly flexible, have low moisture uptake and are consequently useful in a variety of applications, e.g., in adhesive applications since they display good adhesion to both the substrate and the device attached thereto.

Abstract: The present invention provides a resin composition that includes (A) a polymer compound that has, on a side chain of a main chain polymer, through a linkage group containing a hydrogen-bonding group and a ring structure, a terminal ethylenic unsaturated bond, and is soluble or swelling in water or an alkali aqueous solution, and (B) a compound that generates radicals when exposed to light or heat. The invention further provides a thermo/photosensitive composition that includes (A′) a polymer compound that has a non-acidic hydrogen-bonding group on a side chain and is soluble or swelling in water or an alkali aqueous solution, and (B′) a compound that generates radicals when exposed to light or heat.

Abstract: The invention is directed to the use of multifunctional thiol compounds as adhesion promoters and/or primers to enhance the adhesion of photo or electron beam curable polymers, coatings, adhesives, or sealants to gold, other precious metals, and their alloys. Actinic radiation and electron beam (“EB”) radiation can be used to cure such compositions. The resulting cured compositions are optically clear, low Tg (≦30° C.), high refractive index (>1.50 at 1541 nm), thermally, oxidatively, and hydrolytically stable adhesives and/or coatings for glass and/or metal. The adhesive compositions containing such multifunction thiols can survive, without delamination or separation, testing conditions of 85° C. and 85% relative humidity (“RH”) for a time in excess of 500 hours.

Abstract: A dental adhesive composition for bonding dental restoratives to dentin and enamel provides a one-part self-etching, self-priming dental adhesive composition having hydrolysis stable polymerizable acidic adhesive monomers.

Abstract: A radiation-curable composition is comprised of the reaction product of an amine-terminated (poly)aminoamide and a mono-(meth)acrylate or a poly-(meth)acrylate. The radiation-curable composition is a liquid at room temperature and does not undergo substantial volume contraction upon curing and exhibit excellent adhesion to porous and non porous substrates alike.

Abstract: A composition for actinic radiation curable nail coatings and artificial nail tips comprising a BISGMA based urethane resin, an additional polymer, a photoinitiator, and having a viscosity of greater than approximately 80,000 cps. Composition may additionally comprise other additives known in the art and also methods of application of the composition alone and with related compositions.

Abstract: An intaglio printing ink comprising a first binder compound selected from the group of water-soluble or water-thinnable acrylate oligomers, and optionally, a second monomeric binder compound selected from the group comprising water-soluble or water-thinnable PEG diacrylate or polyethoxylated polyol triacrylate monomers to adjust the viscosity of the ink composition. To initiate polymerization of the binder compounds upon irradiation by electromagnetic radiation or electron beam radiation a photoinitiator is included. Further optional additives, such as pigments, fillers, photosensitizers, stabilizers emulsifiers and security pigments may be present. The ink shows excellent wipeability and allows precipitation from the wiping solution.

Abstract: A process for producing scratch-resistant coatings, encompassing the following steps: applying at least one UV-curable coating composition to at least one surface of an article to be coated, said coating composition comprising at least one polymer and/or oligomer P1 containing on average at least one ethylenically unsaturated double bond per molecule, and curing the coating composition by exposure to UV radiation, which comprises conducting the curing of the coating composition under an oxygen-containing protective gas which has an oxygen partial pressure in the range from 0.2 to 18 kPa.

Abstract: The present invention aims to provide an adhesive composition showing high adhesion and cohesion as well as good heat resistance. Adhesive compositions of the present invention include an imide (meth)acrylate, a monomer having a glass transition temperature of −50° C. or less when it is homopolymerized, and a photoinitiator, wherein the content of the imide (meth)acrylate is 1-20 parts by weight per 100 parts by weight of the monomer.

Abstract: The present invention provides a resin composition that includes (A) a polymer compound that has, on a side chain of a main chain polymer, through a linkage group containing a hydrogen-bonding group and a ring structure, a terminal ethylenic unsaturated bond, and is soluble or swelling in water or an alkali aqueous solution, and (B) a compound that generates radicals when exposed to light or heat. The invention further provides a thermo/photosensitive composition that includes (A′) a polymer compound that has a non-acidic hydrogen-bonding group on a side chain and is soluble or swelling in water or an alkali aqueous solution, and (B′) a compound that generates radicals when exposed to light or heat.

Abstract: New polymers, compositions comprising these polymers, and methods of using these compositions are provided. The polymers comprise styrene and maleic anhydride monomers with at least some of the maleic anhydride monomers having certain functional groups bonded thereto. Preferred functional groups include those derived from adhesion promoters (e.g., 2-aminophenol), photoinitiators (e.g., 4-aminoacetophenone), and solubilizers (e.g., 4-aminobenzoic acid). The polymers can be incorporated according to conventional processes into compositions which are then used to form a color filter to be used in a liquid crystal display. The final color filter has a high resolution, is highly resistant to solvents typically used in the color filter manufacturing process, is strongly adhered to the color filter substrate, has superior optical clarity, is highly soluble in a wide range of alkali developers, and has excellent heat and UV light stability.

Abstract: A fluorine-containing phenylmaleimide derivative having a specific structure. A polymer obtained by polymerizing monomers containing the derivative. A polymer containing a specific structural unit and having a weight-average molecular weight of 2,000 to 200,000. A chemically amplified resist composition containing the polymer and a photo acid generator, wherein the proportion of the polymer relative to the total of the polymer and the photo acid generator is 70 to 99.8% by mass. A method for pattern formation, which comprises coating the above composition on a to-be-processed substrate, exposing with a light of 180 nm or less wavelength, and conducting baking and development.

Abstract: New polymers, compositions comprising these polymers, and methods of using these compositions are provided. The polymers comprise styrene and maleic anhydride monomers with at least some of the maleic anhydride monomers having certain functional groups bonded thereto. Preferred functional groups include those derived from adhesion promoters (e.g., 2-aminophenol), photoinitiators (e.g., 4-aminoacetophenone), and solubilizers (e.g., 4-aminobenzoic acid). The polymers can be incorporated according to conventional processes into compositions which are then used to form a color filter to be used in a liquid crystal display. The final color filter has a high resolution, is highly resistant to solvents typically used in the color filter manufacturing process, is strongly adhered to the color filter substrate, has superior optical clarity, is highly soluble in a wide range of alkali developers, and has excellent heat and UV light stability.

Abstract: Membranes made from amphiphilic copolymers are disclosed. The amphiphilic copolymers can be ABA copolymers, where one of A and B is hydrophilic and the other is hydrophobic. The copolymers may be crosslinked to form more stable structures. Crosslinking can be accomplished using a variety of methods, including end to end polymerization of copolymers having terminal unsaturated groups. Molecules such as membrane proteins can be incorporated into the membrane to allow the transport there through of selected components.