Abstract: The subject of the invention is a method for the hot-dip coating, in a liquid bath based on zinc containing aluminum, of a running strip of iron-carbon-manganese austenitic steel, in which said strip is subjected to a heat treatment in a furnace in which an atmosphere that is reducing with respect to iron prevails, in order to obtain a strip covered with a thin manganese oxide layer, and then the strip covered with the thin manganese oxide layer is made to run through said bath, the aluminum content in the bath being adjusted to a value at least equal to the content needed for the aluminum to completely reduce the manganese oxide layer, so as to form, on the surface of the strip, a coating comprising an iron-manganese-zinc alloy layer and a zinc surface layer.

Abstract: The invention relates to a method for feeding lubricant during hot rolling, in which the surfaces of the rolling rolls are fed with a lubricating emulsion, characterized in that said lubricating emulsion, consisting of a lubricating oil having a viscosity between 10 cSt and 400 cSt at 40° C., mixed with water, is directed onto the surfaces of the rolling rolls via at least one lubricant feed nozzle, at a temperature above 0° C. but below 25° C.

Abstract: A device for control of bubbling of a metal bath in a ladle or in another similar metallurgical vessel including a bottom injector linked to a source of supply of pressurized stirring gas to be injected with aid of a pipe provided with a facility for adjusting flow rate, at least one vibration sensor mounted on the vessel itself or on a support frame, a signal processing unit processing a vibratory signal gathered by the sensor, and wherein the signal processing unit includes at least, and in successive order of processing of the vibratory signal, a high-pass analog filter, a digitizer, a digital filter calibrated on vibratory responses of the ladle, and a computer for computing a sliding temporal quadratic mean of RMS type.

Abstract: A high-strength hot-rolled steel sheet excellent in shape fixability having ferrite or bainite as the phase of the largest volume percentage, satisfying all of the following at least at ½ sheet thickness: a mean value of X-ray random intensity ratio in the orientation component group of {100}<011> to {223}<110> to X-ray random diffraction intensity ratio of at least 2.5; a mean value of X-ray random intensity ratio in the three crystal orientation components of {554}<225>, {111}<112>, and {111}<110> to X-ray random diffraction intensity ratio of 3.5 or less; an X-ray intensity ratio to X-ray random diffraction intensity ratio at {100}<011> of at least the X-ray random intensity to X-ray random diffraction intensity ratio at {211}<011>; and an X-ray random intensity ratio to X-ray random intensity ratio diffraction intensity ratio at {100}<011> of at least 2.

Abstract: The subject of the invention is the use of a treatment solution containing sulfate ions for treating the surface of a galvanized steel sheet for the purpose of reducing degradation of the coating during the operation of forming said sheet, and for the purpose of improving the temporary corrosion protection of said sheet. It also relates to a method of lubricating such a coated sheet.

Abstract: The invention discloses an object comprising at least one part made of steel, the composition of which comprises, the contents being expressed by weight, carbon with a content of between 0.005 and 0.27%, manganese between 0.5 and 1.6%, silicon between 0.1 and 0.4%, chromium in a content of less than 2.5%, Mo in a content of less than 1%, optionally one or more elements chosen from nickel, copper, aluminum, niobium, vanadium, titanium, boron, zirconium and nitrogen, the balance being iron and impurities resulting from the smelting, said steel part including at least one zone welded by a high-energy-density beam, characterized in that said welded zone has a microstructure consisting of 60 to 75% self-tempered martensite and, to complement this, 40 to 25% lower bainite, and preferably 60 to 70% self-tempered martensite and, to complement this, 40 to 30% lower bainite.

Abstract: The invention relates to a process for manufacturing a part having very high mechanical properties from a hot-rolled or cold-rolled steel strip, comprising precoating said strip with aluminum or an aluminum alloy, cold deformation of the coated strip, possible cutting of the excess sheet with a view to the final geometry of the part, heating of the part so as to form an intermetallic compound from the steel/precoat interface and to austenitize the steel, transfer of the part to a tool and cooling of the part in the tool at a rate such that the steel has, after being cooled, a martensitic or bainitic structure or a martensite-bainite structure. The precoating is carried out by electroplating, by chemical or physical vapor deposition or by co-rolling.

Abstract: A system, method and software arrangement are provided for generating press-formed parts having a more consistent quality based on improved determination of processing conditions. For example, an apparatus can be configured to compare actual performance values of material properties provided by a material property database with standard values, and to adjust forming conditions such as a forming speed and a blank-holder pressure in accordance with the compared result. A control arrangement can be provided to control a press-forming device using the adjusted forming conditions. Accordingly, it may be possible to reduce occurrences of defects such as cracks and wrinkles when press-forming materials, and to obtain products having consistent quality and substantially identical shapes.

Abstract: The subject of the invention is a method for the hot-dip coating, in a liquid bath based on zinc containing aluminum, of a running strip of iron-carbon-manganese austenitic steel, in which said strip is subjected to a heat treatment in a furnace in which an atmosphere that is reducing with respect to iron prevails, in order to obtain a strip covered with a thin manganese oxide layer, and then the strip covered with the thin manganese oxide layer is made to run through said bath, the aluminum content in the bath being adjusted to a value at least equal to the content needed for the aluminum to completely reduce the manganese oxide layer, so as to form, on the surface of the strip, a coating comprising an iron-manganese-zinc alloy layer and a zinc surface layer.

Abstract: The invention relates to a process for manufacturing a corrosion-resistant cold-rolled sheet of iron-carbon-manganese austenitic steel, comprising the following steps: a sheet whose chemical composition comprises, the contents being expressed by weight: 0.35%?C?1.05%, 16%?Mn?24%, the balance of the composition consisting of iron and inevitable impurities resulting from its smelting, is provided; said sheet is cold-rolled; and a recrystallization annealing treatment is carried out on said sheet in a furnace containing a gas chosen from gases that are reducing with respect to iron, the parameters of said annealing being chosen in such a way that said sheet is covered on both its sides with an essentially amorphous (Fe,Mn)O oxide sublayer and with an external crystalline manganese oxide (MnO) layer, the total thickness of these two layers being equal to or greater than 0.5 microns.

Abstract: The inventive method consists in introducing a stirring gas through the vessel (1) bottom, in receiving a measurable mechanical vibration by at least one sensor fixed to the vessel or to the supporting frame thereof, in filtering the thus detected vibration signals by a high pass filter (13a) and preferably by a low pass filter (13b), in sampling and digitising (15) said vibration signals for exposing them to a second filtering which is digital and calibrated upon the vessel vibration responses, in sequencing said responses, in exposing each sequence to the calculation (17) of a temporal moving mean square, in extracting the total effective value RMS (for ‘Root Mean Square’) of the measured vibration signal therefrom, wherein said effective value is used for controlling the stirring gas flowrate supplied to the vessel. Said invention can be used for the stirring stand of steel making shop ladles, converters, RH processes, electric arc furnaces, etc.

Abstract: Iron-carbon-manganese austenitic steel sheet, the chemical composition of which comprises, the contents being expressed by weight: 0.45%?C?0.75%; 15%?Mn?26%; Si?3%; Al?0.050%; S?0.030%; P?0.080%; N?0.1%; at least one metal element chosen from vanadium, titanium, niobium, chromium and molybdenum, where 0.050%?V?0.50%; 0.040%?Ti?0.50; 0.070%?Nb?0.50%; 0.070%?Cr?2%; 0.14%?Mo?2%; and, optionally, one or more elements chosen from 0.0005%?B?0.003%; Ni?1%; Cu?5%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the amounts of said at least one metal element in the form of precipitated carbides, nitrides or carbonitrides being: 0.030%?Vp?0.150%; 0.030%?Tip?0.130%; 0.040%?Nbp?0.220%; 0.070%?Crp?0.6%; 0.14%?Mop?0.44%.

Abstract: The subject of the invention is a leveller in which at least the first five rolls from the entry of the leveller have a radius/centre-to-centre spacing ratio identical to that of conventional levellers, in which at least the last five rolls from the entry of the leveller have a radius/centre-to-centre spacing ratio close to that of a decurler, and in which the centre-to-centre spacing between the intermediate rolls of the leveller is advantageously increased.

Abstract: An exemplary lubricated hot rolling method is provided which can use a lubricating oil containing, e.g., one or more kinds among an high-basic alkaline-earth metal phenate, high-basic alkaline-earth metal carboxylate, high-basic alkaline-earth salicylate, or high-basic alkaline-earth metal sulfonate having a basicity of 40 mgKOH/g or higher, and has a viscosity at 40° C. of 800 cSt or less. The rolling can be performed by granulating or atomizing the lubricating oil into particulates whose average size is less than 1 mm, supplying the lubricating oil to rolls by using a noncombustible gas whose flow rate is 2000 cm3 or more per minute per lubricating nozzle. The velocity of the oil may be 1 m or more per second. The amount supplied of the lubricating oil can be controlled to 0.01 cm3 or more and 20 cm3 or less per 1 m2 of a surface area of the rolls.