Abstract: A method of forming a steel part is provided. The method includes the steps of coating a first steel plate to obtain a first precoat upon the first steel plate so as to define a first base, a first intermetallic alloy layer on the first base and a first metal alloy layer on the first intermetallic alloy layer. On a first face of the first steel plate the first metal alloy layer is removed in a first area of the first steel plate, while at least part of the first intermetallic alloy layer in the first area remains. A second steel plate is coated to obtain a second precoat upon the second steel plate so as to define a second base, a second intermetallic alloy layer on the second base and a second metal alloy layer on the second intermetallic alloy layer. On a second face of the second steel plate, the second metal alloy layer is removed in a second area of the second metal plate, while at least part of the second intermetallic alloy layer in the second area remains.

Abstract: A method of fabricating a precoated steel plate, the method including coating a steel plate by dipping the steel plate in a molten bath to obtain a precoat upon the steel plate, wherein the precoat includes an intermetallic alloy layer and a metal alloy layer. The intermetallic alloy layer is topped by the metal alloy layer. On at least one face of the plate, the metal alloy layer is removed in an area at a periphery of the plate using a laser beam, while leaving at least part of the intermetallic alloy layer in the area. The at least part of the intermetallic layer in the area has a thickness between 3 and 10 micrometers thick.

Abstract: The invention relates to a steel part, the composition of the steel of which comprises, the contents being expressed by weight: 0.040%?C?0.100%; 0.80%?Mn?2.00%; Si?0.30%; S?0.005%; P?0.030%; 0.010%?Al?0.070%; 0.015%?Nb?0.100%; 0.030%?Ti?0.080%; N?0.009%; Cu?0.100%; Ni?0.100%; Cr?0.100%; Mo?0.100%; and Ca?0.006%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the steel consisting of at least 75% equiaxed ferrite, martensite in an amount not less than 5% but not exceeding 20%, and bainite in an amount not exceeding 10%.

Abstract: The invention relates to a steel part coated with a compound consisting, over more than 90% of its thickness, of at least one Fe/Zn-based phase, the iron weight content of which is equal to 65% or higher and the Fe/Zn ratio of which is between 1.9 and 4, said compound being formed by at least one heat treatment for alloying between said steel and a precoat, said precoat consisting of a zinc alloy comprising, the contents being expressed by weight, between 0.5 and 2.5% aluminum and, optionally, one or more elements chosen from: Pb?0.003%; Sb?0.003%; Bi?0.003%; 0.002%?Si?0.070%; La<0.05%; Ce<0.05%, the balance consisting of zinc and inevitable impurities.

Abstract: Plate consisting of a steel substrate (1) and a precoat (2) consisting of a layer of intermetallic alloy (3) in contact with said substrate, topped by a layer of metal alloy (4), characterized in that, on at least one precoated face of said plate, an area (6) situated at the periphery of said plate has said metal alloy layer removed.

Abstract: The invention relates to a hot-rolled ferritic steel sheet, the composition of the steel of which comprises, the contents being expressed by weight: 0.001?C?0.15%, Mn?1%, Si?1.5%, 6%?Al?10%, 0.020%?Ti?0.5%, S?0.050%, P?0.1%, and, optionally, one or more elements chosen from: Cr?1%, Mo?1%, Ni?1%, Nb?0.1%, V?0.2%, B?0.010%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the average ferrite grain size dIV measured on a surface perpendicular to the transverse direction with respect to the rolling being less than 100 microns.

Abstract: A method of butt-welding steel plates is provided. The method includes the steps of coating a first steel plate by dipping the first steel plate in a molten bath to obtain a first precoat upon the first steel plate. The first precoat includes a first intermetallic alloy layer and a first metal alloy layer, the first intermetallic alloy layer is topped by the first metal alloy layer. On a first face of the first steel plate, the first metal alloy layer is removed in a first area at a first periphery of the first steel plate, while at least part of the first intermetallic alloy layer in the first area remains. A second steel plate is coated by dipping the second steel plate in the molten bath or a further molten bath to obtain a second precoat upon the second steel plate. The second precoat includes a second intermetallic alloy layer and a second metal alloy layer, the second intermetallic alloy layer is topped by the second metal alloy layer.

Abstract: The present invention relates to a method for acting on the temperature of a travelling strip (4) by blowing gas or a water/gas mixture, whereby a plurality of jets of gas or a water/gas mixture, extending toward the surface of the strip and arranged in such a way that the impacts (24, 34) of the jets of gas or water/gas mixture on each surface of the strip are distributed at the nodes of a two-dimensional network, are sprayed onto each face of the strip. The impacts (24) of the jets on one face (A) are not opposite the impacts (34) of the jets on the other face (B), and the jets of gas or water/gas mixture come from tubular nozzles (23, 33) which are supplied by at least one distribution chamber (21, 31) and extend at a distance from the distribution chamber in such a way as to leave a free space for the flow of the returning gas or water/gas mixture parallel to the longitudinal direction of the strip and perpendicular to the longitudinal direction of the strip.

Abstract: The invention deals with a hot-dip galvanized or galvannealed steel sheet wherein, the composition of the steel sheet comprises, by weight: 0.01?C?0.22%, 0.50?Mn?2.0%, 0.2?Si?3.0%, 0.005?Al?2.0%, Mo<1.0%, Cr?1.0%, P<0.02%, Ti?0.20%, V?0.40%, Ni?1.0%, Nb?0.20%, the balance of the composition being iron and unavoidable impurities resulting from the smelting, and the steel sheet comprises a layer of an internal nitride of at least one type of nitride selected from a Si nitride, Mn nitride, Al nitride, complex nitride comprising Si and Mn, or Al and Si, or Al and Mn, or complex nitride comprising Si, Mn and Al, said steel sheet comprising no further outer layer of iron nitride.

Abstract: An austenitic steel sheet excellent in resistance to delayed cracking, the composition of said steel comprising, in weight: 0,35%<C<1,05%, 15%<Mn<26%, Si<3%, Al<0,050%, S<0,030%, P<0,080%, N<0,1%, at least one metallic element X chosen among vanadium, titanium, niobium, molybdenum, chromium: 0,050%<V<0,50%, 0,040%?Ti<0,50%, 0,070%<Nb<0,50%, 0,14%<Mo<2%, 0,070%<Cr<2% and optionally, one or several elements chosen among 0,0005%<B<0,010%, Ni<2%, Cu<5%, the remainder being iron and unavoidable impurities inherent to fabrication, including hydrogen, the quantity Xp of said at least one metallic element under the form of carbides, nitrides or carbonitrides being, in weight: 0,030%<VP<0,40%, 0,030%<Tip<0,50%, 0,040%<Nbp<0,40%, 0,14%<Mop<0,44%, 0,070%<Crp<0,6%, the hydrogen content Hmax designating the maximal hydrogen content that can be measured from a series of at least five specimens, and the quantity Xp, in weight, be

Abstract: The invention relates to a steel plate, the chemical composition of which comprises, the contents being expressed by weight: 0.010%?C?0.20%, 0.06%?Mn?3%, Si?1.5%, 0.005%?Al?1.5%, S?0.030%, P?0.040%, 2.5%?Ti?7.2%, (0.45×Ti)?0.35%?B?(0.45×Ti)+0.70%, and optionally one or more elements chosen from: Ni?1%, Mo?1%, Cr?3%, Nb?0.1%, V?0.1%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting.

Abstract: A coating process for coating at least one side of a running substrate, by vacuum evaporation, with a layer of a sublimable metal or metal alloy, in which said metal or metal alloy is positioned so as to face said side of the substrate in the form of at least two ingots placed in contact with one another, that surface of said ingots facing said side of the substrate being kept parallel to the substrate and at a constant distance from the latter during coating, and also to a coating plant for implementing the process and to a feeder for supply.

Abstract: Exemplary embodiments of a press-forming device, press-forming method, computer program/software arrangement and storage medium can be provided. The exemplary press-forming device can include a material characteristic input configured to input material characteristics. A state variable detector can be configured to measure a state variable comprising a metal mold distortion amount. A processing condition computer arrangement can be configured to determine from a first moment to a second moment at least one particular processing condition. Further, a processing condition controller can be configured to control the at least one processing condition from processing conditions.

Abstract: A method of rolling a strip is provided. The method includes determining a value representative of the lateral position of the strip along a line transverse to a run direction downstream of each stand and calculating algebraic differences between the lateral positions and a reference position. A value of additional tilt is calculated from the algebraic differences to bring the algebraic differences below a predetermined threshold. Calculating the additional tilt values includes multiplying the algebraic differences by a gain matrix K that is determined by modeling relationships linking the algebraic differences and the tilts of the stand rolls. The additional tilt value is transmitted to each of the stands. The steps are repeated at predetermined time intervals until the strip is no longer gripped in the nip of the last stand of the rolling mill. A device for adjusting the lateral position of a strip is also provided.

Abstract: The invention relates to a steel part, the composition of the steel of which comprises, the contents being expressed by weight: 0.040%?C?0.100%; 0.80%?Mn?2.00%; Si?0.30%; S?0.005%; P?0.030%; 0.010%?Al?0.070%; 0.015%?Nb?0.100%; 0.030%?Ti?0.080%; N?0.009%; Cu?0.100%; Ni?0.100%; Cr?0.100%; Mo?0.100%; and Ca?0.006%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the steel consisting of at least 75% equiaxed ferrite, martensite in an amount not less than 5% but not exceeding 20%, and bainite in an amount not exceeding 10%.

Abstract: The invention relates to a process for making a hot stamped coated steel sheet product, comprising the steps of pre-coating a steel strip or sheet with aluminum—or aluminum alloy, cutting said pre-coated steel strip or sheet to obtain a pre-coated steel blank, heating the blank in a furnace preheated to a temperature and during a time defined by diagram according to thickness, at a heating rate Vc between 20 and 700° C. comprised between 4 and 12° C./s and at a heating rate Vc? between 500 and 700° C. comprised between 1.5 and 6° C./s, to obtain a heated blank; then transferring said heated blank to a die, hot stamping the heated blank in the die obtain a hot stamped steel sheet product, cooling at a mean rate Vr between the exit of the heated blank from the furnace, down to 400° C., of at least 30° C./s.

Abstract: The invention relates to a steel part, the composition of the steel of which comprises, the contents being expressed by weight: 0.040%?C?0.100%; 0.80%?Mn?2.00%; Si?0.30%; S?0.005%; P?0.030%; 0.010% S?Al?0.070%; 0.015%?Nb?0.100%; 0.030% Ti?0.080%; N?0.009%; Cu?0.100%; Ni?0.100%; Cr?0.100%; Mo?0.100%; and Ca?0.006%, the balance of the composition consisting of iron and inevitable impurities resulting from the smelting, the microstructure of the steel consisting of at least 75% equiaxed ferrite, martensite in an amount not less than 5% but not exceeding 20%, and bainite in an amount not exceeding 10%.

Abstract: The present invention is related to a steel composition, a process for producing a steel product having said composition, and said steel product itself. According to the invention, a cold-rolled, possibly hot dip galvanized steel sheet is produced with thicknesses lower than 1 mm, and tensile strengths between 800 MPa and 1600 MPa, while the A80 elongation is between 5 and 17%, depending on the process parameters. The composition is such that these high strength levels may be obtained, while maintaining good formability and optimal coating quality after galvanising. The invention is equally related to a hot rolled product of the same composition, with higher thickness (typically about 2 mm) and excellent coating quality after galvanising.

Abstract: A plate is provided. The plate includes a steel substrate and a precoat having a layer of intermetallic alloy in contact with the substrate, topped by a layer of aluminum alloy. On at least one precoated face of the plate, an area situated at the periphery of the plate has the aluminum alloy layer removed. A part and a welded blank are also provided. Methods are also provided.

Abstract: Hot-rolled steel sheet which then can be cold-rolled, coated, the steel in the sheet having the following composition by weight: 0.15%<carbon<0.5% 0.5%<manganese<3% 0.1%<silicon<0.5% 0.01%<chromium<1% titanium<0.2% aluminum<0.1% phosphorus<0.1% sulfur<0.05% 0.0005%<boron<0.08%, the remainder being iron and impurities inherent in processing, the shoot ensuring a very high mechanical resistance after thermal treatment and the aluminum-based coating ensuring a high resistance to corrosion.