Abstract: The invention relates to a blank for a tool die, made of compound steel with a core of high speed steel and a surrounding ring of a different steel, said ring bringing about a prestress in the core. According to the invention, the prestress is due to the fact that the core consists of a high speed steel powder which has been compacted to full density, that the ring consists of a steel alloy, the residual austenite transformation to martensite and consequent volume increase of which is zero or considerably less than the residual austenite transformation to martensite of the high speed steel after the same heat treatment, and that the blank has been hardened and tempered to create in the core a compression stress as a result of the obstruction by the surrounding ring of the volume increase of the core.The invention relates also to a method for manufacturing such blanks. A high speed steel powder is filled into a thick-walled pipe, said pipe consisting of a steel different from high speed steel.

Abstract: The invention relates to a powder metallurgical method for producing high speed steel products, the shape of which is close to the desired final shape of the product, i.e. according to the so called near net shape technique.

Abstract: A powder metallurgical method of producing metal bodies using spherical powder, produced by inert gas atomization, from magnetizable material with a particle size distribution closely approximating the so called Fuller curve for maximum density packing of spherical particles. Said powder is magnetized and filled into a form, which may take place before or after magnetization, said mixed and magnetized powder then sintered in said form with the exclusion of air, to produce a sintered body without communicating porosity.