Abstract: A coating composition which is excellent in crack resistance, alkali resistance and solvent resistance while having a high hardness and which is excellent in recoatability, anti-graffiti property, and removability of graffiti is provided.

Abstract: The present invention relates to (3.beta., 4.alpha.,16.beta.)-16,23,28-trihydroxyolean-12-ene-3-yl-.beta.-D-glucopyra nuronic acid derivatives and a method for preparing the same from Gymnema inodorum leaves, which comprises treating Gymnema inodorum leaves with an aqueous acid solution, extracting the leaves with an alcohol and/or water, concentrating the extract and subjecting to liquid-liquid partition extraction with water and 1-butanol, concentrating and drying/caking the 1-butanol phase under reduced pressure, defatting the cake, extracting soluble components from the cake with a high polar solvent, concentrating and drying/caking the extract to obtain a purified Gymnema inodorum leaf extract, and then applying the purified extract to HPLC to obtain fractions containing glucose absorption inhibiting substances.

Abstract: A method is proposed for the preparation of porous calcium carbonate particles of which each of the particles is not an aggregate but has ink bottle-shaped pores each not communicating with the others. The method comprises: (a) blending particles of heavy calcium carbonate having a specific particle size distribution with from 0.1 to 0.3% by weight of a porosity-forming agent, e.g., sodium chloride; (b) calcining the powder blend at a temperature in the range from 800.degree. C. to 1000.degree. C. to decarbonate the calcium carbonate particles into particles of calcium oxide having pores developed therein; (c) slaking the particles of calcium oxide with steam to convert the calcium oxide particles into particles of calcium hydroxide; (d) drying the particles of calcium hydroxide at a temperature in the range from 100.degree. C. to 350.degree. C.; and (e) carbonating the dried particles of calcium hydroxide with carbon dioxide gas at a temperature in the range from 600.degree. C. to 750.degree.C.

Abstract: Rust preventing synthetic resin compositions to be added to cement or mortar, which have high strength, adhesion and waterproof, contain 0.05.about.5 parts by weight of a primary alkanol-amine having 2 to 8 carbon atoms based on 100 parts by weight of resin solid content in a synthetic resin emulsion.