Abstract: The present invention discloses a catalyst used in preparing vinyl chloride, its method of preparation, and its applications. Said catalyst used in making vinyl chloride comprises activated carbon as a support, a barium compound and a phosphorus compound supported thereon. The barium compound accounts for 0.2% to 20% of the total mass of the catalyst and the phosphorus compound accounts for 0% to 10% of the total mass of the catalyst based on the mass percentage. A water-soluble barium compound, a water-soluble phosphorus compound, an aqueous polymer monomer, and water are mixed to form a solution or emulsion A. The activated carbon is added into the solution or emulsion A. The activated carbon is removed from water after impregnation, spin-dried, and then the monomers are polymerized. The activated carbon, after polymerization step, is heated to remove water and to decompose and carbonize the polymer. The catalyst after carbonization was activated to obtain a catalyst used in making vinyl chloride.
Type:
Grant
Filed:
October 26, 2011
Date of Patent:
June 16, 2015
Assignees:
SHANGHAI CAS ADVANCED RESEARCH INSTITUTE, ZHONGKE YIGONG (XIAMEN) CHEMICAL TECHNOLOGY CO., LTD.
Abstract: The present invention discloses a catalyst used in preparing vinyl chloride, its method of preparation, and its applications. Said catalyst used in making vinyl chloride comprises activated carbon as a support, a barium compound and a phosphorus compound supported thereon. The barium compound accounts for 0.2% to 20% of the total mass of the catalyst and the phosphorus compound accounts for 0% to 10% of the total mass of the catalyst based on the mass percentage. A water-soluble barium compound, a water-soluble phosphorus compound, an aqueous polymer monomer, and water are mixed to form a solution or emulsion A. The activated carbon is added into the solution or emulsion A. The activated carbon is removed from water after impregnation, spin-dried, and then the monomers are polymerized. The activated carbon, after polymerization step, is heated to remove water and to decompose and carbonize the polymer. The catalyst after carbonization was activated to obtain a catalyst used in making vinyl chloride.
Type:
Application
Filed:
October 26, 2011
Publication date:
August 8, 2013
Applicants:
Zhongke Yigong (Xiamen) Chemical Technology Co. Ltd., Shanghai CAS Advanced Research Institute