Abstract: The invention relates to a composition comprising 5-50 wt % of calcium silicate hydrate, 10-60 wt % of at least one water-soluble, acid group-containing polymer comprising polyether groups, and 5-40 wt % of at least one polyalkylene glycol ether. Further disclosed is a process for preparing this composition, and cementitious mixtures comprising the composition. A further aspect of the present invention is the use of the composition of the invention in cementitious mixtures for accelerating the development over time of the dispersing action of the acid group-containing polymer after addition of the mixing water and a subsequently accelerated curing of the mixture.

Abstract: The present invention provides a resin composition for molding, including a chlorinated polyvinyl chloride and a thermal stabilizer, the chlorinated polyvinyl chloride having structural units (a) to (c) represented by formulae (a) to (c) shown below: —CCl2—??(a), —CHCl—??(b), —CH2—??(c), the proportion of the structural unit (a) being 17.5 mol % or less, the proportion of the structural unit (b) being 46.0 mol % or more, and the proportion of the structural unit (c) being 37.0 mol % or less, relative to the total number of moles of the structural units (a), (b), and (c), the chlorinated polyvinyl chloride having a chlorine content of 63 mass % or more and less than 72 mass %, the thermal stabilizer containing a calcium alkyl carboxylate and a zinc compound, and the resin composition for molding having a loss in quantity on heating at 230° C. of less than 2 mass %.

Abstract: The invention relates to an efficient process for the preparation and isolation of rubber particles formed in aqueous media having a tunable level of metal containing anti-agglomerants and rubber particles obtained thereby. The invention further relates to copolymer products comprising the same or derived therefrom.

Abstract: A method for preparing silica nanoparticles includes the steps of: slowly titrating a sodium silicate solution with an acid solution to obtain a silicic acid-containing solution; continuously stirring the silicic acid-containing solution; slowly titrating the silicic acid-containing solution with the acid solution to obtain a silicic acid-enriched solution; continuously stirring the silicic acid-enriched solution; collecting the silicic acid-enriched solution as a silica nanoparticle precursor solution when a pH value of the silicic acid-enriched solution reaches a target pH value; and subjecting the silica nanoparticle precursor solution to a flame spray pyrolysis or a drying-grinding-calcining treatment.

Abstract: A hot melt adhesive material and articles made using the hot melt adhesive to assemble structures in an article. The adhesive material typically is manufactured by blending amorphous polymer with a heterophase polymer having crystallinity into an adhesive composition.

Abstract: Compositions for and methods of digitally printing an ink image onto a woven textile material are provided. A base application is applied to the surface of a woven textile material, especially one comprising synthetic resin fibers prior to application of an ink image layer. The base application comprises an acrylic latex material that is formulated to be printed on with a digital ink while still wet, thereby eliminating the need for an intermediate drying cycle in between base application deposit and printing of the ink image.

Abstract: A polymer composition that contains a polyaryletherketone and thermotropic liquid crystalline polymer, which are melt processed in the presence of a flow modifier. The flow modifier is a functional compound that contains one or more hydroxyl functional groups.

Abstract: Provided is an electric component equipped with a live electrical part and an insulating resin molded article that is molded from a thermoplastic resin composition and is in contact with the live electrical part, wherein: the thermoplastic resin composition includes (A) 60 to 80 parts by mass of a polyphenylene ether resin or a mixture of a polyphenylene ether resin and a styrene resin, (B) 60 to 80 parts by mass of a hydrogenated block copolymer, (C) 5 to 30 parts by mass of a flame retardant, and (D) 0.1 to 3 parts by mass of titanium oxide (in an amount corresponding to 100 parts by mass of the total of (A) to (C)).

Abstract: An aqueous particle-free inkjet ink composition has a pH of 7 to 9, and consists essentially of: (A) water-soluble dye colorants present in a total amount of 2-10 weight %, (B) a water-soluble polymer present in an amount of 1-4 weight %, and an aqueous medium consisting essentially of water. The water-soluble polymer has an acid number ?130 and a molecular weight of 5,000 to 20,000. It comprises: (a) 55-80 mol % of recurring units derived from ethylenically unsaturated polymerizable monomers selected from substituted or unsubstituted styrenes, (meth)acrylates, and combinations thereof, each (meth)acrylate comprising either a pendant phenyl group or an alkyl ester group having 12 to 20 carbon atoms; and (b) 20-35 mol % of recurring units comprising (meth)acrylic acid, all based on total water-soluble polymer recurring units. The one or more water-soluble dye colorants are chosen singly or collectively to provide a hue other than black.

Abstract: The invention relates to an acoustic product composed of composite material, such as a musical musical instrument, a part thereof, an acoustic equipment or like, which is manufactured from raw material comprising at least cellulose based substance and plastic based substance by means of a thermoplastic process, such as by pressing, compression molding, injection molding, extrusion, blow molding by heat, rotational molding and/or the like. The acoustic product has a material composition consisting of fiber substance (1) based on surface modified cellulose and plastic based substance (2), wherein the product has an essentially wood-like, but isotropic sound.

Abstract: A process for preparing a blend of cis-1,4-polybutadiene and syndiotactic 1,2 polybutadiene, the process comprising the steps of (i) polymerizing 1,3-butadiene in the presence of a lanthanide-based catalyst to form a polymerization mixture including cis-1,4-polybutadiene, and (ii) polymerizing 1,3-butadiene in the presence of a cobalt-based catalyst within the polymerization mixture including cis-1,4-polybutadiene to form syndiotactic 1,2-polybutadiene and thereby produce a blend of cis-1,4-polybutadiene and syndiotactic 1,2-polybutadiene.

Abstract: A method for producing a flame-retardance-imparting material comprises: a shredding step of shredding plant material containing stems and/or leaves of tomato plants and/or eggplant plants in a aqueous solvent; and an aqueous solvent removal step or removing the aqueous solvent from the plant material after shredding.

Abstract: The invention provides monolayer films excellent in hydrophilicity and transparency which include a crosslinked resin having a surface enriched with hydrophilic groups, and materials which exhibit excellent properties such as hydrophilicity, antifogging properties and antifouling properties by virtue of having the above monolayer films. A monolayer film is fabricated which includes a crosslinked resin obtained by polymerizing a composition including a compound (I) having an anionic hydrophilic group and a functional group with a polymerizable carbon-carbon double bond, and a compound (II) having three or more hydroxyl groups and three or more functional groups with a polymerizable carbon-carbon double bond, the monolayer film having a gradient (Sa/Da) of not less than 1.1 wherein Sa is the surface concentration of the anionic hydrophilic groups in the monolayer film, and Da is the deep concentration of the hydrophilic groups at ½ of the thickness of the monolayer film.

Abstract: A tire rubber composition that improves dry grip performance to or beyond conventional levels, while retaining grip performance sustainability and wear resistance during high-speed running is provided. A tire rubber composition comprising 40 to 180 parts by weight of carbon black having a nitrogen adsorption specific surface area of 80 to 400 m2/g and 1 to 100 parts by weight of aromatic copolymer blended in 100 parts by weight of diene rubber, the aromatic copolymer being a copolymer of an ?-methylstyrene derivative represented by general formula (I) and indene.

Abstract: Provided is a binder that has satisfactory storage stability and can express an excellent bonding strength for a glass fiber or powdered glass (impart a satisfactory strength to a bonded body with the glass fiber or the powdered glass). The binder of the present invention includes: a polymer having a hydroxyl group; and an ammonium salt of an inorganic acid, in which: the polymer contains a specific structural unit derived from a monomer represented by the general formula (1) and a specific structural unit derived from a monomer containing a carboxylic acid (salt) group.

Abstract: An interlayer comprised of a high flow, low molecular weight thermoplastic resin, and at least one plasticizer is disclosed. The use of a high flow, low molecular weight thermoplastic resin, and a plasticizer creates synergy allowing the flow of the interlayer to be increased without sacrificing other characteristics typically associated with an increased flow (e.g., increased blocking, decreased mechanical strength, and decreased manufacturing capability). In this regard, the high flow, low molecular weight thermoplastic resin provides a flow improvement, resulting in a high flow interlayer. As a result, a thinner interlayer can be utilized in forming multiple layer panels because the resulting thinner interlayer has improved flow properties.

Abstract: Waterborne coatings are described having an acceptable balance of properties both during the storage of coating, application and drying. The period in which irregularities in a freshly applied coating can be repaired without resulting in brush marks is referred to as the open time. Aqueous coatings generally employ dispersed high molecular weight polymers as binders. These binders often provide short open times when the coating is dried since the dispersed polymer particles tend to be immobilized quickly in the edge region of an applied coating. As a result, the viscosity of the coating increases rapidly, which leads to a limited window of workability. The instant invention provides additives that are not volatile but that will extend the time that the film is malleable after it is applied without interfering with other attributes, such as the resistance of the coating to freezing while in the can prior to application.

Abstract: A displacement prevention coating agent is provided which can prevent a displacement in lens processing, which is soluble in water and which exhibits a transparent appearance at least after being cured. The displacement prevention coating agent may coat the front and rear surfaces of a lens so that when cutting processing is performed on an end surface of the lens, a holding position of the front and rear surfaces of the lens held by a chuck device is prevented from being displaced. A water-repellent coat layer may be formed as a membrane such that the end surface has a shape corresponding to a frame. The displacement prevention coating agent may be formed of an aqueous solution whose main components are a hydrophilic resin, a surfactant having a perfluoro group and an emulsion.

Abstract: The present invention relates to a fire resistant glazing unit (10), and in particular to novel curable gelling compositions which may form a fire-resistant hydrogel interlayer (3) between the glass panes (1) of the glazing unit (10). The gelling compositions of the invention comprise 5-40% w/w of a curable hydrogel-forming component (typically an acidic vinyl monomer such as acrylic acid or its metal salt); 20-60% w/w of one or more salts (e.g. magnesium salts); 40-90% w/w of an aqueous vehicle; and the gelling compositions have an acidic p H between p H 1 and 7. Such gelling compositions, when cured to form a hydrogel interlayer, provide excellent fire-resistant properties and also an excellent radiation barrier in the event of a fire.

Abstract: A reaction product is obtained by free-radical emulsion polymerization in an aqueous medium of ethylenically unsaturated monomers including at least one conjugated diene. The free-radical emulsion polymerization is conducted in the presence of a degraded polysaccharide having a DE of 38 to 70 measured according to ISO 5377 (1981 Feb. 15) and optionally an alkyl mercaptan in an amount of no more than 2.5 weight percent based on the total weight of ethylenically unsaturated monomers. A coating composition includes the reaction product, and a paper or a board can be coated with such a coating composition.