Abstract: The invention provides a multilayer film comprising a substrate film and a coating layer arranged on at least one surface of the substrate film, wherein the coating layer contains an oxazoline group and comprises an acrylic resin, the coating layer has a thickness (D) of 5-150 nm, and the ratio (Pl/P2) of the peak intensity (P1) of a peak that has an absorption maximum in a region of 1655±10 cm?1 to the peak intensity (P2) of a peak that has an absorption maximum in a range of 1580±10 cm?1 in the total reflection infrared absorption spectrum of the coating layer and the thickness (D) of the coating layer fulfill the relationship represented by the formula: 0.03?(Pl/P2)/D?0.15.

Abstract: The present invention is a normal temperature-curable hard coat composition containing at least (A) a polysilazane compound having structures shown by the following formula (1) and (B) an alkoxysilane compound. The ratio of [a] the number of Si—H bonds in the polysilazane compound and [b] the number of alkoxy groups in the alkoxysilane compound is in a range of [b]/[a]=1.5 to 3. The present invention provides the normal temperature-curable hard coat composition which has excellent workability on outdoors, cures at normal temperature, improves surface hardness of plastic materials, and is used as an alternative material to glass.

Abstract: Provided is a polyorganosilsesquioxane capable of forming, when cured, a cured product that offers high surface hardness and good heat resistance, is highly flexible, and has excellent processability. The present invention relates to a polyorganosilsesquioxane including a constitutional unit represented by Formula (1). The polyorganosilsesquioxane includes a constitutional unit represented by Formula (I) and a constitutional unit represented by Formula (II) in a mole ratio of the constitutional unit represented by Formula (I) to the constitutional unit represented by Formula (II) of 5 or more. The polyorganosilsesquioxane has a total proportion of the constitutional unit represented by Formula (1) and a constitutional unit represented by Formula (4) of 55% to 100% by mole based on the total amount (100% by mole) of all siloxane constitutional units.

Abstract: The present invention relates to a low refractive layer and an anti-reflective film comprising the same. The low refractive layer can exhibit excellent optical properties such as a low reflectance and a high light transmittance, and excellent mechanical properties such as high wear resistance and scratch resistance at the same time. In particular, due to the excellent alkali resistance, the low refractive layer can maintain excellent physical properties even after alkali treatment. Therefore, when introducing a low refractive layer to the display device, it is expected that the production process can be simplified and further the production rate and the productivity can significantly increase.

Abstract: With applications such as soft robotics being severely hindered by the lack of strong soft actuators, the invention provides a new soft-actuator material—Electrically Actuated Hydraulic Solid (EAHS) material—with a stress-density that outperforms any known electrically-actuatable material. One type of actuator is fabricated by making a closed cell that acts as highly paralyzed version of a standard paraffin actuator. Each cell exhibits microscopic expansion, which is summed to produce macroscopic motion. The closed cellular nature of the material allows the system to be cut and punctured and still operate. It can be produced in a lab or industrial scale, and can be formed using molding, 3D printing or cutting.

Abstract: Disclosed is a heat curable solvent free plastisol composition that exhibits very low volatile organic compound amounts while maintaining high performance characteristics. The present plastisol compositions have solvent substitutes used at amounts up to 15% by weight based on the total composition weight. The solvent substitutes have very low vapor pressures, stable viscosity effects, and are fusible with the plastisol polymers. These solvent substitutes can be used to replace the typical solvents without requiring extensive re-formulation of the plastisol composition. The final plastisol compositions according to the present invention exhibit low VOC measures of less than 0.03 pounds per gallon when measured according to EPA Method 24.

Abstract: There are provided a thermosetting resin composition for a semiconductor package and a prepreg and a metal clad laminate using the same. More particularly, there are provided a thermosetting resin composition for a semiconductor package capable of improving desmear characteristics by using a cyanate based ester resin and a benzoxazine resin in a thermosetting resin composition based on an epoxy resin and improving chemical resistance by using a slurry type filler to have high heat resistance and reliability, and a prepreg and a metal clad laminate using the same.

Abstract: A hardcoat film includes a substrate; a hardcoat layer; and an anti-scratch layer, where the hardcoat layer includes a cured product of polyorganosilsesquioxane, the polyorganosilsesquioxane has a siloxane constitutional unit containing a (meth)acryloyl group and a siloxane constitutional unit containing an epoxy group and is represented by the General Formula (1), a film thickness of the anti-scratch layer is 0.05 to 5 ?m, and the anti-scratch layer includes a cured product of a compound having two or more (meth)acryloyl groups in one molecule, where Ra represents a group containing a (meth)acryloyl group; Rb represents a group containing an epoxy group; Rc represents a monovalent substituent; p, q, and r represent a proportion of Ra, Rb, and Rc in the General Formula (1) respectively; p+q+r is 100; p and q are greater than 0; r is equal to or greater than 0; p/q is 0.01 to 99.

Abstract: [PROBLEM] To provide an antifouling film equipped with protective film having an antifouling layer with excellent antifouling characteristics even after aging, and to a method for manufacturing same. [SOLUTION MEANS] An antifouling film equipped with protective film in which protective film is laminated on an antifouling layer of an antifouling film having an antifouling layer on a substrate film X, the antifouling film equipped with protective film being such that, when the protective film is detached from the antifouling film, a contact angle of water with respect to a surface of the protective film that had been in contact with the antifouling layer of the antifouling film is 90° to 115°. And also a method for manufacturing the aforementioned antifouling film equipped with protective film in which aging is carried out under certain temperature conditions while the protective film is laminated to a surface of the antifouling layer.

Abstract: Urea (multi)-(meth)acrylate (multi)-silane precursor compounds, synthesized by reaction of (meth)acrylated materials having isocyanate functionality with aminosilane compounds, either neat or in a solvent, and optionally with a catalyst, such as a tin compound, to accelerate the reaction. Also described are articles including a substrate, a base (co)polymer layer on a major surface of the substrate, an oxide layer on the base (co)polymer layer; and a protective (co)polymer layer on the oxide layer, the protective (co)polymer layer including the reaction product of at least one urea (multi)-(meth)acrylate (multi)-silane precursor compound synthesized by reaction of (meth)acrylated materials having isocyanate functionality with aminosilane compounds. The substrate may be a (co)polymer film or an electronic device such as an organic light emitting device, electrophoretic light emitting device, liquid crystal display, thin film transistor, or combination thereof.

Abstract: A process for preparing a repellant smooth surface includes applying a coating composition onto a smooth surface of a substrate having hydroxyl functional groups thereon and an average roughness Ra of less than 4 ?m. The coating composition includes: (i) a polymerizable silane or siloxane or both selected from the group consisting of dimethyldimethoxysilane, dimethoxy-methyl(3,3,3-trifluoropropyl)silane, dimethoxy(methyl)octylsilane, diethoxydimethylsilane, (ii) a solvent and (iii) an acid catalyst. The process further includes polymerizing the silane or siloxane or both from the hydroxyl functional groups on the smooth surface of the substrate to form a chemical layer of graft polymers having ends anchored to the smooth surface and applying a lubricant coating over the formed chemical layer to adhere and maintain the lubricant on the smooth surface and form a lubricant-entrenched smooth surface as the repellant smooth surface.

Abstract: [PROBLEM] To provide an antifouling film equipped with protective film having an antifouling layer with excellent antifouling characteristics even after aging, and to a method for manufacturing same. [SOLUTION MEANS] An antifouling film equipped with protective film in which protective film is laminated on an antifouling layer of an antifouling film having an antifouling layer on a substrate film X, the antifouling film equipped with protective film being such that, when the protective film is detached from the antifouling film, a contact angle of water with respect to a surface of the protective film that had been in contact with the antifouling layer of the antifouling film is 90° to 115°. And also a method for manufacturing the aforementioned antifouling film equipped with protective film in which aging is carried out under certain temperature conditions while the protective film is laminated to a surface of the antifouling layer.

Abstract: A compound that is devoid of epoxy groups and has a quantity of alkenyl groups corresponding to 5-1000 times the alkenyl content of a base polymer, and/or an organopolysiloxane that is devoid of alkenyl groups, has an average degree of polymerization of 2-50, and contains, per molecule, 30 mol % or more of siloxane units having epoxycyclohexyl groups bonded to silicon atoms via carbon atoms, are/is blended with a silicone composition for a release film as adhesion-enhancing components.

Abstract: Provided are a medical lubricating member including a silicone base material, and a lubricating coated film which is laminated on at least one surface of the silicone base material, in which the silicone base material contains a reactive functional group in the surface on which the lubricating coated film is laminated, and the lubricating coated film is a film formed of a composition containing a hydrophilic polymer and polyisocyanate; a medical device using the medical lubricating member; and a method of producing the medical lubricating member.

Abstract: A heat conductive sheet of the present invention is a heat conductive sheet containing a curing reaction catalyst, wherein a heat conductive uncured composition 2 not containing a curing reaction catalyst is joined to at least one principal surface of the heat conductive sheet 1 containing a curing reaction catalyst. The heat conductive sheet 1 containing a curing reaction catalyst contains the curing reaction catalyst in an amount necessary to cure the heat conductive uncured composition. A mounting method of the present invention includes: joining a heat conductive uncured composition 2 not containing a curing reaction catalyst to at least one principal surface of the heat conductive sheet 1 containing a curing reaction catalyst, and curing the heat conductive uncured composition by diffusion of the curing reaction catalyst contained in the heat conductive sheet 1.

Abstract: An adhesive includes a polymeric latex, a penetrant selected from the group consisting of: terpenes, polylimonene, limonene, carvone, ?-pinene, citral, dipentene, 1,8-cineole, eucalyptol, citronellol, geraniol, citronellene, terpinen-4-ol, borneol, camphor, guayule resin, and combinations thereof; and a reinforcing filler. The adhesive has a solids content of 35-65% and a pH of 9 to 12. Articles of manufacture, such as tires and air springs incorporate the adhesive to join rubber interfaces. A method of making the adhesive is also is provided.

Abstract: Provided is a resin composition containing polymethallyl alcohol (A) having a repeating structural unit represented by the following formula (1) in an amount of greater than or equal to 30 mol %, and a metal ion (B), a content of the metal ion (B) being greater than or equal to 0.05 ?mol per 1 g of the polymethallyl alcohol (A); a method of producing the resin composition; and a molding containing the resin composition.

Abstract: There are provided a modified silicone compound prepared by reacting: (A) a siloxane diamine represented by the general formula (1); (B) a maleimide compound with at least two N-substituted maleimide groups in the molecular structure; and (C) an amine compound with an acidic substituent; and also provided a thermosetting resin composition, a prepreg, a laminated plate, and a printed wiring board that are formed by using this compound. The multi-layered printed wiring board produced by using the laminated plate formed by using the prepreg obtained from the modified silicone compound and the thermosetting resin composition of the present invention through laminate molding has an excellent glass transition temperature, coefficient of thermal expansion, copper foil adhesion, hygroscopicity, hygroscopic solder heat resistance, and copper-stuck solder heat resistance.

Abstract: A liquid curable silicone adhesive composition is provided. The composition is generally storage stable as a one-part composition at room temperature, can primarily cure at room temperature in the presence of moisture, and can secondarily cure at high temperatures, and can form a strong adhesive layer on a substrate or member. The liquid curable silicone adhesive composition comprises: a curable reactive organopolysiloxane which has a radical reactive group and a condensation reactive group in the same molecule or throughout the mixture; a condensation reaction catalyst; an organic peroxide; an adhesion imparting agent; and a crosslinkable silane. Herein, regarding the storage modulus (G?1) of a cured product obtained by primarily curing the composition in the presence of moisture approximately at room temperature, along with the storage elastic modulus (G?2) of a cured pro duct obtained by curing the composition, the increase rate (?) of the storage elastic modulus is at least 50%.

Abstract: A curable coating composition includes: (a) a polymer including at least two active methylene functional groups; (b) a polyisocyanate crosslinker; and (c) a transition metal catalyst. Substrates at least partially coated with these coating compositions are further disclosed. Methods for preparing the coating are further disclosed. Multi-layer coatings including these coating compositions are further disclosed.