Patent number: 6485825Abstract: The present invention is a pressure-sensitive adhesive tape or sheet prepared by laminating a pressure-sensitive adhesive layer onto one side of an urethane resin layer consisting of 100 weight parts of a polyol component and A weight parts of a polyisocyanate component with a distance between cross-links (weight average molecular weight/number of isocyanate groups) of 220-570, wherein the aforementioned A is represented by the following equation A=100aX/Y (in this equation, a is a constant 0.067-0.135, X is the hydroxide value of the aforementioned polyol component, and Y is the weight percent concentration of isocyanate groups in the polyisocyanate component), and, at 5° C. and 35° C., the strength at a 2% elongation is 0.40-2.20 Kg/15 mm-width and the breaking elongation is 50-300%.Type: GrantFiled: October 23, 2000Date of Patent: November 26, 2002Assignee: Sekisui Chemical Co., Ltd.Inventors: Masahiko Heguri, Yoshiyuki Miyake, Hiroshi Murayama
-
Patent number: 6482523Abstract: An adhesive for lamination which comprises a resin whose dynamic wettability to a film substrate is at least 0.20 mN alone or in combination with a polyisocyanate curing agent, said adhesive for lamination having a good adhesiveness to a film substrate such as a plastic film, a metal foil, a metallized film or paper.Type: GrantFiled: March 29, 1999Date of Patent: November 19, 2002Assignee: Nippon Polyurethane Industry Co., Ltd.Inventors: Yukihiro Morikawa, Hiroyoshi Yano, Ichiro Higashikubo, Toshiaki Sasahara
-
Patent number: 6482492Abstract: A spacemesh structure for shoe making includes an upper mesh-texture layer, a lower mesh-texture layer and a reinforced structure in between. The reinforced structure comprises a plurality of supporting lumps arranged as a two dimensional array with gaps between two supporting lumps. A plurality of girders are disposed in the gaps in one direction leaving some gaps between every two adjacent lumps located between two adjacent girders.Type: GrantFiled: May 25, 2001Date of Patent: November 19, 2002Inventor: Wen-Yau Hung
-
Patent number: 6479576Abstract: Described is a multi-layer film comprising, (a) at least one first layer of polyamide; (b) at least one second layer of polyethylene or an ethylene-copolymerizate containing fine-particulate titanium dioxide, a majority of the titanium dioxide particles having a diameter of between 5 and 30 nm; (c) optionally at least one EVOH-containing third layer; and (d) optionally at least one bonding layer. The multi-layer film has a value of from 5 to 200, as determined from the summation of the product of the following equation (I) for all second layers of the multi-layer film, (A×B) Equation (I) Equation (I) is calculated for each second layer, A is the thickness of the second layer in micrometers, and B is the weight percent of titanium dioxide present in the second layer, based on the total weight of the second layer. Also described is the use of the film according to the present invention as a packaging material for foodstuffs.Type: GrantFiled: March 22, 2001Date of Patent: November 12, 2002Assignee: Wolff Walsfode AGInventors: Holger Eggers, Rainer Brandt
-
Patent number: 6472480Abstract: A coating composition is disclosed that is intended for application to the interior surface of a can and is free of Bisphenol A diglycidyl ether and comprises a phenoxy group-containing or amino group-containing resin, a nonaqueous carrier and a polyester resin formed from (a) isophthalic acid, (b) naphthalene dicarboxylic acid or an ester thereof, (c) trimellitic anhydride or trimethylpropane and (d) neopentyl glycol.Type: GrantFiled: February 20, 2001Date of Patent: October 29, 2002Assignee: BP Corporation North America Inc.Inventor: Ronald Leslie Anderson
-
Patent number: 6465604Abstract: The invention comprises a vulcanizable composition comprising a sulfur vulcanizable rubber, a sulfur vulcanizing agent, an accelerating agent in an amount effective to accelerate vulcanization and sufficient to not substantially inhibit vulcanization, and an amount effective to improve the hardness stabilization of said rubber upon vulcanization of a pyrimidine derivative. The invention also comprises a method of improving the hardness stabilization of a composition comprising a sulfur vulcanizable rubber by adding the above accelerating agent and pyrimidine derivative to the composition.Type: GrantFiled: March 21, 2001Date of Patent: October 15, 2002Assignee: Flexsys America L.P.Inventors: Horng-Jau Lin, Otto William Maender
-
Patent number: 6461802Abstract: The coating quality of an adhesive layer applied in direct contact on a polyester film is improved by using an alkyl (poly)glycoside as surfactant. A polyester film carrying such layer is suitable as support for a photosensitive material.Type: GrantFiled: July 31, 2000Date of Patent: October 8, 2002Assignee: Agfa-GevaertInventors: Etienne Van Thillo, Patrick Mertens, Jozef Boeykens, Filip Vandaele
-
Patent number: 6440553Abstract: A pressure-sensitive adhesive composition, wherein the storage elastic modulus [G′] at room temperature is at least 2×106 dyne/cm2 and the adhesive strength at room temperature is 1 kg/20 mm width or higher. Preferably, a pressure-sensitive adhesive composition comprising a polymer having a polycarbonate structure having a repeating unit represented by the following formula wherein R represents a straight chain or branched hydrocarbon group having from 2 to 20 carbon atoms, a pressure-sensitive adhesive sheet, a sealing material, a reinforcing sheet, and a pressure-sensitive sheet for printing, each having the pressure-sensitive adhesive composition.Type: GrantFiled: January 31, 2001Date of Patent: August 27, 2002Assignee: Nitto Denko CorporationInventors: Yasuyuki Tokunaga, Masahiko Ando, Takeshi Yamanaka, Waka Hikosaka, Makoto Kojima, Shin-ichi Kouno, Hiroaki Mashiko, Hiroshi Wada, Hiroshi Yamamoto, Yoshikazu Soeda, Naoki Matsuoka, Katsuya Kume, Mitsuo Kuramoto
-
Patent number: 6429159Abstract: The present invention is directed to a stretchable adhesive nonwoven prepared by laminating continuous filaments made of a thermoplastic polyurethane resin, which comprises an aliphatic diisocyanate and/or an aromatic diisocyanate, a polymeric diol and a chain-extending agent and has a hardness (JIS-A hardness) of 65 to 98 degree and a flow initiating temperature within a range from 80 to 150° C., into a sheet, and fusion-bonding the filaments themselves with their own heat at the contact point of the laminated filaments thereby to form fibers, and a laminate containing the same. The adhesive nonwoven fabric of the present invention is rich in flexibility and is excellent in adhesion and air permeability.Type: GrantFiled: July 19, 2000Date of Patent: August 6, 2002Assignees: Kanebo Limited, Kanebo Gohsen, LimitedInventors: Noboru Watanabe, Tsutomu Teshima, Yukio Yamakawa, Yutaka Tanaka, Teruyoshi Kawada
-
Patent number: 6399205Abstract: The present invention is embodied in a polyurethane composition suitable for coating, casting or laminating, which incorporates a prescribed additive selected to increase the composition's electrical conductivity without adversely affecting the composition's transparency and percent haze and without adversely affecting its adhesion to an underlying substrate or its environmental durability, especially with regard to humidity resistance. The prescribed additive is an ionizable metal salt of a perfluoroalkylsulfonimide, in a weight percent of 0.5 to 5.0, with the metal being an alkali metal and the preferred perfluoroalkylsulfonimide being trifluoromethanesulfonimide. The most preferred salt is lithium trifluoromethanesulfonimide. The preferred polyurethane include both aliphatic polyetherurethanes and aliphatic polyesterurethanes.Type: GrantFiled: June 1, 2000Date of Patent: June 4, 2002Assignee: Pilkington Aerospace Inc.Inventors: Stephen L. Sandlin, Lin Hin Hoo, Marlowe V. Moncur
-
Patent number: 6395391Abstract: An adhesive tape for electronic parts which comprises a metal substrate and an adhesive layer A and an adhesive layer B and an adhesive layer C laminated in order wherein said adhesive A comprises a polyimide consisting of 100-20% by mol of the repeating unit represented by the following formula-(1a) and 0-80% by mol of the repeating unit represented by the following formula (1b), said adhesive B comprises a polyimide consisting of 100-40% by mol of the repeating unit represented by the following formula (1a) and 0-60% by mol of the repeating unit represented by the following formula (2), and the adhesive layer A and the adhesive layer B have each a different glass transition temperature: wherein Ar represents a divalent group selected from the specified structures containing aromatic rings, R is an alkylene group having 1 to 10 carbon atoms or —CH2OC6H4—, the methylene group of which attaches to Si, and n means an integer of 1 to 20.Type: GrantFiled: April 27, 2000Date of Patent: May 28, 2002Assignee: Tomoegawa Paper Co., Ltd.Inventors: Osamu Oka, Jun Tochihira, Fumiki Komagata
-
Patent number: 6387475Abstract: An aqueous adhesive composition with good release properties comprising a water based adhesive and a metal activated dicarboxylic acid anhydride starch derivative as release agent. This adhesive composition is useful in forming coreless paper rolls.Type: GrantFiled: April 5, 2000Date of Patent: May 14, 2002Assignee: National Starch and Chemical Investment Holding CorporationInventors: Edmund W. Figiel, Robert L. Billmers