Abstract: The invention relates to multi-layer oxide ceramic bodies and in particular to presintered multi-layer oxide ceramic blanks and oxide ceramic green bodies suitable for dental applications. These bodies can be thermally densified by further sintering without distortion and are thus particularly suitable for the manufacture of dental restorations. The invention also relates to a process for the manufacture of such multi-layer oxide ceramic bodies as well as to a process for the manufacture of dental restorations using the multi-layer oxide ceramic bodies.

Abstract: Zirconia dental ceramics exhibiting opalescence and having a grain size in the range of 10 nm to 300 nm, a density of at least 99.5% of theoretical density, a visible light transmittance at or higher than 45% at 560 nm, and a strength of at least 800 MPa.

Abstract: Zirconia dental ceramics exhibiting opalescence and having a grain size in the range of 10 nm to 300 nm, a density of at least 99.5% of theoretical density, a visible light transmittance at or higher than 45% at 560 nm, and a strength of at least 800 MPa.

Abstract: The invention relates to multi-layer oxide ceramic bodies and in particular to presintered multi-layer oxide ceramic blanks and oxide ceramic green bodies suitable for dental applications. These bodies can be thermally densified by further sintering without distortion and are thus particularly suitable for the manufacture of dental restorations. The invention also relates to a process for the manufacture of such multi-layer oxide ceramic bodies as well as to a process for the manufacture of dental restorations using the multi-layer oxide ceramic bodies.

Abstract: Zirconia dental ceramics exhibiting opalescence and having a grain size in the range of 10 nm to 300 nm, a density of at least 99.5% of theoretical density, a visible light transmittance at or higher than 45% at 560 nm, and a strength of at least 800 MPa.

Abstract: Zirconia dental ceramics exhibiting opalescence and having a grain size in the range of 10 nm to 300 nm, a density of at least 99.5% of theoretical density, a visible light transmittance at or higher than 45% at 560 nm, and a strength of at least 800 MPa.

Abstract: Inhibitors of carbonic anhydrase-II derived from sulfanilamide are reported.

Abstract: One embodiment of the invention relates to treating diseases associated with increased urease enzyme activity comprising administering an effective amount of a compound selected from a group consisting of 28 thiazoles Schiff bases. Kinetic studies were performed on ten (10) of the most active compounds.

Abstract: The invention relates to multi-layer oxide ceramic bodies and in particular to presintered multi-layer oxide ceramic blanks and oxide ceramic green bodies suitable for dental applications. These bodies can be thermally densified by further sintering without distortion and are thus particularly suitable for the manufacture of dental restorations. The invention also relates to a process for the manufacture of such multi-layer oxide ceramic bodies as well as to a process for the manufacture of dental restorations using the multi-layer oxide ceramic bodies.

Abstract: Zirconia dental ceramics exhibiting opalescence and having a grain size in the range of 10 nm to 300 nm, a density of at least 99.5% of theoretical density, a visible light transmittance at or higher than 45% at 560 nm, and a strength of at least 800 MPa.

Abstract: One embodiment of the invention relates to treating diseases associated with increased urease enzyme activity comprising administering an effective amount of a compound selected from a group consisting of 28 thiazoles Schiff bases. Kinetic studies were performed on ten (10) of the most active compounds.

Abstract: A set of blocks, for playing a game comprises a plurality of blocks, each block having one characteristic selected from the first category and one characteristic selected from the second category. At least some of the characteristics in the first category are different from one another and at least some of the characteristics in the second category are different from one another. Categories can include a degree of abstraction and may include shape, size, colour, texture, weight and surface finish. The blocks can be provided with a game board and a die, for playing a game or for diagnosis. The blocks can be used for play, and for diagnosis of children with autism or other individuals with other neurological disorders.

Abstract: A dental article includes yttria stabilized tetragonal zirconia polycrystalline ceramic, and no more than about 0.15 wt. % of one or more coloring agents of one or more of: Fe, Er, Co, Pr, Tb, Cr, Nd, Ce, V, Eu, Ho, Ni, and Cu, oxides thereof, and combinations thereof, whereby the dental article is provided with a color corresponding to a natural tooth shade; and wherein the dental article has a flexural strength of at least about 800 MPa. Corresponding methods are also described.

Abstract: A dental article includes yttria stabilized tetragonal zirconia polycrystalline ceramic, and no more than about 0.15 wt. % of one or more coloring agents of one or more of: Pr, Tb, Cr, Nd, Co, oxides thereof, and combinations thereof, whereby the dental article is provided with a color corresponding to a natural tooth shade; and wherein the dental article has a flexural strength of at least about 800 MPa. Corresponding methods are also described.

Abstract: A dental article includes yttria stabilized tetragonal zirconia polycrystalline ceramic, and no more than about 0.15 wt. % of one or more coloring agents of one or more of: Pr, Tb, Cr, Nd, Co, oxides thereof, and combinations thereof, whereby the dental article is provided with a color corresponding to a natural tooth shade; and wherein the dental article has a flexural strength of at least about 800 MPa. Corresponding methods are also described.

Abstract: A dental article includes yttria stabilized tetragonal zirconia polycrystalline ceramic, and no more than about 0.15 wt. % of one or more coloring agents of one or more of: Pr, Tb, Cr, Nd, Co, oxides thereof, and combinations thereof, whereby the dental article is provided with a color corresponding to a natural tooth shade; and wherein the dental article has a flexural strength of at least about 800 MPa. Corresponding methods are also described.

Abstract: A step-down sucking method is provided for minimizing the weaning stress of newborn calves. The method features feeding newborn calves with a sufficient amount of milk corresponding to 15-25% of body weight for 3-5 weeks following birth, and then with a stepwise decreased amount of milk corresponding finally to 8-15% of body weight for 3-7 days, with the differential amount replaced with water and then with gradually decreased amounts of milk from 8-15% to zero % of the body weight and with solid feedstuffs for a period from 5 weeks to 6-8 weeks after birth, thereby inducing the calves to maximally take solid feedstuff with minimal weaning stress.

Abstract: A step-down sucking method is provided for minimizing the weaning stress of newborn calves. The method features feeding newborn calves with a sufficient amount of milk corresponding to 15-25% of body weight for 3˜5 weeks following birth, and then with a stepwise decreased amount of milk corresponding finally to 8-15% of body weight for 3-7 days, with the differential amount replaced with water and then with gradually decreased amounts of milk from 8-15% to zero % of the body weight and with solid feedstuffs for a period from 5 weeks to 6-8 weeks after birth. In the method, suckling with a large amount of milk (amounting to 15-25% of body weight) is conducted for 25-35 days after birth, followed by suckling with a decreased amount of milk (amounting to 8-15% of body weight) for 10-20 days, thereby inducing the calves to maximally take solid feedstuff with minimal weaning stress.

Abstract: Methods of forming a colored ceramic body or dental article are described that include: (a) forming a body from a ceramic-containing powder; (b) shaping the body into a desired shape; and (c) firing the shaped body in an atmosphere comprising at least one coloring agent. Methods of forming a fully dense ceramic body that lacks discoloration, are also described which include: (a) forming a body from a ceramic-containing powder; (b) shaping the body into a desired shape; (c) placing the shaped body in a firing atmosphere containing at least one impurity that promote discoloration of the ceramic body; (d) placing the ceramic body in proximity to an atmosphere powder; and (e) firing the shaped body in proximity to an atmosphere powder; wherein the atmosphere powder acts as at least one of a barrier and a getter for the at least one impurity.

Abstract: Methods of forming a colored ceramic body or dental article are described that include: (a) forming a body from a ceramic-containing powder; (b) shaping the body into a desired shape; and (c) firing the shaped body in an atmosphere comprising at least one coloring agent. Methods of forming a fully dense ceramic body that lacks discoloration, are also described which include: (a) forming a body from a ceramic-containing powder; (b) shaping the body into a desired shape; (c) placing the shaped body in a firing atmosphere containing at least one impurity that promote discoloration of the ceramic body; (d) placing the ceramic body in proximity to an atmosphere powder; and (e) firing the shaped body in proximity to an atmosphere powder; wherein the atmosphere powder acts as at least one of a barrier and a getter for the at least one impurity.