Abstract: A thermoplastic elastomer exhibiting scarce tendency of depositing gummy crust around the extrusion die upon extrusion molding articles therefrom and a superior oil-resistance, which comprises (A) a crystalline polyolefin resin and (B) a cross-linked rubber component produced by a specific melt-kneading technique and which has a certain high level of gel content, a high oil-resistance and a certain reduced rate of deposition of gummy crust on the extrusion die.

Abstract: This invention relates to a method for manufacturing an olefinic thermoplastic elastomer composition, characterized by disposing specific kneading segment at least at one place of the screw on the occasion of manufacturing an olefinic thermoplastic elastomer composition comprising a polyolefin resin and a crosslinked rubber by dynamic crosslinking with a twin screw extruder.

Abstract: The present invention relates to a laminate comprising an olefinic thermoplastic elastomer which comprises: (a) a substratum layer comprising an olefinic thermoplastic elastomer composition (A) having the following characteristics {circle around (1)} to {circle around (3)}: {circle around (1)} 9≦Y−0.43X≦27  (1)  wherein X denotes the JIS A-hardness value (a dimensionless value) of the olefinic thermoplastic elastomer composition determined according to the prescription of JIS K6301 and Y represents the compression set value (expressed by %) of the olefinic thermoplastic elastomer composition determined according to the prescription of JIS K6301 under a condition of 70° C.

Abstract: The present invention relates to an olefinic thermoplastic elastomer composition obtainable by dynamically heat treating 5 to 50 parts by weight of a polypropylene resin (A) and 50 to 95 parts by weight of an &agr;-olefinic copolymer (B) having a Mooney viscosity ML1+4 (100° C.) of 60 to 250 in the absence of a crosslinking agent.

Abstract: An olefin thermoplastic elastomer composition comprises a crystalline polyolefin resin (A) and an ethylene/&agr;-olefin/nonconjugated polyene copolymer rubber (B), and optionally a softener (C) and/or an inorganic filler (D), in a specific ratio. The copolymer rubber (B) is prepared by the use of a metallocene catalyst and comprises ethylene, an &agr;-olefin of 3 to 20 carbon atoms and a nonconjugated polyene. This composition ca provide molded products of more excellent tensile strength, elongation at break, elastomeric properties (elongation set, permanent compression set, etc.), heat resistance and low-temperature properties than the conventional non-crosslinked olefin thermoplastic elastomers, even if the composition is in the non-crosslinked form. The composition in the partially or completely crosslinked form can provided molded products of more excellent low-temperature properties, tensile strength, elongation at break and elastomeric properties than the conventional vulcanized rubbers.

Abstract: An olefin thermoplastic elastomer composition which is superior in the resistance to oils, heat resistance, formability and flexibility is provided, said elestomer composition comprising the components 1 (A) 40-90 parts by weight of a polypropylene resin having a melt flow rate (determined at 230° C. under a load of 2.16 kg according to ASTM D 1238) of 0.

Abstract: The olefin thermoplastic elastomer of the invention has an islands-sea structure, in which the average particle diameter of the islands phases is not more than 2 &mgr;m, and has a gel fraction ranging from 0.5 to 15% by weight and a quantity of heat of melt at a temperature of 125° C. or below, as measured in a different scanning calorimeter (DSC), of 40% or more of the total quantity of heat of melt. The olefin thermoplastic elastomer can be obtained by melt blending in the presence of a crosslinking agent of a specific amount a blend that contains specific amounts of: a high density polyethylene having a density of 0.940 g/cm3 or more, or a crystalline ethylene polymer having a crystallinity determined by a DSC method of 10% or more and a density of less than 0.940 g/cm3, an ethylene/&agr;-olefin(/non-conjugated polyene) copolymer rubber comprising ethylene, an &agr;-olefin of 3 to 20 carbon atoms and optionally a non-conjugated polyene, and a polypropylene.

Abstract: There is provided an oil filter capable of preliminarily confirming a correct assembling of a valve body to a holder and preventing the valve body from being abnormally assembled.

Abstract: The resin composition for a skin member according to the present invention comprises a completely or partially crosslinked olefin thermoplastic elastomer (A) in an amount of 100 parts by weight, an organopolysiloxane (B) having a viscosity (JIS K2283, 25° C.) of not less than 1×106 cSt, preferably 1×106 to 1×108 cSt in an amount of 2 to 20 parts by weight, an organopolysiloxane (C) having a viscosity (JIS K2283, 25° C.) of not less than 10 cSt and less than 1×106 cSt in an amount of 0.5 to 5 parts by weight, and optionally, a polyolefin resin (D) in an amount of 5 to 150 parts by weight and/or a fluoropolymer (E) in an amount of 0.5 to 10 parts by weight. The other resin composition for a skin member according to the invention comprises a completely or partially crosslinked olefin thermoplastic elastomer (A) in an amount of 100 parts by weight, a fluoropolymer (E) in an amount of 0.

Abstract: The foamed laminate based on olefin according to the present invention is composed of a substrate layer of a foamed body made of either an ethylenic thermoplastic elastomer comprising a polyethylene resin and an ethylene/&agr;-olefin copolymer having a Mooney viscosity ML1+4 (100° C.) of 90-250 and an ethylene content of 70-95 mole % or an ethylenic thermoplastic elastomer composition comprising 100 parts by weight of an olefinic thermoplastic elastomer and 1-20 parts by weight of an olefinic thermoplastic resin and, under lamination thereon, a skin layer made of either an ultrahigh molecular weight polyolefin resin having an intrinsic viscosity of 3.5-8.3 dl/g or made of an olefinic thermoplastic elastomer composition comprising an olefinic thermoplastic elastomer and a lubricant.

Abstract: This invention relates to a method for manufacturing an olefinic thermoplastic elastomer composition, characterized by disposing specific kneading segment at least at one place of the screw on the occasion composition manufacturing an olefinic thermoplastic elastomer composition comprising a polyolefin resin and a crosslinked rubber by dynamic crosslinking with a twin screw extruder.

Abstract: The present invention relates to an olefinic thermoplastic elastomer composition which comprises a crystalline polyolefin resin (A), an ethylene-&agr;-olefin-non-conjugated polyene copolymer rubber (B) and at least on rubber (C) selected from polyisobutylene, butyl rubber and a propylene-ethylene copolymer rubber having a propylene content of 50 mol % or more or an ethylene-&agr;-olefin copolymer (D) having a density of 0.870 to 0.

Abstract: A hydrogen storage material which is an AB5 type hydrogen storage alloy having a CaCu5 type crystal structure represented by general formula: MmNiaMnbAlcCod wherein Mm denotes a misch metal, 4.0<a≦4.3, 0.25≦b≦0.4, 0.25≦c≦0.4, 0.3≦d≦0.5, and 5.05≦a+b+c+d≦5.25, or general formula: MmNiaMnbAlcCodXe wherein Mm denotes a misch metal, X is Cu and/or Fe, 4.0<a≦4.3, 0.25≦b≦0.4, 0.25≦c≦0.4, 0.3≦d≦0.5, 0<e≦0.1, and 5.05≦a+b+c+d+e≦5.25, characterized in that the lattice length on the c-axis is 404.9 pm to 405.8 pm.

Abstract: An trim material for the interior of an automobile obtained by successive injection molding. The trim comprises a surface layer and a base layer. The surface layer is formed from a composition comprising: (A) a partially cross-linked thermoplastic elastomer comprising a polypropylene resin and an &agr;-olefin copolymer rubber, and (B) a polybutylene-1 resin. The base layer is formed of a polypropylene resin or a blend of polypropylene resin and an organic filler. The interior trim material is lightweight, is easily recycled, and generates no hazardous gas when incinerated.

Abstract: A process is provided for the production of expanded olefinic thermoplastic elastomer product having good external appearance, flexibility and heat resistance. This process features using, as raw materials, a particular olefinic thermoplastic elastomer and carbon dioxide as a blowing agent.

Abstract: This invention relates to a perfectly or partially crosslinked olefinic thermoplastic elastomer composition which comprises 10 to 90 parts by weight of a crystalline polyolefin (a), 90 to 10 parts by weight of an olefin-based copolymer rubber (b) (the total amount of the components (a) and (b) being 100 parts by weight) and 3 to 100 parts by weight of a paraffinic mineral oil softening agent (c) having an evaporation loss of 0.4% by weight or less at a condition of 200° C., atmospheric pressure and 1 hour and having a kinetic viscosity (40° C.

Abstract: A thermoplastic elastomer based on olefin which can be produced simply by melt-kneading 5-60% by weight of a polyethylene resin (A) together with 40-95% by weight of an ethylene/&agr;-olefin copolymer (B) with optional subsidiary component(s) before the kneaded mass is molded into a formed product, the said elastomer being capable of recycling for reclamation and exhibiting the following characteristics {circle around (1)} to {circle around (3)} namnely, 9≦Y−0.43 X≦27  (1) {circle around (1)} in which X denotes the JIS A-hardness value (a dimensionless value) of the thermoplastic elastomer based on olefin determined according to the prescription of JIS K 6301 and Y represents the permanent compressive strain value (expressed by %) of the thermoplastic elastomer based on olefin determined according to the prescription of JIS K 6301 under a condition of 70° C.

Abstract: A glass run channel comprising a glass run channel body composed of a bottom wall and side walls extending from two opposite edges of the bottom wall, the glass run channel body having a substantially U-shaped section and provided with a groove, and tonguelike draining parts protruding from vicinities of distal edges of the side walls toward the bottom wall of the glass run channel body so as to become proximate to each other. Each of the tonguelike draining parts has a window glass contact part composed of a surface to be brought into contact with a window glass, which comprises a layer of a thermoplastic elastomer and a layer of an ultrahigh molecular weight polyolefin composition. The layer of ultrahigh molecular weight polyolefin composition is arranged so as to contact a window glass. The ultrahigh molecular weight polyolefin composition comprises at least a polyolefin (composition) having a specified intrinsic viscosity and an olefinic thermoplastic elastomer.

Abstract: A method for treating surfaces of titanium or titanium alloys which includes the steps of applying a treatment for removing surface adhesion substances from the surface and then forming a transparent protective layer on the surface.

Abstract: A foamed pad material for low-pressure compression molding which comprises a crosslinked rubbery olefinic soft resin foam and exhibits (a) a hysteresis loss of not greater than 40%, (b) a gel fraction of 20 to 98%, and (c) a density of 0.025 to 0.30 g/cm.sup.3. This foamed pad material is excellent in heat weldability with core forming materials and exhibits excellent heat resistance, strain resistance, moldability and restoring properties at the time of low-pressure compression molding at which compression and drawing are carried out at high temperatures. Moreover, the foamed pad material can allow the molded skin material to have cushioning properties with high flexibility and further to have improved feeling.