Abstract: The polishing pad is useful for polishing at least one of magnetic, optical and semiconductor substrates. The polishing pad includes a polishing layer having a polyurethane window. The polyurethane window has a cross-linked structure formed with an aliphatic or cycloaliphatic isocyanate and a polyol in a prepolymer mixture. The prepolymer mixture is reacted with a chain extender having OH or NH2 groups and having an OH or NH2 to unreacted NCO stoichiometry less than 95%. The polyurethane window has a time dependent strain less than or equal to 0.02% when measured with a constant axial tensile load of 1 kPa at a constant temperature of 60° C. at 140 minutes, a Shore D hardness of 45 to 90 and an optical double pass transmission of at least 15% at a wavelength of 400 nm for a sample thickness of 1.3 mm.

Abstract: A chemical mechanical polishing pad is provided, comprising: a polishing layer having a polishing surface; and, a light stable polymeric endpoint detection window, comprising: a polyurethane reaction product of an aromatic polyamine containing amine moieties and an isocyanate terminated prepolymer polyol containing unreacted —NCO moieties; and, a light stabilizer component comprising at least one of a UV absorber and a hindered amine light stabilizer; wherein the aromatic polyamine and the isocyanate terminated prepolymer polyol are provided at an amine moiety to unreacted —NCO moiety stoichiometric ratio of <95%; wherein the light stable polymeric endpoint detection window exhibits a time dependent strain of ?0.02% when measured with a constant axial tensile load of 1 kPa at a constant temperature of 60° C. at 100 minutes and an optical double pass transmission of ?15% at a wavelength of 380 nm for a window thickness of 1.

Abstract: A chemical mechanical polishing pad is provided, comprising: a polishing layer having a polishing surface; and, a light stable polymeric endpoint detection window, comprising: a polyurethane reaction product of an aromatic polyamine containing amine moieties and an isocyanate terminated prepolymer polyol containing unreacted —NCO moieties; and, a light stabilizer component comprising at least one of a UV absorber and a hindered amine light stabilizer; wherein the aromatic polyamine and the isocyanate terminated prepolymer polyol are provided at an amine moiety to unreacted —NCO moiety stoichiometric ratio of <95%; wherein the light stable polymeric endpoint detection window exhibits a time dependent strain of ?0.02% when measured with a constant axial tensile load of 1 kPa at a constant temperature of 60° C. at 100 minutes and an optical double pass transmission of ?15% at a wavelength of 380 nm for a window thickness of 1.

Abstract: The polishing pad is useful for polishing at least one of magnetic, optical and semiconductor substrates. The polishing pad includes a polishing layer having a polyurethane window. The polyurethane window has a cross-linked structure formed with an aliphatic or cycloaliphatic isocyanate and a polyol in a prepolymer mixture. The prepolymer mixture is reacted with a chain extender having OH or NH2 groups and having an OH or NH2 to unreacted NCO stoichiometry less than 95%. The polyurethane window has a time dependent strain less than or equal to 0.02% when measured with a constant axial tensile load of 1 kPa at a constant temperature of 60° C. at 140 minutes, a Shore D hardness of 45 to 90 and an optical double pass transmission of at least 15% at a wavelength of 400 nm for a sample thickness of 1.3 mm.

Abstract: There is provided a multistage polymer that comprises (a) at least one soft polymer having glass transition temperature of 40° C. or lower, and (b) at least one hard polymer having glass transition temperature higher than 40° C., wherein the glass transition temperature of said hard polymer is at least 10° C. higher than the glass transition temperature of said soft polymer, wherein the weight ratio of said hard polymer to said soft polymer is from 1.01:1 to 100:1, and wherein said multistage polymer, after exposure to liquid water followed by drying at temperatures below 100° C., shows maximum thermal transition temperature in an atmosphere of 0% relative humidity that differs by 20° C. or less from the maximum thermal transition temperature in an atmosphere of 75% relative humidity.

Abstract: Protective film forming compositions useful as medical films and other related wound care and treatment articles, including liquid bandages are prepared from emulsion polymers, including a polymer blend including at least one hard emulsion polymer component and at least one soft emulsion polymer component, having the required dynamic storage modulus and mean Tg of the hard and soft polymer blend components.