Abstract: The present disclosure provides a method of preparing a composition of a cold setting geo-polymer based building material. The cold-setting geo-polymer concrete is a green concrete that requires curing at ambient conditions. The method includes mixing one or more aggregates and a plurality of chemical ingredients in a mixing apparatus, and chemically activating an obtained geo-polymer concrete mix by adding an alkaline activator. The one or more aggregates include a plurality of stone chips and a plurality of sand particles. The plurality of chemical ingredients includes a fly ash and a calcium hydroxide solution. The fly ash includes one or more alumino-silicate aggregates. The fly ash, the plurality of sand particles and the calcium hydroxide solution, and the plurality of stone chips are mixed in a first pre-determined ratio. The alkaline activator prevents temperature curing of the cold-setting geo-polymer concrete.

Abstract: The present invention provides a process for cold briquetting and pelletization of ferrous or non-ferrous or mineral fines using iron bearing hydraulic mineral binders for metallurgical applications, said process consisting the steps of: mixing 80-95% by Wt. of a metallurgical/mineral/carbonaceous/oil contaminated dust/fines/sludge with 3-10% by Wt. of an iron bearing hydraulic mineral binder and optionally with 2-6% by Wt. water and 0.05 to 0.20% by Wt. of a surface active agent to form a homogenized dry mix/slurry, pelletizing/compacting the dry mix/slurry to form an agglomerated mass, and curing the agglomerated mass for 3-20 days by exposing the agglomerated mass to atmospheric air for 10-14 hours followed by moisture treatment.

Abstract: The present invention describes a process for manufacture of high iron hydraulic cement clinker in production of cement and cementation binder for application in construction activity and in metallurgical industry for sintering of iron ore fines and making cold bonded briquettes and pellets. The process is cost effective and flexible for utilization of wide varieties of raw material consisting of lime and iron in production of high iron cements for different applications.

Abstract: The present invention provides a process for cold briquetting and pelletization of ferrous or non-ferrous or mineral fines using iron bearing hydraulic mineral binders for metallurgical applications, said process consisting the steps of: mixing 80-95% by Wt. of a metallurgical/mineral/carbonaceous/oil contaminated dust/fines/sludge with 3-10% by Wt. of an iron bearing hydraulic mineral binder and optionally with 2-6% by Wt. water and 0.05 to 0.20% by Wt. of a surface active agent to form a homogenized dry mix/slurry, pelletizing/compacting the dry mix/slurry to form an agglomerated mass, and curing the agglomerated mass for 3-20 days by exposing the agglomerated mass to atmospheric air for 10-14 hours followed by moisture treatment.

Abstract: The present invention describes a process for manufacture of high iron hydraulic cement clinker in production of cement and cementation binder for application in construction activity andin metallurgical industry for sintering of iron ore fines and making cold bonded briquettes and pellets. The process is cost effective and flexible for utilization of wide varieties of raw material consisting of lime and iron in production of high iron cements for different application.

Abstract: The invention relates to a process for the stabilisation of soluble chromium in contaminated solids by down draft sintering by mixing chromium contaminated solids with different proportions of CaO, MgO, Al2O3, SiO2, SO4 and solid carbon bearing waste materials to maintain the desired ratio of CaO/SiO2, SiO2/Al2O3+Fe2O3 and SO3/Cr in the mixture. The Cr(VI) and chromates are converted into non-leachable compounds.