Abstract: A process for the production of high density hydration resistant sintered lime which comprises washing limestone having impurities of less than 2% to remove external impurities, crushing the washed limestone to a size of 25 mm or below, calcining the limestone at a temperature in the range of 1000 to 1150° C. for a period in the range of 2 to 3 hours to form a calcined mass, hydrating the calcined mass, drying the hydrated mass by known methods, deagglomerating the dried hydrated mass with 1 to 4 weight percent of an additive selected from the group consisting of a transition metal oxide capable of forming a low melting compound, a rare earth metal oxide capable of forming a solid solution, and mixtures thereof, pelletizing the resultant mixture at a pressure of at least 1000 Kg/lcm2, sintering the pellets at a temperature In the range of 1500° C. to 1650° C. for a period In the range of 24 hours and allowing the resultant sintered pellets to cool.