Abstract: Spheroidal polyester polymer particles, as well as preforms and stretch blow molded bottles made from the spheroidal particles, are provided which have: A) an It.V. of at least 0.72 dL/g, and either B) at least two melting peaks (on a DSC first heating scan), wherein one of said at least two melting peaks is a low peak melting point having a peak temperature within a range of 140° C. to 220° C.

Abstract: In one embodiment of the present invention, spheroidal polyester polymer particles, as well as articles such as films, sheets, tubes, and the like made from the spheroidal particles, are provided. According to various embodiments of the invention, the particles may have an intrinsic viscosity (It.V.) of at least 0.65 dL/g and a degree of crystallinity less than about 45 percent. In another embodiment, the polyester polymer can comprise at least 4 mole percent and no more than 20 mole percent of residues other than ethylene glycol residues.

Abstract: This invention relates to a polyester/polyamide blend having an excellent gas barrier property. More particularly, the present invention relates to combinations of a polyethylene terephthalate polymer and a polyamide polymer having an excellent gas barrier property and short oxygen scavenging induction periods, where the polyamide polymer has a C:A terminal group concentration ratio of 2:1 or more and a C+A terminal group concentration of at least 0.17 meq/g of polyamide polymer, wherein C represents a cumulative total of a terminal carboxyl group concentration and a terminal hydrocarbyl group concentration expressed in meq/g of polyamide, and A represents a terminal amine group concentration expressed in meq/g of polyamide.

Abstract: This invention relates to a polyester/polyamide blend having an excellent gas barrier property. More particularly, the present invention relates to combinations of a polyethylene terephthalate polymer and a polyamide polymer having an excellent gas barrier property and short oxygen scavenging induction periods, where the polyamide polymer has a C:A terminal group concentration ratio of 2:1 or more and a C+A terminal group concentration of at least 0.17 meq/g of polyamide polymer, wherein C represents a cumulative total of a terminal carboxyl group concentration and a terminal hydrocarbyl group concentration expressed in meq/g of polyamide, and A represents a terminal amine group concentration expressed in meq/g of polyamide.

Abstract: A solid concentrate is provided having a combination of a transition metal present in an amount ranging from 1000 to 40,000 ppm (weight by metal) and a polyester polymer present in an amount of at least 40 wt. % based on the weight of the concentrate. Concentrates made with highly modified polyester polymers are easy to compound with transition metals forming less brittle polymer upon melt extrusion. Bottle preforms and oxygen scavenging bottles can be made from these concentrates by combining solid polyester particles, solid polyamide particles, and solid these concentrate particles c into an melt processing zone, forming a melt, and forming an article directly from the melt. The b* color and the L* color and the haze levels of the preforms are improved over the preforms made with liquid carriers instead of solid concentrates.

Abstract: A process for coextrusion-molding a multilayer article comprising coextruding at a selected coextuding temperature (i) a first outer polymer resin layer having a) a viscosity, b) a melting temperature, and c) a degradation temperature at the selected coextuding temperature, and (ii) a second inner polymer resin layer having a) a viscosity, b) a melting temperature, and c) a degradation temperature at the selected coextuding temperature, wherein the ratio of the outer polymer resin viscosity to the inner polymer resin viscosity at the coextuding temperature is less than or equal to about 1 and the coextuding temperature is above the melting temperature of the highest melting resin and below the degradation temperature of the lowest degrading resin to form a multilayer article.

Abstract: A process for coinjection-molding a multilayer article comprising coinjecting at a selected coinjecting temperature (i) a first outer polymer resin layer having a viscosity at the selected coinjecting temperature, and (ii) a second inner polymer resin layer having a viscosity at the selected coinjecting temperature, wherein the ratio of the outer polymer resin viscosity to the inner polymer resin viscosity at the coinjecting temperature is less than or equal to about 2 and the coinjecting temperature is above the melting temperature of the highest melting resin and below the degradation temperature of the lowest degrading resin to form a multilayer article. Processes for coextrusion are also provided.