Abstract: A method of producing the low glare, high print gloss paper of the invention comprises the steps of providing a paper substrate, coating the substrate with an aqueous coating composition having, as a dry parts by weight per 100 parts of pigment, 50-90 parts coarse delaminated clay pigment having a particle size of 8-12 microns and 10-20 parts calcium carbonate having a particle size of between 0.7 and 1.1 microns, drying the coating; and supercalendering the coated substrate with at least two passes per side with rolls having a surface roughness of 90-130 Ra. The step of supercalendering imparts a Parker Print-Surf roughness of 1.7-2.2 microns and a sheet gloss of about 25-30. Four color printing produces a print gloss of 65-70 and a delta gloss of at least 38.

Abstract: A method of producing the low glare, high print gloss paper of the invention comprises the steps of providing a paper substrate, coating the substrate with an aqueous coating composition having, as a dry parts by weight per 100 parts of pigment, 50-90 parts coarse delaminated clay pigment having a particle size of 8-12 microns and 10-20 parts calcium carbonate having a particle size of between 0.7 and 1.1 microns, drying the coating; and supercalendering the coated substrate with at least two passes per side with rolls having a surface roughness of 90-130 Ra. The step of supercalendering imparts a Parker Print-Surf roughness of 1.7-2.2 microns and a sheet gloss of about 25-30. Four color printing produces a print gloss of 65-70 and a delta gloss of at least 38.

Abstract: A method of producing the low glare, high print gloss paper of the invention comprises the steps of providing a paper substrate, coating the substrate with an aqueous coating composition having, as a dry parts by weight per 100 parts of pigment, 50-90 parts coarse delaminated clay pigment having a particle size of 8-12 microns and 10-20 parts calcium carbonate having a particle size of between 0.7 and 1.1 microns, drying the coating; and supercalendering the coated substrate with at least two passes per side with rolls having a surface roughness of 90-130 Ra. The step of supercalendering imparts a Parker Print-Surf roughness of 1.7-2.2 microns and a sheet gloss of about 25-30. Four color printing produces a print gloss of 65-70 and a delta gloss of at least 38.

Abstract: A method and apparatus are disclosed for making a high bulk, coated paper of a unique structure with the coating forming a lower portion of the total caliper and the paper base forming a higher portion of the total caliper than conventionally made coated paper of the same weight. The process includes the step of using furnish with a high percentage of mechanical pulp, applying that furnish to papermachine wires, preferably with a gap former, coating the paper with a coating containing a plastic pigment, preferably of 4 or more parts per 100 parts of coating pigment, and calendering the coated paper at a nip loading less than conventional supercalendering nip loading. Preferably, the finished coated paper will have a 75° TAPPI gloss of 40 or above. The method and apparatus can be used to make lightweight or other weights of coated paper.

Abstract: A method and apparatus are disclosed for making a high bulk, coated paper of a unique structure with the coating forming a lower portion of the total caliper and the paper base forming a higher portion of the total caliper than conventionally made coated paper of the same weight. The process includes the step of using furnish with a high percentage of mechanical pulp, applying that furnish to papermachine wires, preferably with a gap former, coating the paper with a coating containing a plastic pigment, preferably of 4 or more parts per 100 parts of coating pigment, and calendering the coated paper at a nip loading less than conventional supercalendering nip loading. Preferably, the finished coated paper will have a 75° TAPPI gloss of 40 or above. The method and apparatus can be used to make lightweight or other weights of coated paper.