Abstract: The laser diode is based on Al In Ga N alloy and consists of: a bottom cladding layer of n-type conductivity, a bottom waveguide layer of n-type conductivity, a light emitting layer, an electron blocking layer of p-type conductivity, an upper waveguide layer of p-type conductivity, an upper cladding layer of p-type conductivity and a subcontact layer, doped with acceptors with concentration level above 1020 cm?3. The diode characterizes in that its bottom cladding layer (1) of n-type is made of GaOxN1-x alloy in which x>0.0005. A method of fabricated such laser diode in epitaxial growth of a layer structure consisting of at least a bottom cladding layer of n-type conductivity comprising at least one GaOxN1-x layer (1, 1a, 1c) in which x>0.0005, consisting in that the GaOxN1-x layer (1a, 1c) is fabricated using a high pressure method of nitride solution in gallium at pressure higher than 800 MPa.

Abstract: The method of fabrication of highly resistive GaN bulk crystals by crystallization from the solution of atomic nitrogen in the molten mixture of metals, containing gallium in the concentration not lower than 90 at. % and the Periodic Table group II metals: calcium, beryllium or in the concentration of 0.01-10 at. %, at the temperature 1300-1700° C., under the nitrogen pressure 0.5-2.0 GPa and in the presence of temperature gradient characterized by the temperature gradient not higher than 10° C./cm.