Abstract: A capacitor comprising an aluminum anode and a dielectric layer comprising phosphate doped aluminum oxide and process for making the capacitor. The capacitor has a CV Product of at least 9 ?F?V/cm2 at 250 volts. Furthermore, the capacitor is formed by the process of: forming an aluminum plate; contacting the plate with an anodizing solution comprising glycerine, 0.1 to 1.0%, by weight, water and 0.01 to 0.5%, by weight, orthophosphate; applying a voltage to the aluminum plate and determining an initial current; maintaining the first voltage until a first measured current is no more than 50% of the initial current; increasing the voltage and redetermining the initial current; maintaining the increased voltage until a second measured current is no more than 50% of the redetermined initial current, and continuing the increasing of the voltage and maintaining the increased voltage until a final voltage is achieved.

Abstract: An electrolyte solution for anodizing a metal and a capacitor comprising the anodized metal. The electrolyte comprises more than about 5%, by weight, and less than about 30%, by weight, water; about 0.1 to 20%, by weight, ionogen and an aprotic polar solvent. The ionogen comprises phosphoric acid and an alkanol amine in an amount, and ratio, sufficient to maintain a pH of about 4 to about 9.

Abstract: A capacitor comprising an aluminum anode and a dielectric layer comprising phosphate doped aluminum oxide and process for making the capacitor. The capacitor has a CV Product of at least 9 ?F?V/cm2 at 250 volts. Furthermore, the capacitor is formed by the process of: forming an aluminum plate; contacting the plate with an anodizing solution comprising glycerine, 0.1 to 1.0%, by weight, water and 0.01 to 0.5%, by weight, orthophosphate; applying a voltage to the aluminum plate and determining an initial current; maintaining the first voltage until a first measured current is no more than 50% of the initial current; increasing the voltage and redetermining the initial current; maintaining the increased voltage until a second measured current is no more than 50% of the redetermined initial current, and continuing the increasing of the voltage and maintaining the increased voltage until a final voltage is achieved.

Abstract: A therapeutic medical device system comprising an electrolytic capacitor including an anode, cathode and an electrolyte. The anode is anodized in an electrolyte comprises an aqueous solution of alkanol amine, phosphoric acid and an organic solvent preferably defined by formula 1: CH3—(OCH2CH2)m—OCH3 ??Formula 1 wherein m is an integer from 3 to 10.

Abstract: An anodizing solution, and method of anodizing, comprising suspending at least one aluminium substrate in an anodizing solution and applying an anodizing current to the anodizing solution. The anodizing solution comprises 0.01-5%, by weight, sodium silicate and 0.01-5%, by weight, ?-amino acid.

Abstract: A capacitor comprising an aluminum anode and a dielectric layer comprising phosphate doped aluminum oxide and process for making the capacitor. Furthermore, the capacitor is formed by the process of: forming an aluminum plate; pre-hydrating the aluminum; contacting the plate with an anodizing solution comprising glycerine, 0.1 to 1.0%, by weight, water and 0.01 to 0.5%, by weight, orthophosphate; applying a voltage to the aluminum plate and determining an initial current; maintaining the first voltage until a first measured current is no more than 50% of the initial current; increasing the voltage and redetermining the initial current; maintaining the increased voltage until a second measured current is no more than 50% of the redetermined initial current, and continuing the increasing of the voltage and maintaining the increased voltage until a final voltage is achieved.

Abstract: An electrolyte solution for anodizing a metal and a capacitor comprising the anodized metal. The electrolyte comprises more than about 5%, by weight, and less than about 30%, by weight, water; about 0.1 to 20%, by weight, ionogen and an aprotic polar solvent. The ionogen comprises phosphoric acid and an alkanol amine in an amount, and ratio, sufficient to maintain a pH of about 4 to about 9.

Abstract: A method of protecting surface mount capacitors from moisture and oxygen corrosion by applying a thermally curable pre-coat resin to a portion of the terminals of a capacitor and encapsulating the capacitor element(s) with a protective resin. The pre-coat resin is substantially rigid at ambient temperatures and flexible at elevated temperatures and is preferably a lactone-containing epoxy resin. The pre-coat resin may be applied to a solder coating-free portion of the terminals by brush or wiper prior to encapsulating the capacitor element(s) with the protective resin.

Abstract: A capacitor comprising an aluminum anode and a dielectric layer comprising phosphate doped aluminum oxide and process for making the capacitor. The capacitor has a CV Product of at least 9 ?F-V/cm2 at 250 volts. Furthermore, the capacitor is formed by the process of: forming an aluminum plate; contacting the plate with an anodizing solution comprising glycerine, 0.1 to 1.0%, by weight, water and 0.01 to 0.5%, by weight, orthophosphate; applying a voltage to the aluminum plate and determining an initial current; maintaining the first voltage until a first measured current is no more than 50% of the initial current; increasing the voltage and redetermining the initial current; maintaining the increased voltage until a second measured current is no more than 50% of the redetermined initial current, and continuing the increasing of the voltage and maintaining the increased voltage until a final voltage is achieved.

Abstract: The metal oxide surface coating of an anodized valve metal may be made conductive under certain conditions so that conductive coatings can be electrolytically deposited on the surface of the oxide. When a dry polar aprotic electrolyte solution is used at a reduced temperature and a relatively high field is applied, the oxide ceases to be insulative. The process is reversible, meaning that there is no permanent change in the oxide.

Abstract: An electrolytic capacitor comprising an anode, cathode and an electrolyte. The electrolyte comprises an aqueous solution comprising a compound of formula 1: CH3—(OCH2CH2)m—OCH3Formula 1 wherein m is an integer from 3 to 10. The electrolyte also comprises an ionogen.

Abstract: An electrolytic capacitor comprising an anode, cathode and an electrolyte. The electrolyte comprises: about 35-60%, by weight water; about 10-55%, by weight organic solvent; about 0.05 to 10%, by weight, sulphuric acid; about 0.05 to 10%, by weight, boric acid; and about 0.05 to 10%, by weight, phosphorus oxy acid.

Abstract: Non-aqueous electrolytic solutions suitable for anodizing valve metal derivative anodes, methods of anodizing using non-aqueous electrolytic solutions, and capacitors prepared with non-aqueous electrolytic solutions. The non-aqueous electrolytic solution comprises glycerine and at least one soluble salt formed by the neutralization of at least one non-halogen-containing organic or inorganic acid anion with at least one alkali metal, ammonium, or protonated amine cation; wherein the acid anion is derived from an acid having a pKa lower than phosphoric acid.

Abstract: An electrolyte for a capacitor and capacitor containing the electrolyte. The electrolyte has up to about 85%, by weight, water, up to about 65%, by weight organic solvent and an acid defined by HOOC—(CH2)x—COOH wherein x is 3, 5, 7 or 9, and ammonium hydroxide.

Abstract: An electrolytic capacitor comprising an anode, cathode and an electrolyte. The electrolyte comprises: about 35-60%, by weight water; about 10-55%, by weight organic solvent; about 0.05 to 10%, by weight, sulphuric acid; about 0.05 to 10%, by weight, boric acid; and about 0.05 to 10%, by weight, phosphorus oxy acid.

Abstract: A method of protecting surface mount capacitors from moisture and oxygen corrosion by applying a thermally curable pre-coat resin to a portion of the terminals of a capacitor and encapsulating the capacitor element(s) with a protective resin. The pre-coat resin is substantially rigid at ambient temperatures and flexible at elevated temperatures and is preferably a lactone-containing epoxy resin. The pre-coat resin may be applied to a solder coating-free portion of the terminals by brush or wiper prior to encapsulating the capacitor element(s) with the protective resin.

Abstract: An electrolyte solution for anodizing a metal and a capacitor comprising the anodized metal. The electrolyte comprises more than about 5%, by weight, and less than about 30%, by weight, water; about 0.1 to 20%, by weight, ionogen and an aprotic polar solvent. The ionogen comprises phosphoric acid and an alkanol amine in an amount, and ratio, sufficient to maintain a pH of about 4 to about 9.

Abstract: An electrolyte for a capacitor and capacitor containing the electrolyte. The electrolyte has up to about 85%, by weight, water, up to about 65%, by weight organic solvent and an acid defined by HOOC—(CH2)x—COOH wherein x is 3, 5, 7 or 9, and ammonium hydroxide.

Abstract: An electrolytic capacitor comprising an anode, cathode and an electrolyte.

Abstract: An electrolytic capacitor comprising an anode, cathode and an electrolyte. The electrolyte comprises: about 35-60%, by weight water; about 10-55%, by weight organic solvent; about 0.05 to 10%, by weight, sulphuric acid; about 0.05 to 10%, by weight, boric acid; and about 0.05 to 10%, by weight, phosphorus oxy acid.