Abstract: Disclosed is a semi-hardened pressure sensitive adhesive film to be used in the semi-hardened state and having excellent printing step absorption properties. The adhesive film according to the present invention contains a radial polymer composition and a cationic polymer composition, and the radial polymer composition is primarily cross-linked to maintain the semi-hardened state. When applied onto a substrate through a printing step, the present invention has excellent step absorption properties and adhesion properties and excellent durability even under high-temperature and high-humidity conditions.

Abstract: A high-refractive adhesive film includes: a thermosetting resin matrix; and high refractive particles dispersed in the thermosetting resin matrix. The refraction index of the high-refractive particles is higher than that of the thermosetting resin matrix.

Abstract: Disclosed is a semi-hardened pressure sensitive adhesive film to be used in the semi-hardened state and having excellent printing step absorption properties. The adhesive film according to the present invention contains a radial polymer composition and a cationic polymer composition, and the radial polymer composition is primarily cross-linked to maintain the semi-hardened state. When applied onto a substrate through a printing step, the present invention has excellent step absorption properties and adhesion properties and excellent durability even under high-temperature and high-humidity conditions.

Abstract: The present invention provides an optical adhesive sheet including a layered structure of a first adhesive layer and a second adhesive layer, in which the first adhesive layer has a glass transition temperature of ?50° C. to ?30° C. and a modulus of 0.3×105 Pa to about 0.6×105 Pa, and the second adhesive layer has a glass transition temperature of ?20° C. to ?10° C. and a modulus of 0.7×105 Pa to 1.0×105 Pa.

Abstract: Provided are an adhesive bonding composition for optical use and a multistage curing method thereof, the composition including a methacrylate-based monomer and an acrylate-based monomer, in which a weight ratio of the methacrylate-based monomer to the acrylate-based monomer ranges from about 1:1 to about 1:10.

Abstract: Provided is an adhesive composition including: a (meth)acrylic acid ester-based photo-curable resin; and an oxygen-free di-functional diene-based rubber hardener.

Abstract: The present invention relates to an optical adhesive film including plate-type inorganic nanoparticles and a curable resin. The optical adhesive film has improved barrier characteristics to moisture and gas, improved light-transmittance, and excellent durability and peel characteristics.

Abstract: Provided is a urethane adhesive composition for a touch panel having a glass transition temperature between ?20° C. to ?50° C., and which, as a cured composition, has an elasticity of 50,000 Pa to 70,000 Pa at 60° C. to 80° C.

Abstract: Provided are an adhesive composition for a touch panel, including: a hydrophilic functional group-containing monomer and an adhesion promoter, wherein a dielectric constant at a frequency of 100 kHz to 2 MHz is 3.5 or less, and a storage modulus is 1.0×105 Pa to 7.0×105 Pa at 25° C. to 85° C., and an adhesive film including an adhesive layer including a cured product of the adhesive composition for a touch panel. In addition, provided is a touch panel including: a conductive plastic film having a conductive layer formed on one surface; and an adhesive layer attached onto the conductive layer and including a cured product of the adhesive composition for a touch panel.

Abstract: Disclosed is a semi-hardened pressure sensitive adhesive film to be used in the semi-hardened state and having excellent printing step absorption properties. The adhesive film according to the present invention contains a radial polymer composition and a cationic polymer composition, and the radial polymer composition is primarily cross-linked to maintain the semi-hardened state. When applied onto a substrate through a printing step, the present invention has excellent step absorption properties and adhesion properties and excellent durability even under high-temperature and high-humidity conditions.

Abstract: The present invention relates to an optical adhesive film which has excellent adhesive strength at room temperature and has improved efficiency in a rework process since peel strength is low at high temperatures. When attaching a touchscreen panel and an LCD by using the adhesive film of the present invention and separating the touchscreen panel and the LCD at high temperatures, the touchscreen panel and the LCD can be separated from each other without causing damage thereto. Additionally, the optical film of the present invention comprises two adhesive layers, wherein peeling occurs at the first adhesive layer having an adhesive composition such that a peeling surface can be controlled according to the convenience of a user.

Abstract: Provided are an adhesive bonding composition for optical use and a multistage curing method thereof, the composition including a methacrylate-based monomer and an acrylate-based monomer, in which a weight ratio of the methacrylate-based monomer to the acrylate-based monomer ranges from about 1:1 to about 1:10.

Abstract: Provided is an adhesive composition including: a (meth)acrylic acid ester-based photo-curable resin; and an oxygen-free di-functional diene-based rubber hardener.

Abstract: The present invention provides an optical adhesive sheet including a layered structure of a first adhesive layer and a second adhesive layer, in which the first adhesive layer has a glass transition temperature of ?50° C. to ?30° C. and a modulus of 0.3×105 Pa to about 0.6×105 Pa, and the second adhesive layer has a glass transition temperature of ?20° C. to ?10° C. and a modulus of 0.7×105 Pa to 1.0×105 Pa.

Abstract: A high-refractive adhesive film includes: a thermosetting resin matrix; and high refractive particles dispersed in the thermosetting resin matrix. The refraction index of the high-refractive particles is higher than that of the thermosetting resin matrix.

Abstract: Provided are an adhesive composition for a touch panel, including: a hydrophilic functional group-containing monomer, wherein a dielectric constant at a frequency of 100 kHz to 2 MHz is 3.5 or less, and an adhesive film having an adhesive layer including a cured product of the adhesive composition for a touch panel. In addition, provided is a touch panel including: a conductive plastic film having a conductive layer formed on one surface; and an adhesive layer attached onto the conductive layer and including a cured product of the adhesive composition for a touch panel.

Abstract: The present invention relates to an optical adhesive film including plate-type inorganic nanoparticles and a curable resin. The optical adhesive film has improved barrier characteristics to moisture and gas, improved light-transmittance, and excellent durability and peel characteristics.

Abstract: Provided are an adhesive composition for a touch panel, including: a hydrophilic functional group-containing monomer and an adhesion promoter, wherein a dielectric constant at a frequency of 100 kHz to 2 MHz is 3.5 or less, and a storage modulus is 1.0×105 Pa to 7.0×105 Pa at 25° C. to 85° C., and an adhesive film including an adhesive layer including a cured product of the adhesive composition for a touch panel. In addition, provided is a touch panel including: a conductive plastic film having a conductive layer formed on one surface; and an adhesive layer attached onto the conductive layer and including a cured product of the adhesive composition for a touch panel.

Abstract: Provided is a laminate comprising a composite first adhesive layer in which a printed portion is embedded within an adhesive portion. The laminate can solve the bending phenomenon caused by raised parts, have a reduced thickness, allow manufacturing thereof due to a simplified process, and remedy problems arising from faulty lamination.

Abstract: Provided is a urethane adhesive composition for a touch panel having a glass transition temperature between ?20° C. to ?50° C., and which, as a cured composition, has an elasticity of 50,000 Pa to 70,000 Pa at 60° C. to 80° C.