Abstract: The present invention provides titania particles which are formed by providing a titania sol and spray drying the titania sol. A morphology of the dried titania particles is controlled by producing the titania sol from a TiO2 containing slurry and controlling the pH of the slurry to be 3 pH units or more from the iso-electric point of the titania by adding a peptizing agent to reduce an extent to which the titania sol is flocculated, or by producing the titania sol from a TiO2 containing slurry and adjusting the iso-electric point to be 3 pH units or more from the pH of the slurry by adding a dispersant to reduce an extent to which the titania sol is flocculated. The titania particles have a continuous exterior convex surface, a diameter of 30 ?m or less, a BET specific surface area of 50 m2/g or more, and are porous.

Abstract: The present invention provides a coating composition suitable for use in forming a coating that can reduce a concentration of pollutant gases in the environment. The coating composition includes from 0.01 to 10 vol.-% of mesoporous titania particles, relative to a total volume of the coating composition, and from 5 to 99.99 vol.-% of a polymeric material, relative to the total volume of the coating composition. The mesoporous titania particles have a continuous exterior convex surface, a particle diameter of ?1 ?m but ? to 50 ?m, a BET specific surface area of from 30 to 350 m2/g, a modal pore diameter of ?5 nm but ?50 nm, and a pore size distribution so that 85% or more of a total pore volume is associated with pores having a diameter of 10 ?m or less.

Abstract: The present invention provides titania particles which are formed by providing a titania sol and spray drying the titania sol. A morphology of the dried titania particles is controlled by producing the titania sol from a TiO2 containing slurry and controlling the pH of the slurry to be 3 pH units or more from the iso-electric point of the titania by adding a peptizing agent to reduce an extent to which the titania sol is flocculated, or by producing the titania sol from a TiO2 containing slurry and adjusting the iso-electric point to be 3 pH units or more from the pH of the slurry by adding a dispersant to reduce an extent to which the titania sol is flocculated. The titania particles have a continuous exterior convex surface, a diameter of 30 ?m or less, a BET specific surface area of 50 m2/g or more, and are porous.

Abstract: The invention provides a process for the production of titania particles with a desired morphology. The process comprises providing a titania sol and then drying the sol to provide dried titania particles. The process is characterized in that the morphology of the dried titania particles is controlled by applying one or more of the following criteria: (a) the titania sol is produced from a TiO2 containing slurry obtained using a precipitation step in a sulphate process, wherein the size of micelles formed during the precipitation is controlled; (b) the titania sol is produced from a TiO2 containing slurry and the pH of the slurry is controlled in order to affect the extent to which the titania sol is flocculated; (c) the titania sol is produced from a TiO2 containing slurry and the iso-electric point of the titania is adjusted in order to affect the extent to which the titania sol is flocculated; (d) the titania sol is dried by application of heat and the temperature used during the drying step is controlled.

Abstract: The invention provides a process for the production of titania particles with a desired morphology. The process comprises providing a titania sol and then drying the sol to provide dried titania particles. The process is characterised in that the morphology of the dried titania particles is controlled by applying one or more of the following criteria: (a) the titania sol is produced from a TiO2 containing slurry obtained using a precipitation step in a sulphate process, wherein the size of micelles formed during the precipitation is controlled; (b) the titania sol is produced from a TiO2 containing slurry and the pH of the slurry is controlled in order to affect the extent to which the titania sol is flocculated; (c) the titania sol is produced from a TiO2 containing slurry and the iso-electric point of the titania is adjusted in order to affect the extent to which the titania sol is flocculated; (d) the titania sol is dried by application of heat and the temperature used during the drying step is controlled.