Abstract: Applicants have discovered that low pullout strength of optical fiber is attributable to volatile, unreacted monomers and impurities which result from the incomplete polymerization of liquid coating materials. They have further discovered that removing these unreacted liquids as by heating in air, heating in vacuum or by application of a solvent mixture improves fiber coating adhesion. By heating cured polymer-coated fiber in air at temperatures of 100.degree. C. or more, the fiber pullout strength is enhanced by 25% or more. This postcure heating can advantageously be clone off-line by placing loosely wound fiber in a heated oven. Alternatively, the postcure heating can be done on-line by reel-to-reel passage of the fiber through a heated furnace. Preferred temperatures are in the range 100.degree. C.-300.degree. C. Even greater enhancement of pullout strength can be effected by heating in vacuum or by solvent extraction.

Abstract: Optical fiber and cable performance are assured by a category of UV-cured polyurethane acrylates. Low cost is the consequence of use of the polycarbonate oligomer. Good performance and long life are ascribed to other ingredients of the coatings. Dependence on the hindered phenols for antioxidant protection assures sufficient protection for these inherently stable materials without incurring fiber damage found to result from use of hindered amine antioxidants.

Abstract: A silica-based optical fiber is provided, which has improved resistance to static fatigue. The fiber includes an outer layer of modified, fused silica which contains zirconia and, optionally, alumina.