Abstract: A macroporous-structured polymeric aerogel, and methods for making and using the same, having a polymeric matrix that includes macropores is disclosed.

Abstract: Thermally treated aerogel compositions that include polyamic amides in an amount less than the aerogel compositions that include polyamic amides prior to thermal treatment, and articles of manufacture that include or are manufactured from the aerogel compositions are described.

Abstract: An aerogel that includes an open-cell structured polymer matrix is disclosed. The aerogel includes 5 wt. % to 50 wt. % of a polyamic amide polymer, based on the total weight of the aerogel, pores and at least 90% of the pore volume of the aerogel is made up of macropores, a porosity of at least 50%, as measure according to ASTM D4404-10, a density of 0.01 g/cm3 to 0.5 g/cm3, and the aerogel is thermally stable to resist browning at 330° C.

Abstract: An aerogel that includes an open-cell structured polymer matrix that can have 5 wt. % to 50 wt. % of a polyamic amide polymer, based on the total weight of the aerogel is disclosed. The aerogel can have a density of 0.05 g/cm3 to 0.35 g/cm3 and can be thermally stable to resist browning at 330° C.

Abstract: Thermally treated aerogel compositions that include polyamic amides in an amount less than the aerogel compositions that include polyamic amides prior to thermal treatment, and articles of manufacture that include or are manufactured from the aerogel compositions are described.

Abstract: Aerogel filled polymeric composites, methods of making and uses thereof are described. A polymeric composite material can include a continuous polymeric matrix and a discontinuous phase that includes a plurality of polymeric aerogel particles dispersed within the continuous polymeric matrix.

Abstract: Thermally treated aerogel compositions that include polyamic amides in an amount less than the aerogel compositions that include polyamic amides prior to thermal treatment, and articles of manufacture that include or are manufactured from the aerogel compositions are described.

Abstract: Thermally treated aerogel compositions that include polyamic amides in an amount less than the aerogel compositions that include polyamic amides prior to thermal treatment, and articles of manufacture that include or are manufactured from the aerogel compositions are described.

Abstract: Disclosed is a method for producing an organic polymer aerogel and corresponding aerogels and articles of manufacture comprising such aerogels. The method can include polymerizing an organic polymerizable material in the presence of an organic solvent having a high vapor pressure and/or a low boiling point to obtain an organic polymer gel comprising an organic polymer matrix and the organic solvent, and subcritical or ambient drying the organic polymer gel under conditions suitable to remove the step (a) organic solvent and form an organic polymer aerogel.

Abstract: An aerogel that includes an open-cell structured polymer matrix that can have 5 wt. % to 50 wt. % of a polyamic amide polymer, based on the total weight of the aerogel is disclosed. The aerogel can have a density of 0.05 g/cm3 to 0.35 g/cm3 and can be thermally stable to resist browning at 330° C.

Abstract: A macroporous-structured polymeric aerogel, and methods for making and using the same, having a polymeric matrix that includes macropores is disclosed.

Abstract: An aerogel comprising an open-cell structured polymer matrix that includes a polyamic amide polymer is described.

Abstract: A method of making an aerogel is described. The method can include obtaining a solution comprising polyamic acid and an imidazole, adding a dehydrating agent to the solution in an amount where the molar ratio of the imidazole to the dehydrating agent is 0.17:1 to 2.8:1 and reacting the solution at room temperature to 100° C. to produce a polymer matrix gel comprising a polyamic amide, and drying the polymer matrix gel to form an aerogel comprising an open-cell structured polymer matrix that includes 5 wt. % to 50 wt. % of the polyamic amide based on the total weight of the polymer aerogel.

Abstract: A method of making an aerogel is described. The method can include obtaining a solution comprising polyamic acid and an imidazole, adding a dehydrating agent to the solution in an amount where the molar ratio of the imidazole to the dehydrating agent is 0.17:1 to 2.8:1 and reacting the solution at room temperature to 100° C. to produce a polymer matrix gel comprising a polyamic amide, and drying the polymer matrix gel to form an aerogel comprising an open-cell structured polymer matrix that includes 5 wt. % to 50 wt. % of the polyamic amide based on the total weight of the polymer aerogel.

Abstract: An aerogel comprising an open-cell structured polymer matrix that includes a polyamic amide polymer is described.

Abstract: Aerogel compositions that include polyamic amides, methods for preparing the aerogel compositions, and articles of manufacture that include or manufactured from the aerogel compositions are described.

Abstract: Aerogel compositions that include polyamic amides, methods for preparing the aerogel compositions, and articles of manufacture that include or manufactured from the aerogel compositions are described.

Abstract: An apparatus for making and using a fastener suitable for use in airplane manufacture or repair that is coated with a pre-mixed moisture cure sealant. The sealant layer is coated with a frangible moisture barrier that will break apart when the fastener is installed, thus exposing the sealant to a moisture source. Once exposed to moisture, the sealant will begin to cure. Preferred embodiments also provide a premature cure indicator that provides a visual indication that the outer moisture resistant layer has been damaged.

Abstract: An apparatus for making and using a fastener suitable for use in airplane manufacture or repair that is coated with a pre-mixed moisture cure sealant. The sealant layer is coated with a frangible moisture barrier that will break apart when the fastener is installed, thus exposing the sealant to a moisture source. Once exposed to moisture, the sealant will begin to cure. Preferred embodiments also provide a premature cure indicator that provides a visual indication that the outer moisture resistant layer has been damaged.

Abstract: A synthesis of a new pyrazole-containing monomer by means of an easily implemented two-step process. This monomer can be electropolymerized to yield a stable n-doping polymer that may easily be electrochemically characterized. It is demonstrated that the electrochemical behavior of the polymer films produced is dependent upon the conditions applied during electrodeposition. Films deposited by cycling only at relatively positive potentials (0 to 2000 mV) show less intense n-doping responses than those films obtained by scanning the applied potential throughout a wider range (?2000 mV to 2000 mV).