Abstract: Electrical insulation which has good dielectric strength, good radiation resistance, and good thermal resistance at temperatures of up to 500.degree. C. and, preferably up to 1700.degree. C., includes a substrate which is flexible, has the form of a filament, sheet, wrapper, tape or sleeve, and consists essentially of inorganic materials selected from the group consisting of inorganic fibers and metals, metalloids, or alloys; and at least one layer of at least one oxide of an alkoxide-forming element provided on the substrate to impregnate and/or coat same. The insulation is prepared by a process including applying a solution containing an alkoxy gel polymer, optionally additionally containing at least one inorganic material in finely divided form, to the substrate to provide a treated substrate useful as a preform when allowed to set under ambient conditions.

Abstract: A flexible resin adhesive coated substrate is made by: (A) coating a sheet material with a wet, heat reactive adhesive resin, containing a monomer and an amount of an ultraviolet radiation sensitive photoinitiator effective to cause polymerization of monomer in response to ultraviolet radiation, and (B) applying ultraviolet radiation to the adhesive resin coating on the sheet material to polymerize monomer without the application of heat, forming a dry, uncured coating of adhesive bonded to the sheet material.

Abstract: A porous, electrical insulating adhesive substrate is made by (A) electrostatically coating a flexible sheet material with heat reactive adhesive resin particles, having an average particle size of between about 1 micron to 2,000 microns, the adhesive particles are applied in a predetermined pattern on the sheet covering from about 10 percent to 90 percent of the sheet material area, the area between the resin pattern not being coated; and then (B) heating the patterned coated sheet material between about 65.degree. C to 250.degree. C, forming a discontinuous, 0.25 mil to 25 mil (0.006 mm to 0.

Abstract: A porous, electrical insulating adhesive substrate is made by (A) electrostatically coating a flexible sheet material with heat reactive adhesive resin particles, having an average particle size of between about 1 micron to 2,000 microns, the adhesive particles are applied in a predetermined pattern on the sheet covering from about 10 percent to 90 percent of the sheet material area, the area between the resin pattern not being patterned and then (B) heating the patterened coated sheet material between about 65.degree.C to 250.degree.C, forming a discontinuous, 0.25 mil to 25 mil (0.006 mm to 0.