Abstract: A method for producing PHA polymer includes using bacteria in which the bacteria are grown under heterotrophic conditions using an organic substance as carbon source and exponential growth conditions. The bacteria are then cultivated under autotrophic conditions under an atmosphere of H2, CO2 and O2, wherein the O2 content is less than 10% (v/v) and the pressure is more than 1 barg.

Abstract: Polyethylene composition with improved balance of mechanical and optical properties, comprising (all percentages being by weight): A) from 90 to 99.7% of a LLDPE having a density from 0.91 to 0.94 g/cm3 and a ratio MIF/MIE equal to or higher than 20, where MIF is the melt flow index at 190° C. with a load of 21.60 kg, and MIE is the melt flow index at 190° C. with a load of 2.16 kg, both determined according to ISO 1133; B) from 0.3 to 10% of a LDPE having MIE from 0.1 to 0.6 g/10 min.

Abstract: Solid adducts comprising MgCl2, ethanol and water characterized in that the amount of ethanol ranges from 50% to less than 57% by weight, the amount of water is ranges from 0.5 to 5% by weight, the ethanol/water weight ratio is lower than 60 and the porosity determined with Hg method due to pores with radius up to 1 ?m and expressed in cm3/g, is lower than 0.2.

Abstract: A two steps polymerization process for obtaining a polyolefin composition comprising: a) from 25 wt % to 70 wt % of a propylene homopolymer or a propylene-ethylene copolymer containing from 0.1 wt % to 10 wt % of ethylene derived units; b) from 27 wt % to 70 wt % of a copolymer of ethylene and at least one C3-C20 alpha olefins, wherein the ethylene derived units content ranges from 15 wt % to 70 wt %; c) from 3 wt % to 20 wt % of polyethylene homopolymer or an ethylene and at least one C3-C20 alpha olefins copolymer; the sum a)+b)+c) being 100, wherein said process comprises: step a) contacting under polymerization conditions propylene, optionally ethylene and the catalyst system in order to obtain component a), step b) contacting under polymerization conditions ethylene and at least one C3-C20 alpha-olefins and the catalyst system in order to obtain components b) and c); wherein the catalyst system comprises a metallocene compound and an iron complex.

Abstract: Polyolefin compositions suitable for injection molded items e.g. for impact bumpers and car interiors comprising from 30% to 90% by weight of an heterophasic propylene polymer composition (A); and from 10% to 70% by weight of a multimodal ethylene/butene-1 copolymer (B); having density from 0.850 to 0.935 g/cm3, total comonomer content from 6% to 30% by weight, Mw/Mn from 4 to 20; intrinsic viscosity in decalin at 135° C. from 1.0 to 4.0 dL/g, and comprising an HDPE fraction (HDPE % wt) up to 30% wt; further comprising from 0 to 50% by weight of a filler (C) and optionally, in amount up to 10% by weight with respect to the overall composition, an impact modifier masterbatch component D consisting of an ultra-soft heterophasic copolymer component.

Abstract: A polymer filament or fiber comprising a polyethylene material (I) having the following features: a) a density of 0.900 g/cm3 or higher; b) a MI21 value of 25 g/10 min.; c) a MFR value from 25 to 60; the said fiber being stretched by drawing with a draw ratio from 1.5 to 10.

Abstract: A novel gas phase polymerization method is devised, for polymerization of low and ultralow density polyethylene.

Abstract: A novel polyethylene is devised which polyethylene is particularly advantageous for manufacturing rotomoulded articles.

Abstract: Polyethylene composition with improved balance of mechanical and optical properties, comprising (all percentages being by weight): A) from 90 to 99.7% of a LLDPE having a density from 0.91 to 0.94 g/cm3 and a ratio MIF/MIE equal to or higher than 20, where MIF is the melt flow index at 190° C. with a load of 21.60 kg, and MIE is the melt flow index at 190° C. with a load of 2.16 kg, both determined according to ISO 1133; B) from 0.3 to 10% of a LDPE having MIE from 0.1 to 0.6 g/10 min.

Abstract: Solid adducts comprising MgCl2, ethanol and water characterized in that the amount of ethanol ranges from 50% to less than 57% by weight, the amount of water is ranges from 0.5 to 5% by weight, the ethanol/water weight ratio is lower than 60 and the porosity determined with Hg method due to pores with radius up to 1 ?m and expressed in cm3/g, is lower than 0.2.

Abstract: A two steps polymerization process for obtaining a polyolefin composition comprising: a) from 25 wt % to 70 wt % of a propylene homopolymer or a propylene-ethylene copolymer containing from 0.1 wt % to 10 wt % of ethylene derived units; b) from 27 wt % to 70 wt % of a copolymer of ethylene and at least one C3-C20 alpha olefins, wherein the ethylene derived units content ranges from 15 wt % to 70 wt %; c) from 3 wt % to 20 wt % of polyethylene homopolymer or an ethylene and at least one C3-C20 alpha olefins copolymer; the sum a)+b)+c) being 100, wherein said process comprises: step a) contacting under polymerization conditions propylene, optionally ethylene and the catalyst system in order to obtain component a), step b) contacting under polymerization conditions ethylene and at least one C3-C20 alpha-olefins and the catalyst system in order to obtain components b) and c); wherein the catalyst system comprises a metallocene compound and an iron complex.

Abstract: Polyolefin compositions suitable for injection moulded items e.g. for impact bumpers and car interiors comprising from 30% to 90% by weight of an heterophasic propylene polymer composition (A); and from 10% to 70% by weight of a multimodal ethylene/C6-C12 alpha olefin copolymer (B); having density from 0.850 to 0.920 g/cm3, total comonomer content from 6% to 30% by weight, Mw/Mn from 4 to 20; intrinsic viscosity in decalin at 135° C. from 1.0 to 4.0 dL/g, and comprising an HDPE fraction (HDPE % wt) up to 30% wt; further comprising up to 50% by weight of a filler (C) and optionally, in amount up to 10% by weight with respect to the overall composition, an impact modifier masterbatch component (D) consisting of a ultra-soft heterophasic copolymer component.

Abstract: The invention refers to a process for preparing a supported catalyst system for the polymerization of olefins comprising at least one active catalyst component on a support, the process comprising A) impregnating a dry porous support component with a mixture comprising at least one precatalyst, at least one cocatalyst, and a first solvent, such that the total volume of the mixture is from 0.8 to 2.0 times the total pore volume of the support component, and B) thereafter, adding a second solvent in an amount of more than 1.5 times the total pore volume of the support component. The invention refers further to a catalyst system made by this process and the use of this catalyst system for polymerization or copolymerization of olefins.

Abstract: New plastomer material for use in automotive parts such as bumpers is devised here, which is a novel polyethylene produced by a gas phase process.

Abstract: A novel PE material is devised showing excellent mechanical/optical properties and process ability, e.g. for film extrusion. The polyethylene of the invention is produced in one single e.g. gas phase reactor.

Abstract: A multimodal ethylene copolymer having the following properties: i) density comprised in the range from 0.880 to 0.955 g/cm3; ii) total comonomer content ranging from 6% to 25% by weight; iii) content of 1-butene derived units ranging from 0 to 2% by weight; iv) Mw/Mn comprised from 4 to 20; v) intrinsic viscosity (decalin at 135° C. as determined according to EN ISO 1628-312003) comprised between 1.0 and 4.0 dL/g; said multimodal ethylene copolymer comprises from 10% to 80% by weight of a first polyethylene component and being detected at the Crystaf® apparatus at a temperature higher than 75° C. and from 90% to 20% by weight of a second polyethylene component being a copolymer being detected at a Crystaf® apparatus at a temperature lower than 75° C.; wherein said multimodal ethylene copolymer being fractionated into 12 fractions by means of the Holtrup analysis, the fractions containing more than 2% by weight of the total amount of material meet the following relationship: Cf/HDPE>?0.0075HDPE+0.

Abstract: Polyolefin compositions suitable for injection moulded items e.g. for impact bumpers and car interiors comprising from 30% to 90% by weight of an heterophasic propylene polymer composition (A); and from 10% to 70% by weight of a multimodal ethylene/C6-C12 alpha olefin copolymer (B); having density from 0.850 to 0.920 g/cm3, total comonomer content from 6% to 30% by weight, Mw/Mn from 4 to 20; intrinsic viscosity in decalin at 135° C. from 1.0 to 4.0 dL/g, and comprising an HDPE fraction (HDPE % wt) up to 30% wt; further comprising up to 50% by weight of a filler (C) and optionally, in amount up to 10% by weight with respect to the overall composition, an impact modifier masterbatch component (D) consisting of a ultra-soft heterophasic copolymer component.

Abstract: A novel PE material is devised showing excellent mechanical/optical properties and process ability, e.g. for film extrusion. The polyethylene of the invention is produced in one single e.g. gas phase reactor.

Abstract: A polypropylene composition comprising: A) from 30% to 90% by weight of a propylene polymer composition comprising: a1) from 20% to 90% of a propylene homopolymer, or a copolymer of propylene containing 3% or less of derived units of ethylene or C4-C10 ?-olefin(s) or of combinations thereof, said homopolymer or copolymer having a content of isotactic pentads (mmmm), measured by 13C NMR on the fraction insoluble in xylene at 25° C., higher than 96; a2) from 10% to 80%, of a copolymer of ethylene containing from 40% to 70% of derived units of propylene or C4-C10 ?-olefin(s) or of combinations thereof; B) from 10% to 70% by weight of a multimodal ethylene copolymer wherein the comonomer is selected from the derived units of alpha olefins of formula CH2?CHT wherein T is a C3-C10 alkyl group; having the following properties: i) density (with ISO 1183) comprised in the range from 0.850 to 0.

Abstract: A novel polyethylene is devised which polyethylene is particularly advantageous for manufacturing rotomoulded articles.